The purpose of the work presented in this paper is to analyze locally (at the element level) the contact behavior of a soil-pile contact problem. Therefore, a 2D shear test is modeled using the Finite Element Method. The formulation of a 4 nodded zero-thickness interface element of Beer is chosen with a linear interpolation function. Four constitutive contact models adapted for contact problems have been implemented. The Mohr-Coulomb and Clough and Duncan models were chosen initially, due to the ease of implementation and few number of parameters needed. After, more complicated models in the framework of elasto-plasticity such as: Lashkari and Mortara were implemented for the first time into the finite element code of the shear test problem. They include other phenomena such as: relative density of soil, the stress level and sand dilatancy. From the results the relation between shear displacement and shear stress has been deduced. Finally, a discussion of the advantages and the drawbacks during computation of each model is given at the end.
Fatigue is of relevance not only for metals but also for concrete. The current knowledge about fatigue behaviour of concrete is, however, incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Some macroscopic effects of this process are well known but the governing material changes behind them are still less studied. The focus of the present contribution lay on a systematic and comprehensive investigation of the fatigue process under cyclic compressive loading. The aim was to obtain a deeper insight and to provide a better understanding of the damage process in the material. Cylindrical specimens were tested with a number of cycles to failure between 106 and 107. Various methods of non-destructive and destructive testing were used to investigate macroscopic and microscopic changes in the material. One main result was that the changes in the macroscopic material behaviour could not be explained only by the development of micro cracks. The results indicated that the related changes in the fatigue behaviour originate rather from viscous processes in the cement stone, similar to the process of creep. A sound description of the possible processes was derived from the obtained experimental results which concerns material structure during fatigue loading. It has been shown that in case of isotropic material behaviour a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain relationship caused by fatigue.