The discussions on the nanoconfinement effect on the glass transition and glassy dynamics phenomena have yielded many open questions. Here, the thickness dependence of the thermal glass transition temperature of thin films of a PVME/PS blend is investigated by ellipsometry. Its thickness dependence was compared to that of the dynamic glass transition (measured by specific heat spectroscopy), and the deduced Vogel temperature (T0). While and T0 showed a monotonous increase, with decreasing the film thickness, the dynamic glass transition temperature () measured at a finite frequency showed a non-monotonous dependence that peaks at 30 nm. This was discussed by assuming different cooperativity length scales at these temperatures, which have different sensitivities to composition and thickness. This non-monotonous thickness dependence of disappears for frequencies characteristic for T0. Further analysis of the fragility parameter, showed a change in the glassy dynamics from strong to fragile, with decreasing film thickness.
Thermal and dynamic glass transition of ultrathin films of homopolymers and a miscible polymer blend
(2017)
Despite the decade long controversial discussion on the effect of nanometer confinement on the glass transition temperature (Tg) of ultrathin polymer films, there is still no consistent picture. Here, the dynamic calorimetric glass transition of ultrathin films of a blend, which is miscible in the bulk, is directly investigated by specific heat spectroscopy. By a self-assembling process, a nanometer thick surface layer with a higher molecular mobility is formed at the polymer/air interface. By measuring the dynamic calorimetric Tg in dependence on the film thickness, it was shown that the Tg of the whole film was strongly influenced by that nanometer thick surface layer, with a lower Tg. Since the observed thickness dependence of the dynamic Tg is similar to the thickness dependence of the Tg for thin films of homopolymers, it is concluded that also for homopolymer a highly mobile surface layer is relevant for the widely observed Tg depression.