To arrive to sustainable hydrogen-based energy solutions, the understanding of water-splitting catalysts plays the most crucial role. Herein, state-of-the-art hypotheses are combined on electrocatalytic active metal sites toward the oxygen evolution reaction (OER) to develop a highly efficient catalyst based on Earth-abundant cobalt and zinc oxides.
The precursor catalyst Zn0.35Co0.65O is synthesized via a fast microwaveassisted approach at low temperatures. Subsequently, it transforms in situ from the wurtzite structure to the layered γ-Co(O)OH, while most of its zinc leaches out. This material shows outstanding catalytic Performance and stability toward the OER in 1 m KOH (overpotential at 10 mA cm−2 ηinitial = 306 mV, η98 h = 318 mV). By comparing the electrochemical results and ex situ analyses to today’s literature, clear structureactivity correlations are able to be identified. The findings suggest that coordinately unsaturated cobalt octahedra on the surface are indeed the active centers for the OER.
The photocatalytic (PC) performance of titanium dioxide (TiO2) nanoparticles strongly depends on their specific surface, the presence of crystal defects, their crystal phase, and the exposed crystal facets. In order to understand which of these factors contributes most significantly to the PC activity of TiO2 colloids, all of them have to be individually analyzed. This study entails the synthesis of five anatase nanocrystal samples. By maintaining the same reactant ratios as well as hydrothermal sol–gel synthesis route and only varying the autoclaving time or temperature, different crystallite sizes are obtained under comparable experimental conditions. A decrease in PC performance with increase in specific surface area is found. Such an unexpected counterintuitive result establishes the basis for a better understanding of the crucial factors that ultimately determine the PC activity. These are investigated by studying nanocrystals bulk and surface structure and morphology using a selection of complementary analysis methods (X-ray photoelectron spectroscopy (XPS), X-ray absorption fine structure (XAFS), X-ray diffraction (XRD)…). It is found that a change in the nanocrystal morphology from an equilibrium state truncated tetragonal bipyramid to a more elongated rod-like structure accompanied by an increase in oxygen vacancies is responsible for an augmented PC activity of the TiO2 nanocrystals.
Currently great effort is made to find materials and technologies for the recycling of phosphate from wastewater.
Herein, we present an in-depth study of the Phosphate adsorption mechanism of a promising adsorber material, a Zn−Fe−Zr oxyhydroxide-based nanostructured precipitate. The behavior of the multicomponent nanomaterial, consisting of both crystalline and amorphous parts, is investigated via X-ray absorption fine structure spectroscopy and Mössbauer spectroscopy, revealing the importance of the nanostructured composition for the phosphate adsorption. We found evidence that adsorption takes place especially in the vicinity of iron sites in the amorphous part of the material.