In-plane shear behaviour of earthen materials panels strengthened with polyester fabric strips
(2016)
An experimental investigation was carried out to study the in-plane shear behaviour of earthen material Panels strengthened with polyester fabric strips. Strengthened panels were developed to exploit the strength potential of earthen materials and to solve its lack of tensile strength, significantly improving not only strength but also ductility. Three earthen materials were considered: cob, earth block masonry (EBM) and rammed earth (RE). As first approach the strengthening configuration, based on different adhesive materials, was tested only for cob panels. As part of the study the results of a big testing campaign of unstrengthened Panels were considered. Seven strengthened panels were tested in diagonal compression/shear.A unique reinforcement orientation was used. The results of these tests are presented in this paper, and include the load-displacement behaviours, crack patterns, failure modes. The results showed that the reinforcement was the most effective in EBM panels, with increase in strength and ductility observed. In RE and cob panels the reinforcement did not likely contribute significantly to the shear resistance, due to a lack of embedment length of the strips. Instead, in EBM it was likely that the vertical reinforcement acted in tension to restrain shear induced dilation and to restrain sliding.
In-plane shear behaviour of earthen materials panels strengthened with polyester fabric strips
(2016)
An experimental investigation was carried out to study the in-plane shear behaviour of earthen material panels strengthened with polyester fabric strips. Strengthened panels were developed to exploit the strength potential of earthen materials and to solve its lack of tensile strength, significantly improving not only strength but also ductility. Three earthen materials were considered: cob, earth block masonry (EBM) and rammed earth (RE). As first approach the strengthening configuration, based on different adhesive materials, was tested only for cob panels. As part of the study the results of a big testing campaign of unstrengthened Panels were considered. Seven strengthened panels were tested in diagonal compression/shear.A unique reinforcement orientation was used. The results of these tests are presented in this paper, and include the load-displacement behaviours, crack patterns, failure modes. The results showed that the reinforcement was the most effective in EBM panels, with increase in strength and ductility observed. In RE and cob panels the reinforcement did not likely contribute significantly to the shear resistance, due to a lack of embedment length of the strips. Instead, in EBM it was likely that the vertical reinforcement acted in tension to restrain shear induced dilation and to restrain sliding.
To study the mechanical interface behavior of single-walled carbon nanotubes (CNTs) embedded in a noble metal, we performed CNT-metal pull-out tests with in situ scanning electron microscope experiments. Molecular dynamics (MD) simulations were conducted to predict force-displacement data during pull-out, providing critical forces for failure of the system. In MD simulations, we focused on the influence of carboxylic surface functional groups (SFGs) covalently linked to the CNT. Experimentally obtained maximum forces between 10 and 102 nN in palladium and gold matrices and simulated achievable pulling forces agree very well. The dominant failure mode in the experiment is CNT rupture, although several pull-out failures were also observed. We explain the huge scatter of experimental values with varying embedding length and SFG surface density. From simulation, we found that SFGs act as small anchors in the metal matrix and significantly enhance the maximum forces. This interface reinforcement can lead to tensile stresses sufficiently high to initiate CNT rupture. To qualify the existence of carboxylic SFGs on our CNT material, we performed analytical investigation by means of fluorescence labeling of surface species and discuss the results. With this contribution, we focus on a synergy between computational and experimental approaches involving MD simulations, nano scale testing, and analytics (1) to predict to a good degree of accuracy maximum pull-out forces of single-walled CNTs embedded in a noble metal matrix and (2) to provide valuable input to understand the underlying mechanisms of failure with focus on SFGs. This is of fundamental interest for the design of future mechanical sensors incorporating piezoresistive single-walled CNTs as the sensing element.