Nanoparticles (NPs) have become important materials for a variety of chemical technologies, including catalysis. One of the main challenges is the reduction of green house gases, such as CO2. One opportunity besides the capturing is the conversion to synthesis gas via the reverse water-gas shift reaction.
A facile and efficient method is described for the solvothermal synthesis of size-tunable, stable, and uniform NiCu core-shell NPs. The diameter of the NPs can be tuned in a range from 6 nm to 30 nm and the Ni:Cu ratio from 30:1 to 1:1. The NPs are structurally characterized with combination of transmission electron microscopy, anomalous small-angle X-ray scattering, X-ray photoelectron spectroscopy, and X-ray absorption fine structure. Using these analytical methods, a core-shell-shell structure their chemical composition is elucidated. A depletion from the core to the shell is observed, with the core consisting of NiCu alloy, surrounded by an inner Ni-rich shell and an outer NiO shell. The SiO2-supported NiCu core-shell NPs show pronounced selectivity of >99% for CO in the catalytic reduction of CO2 to CO using hydrogen as reactant (reverse water–gas shift reaction).
Upconversion nanoparticles are characterized by their ability to convert low energy near-infrared excitation in high energy emissions in the visible range. This is enabled by sequential absorption of two or more photons via energy transfer from the sensitizer lanthanide ion Yb3+ to an activator lanthanide ion, e.g. Er3+. Yb3+ sensitation has the advantage of 980 nm excitation achieved by commercial available low power cw laser modules.
Nevertheless, for some applications, especially in aqueous media, which is predominantely in bioanalytical applications, there is the drawback of a local Absorption maximum of water at this wavelength. Sample heating can occur, and excitation power density is strongly distance dependent.
To overcome this issue, the idea is to shift the excitation wavelength to 808 nm. This can be achieved by a tandem-excitation using Nd3+ and Yb3+ ions. Nd3+ gets excited by 808 nm irradiation and transfers the energy to Yb3+, which triggers the upconversion emission of the Er3+ ions. Therefore, it is mandatory to separate Nd3+ and Er3+ by core-shell architecture for reducing the energy backtransfer from Er3+ to Nd3+.
To further enhance the upconversion luminescence an additional inert shell formed by the host material NaYF4 reduces the quenching effects caused by surface defects and dangling bonds.