Die Oberflächen nichtrostender Stähle sind durch eine Passivschicht geschützt. Ist diese beschädigt oder unvollständig ausgebildet, sind Anlagenkomponenten in Gefahr, durch Korrosionsangriffe zerstört zu werden.
KorroPads liefern ein valides Prüfergebnis zum Zustand der Passivschicht. Der Schnelltest dauert nur 15 min.
The KorroPad indicator test was invented at the Federal Institute for Materials Research and Testing to detect stainless-steel surfaces susceptible to pitting corrosion. The KorroPad indicator test is thus an interesting alternative for manufacturers, processors, users and researchers to time consuming exposition experiments and complex electrochemical investigations, which are normally used to reveal surface-related processing errors resulting in reduced pitting corrosion resistance. Furthermore, the KorroPad indicator test can be used to visualize alloy- and microstructure-related factors causing susceptibility to pitting corrosion. The detection limit of the KorroPad indicator test was characterized in this work using reference alloys with different chromium content (5 % to 18 %). The alloy-specific detection limit was shifted successfully to higher chromium content by increasing the concentrations of NaCl and K3[Fe(CN)6]. The modified KorroPads can now be used to establish an alloy-specific quality control regarding the pitting corrosion resistance of different stainless steel grades.
Mit der KorroPad-Prüfung können lochkorrosionsanfällige Oberflächenbereiche einfach, schnell und kostengünstig nachgewiesen werden. Das KorroPad ist damit für Hersteller, Verarbeiter, Anwender und Forscher eine interessante Alternative zu zeitintensiven Auslagerungsversuchen und elektrochemischen Untersuchungsmethoden, die normalerweise bei der Charakterisierung nichtrostender Stähle zur Anwendung kommen. Mit der KorroPad-Prüfung können auch werkstoff- und gefügebedingte Einflussfaktoren sichtbar gemacht werden, die Lochkorrosionsanfälligkeit verursachen. Um dies zu veranschaulichen, wird die Nachweisgrenze des KorroPads an Referenzlegierungen mit abgestuftem Chromgehalt aufgezeigt. Darauf aufbauend wird dargestellt, wie die Sensibilisierung nichtrostender Stähle durch Chromverarmung mit einer gezielten Verschärfung der KorroPad-Prüfung nachgewiesen werden kann.
Mit der KorroPad-Prüfung können lochkorrosionsanfällige Oberflächenbereiche einfach, schnell und kostengünstig nachgewiesen werden. Das KorroPad ist damit für Hersteller, Verarbeiter, Anwender und Forscher eine interessante Alternative zu zeitintensiven Auslagerungsversuchen und elektrochemischen Untersuchungsmethoden, die normalerweise bei der Charakterisierung nichtrostender Stähle zur Anwendung kommen. Mit der KorroPad-Prüfung können auch werkstoff- und gefügebedingte Einflussfaktoren sichtbar gemacht werden, die Lochkorrosionsanfälligkeit verursachen. Um dies zu veranschaulichen, wird die Nachweisgrenze des KorroPads an Referenzlegierungen mit abgestuftem Chromgehalt aufgezeigt. Darauf aufbauend wird dargestellt, wie die Sensibilisierung nichtrostender Stähle durch Chromverarmung mit einer gezielten Verschärfung der KorroPad-Prüfung nachgewiesen werden kann.
Mit der KorroPad-Prüfung können lochkorrosionsanfällige Oberflächen einfach, schnell und kostengünstig nachgewiesen werden. Das KorroPad ist damit für Hersteller, Verarbeiter, Anwender und Forscher eine interessante Alternative zu zeitintensiven Auslagerungsversuchen und elektrochemischen Untersuchungsmethoden, die normalerweise bei der Charakterisierung nichtrostender Stähle zur Anwendung kommen. Mit der KorroPad-Prüfung können aber auch werkstoff und gefügebedingte Einflussfaktoren sichtbar gemacht werden, die Lochkorrosionsanfälligkeit verursachen. Um dies zu veranschaulichen, wird die Nachweisgrenze des KorroPads an Referenzlegierungen mit abgestuftem Chromgehalt aufgezeigt.
Darauf aufbauend wird dargestellt, wie die Sensibilisierung nichtrostender Stähle durch Chromverarmung mit einer gezielten Verschärfung der KorroPad-Prüfung nachgewiesen werden kann.
Mit der KorroPad-Prüfung können lochkorrosionsanfällige Oberflächen einfach, schnell und kostengünstig nachgewiesen werden. Das KorroPad ist damit für Hersteller, Verarbeiter, Anwender und Forscher eine interessante Alternative zu zeitintensiven Auslagerungsversuchen und elektrochemischen Untersuchungsmethoden, die normalerweise bei der Charakterisierung nichtrostender Stähle zur Anwendung kommen. Mit der KorroPad-Prüfung können aber auch werkstoff- und gefügebedingte Einflussfaktoren sichtbar gemacht werden, die Lochkorrosionsanfälligkeit verursachen. Um dies zu veranschaulichen, wird die Nachweisgrenze des Korro-Pads an Referenzlegierungen mit abgestuftem Chromgehalt aufgezeigt. Darauf aufbauend wird dargestellt, wie die Sensibilisierung nichtrostender Stähle durch Chromverarmung mit einer gezielten Verschärfung der KorroPad-Prüfung nachgewiesen werden kann.
Ergebnisse aus dem AiF Forschungsvorhaben IGF 18823 N/1 "Optimierung von Korundschleifprozessen"
Ein Referenzwerkstoff mit einem definierten Oberflächenzustand wurde zunächst umfassend mittels elektrochemischer Korrosionsuntersuchungen, KorroPad-Untersuchungen und oberflächenanalytischer Verfahren charakterisiert. Anhand definierter Schleifversuche an diesem Referenzzustand wurden anschließend verschiedene Schleifparameter variiert, deren Auswirkungen auf die Korrosionsbeständigkeit mit den gleichen Methoden beurteilt wurden. Somit war es möglich, den Einfluss einzelner Schleifparameter auf das Korrosionsverhalten aufzuzeigen.
Rohrsysteme und Behälter aus nichtrostendem Stahl sind prinzipiell vor Korrosion geschützt.
Ist die Passivschicht auf der Stahloberfläche jedoch beschädigt, geht dieser Schutz verloren. Das KorroPad-Verfahren ist ein Schnelltest zur Überprüfung der Passivschicht. Die Anwendung ist einfach und dauert nur 15 Minuten.
Quenching and partitioning (Q&P) heat Treatment increases the deformability of high-strength martensitic steels. Therefore, it is necessary to have some metastable austenite in the microstructure, which transforms in martensite during plastic deformation (TRIP effect). The austenitic-martensitic microstructure is gained by an increased austenitization temperature, water quenching and additional partitioning. The partitioning enables local carbon diffusion, which stabilizes retained austenite and leads to partial reversion of martensite to austenite. The influence of partitioning time was studied for the martensitic stainless steel AISI 420 (X46Cr13, 1.4034). In line with these efforts, metallographic, XRD and EBSD measurements were performed to characterize the microstructural evolution. The mechanical properties were tested using tension and compression loading. Additional corrosion investigations showed the benefits of Q&P heat treatment compared to conventional tempering. The reversion of austenite by the partitioning treatment was verified with EBSD and XRD. Furthermore, the results of the mechanical and corrosion testing showed improved properties due to the Q&P heat treatment.
Nickel-free, nitrogen alloyed austenitic stainless-steels, with about 19 wt.-% Mn and 0,8 wt. % N, are an interesting alternative to classic CrNi austenitic stainless steels due to their superior mechanical properties (Rm > 900 MPa, A5 > 50 %, Av > 350 J) in the solution annealed condition. The formation of chromium-rich nitrides during suboptimal heat treatment, processing or application leads to an inhomogeneous distribution of alloying elements in the microstructure, which reduces the corrosion resistance. Consequently, an accurate knowledge of the sensitization behavior is indispensable for the use of nickel-free, high-nitrogen austenitic stainless steels. The relationship between artificial aging, phase formation and corrosion resistance was investigated on the alloys X8CrMnN18-19 (1.3815) and X8CrMnMoN18-19-2 (1.4456), both alloyed with 0,8 wt.-% Nitrogen, in the present work. The microstructural evolution was studied by LM and SEM while the corrosion resistance was characterized with the electrochemical potentiodynamic reactivation (EPR) and the KorroPad indicator-test. Both alloys showed increased corrosion susceptibility within critical aging parameters. Finally, a sensitization diagram was described successfully for both alloys showing the positive effect of molybdenum.
Nickel-free, nitrogen alloyed austenitic stainless-steels, with about 19 wt.-% Mn and 0,8 wt. % N, are an interesting alternative to classic CrNi austenitic stainless steels due to their superior mechanical properties (Rm > 900 MPa, A5 > 50 %, Av > 350 J) in the solution annealed condition. The formation of chromium-rich nitrides during suboptimal heat treatment, processing or application leads to an inhomogeneous distribution of alloying elements in the microstructure, which reduces the corrosion resistance. Consequently, an accurate knowledge of the sensitization behavior is indispensable for the use of nickel-free, high-nitrogen austenitic stainless steels. The relationship between artificial aging, phase formation and corrosion resistance was investigated on the alloys X8CrMnN18-19 (1.3815) and X8CrMnMoN18-19-2 (1.4456), both alloyed with 0,8 wt.-% Nitrogen, in the present work. The microstructural evolution was studied by LM and SEM while the corrosion resistance was characterized with the electrochemical potentiodynamic reactivation (EPR) and the KorroPad indicator-test. Both alloys showed increased corrosion susceptibility within critical aging parameters. Finally, a sensitization diagram was described successfully for both alloys showing the positive effect of molybdenum.
Der Vortrag behandelt die Ergebnisse des gleichnamigen IGF-Forschungsvorhabens Nr. 18823 N/1. Ziel des Vorhabens war die Untersuchung einer möglichen, negativen Beeinflussung der Korrosionsbeständigkeit nichtrostender Stähle nach einer korundbasierten Schleifbearbeitung der Oberflächen. Auf Basis der Erkenntnisse aus dem Vorhaben Regelwerke und technische Merkblätter entstehen, in denen Schleifparameter, Grenzbereiche oder auch notwendige Nacharbeiten fest-gelegt werden, die es den Unternehmen ermöglichen, mit den gegebenen Verfahren und Schleifmitteln unkritisch hinsichtlich der späteren Korrosionsbeständigkeit im Einsatzfall zu schleifen. Dies gilt in besonderem Maße für Korundschleifbänder, die in industriellen Schleifprozessen eine sehr große Bedeutung besitzen.
Durch eine breite Beteiligung von Schleifmittelherstellern, -anwendern und wissenschaftlichen Einrichtungen im projektbegleitenden Ausschuss (PA) konnte der vielschichtige Themenkomplex „Schleifen“ im Kontext zu den Projektzielen umfassend untersucht werden. Es wurden praxisrelevante Parameterfelder definiert, die eine erfolgreiche Aufklärung der Projektfragestellung ermöglichten.
Im Zuge der Untersuchungen wurde ein signifikanter Einfluss beim Einsatz von Granulatschleifbändern auf das Korrosionsverhalten geschliffener Oberflächen festgestellt. Damit zeigten geschliffene Oberflächen regelmäßig eine schlechtere Korrosionsbeständigkeit als Oberflächen, die mit sonst gleichen Parametern mit einlagig gestreuten Bändern bearbeitet wurden.
Die durch einige Untersuchungsergebnisse aus vorangegangenen AiF-Vorhaben ursprünglich verfolgte These, dass Unterschiede in der Korrosionsbeständigkeit auf die Kornart der Schleifmittel Korund bzw. SiC zurückzuführen ist, konnte nur bedingt bestätigt werden. Bei den systematischen Untersuchungen innerhalb dieses Projektes erwies sich der Einfluss der Kornart im Vergleich zum Einfluss des Schleifbandtyps (Granulat bzw. einlagig gestreutes Korn) als weniger relevant.
Durch weiterführende Untersuchungen konnten auf Oberflächen, die mit Granulatschleifbändern bearbeitet wurden, große Materialaufplattungen aus Eigenmaterial festgestellt werden. Das Eigenmaterial wird dabei im Schleifprozess zunächst abgetragen und aufgrund der Topografie des Schleifbandes zeitweise auf den Bändern festgehalten. Später lösen sich diese Materialanhäufungen vom Band ab und können prozessbedingt durch Wärme- und Krafteinwirkung auf den bearbeiteten Oberflächen aufgeplattet werden. Durch REM und KorroPad Untersuchungen ließen sich Bereiche mit solchen Eigenmaterialaufplattungen eindeutig als wesentliche Ausgangspunkte für Korrosionsprozesse identifizieren. Das aufgeplattete Material ist stark verformt, thermisch beeinflusst und bildet eine Spaltgeometrie zur Bauteiloberfläche aus. Diese Veränderungen führen zur Störung der Passivschichtausbildung in diesen Bereichen und verursachen damit eine erhöhte Korrosionsanfälligkeit der Oberflächen.
Durch gezielte Nachbearbeitungsprozesse ist es möglich, die Eigenmaterialaufplattungen von den Oberflächen zu entfernen. Im Rahmen des Vorhabens wurde dazu eine Nachbearbeitung mittels Schleifvlies geprüft, die zu einer Entfernung der Eigenmaterialaufplattungen und damit zu einer Wiederherstellung der erwarteten Korrosionsbeständigkeit führte. Wird der Endschliff von Oberflächen mit einlagig gestreutem Korn ausgeführt, sind ebenfalls keine korrosionsrelevanten Materialaufplattungen zu erwarten.
Die in einem vorhergehenden AiF Vorhaben IGF 17136 N/1 entwickelte Methode der KorroPad-Prüfung konnte auch hier erfolgreich für die Untersuchung der Auswirkung unterschiedlicher Prozessparameter auf die Korrosionsbeständigkeit der Oberflächen eingesetzt werden. Zudem erwies sich das EPR-SL-Verfahren als ein weiterer Ansatz, um die Passivschichtstabilität verschieden geschliffener Oberflächen vergleichend untersuchen zu können.
Mit den nun vorliegenden Erkenntnissen können kmU künftig durch Anpassungen und Optimierung von Schleifprozessen eine gute Korrosionsbeständigkeit der bearbeiteten Oberflächen sicherstellen. Die Optimierung der Prozessparameter und -schritte kann durch den Einsatz der KorroPad-Prüfung Inhouse erfolgen und somit die laufende Fertigung im Rahmen der Qualitätsprüfung überwacht und dokumentiert werden.
In diesem Vortrag werden Ergebnisse des gleichnamigen AiF Forschungsvorhabens gezeigt, die einen deutlichen Einfluss verschiedener Schleifmittel auf die Korrosionsbeständigkeit von damit geschliffenen nichtrostender Stahloberflächen belegen. Es konnten ein signifikanter Einfluss durch die Verwendung von Granulatschleifbändern festgestellt werden, der die Korrosionsbeständigkeit der Oberflächen drastisch reduziert. Grund sind auf der Oberfläche zurückbleibende Materialaufplattungen von Eigenmaterial aus dem Schleifprozess. Es wurden unterschiedliche Korrosionsuntersuchungen durchgeführt und mittels Oberflächenanalytik untermauert.