Changes in the global bulk and local structures, of three different barium compounds (BaZrO3, BaF2, and BaFCl),were induced by mechanical milling and followed using X-ray powder diffraction (PXRD), subsequent microstructure analysis, and 137Ba solid state NMR spectroscopy. Harder materials like BaZrO3 experience significantly higher structural changes upon milling than softer materials like BaF2. Moreover, soft materials with layered structures, like BaFCl, show a pronounced structural change during the milling process. By combining PXRD and solid state NMR, detailed information on the changes to the global and local structures were obtained, which are of interest for mechanochemical synthesis, mechanically treated catalysts or ionic conductors.
This study investigates the mechanochemical reactions between AgBr 3-picolylamine and 4-picolylamine. The use of different stoichiometry ratios of the reagents allows [(AgBr)(n-pica)]n and [(AgBr)2(n-pica)]n to be obtained, and we report the new structures of [(AgBr)2(3-pica)]n and [(AgBr)2(4-pica)]n which are characterized by the presence of the following: (a) infinite inorganic chains, (b) silver atom coordinated only by bromide atoms and (c) argentophilic interactions. Furthermore, we studied the interconversion of [(AgBr)(n-pica)]n/[(AgBr)2(n-pica)]n by mechanochemical and thermal properties. The in situ experiments suggest that [(AgBr)(3-pica)]n is kinetically favoured while [(AgBr)2(3-pica)]n is converted into [(AgBr)(3-pica)]n only with a high excess of the ligand. Finally, the liquid nature of the ligands is not sufficient to assist the grinding process, and the complete reaction is observed with the addition of a small quantity of acetonitrile.
The application of lithium-sulfur (Li-S) batteries is still limited by their rapid capacity fading. The pulverization of the sulfur positive electrode after the lithiation and the consequence dissolution of long chain polysulfides in organic solvents lead to the shuttle effect. To address these issues, here we report the mechanochemical preparation of ZIF-8 (Zeolitic Imidazole Framework-8)-based composites as sulfur hosts for positive electrodes in Li-S batteries. We studied different methods for the incorporation of conductive carbon. Also, the replacement of Zn2+ metal centers by other bivalent metals (Cu2+, Co2+ and Ni2+), enabled the preparation of other ZIF-8-based materials. The positive electrode ZIF-8/C/S8 showed initial discharges of 772 mA h g−1 while the pristine one, ZIF-8/S8, displayed 502 mA h g−1. The enhanced performance of 54% for ZIF-8/C/S8 indicates that the direct mechanochemical synthesis of ZIF-8 with conductive carbon is beneficial at initials charge/discharge process in comparison to traditional slurry preparation (ZIF-8/S8). Also, the Li2S6 absorption tests shows 87% of discoloration with ZIF-8/C/S8, confirming the better polysulfides absorption.
Catalysts derived from pyrolysis of metal organic frameworks (MOFs) are promising candidates to replace expensive and scarce platinum-based electrocatalysts commonly used in polymer electrolyte membrane fuel cells. MOFs contain ordered connections between metal centers and organic ligands. They can be pyrolyzed into metal- and nitrogen-doped carbons, which show electrocatalytic activity toward the oxygen reduction reaction (ORR). Furthermore, metal-free heteroatom-doped carbons, such as N-F-Cs, are known for being active as well. Thus, a carbon material with Co-N-F doping could possibly be even more promising as ORR electrocatalyst. Herein, we report the mechanochemical synthesis of two polymorphs of a zeolitic imidazole framework, Co-doped zinc 2-trifluoromethyl-1H-imidazolate (Zn0.9Co0.1(CF3-Im)2). Time-resolved in situ X-ray diffraction studies of the mechanochemical formation revealed a direct conversion of starting materials to the products. Both polymorphs of Zn0.9Co0.1(CF3-Im)2 were pyrolyzed, yielding Co-N-F containing carbons, which are active toward electrochemical ORR.
The mechanism of mixed-ligand metal–organic framework (MOF) formation, and the possible role of intermediate single-ligand metal complexes during mechanosynthesis, have not been explored yet. For the first time, we report here in situ real-time monitoring of the mechanochemical formation mechanism of mixed-ligand MOFs. Our results show that binary phases can act as intermediates or competing products in one-pot and stepwise synthesis.
Water-stable metal−organic frameworks (MOFs) with proton-conducting behavior have attracted great attention as promising materials for proton-exchange membrane fuel cells. Herein, we report the mechanochemical gram-scale synthesis of three new mixed-ligand phosphonate-based MOFs, {Co(H2PhDPA)(4,4′-bipy)H2O)·2H2O}n (BAM-1), {Fe(H2PhDPA)(4,4′-bipy) (H2O)·2H2O}n (BAM-2), and {Cu(H2PhDPA)(dpe)2(H2O)2·2H2O}n (BAM-3) [where H2PhDPA = phenylene diphosphonate, 4,4′-bipy = 4,4′-bipyridine, and dpe = 1,2-di(4-pyridyl)ethylene]. Single-crystal X-ray diffraction measurements revealed that BAM-1 and BAM-2 are isostructural and possess a three-dimensional (3D) network structure comprising one-dimensional (1D) channels filled with guest water molecules. Instead, BAM-3 displays a 1D network structure extended into a 3D supramolecular structure through hydrogenbonding and π−π interactions. In all three structures, guest water molecules are interconnected with the uncoordinated acidic hydroxyl groups of the phosphonate moieties and coordinated water molecules by means of extended hydrogen-bonding interactions. BAM-1 and BAM-2 showed a gradual increase in proton conductivity with increasing temperature and reached 4.9 × 10−5 and 4.4 × 10−5 S cm−1 at 90 °C and 98% relative humidity (RH). The highest proton conductivity recorded for BAM-3 was 1.4 × 10−5 S cm−1 at 50 °C and 98% RH. Upon further heating, BAM-3 undergoes dehydration followed by a phase transition to another crystalline form which largely affects its performance. All compounds exhibited a proton hopping (Grotthuss model) mechanism, as suggested by their low activation energy.
Crystalline porous materials are recognized as promising proton conductors for the proton exchange membrane (PEM) in fuel cell technology owing to their tunable framework structure. However, it is still a challenging bulk synthesis for real-world applications of these materials. Herein, we report the mechanochemical gram-scale synthesis of two isostructural metal hydrogen-bonded organic frameworks (MHOFs) of Co(II) and Ni(II) based on 1-hydroxyethylidenediphosphonic acid (HEDPH4) with 2,2′-bipyridine (2,2′-bipy): Co(HEDPH3)2(2,2′-bipy)·H2O (1) and Ni(HEDPH3)2(2,2′-bipy)·H2O (2). In situ monitoring of the mechanochemical synthesis using different synchrotron-based techniques revealed a one-step mechanism – the starting materials are directly converted to the product. With the existence of extensive hydrogen bonds with amphiprotic uncoordinated phosphonate hydroxyl and oxygen atoms, both frameworks exhibited proton conduction in the range of 10–4 S cm–1 at room temperature under humid conditions. This study demonstrates the potential of green mechanosynthesis for bulk material preparation of framework-based solid-state proton conductors.
The oxygen reduction reaction (ORR) is a common process in a variety of electrochemical devices, like fuel cells and metal air batteries. The sluggish kinetics of the ORR require an electrocatalyst to pass this bottleneck.[1] Currently, the most used catalytical systems are platinum-based, with several drawbacks, such as the high cost, low availability, and deactivation by CO poisoning.[2] Efforts are made to develop efficient, durable and low cost catalysts to promote the commercialization of fuel cells.
Non-precious metal catalysts are promising candidates for efficient ORR catalysis. It has been shown that pyrolyzing metal organic frameworks (MOFs) under inert conditions yields carbon-rich materials, with evenly distributed metal sites, which possess promising electrocatalytic activity.[3] One widely used type of MOF as ORR catalyst precursors is the zeolitic imidazole framework (ZIF) where metal cations are linked through imidazole-based ligands. Their porous nature is partially retained after carbonization, making MOFs very suitable precursor materials.
Herein we report the mechanochemical synthesis and structural analysis of Co-doped ZIF-8 (Zn), as well as two polymorphs (dense and prorous) of fluorinated Co-doped CF3-ZIF-8 (Zn). The samples showed electrochemical performance comparable to platinum after carbonization for 1 h at temperatures ranging between 850 – 1000°C.
Carbonization of fluorinated metal-organic frameworks (MOFs) should yield fluorinated nitrogen- and metal-doped carbons (F-NMCs), which are a combination of NMCs and fluorinated carbons, each promising electrocatalysts on their own. We synthesized two polymorphs of a fluorinated MOF by mechanical ball mill grinding, and carbonized them to yield potential electrocatalyt materials. The catalytical activity towards the oxygen reduction reaction (ORR) was examined, finding good activites. Simulations from a theoretic model helped assesing the stability of proposed catalytic sites and understanding the measured activites towards the ORR catalysis.
The oxygen reduction reaction (ORR) is a common process in a variety of electrochemical devices, like fuel cells
and metal air batteries. The sluggish kinetics of the ORR require an electrocatalyst to pass this bottleneck.[1]
Currently, the most used catalytical systems are platinum-based, with several drawbacks, such as the high cost,
low availability, and deactivation by CO poisoning.[2] Efforts are made to develop efficient, durable and low cost
catalysts to promote the commercialization of fuel cells.
Non-precious metal catalysts are promising candidates for efficient ORR catalysis. It has been shown that
pyrolyzing metal organic frameworks (MOFs) under inert conditions yields carbon-rich materials, with evenly
distributed metal sites, which possess promising electrocatalytic activity.[3] One widely used type of MOF as ORR
catalyst precursors is the zeolitic imidazole framework (ZIF) where metal cations are linked through imidazolebased ligands.
Herein we report the mechanochemical synthesis, structural analysis and of Co-doped ZIF-8 (Zn), as well as its
fluorinated counterpart Co-doped CF3
-ZIF-8 (Zn). The samples showed electrochemical performance comparable
to platinum after carbonization for 1h at temperatures ranging between 850 – 1000°C.
Mechanochemical transformations offer environmentally benign synthesis routes, whilst enhancing both the speed and selec-tivity of reactions. In this light, mechanochemistry promises to trans-form the way in which chemistry is done in both academia and indus-try but is greatly hindered by a current lack in mechanistic understand-ing. The continued development and use of time-resolved in situ(TRIS) approaches to monitor mechanochemical reactions provides a new dimension to elucidatethese fascinating transformations. We here discuss recent trends in method development that have pushed the boundaries of mechanochemical research. New features of mech-anochemical reactions obtained by TRIS techniques are subse-quently discussed, shedding light on how different TRISapproaches have beenused. Emphasis is placed on the strength of combining complementary techniques. Finally, we outline our views for the po-tential of TRIS methods in mechanochemical research, towards es-tablishing a new, environmentally benign paradigm in the chemical sciences
Mechanochemical reactions are driven by the direct absorption of mechanical energy by a solid (often crystalline) material. Understanding how this energy is absorbed and ultimately causes a chemical transformation is essential for understanding the elementary stages of mechanochemical transformations. Using as a model system the energetic material LiN3 we here consider how vibrational energy flows through the crystal structure. By considering the compression response of the crystalline material we identify the partitioning of energy into an initial vibrational excitation. Subsequent energy flow is based on concepts of phonon–phonon scattering, which we calculate within a quasi-equilibrium model facilitated by phonon scattering data obtained from Density Functional Theory (DFT). Using this model we demonstrate how the moments (picoseconds) immediately following mechanical impact lead to significant thermal excitation of crystalline LiN3, sufficient to drive marked changes in its electronic structure and hence chemical reactivity. This work paves the way towards an ab initio approach to studying elementary processes in mechanochemical reactions involving crystalline solids.
Mechanochemistry has become a sustainable and attractive cost-effective synthetic technique, largely used within the frame of crystal engineering. Cocrystals, namely, crystalline compounds made of different chemical entities within the same crystal structure, are typically synthesized in bulk via mechanochemistry; however, whereas the macroscopic aspects of grinding are becoming clear, the fundamental principles that underlie mechanochemical cocrystallization at the microscopic level remain poorly understood. Time-resolved in situ (TRIS) monitoring approaches have opened the door to exceptional detail regarding mechanochemical reactions. We here report a clear example of cocrystallization between two solid coformers that proceeds through the formation of a metastable low melting binary eutectic phase. The overall cocrystallization process has been monitored by time-resolved in situ (TRIS) synchrotron X-ray powder diffraction with a customized ball milling setup, currently available at μ Spot beamline at BESSY-II, Helmholtz-Zentrum Berlin. The binary system and the low melting eutectic phase were further characterized via DSC, HSM, and VT-XRPD.
The debate on the mechanisms which underpin mechanochemical reactions via ball mill grinding is still open. Our ability to accurately measure the microstructural (crystal size and microstrain) evolution of materials under milling conditions as well as their phase composition as a function of time is key to the in-depth understanding of the kinetics and driving forces of mechanochemical transformations. Furthermore, all ball milling reactions end with a steady state or milling equilibrium – represented by a specific phase composition and relative microstructure – that does not change as long as the milling conditions are maintained. The use of a standard sample is essential to determine the instrumental contribution to the X-ray powder diffraction (XRPD) peak broadening for time-resolved in situ (TRIS) monitoring of mechanochemical reactions under in operando conditions. Using TRIS-XRPD on a ball milling setup, coupled with low-energy synchrotron radiation, we investigated different data acquisition and analysis strategies on a silicon standard powder. The diffraction geometry and the microstructural evolution of the standard itself have been studied to model the instrumental contribution to XRPD peak broadening throughout the grinding activity. Previously proposed functions are here challenged and further developed. Importantly, we show that minor drifts of the jar position do not affect the instrumental resolution function significantly. We here report and discuss the results of such investigations and their application to TRIS-XRPD datasets of inorganic and organic ball mill grinding reactions.
Mechanochemistry has become a valuable tool for the synthesis of new molecules, especially in the field of organic chemistry. In the present work, we investigate the kinetic profile of the chlorination reaction of N-3-ethyl-5,5-dimethylhydantoin (EDMH) activated and driven by ball milling. The reaction has been carried out using 2 mm, 4 mm, 5 mm, 6 mm, and 8 mm ball sizes in a new small custom-made Perspex milling jar. The Crystal structure of the starting material EDMH and the 1-chloro-3-ethyl5,5′-dimethyl hydantoin (CEDMH) chlorination product was solved by single-crystal X-ray diffraction. The reaction was monitored, in situ and in real time, by both powder X-ray diffraction (PXRD) and Raman spectroscopy. Our kinetic data show that the reaction progress to equilibrium is similar at all milling ball sizes. The induction period is very short (between 10 and 40 s) when using 4 mm, 5 mm, 6 mm, and 8 mm balls. For the reaction performed with a 2 mm ball, a significantly longer induction period of 9 min was observed. This could indicate that an initial energy accumulation and higher mixing efficiency are necessary before the reaction starts. Using different kinetic models, we found that the amount of powder affected by critical loading conditions during individual impacts is significantly dependent on the ball size used. An almost linear correlation between the rate of the chemical transformations and the ball volume is observed.
Mechanochemistry offers a unique opportunity to modify and manipulate crystal forms, often providing new products as compared with conventional solution methods. While promising, there is little known about how to control the solid form through mechanochemical means, demanding dedicated investigations. Using a model organic cocrystal system (isonicotinamide:glutaric acid), we here demonstrate that with mechanochemistry, polymorphism can be induced in molecular solids under conditions seemingly different to their conventional thermodynamic (thermal) transition point.
Whereas Form II converts to Form I upon heating to 363 K, the same transition can be initiated under ball milling conditions at markedly lower temperatures (348 K). Our results indicate that mechanochemical techniques can help to reduce the energy barriers to solid form transitions, offering new insights into controlling polymorphic forms. Moreover, our results suggest that the nature of mechanochemical transformations could make it difficult to interpret mechanochemical solid form landscapes using conventional equilibrium-based tools.
Unintended Rate Enhancement in Mechanochemical Kinetics by Using Poly(methyl methacrylate) Jars
(2022)
Time-resolved in situ (TRIS) X-ray diffraction has changed how mechanochemical transformations are studied but requires the use of X-ray transparent jars often made from poly(methyl methacrylate) (PMMA). However, using PMMA jars can alter the apparent kinetics of mechanochemical polymorphism by an order of magnitude, questioning the interpretability of established TRIS methods. Our results suggest that rate enhancement in PMMA jars may not be dominated by chemical effects of the polymer, but rather a result of different equilibrium temperatures within the jar. These features must be better understood before control over mechanochemical reactions can be achieved.
Mechanochemistry provides polymorphs that are difficult to obtain by conventional solution-based methods. Based on the nicotinamide and pimelic acid cocrystal, we demonstrated that the ball size, frequency, and temperature are essential parameters. Our results indicate that fine-tuning the energy input during a mechanochemical reaction can provide control over polymorphism.
Time resolved in situ (TRIS) monitoring has revolutionised the study of mechanochemical transformations but has been limited by available data quality. Here we report how a combination of miniaturised grinding jars together with innovations in X-ray powder diffraction data collection and state-of-the-art analysis strategies transform the power of TRIS synchrotron mechanochemical experiments. Accurate phase compositions, comparable to those obtained by ex situ measurements, can be obtained with small sample loadings. Moreover, microstructural parameters (crystal size and microstrain) can be also determined with high confidence. This strategy applies to all chemistries, is readily implemented, and yields high-quality diffraction data even using a low energy synchrotron source. This offers a direct avenue towards the mechanochemical investigation of reactions comprising scarce, expensive, or toxic compounds. Our strategy is applied to model systems, including inorganic, metal-organic, and organic mechanosyntheses, resolves previously misinterpreted mechanisms in mechanochemical syntheses, and promises broad, new directions for mechanochemical research.
Herein we report the synthesis of a zeolitic imidazolate framework (ZIF-8) by an easy “mix and wait” procedure. In a closed vial, without any interference, the mixture of 2-methylimidazole and basic zinc carbonate assembles into the crystalline product with approx. 90% conversion after 70 h. The reaction exhibits sigmoidal kinetics due to the self-generated water which accelerates the reaction.