Many new technologies are based on applications in extreme conditions, such as at low temperatures or in hydrogen environment. This involves new requirements on material properties, in particular regarding their operability and reliability. To fulfil this demand, the tribological behaviour of PTFE- and PEEK-matrix composites filled with carbon fibres were investigated at cryogenic temperatures and in hydrogen by means of surface analyses. For a better understanding of the tribological behaviour, and because of the temperature-dependent characteristics of polymer materials, thermal and mechanical properties of selected composites were initially investigated at low temperatures. Thermal shock experiments as well as cryo- and hydrogen treatments were carried out. Different coefficients of thermal expansion within the composite lead to debondings of particles, particularly in the case of PTFE materials. Tensile tests indicate that the YOUNG'S modulus increases at T= 77 K compared to room temperature. However, this improvement at low temperatures is moderate for PEEK composite which is already under its glass transition at room temperature. In the main investigation, tribological experiments were carried out at first at T= 77 K to observe the influence of the matrix, fillers and fibres on the material behaviour comparing to room temperature. The reduction of the friction coefficient and wear at low temperatures has been attributed to the low temperature properties of the polymer in particular due to the higher YOUNG'S modulus at T= 77 K. Whereas at room temperature friction and wear depend strongly of the CF content, the quantity of fillers and fibres does not have a significant effect on the tribological behaviour at low temperatures. At T= 77 K, the tribological behaviour of PTFE and PEEK composites is mainly influenced by the matrix. PEEK composites have a better tribological performance than PTFE materials especially regarding the wear resistance. Furthermore, the influence of the cryogenic medium was determined with experiments carried out in LN2 (T= 77 K), LH2 (T= 20 K) and LHe (T= 4.2 K), as well as in helium at T= 77 K and hydrogen at room temperature. The thermal properties of the cryogenic medium have a significant influence on the tribological performances of the composites. Due to the lower frictional heat at low sliding speed, the effect of low temperatures on the tribological behaviour of these composites was more clearly detected in this case, with a change in wear mechanism from mainly adhesive to more abrasive. Experiments in LN2 give the best friction and wear performance at low as well as at high sliding speed. The behaviour of these composites in LHe does not benefit from the low temperature properties of polymers due to the low heat of evaporation of LHe. The influence of hydrogen was particularly seen after the tribological experiments performed in LH2 on the surface of the disc. The reduction effect of hydrogen may have an influence on the tribochemical reactions which appear during sliding, enhancing the formation of iron fluorides, but no influence of the metal fluorides on the tribological performance could be determined in this study.
The international research project HYCREF, funded by the European Commission in the 5 th Framework programme, aimed to develop methods to prepare homogenous and stable water-, soiland waste reference materials contaminated with mineral oil hydrocarbons and to test certify the mineral oil content by gas chromatographic methods. As mineral oil products are important sources for environmental contaminations a high need exists for certified reference materials for their determination using the new gas chromatographic methods (soil: ISO/FDIS 16703, waste: ENpr 14039, water: ISO 9377-2). The experimental conditions and results for preparation and characterisation of a total of nine reference materials (3 water-, 3 soil- and 3 waste materials) are described and discussed. Target values for the reference materials were defined at the beginning of the project in order to have clear quality criteria, which could be compared with the achieved results at the end of the project. These target specifications were related to the maximum uncertainty from test certification exercises (< 5 % for soil/waste and < 10 % for water), the maximum inhomogeneity between bottles (< 3 %) and minimum requirements for stability (> 5 years for soil/waste and > 2 years for water). The feasibility studies showed that solid materials (soil, waste) could be prepared sufficiently homogenous and stable. The test certified values of the 6 solid materials comprise a wide range of mineral oil content from about 200-9000 mg/kg with expanded uncertainties between 5.7-13.1 % using a coverage factor k (k = 2). The development of new water reference materials –the so-called “spiking pills” for an offshore- and a land-based discharge water represents one of the most innovative aspects of the project. The spiking pill technology facilitates the application and storage and improves the material stability compared with aqueous materials. Additional to the preparation and test certification of the reference materials investigations on the analytical method for the determination of mineral oil hydrocarbons were performed. The results obtained in relation to the optimisation of analytical method (extraction procedure, sample pretreatment, clean-up and measurement) were provided to the respective working group of ISO/TC 190, ISO/TC 147 and CEN/TC 292 and were incorporated into the ongoing standardisation procedures. The new version of ISO/FDIS 16703 (July 2004) includes the improvements based on HYCREF results, for example the increase of the solvent/sample ratio, the removal of acetone from the organic extracts and the use of column technique instead of batch technique for clean-up.
Tensile testing according to EN 10002-1 is one of the basic mechanical tests to characterise the mechanical properties of metallic materials. This testing procedure has been regularly under development for many decades in order to modify and amend it and to bring it up to an up to date standard. Today tensile testing for quality control in metals manufacturing industry is routinely performed automatically with computer controlled testing machines. Due to economical needs of industry proposals were made by a European Standard Committee to amend the standard EN 10002-1. A European research project with the acronym TENSTAND was started to validate the proposed modifications of the tensile testing standard. The work package 4 of the project was to validate the machine control characteristics. A comparison test program was started with ten partners, 4 test piece geometries and 3 test parameters for 6 materials, partly with upper and lower yield strength and partly with 0.2 % proof strength to compare experimental results according to the proposal to modify the standard EN 10002-1. Initially testing in the strain control mode was introduced as well as switching of the control mode to crosshead control 1 and switching of the testing speed at appropriate points during the test. The comparison test was evaluated statistically and scientifically. The following conclusions were derived from the comparison test and summarised as recommendations to the standard committees. The scatter of the material properties were not significantly reduced by introducing the amended testing procedure. Few of the reasons for the continuously observed scattercan be identified as follows: The material properties are observed to be widely dependent on the testing speed. As a consequence the range for the allowed testing speed must be reduced. The closed loop control was not optimised sufficiently in some tests, the use of complicated testing machine software led to misinterpretation of software commands, individual testing equipment and implementation of the tensile testing procedure led also to scatter of the material properties which lay in a range of few percent. This is blurred by the inhomogeneity of the material.