In this study, the optimized fabrication and evolution of the microstructure and magnetic Transition behavior of the melt-extraction LaFe11.2Si1.8 microwires have been studied. After the optimization of extraction technique (heating power 22 KW, feeding rate 30-50 mm/s, rotation velocity 1700 r/min), the content of La Fe,Si)13 phase in the as-extracted microwires was 54 wt% due to the high solidification velocity, which was increased to 85 wt% via annealing at 1373 K for 20 min. The amount of La(Fe,Si)13 phase was increased and the composition of La(Fe,Si)13 phase became more homogenized through peritectic reaction and short-distance diffusion in the microwires during annealing process. The coexistence of the nanocrystalline and amorphous structures contributed to the broad magnetic Transition temperature range of the as-extracted and annealed microwires. The annealed microwires exhibited a second-order magnetic transformation behavior and showed a maximum magnetic entropy Change jDSMjmax of 6.2 J/kgK and working temperature interval of 36.0 K under a magnetic field of 20 kOe.