Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (22) (entfernen)
Sprache
- Englisch (22)
Referierte Publikation
- nein (22) (entfernen)
Schlagworte
- Corrosion (15)
- Geothermal (7)
- CCS (4)
- CCUS (4)
- Polyaniline (4)
- Steel (4)
- CO2 (3)
- CO2 quality (3)
- Carbon steel (3)
- Coating (3)
- Copper (3)
- Impurities (3)
- Martensitic steel (3)
- Pipeline network (3)
- CCU (2)
- Carbon steels (2)
- Coatings (2)
- Geothermal energy (2)
- Lead (2)
- Recommendations (2)
- SiO2 (2)
- Superaustenite steel (2)
- Supercritical/dense phase CO2 (2)
- Utilization (2)
- Whole-chain CCS scenario (2)
- Biodiesel (1)
- CO2 Corrosion (1)
- Capture (1)
- Carbon (1)
- Carbon capture (1)
- Carbon dioxide (1)
- Cement (1)
- Condensation (1)
- Corrosion and storage (CCUS) technology (1)
- Corrosion prevention (1)
- Corrosion resistant materials (1)
- Crevice corrosion (1)
- Dense phase (1)
- Droplet (1)
- Droplet corrosion (1)
- EIS (1)
- Electrochemistry (1)
- FAME (1)
- Injection (1)
- Passive film (1)
- Pipelines (1)
- Polyaniniline (1)
- Polymer in fuels (1)
- Protective coating (1)
- RME (1)
- SiO 2 (1)
- Sibayak (1)
- Silicate (1)
- Sol-gel coating (1)
- Standardization (1)
- Storage (1)
- X-ray photoelectron spectroscopy (1)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (22) (entfernen)
Geothermal brine is a complex system containing a wide variety of dissolved salts resulting from the condition s in a geothermal well. These fluids lead to corrosion in pipes and other parts of geothermal system construction and necessitate intense research efforts in finding new suitable materials. Carbon steel is susceptible to corrosion in geothermal brine especially when it is exposed to a high temperature and high-pressure medium, which is considered to be an aggressive environment. An artificial geothermal water, bas ed on a brine composition found in Indonesia, was used to investigate the performance of high alloyed materials. The electrolyte has pH 4 and contains 1,500 mg/l Cl-, 20 mg/l SO4 2-, 15 mg/l HCO3 -, 200 mg/l Ca 2+, 250 mg/l K+, and 600 mg/l Na+. In order to protect the bare material in geothermal application, it is necessary to either use high alloyed material s or coatings. In this research, a coating system consisting of polyaniline and silicon dioxide was investigated regarding its behavior to protect carbon steel. In detail, the effect of SiO2 and polyaniline (PANi) addition was evaluated by exposure and electrochemical tests for 7 days, i.e. electrochemical impedance spectroscopy (EIS) and open circuit potential (OCP ) at room temperature and 150 °C with 1 MPa pressure .
This work examined the droplet corrosion of CO2 pipeline steels caused by impurities in CO2 supercritical/dense phase at 278 K, simulating the underground transport condition. The wetting properties of carbon steels (X52 and X70) as well as martensitic steel UNS S41500, and superaustenite UNS N08031 were studied by contact angle measurement, revealing reactive wetting behavior of carbon steels. Exposure tests with CO2 saturated water droplet on steel surface showed that the impurities (220 ppmv SO2 and 6700 ppmv O2) diffused into the droplet and then reacted with metal coupons in supercritical/dense phase condition, forming the corrosion product instantly during pumping process. Due to the active wetting behavior, the carbon steels suffered from heavily attack, while negligible corrosion product was observed in cases of martensitic steel UNS S41500 and superaustenite UNS 08031 coupons. Condensation experiments that were carried out on fresh polished coupons in CO2 with 1200 ppmv H2O showed that the formation and aggregation of droplet is dependent on the presence of impurities. Without SO2 and O2, the same concentration of H2O did not cause observable corrosion process after a week of exposure. With 220 ppmv SO2 and 6700 ppmv O2 even low water concentration (5-30 ppmv) still resulted in heterogeneous nucleation and subsequent growth of droplets, leading to corrosive process on carbon steel surface albeit to a lesser extent.