Characterization of multiphase metal matrix composites by means of CT and neutron diffraction
(2016)
The present study examines the relationship between the microstructure of multiphase MMC and their damage mechanisms. The matrix AlSi12CuMgNi was combined with 15% vol. Al2O3 (short fibres) and with 7% vol. Al2O3 + 15% vol. SiC (short fibres and whiskers, respectively). The experimental approach encompasses 3D microstructure characterization by means of computed tomography of samples (a) as-received, (b) after heat treatment, and (c) after compression tests at room temperature. The volume fraction of different phases, their distribution, their orientation and the presence of defects and damage are studied.
Influence of addition of SiC whiskers on mechanical properties of composite was investigated. Phase-specific load partition analysis for samples with fibre plane parallel to load was perform by using neutron diffraction measurements during in-situ compression. It shows damage in the Si phase, while Al2O3 short fibres carry load without damage until failure. The computed tomography observations confirm the load partition analysis.
The paper addresses the ‘Determining the influence of preparation and measurement conditions on bonding strength using CAT-Technology’ and the follow points are discussed in more detail: Motivation, CAT – Technology, Influence of bonding area on bonding strength, Influence of storing & measurement temperatures and Influence of substrate thickness and coating support.
Characterization of the mechanical properties of interphases is essential when designing multicomponent materials such as fiber-reinforced matrices, protective coatings or multi-layered structures for integrated circuits. It can provide vital information about the durability of the finished product as a composite because failure is often initiated in the interfacial region induced by internal or external stress during fabrication or service. Nanoindentation is a powerful tool for investigating mechanical properties on the micro/nano scale. However, there are some challenges associated with conducting nanoindentation near interface regions. One main challenge is that the small thickness of the interphase region (typically 1-2µm) makes it difficult to apply several adjacent indents without overlap. Another issue is that the indentations are usually restricted by local reinforcement, and it becomes difficult to isolate the change in mechanical properties due solely to interphase formation. In this study we try to gauge the feasibility of nanoindentation for characterizing epoxy/Cu interphases. We develop a sample preparation method and optimize nanoindentation parameters in an attempt to avoid the restrictions mentioned above. Atomic force microscopy (AFM) and finite element analysis are employed as reference techniques to evaluate the effectiveness of our technique. We show the influence of preparation method and nanoindentaion parameters on measurements of interphase properties and how they relate the mentioned challenges.