Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2016 (22) (entfernen)
Dokumenttyp
- Vortrag (8)
- Zeitschriftenartikel (7)
- Beitrag zu einem Tagungsband (7)
Sprache
- Englisch (22)
Schlagworte
- Wear (7)
- Friction (6)
- Niobium carbide (6)
- NbC (5)
- SRV (4)
- China (3)
- Machining (3)
- Standards (3)
- Hard materials (2)
- Hardness (2)
Eingeladener Vortrag
- nein (8)
Hydraulic oils are well established formulations developed around the pump test. Requirements for energy efficiency and also environmentally acceptable properties increased the demand for development. In the same time, system pressure and the used of servo-hydraulic vanes increased bringing specific formulations and materials to their limit.
The vane pump is a key component in hydraulic systems and many other tribosystems in hydraulic circuits operate under different tribological operating conditions. The concept for ranking of hydraulic oils consists in using existing SRV-based ASTM test methods for evaluation of friction, wear and extreme pressure properties: D6425, friction and wear of oils (homologue to DIN 51834-2), D7421, extreme pressure properties of oils and D7755, wear volumes of ball and disks (homologue to DIN 51834-3. The tribological properties are assessed under the regime of mixed/boundary lubrication The SRV-based concept of tribological profile generates the wear volumes on two triboelements (specimen) and the extreme pressure properties as well as the evolution of friction in the wear and extreme pressure load step test. Thus, the benchmark and validation of hydraulic oils bear on a wider range of tribological properties. Round robin test results using the aforementioned testing concept will be shown. Another outcome is tribological set limits for inclusion in hydrau¬lic oil speci¬fications.
In the state-of-the-art technology, the impact of additives on friction and wear is evaluated in recipes with fixed concentrations. For the development of formulations it is desirable to determine the lowest effective concentration or the concentration at which failure was initiated or excessive wear began. Through a new development of the SRV® machine it is now possible to change the lubricant composition of a test specimen in a reproducible manner, in sub-pro Mill steps during the SRV® testing. This technology is used in the present article to define the optimum additive concentration with regard to wear and friction in a system of base oil and additive. Exemplary selected base oil and additive variants are tested here. The load parameters during testing are selected in such a way that they correspond to later application. The new data acquisition capabilities enable new possibilities for optimizing lubricant formulations in practice-oriented model-tribometer tests. “Cliff“ testing aims to identify in engine or gear tests the induction time or off-set point (“cliff“) after which wear and friction increased of failure occurred. Explanations for friction and wear increased as well as failures, which occurred during engine tests, can be derived from SRV® testing of oil samples taken or collected at different engine test times and correlating these with their friction, wear and EP data in respect to depleting curves for specific additives or other oil properties. A “cause-root” analysis is done by plotting SRV® data versus functional properties. The collected oil samples must be fully SRV® tested and chemically analyzed.
Several phases, like Nb₄C₃, Nb₆C₅ and other short and long range ordered phases occur in the region of homogeneity of NbCₓ (0,75≤ x ≤1.0) in the binary phase diagram. Properties, like micro-hardness, hot hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, the addition of secondary carbides and the type of binder. Supporting results from different grades with varying C/Nb ratio or binder types were illuminated. Thus, the NbC system offers to producers a wider process window, than WC. The impact of These tailored properties on sliding wear and cutting performance was illuminated by tribological and machining results. Niobium is today largely available. NbC can be synthesized by carbothermal conversion of Nb₂O₅ or be metallurgically grown and leached out, provides comparably low friction in many relevant tribo-contacts and displays low wear. NbC and Nb₂O₅ have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO₃ and Co₃O₄.
Substitution of tungsten carbide by niobium carbide as cutting materials and for wear protection
(2016)
Several phases, like Nb₄ C₃ , Nb₆C₅ and other short and long range ordered phases occur in the region of homogeneity of NbCₓ (0.75 ≤ x ≤ 1.0) in the binary phase diagram. Properties, like micro-hardness, hot hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, the addition of secondary carbides and the type of binder. Supporting results from different grades with varying C/Nb ratio or binder types were illuminated. Thus, the NbC system offers to producers a wider process window, than WC. The impact of these tailored properties on sliding wear and cutting performance was illuminated by tribological and machining results.
Niobium is today largely available. NbC can be synthesized by carbothermal conversion of Nb₂O₅ or be metallurgically grown and leached out, provides comparably low friction in many relevant tribo-contacts and displays low wear. NbC and Nb₂O₅ have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO₃ and Co₃ O₄ .
Substituting tungsten carbide (WC) as cutting tools and for wear protection by niobium carbide (NbC)
(2016)
As a refractory carbide, niobium carbide (NbC) is today still a forgotten carbide with hidden properties, such as wear resistance, thus qualifying NbC for the group of tribological materials with enhanced wear resistance. Several phases, like Nb₄C₃, Nb₆C₅ and other short and long range ordered phases occur In the region of homogeneity of NbCx (0,75≤ x ≤1.0) in the binary phase diagram, which enable the tailoring of properties and offers a much wider process window than known from WC. The type binder (Co, Ni, NiMo) and its concentration as well as the sintering process (SPS, liquid phase sintering) determine the box “hardness-toughness”, which will be illuminated based on more than 100 grades.
The impact of these tailored properties on sliding wear (T= 22/400°C; v= 0,1-10 m/s) and cutting performance will be illuminated by tribological and machining results. Cutting test results under emulsion and coolant-free operation of cobalt and Fe3Al bonded, straight NbC versus WC based inserts against different alloys (C60, 100Cr6, 42CrMo4, X90CrMoV18, 300WA, GG35) will be highlighted.
Results of rolling contact fatigue (RCF) tests by balls-on-rod (BOR) method and two-roller methods have been compared to those by the balls-on-flat (BOF) method by using three different silicon nitride grades. The results suggest that the two-roller method could differentiate the bearing grade materials in terms of wear behavior.
„Cliff“-testing by using SRV
The identification in engine or gear tests of the induction time or off-set point („cliff“), after which wear and friction increased.
“Cliff” testing as auxiliary method supports the interpretation of engine tests, as it enhances the values of expensive engine tests, because it enables correlations between friction & wear, either from engine or in SRV tests, with additive depletion, oxidation, viscometrics and dispersancy/detergency.
Oil samples taken in discrete intervals and “Cliff” tested monitors the evolution of tribological and functional properties versus engine running time. “Cliff” testing by using SRV is a purposeful tool in order to secure and accelerate metallurgical developments and the development of lubricant formulations.
In order to achieve greater efficiency or to meet light weight requirements, components are downsized. This, however, increases the load, e.g., Hertzian or nominal contact pressures and stresses of tribosystems. This load is expressed as pₐ·v-value, the product of nominal contact pressure and sliding velocity. pₐ·v-values are an effective tool for design engineers for predicting low wear/high wear transitions. Therefore, in the present work, topographical analysis has been combined with the plasticity of micro-asperities and the flash temperatures to estimate the limits of pₐ·v diagrams. The central piece of this set of models presented here is the calculations for flash temperatures and contact mechanics of micro-asperities. This central piece is used to predict the performance of materials in high velocity (turbines, machinery) and low velocity (human joint) applications. It is shown that the model combination suggested here is a useful tool for screening and preselecting a candidate and new materials with respect to tribological requirements before engaging in expensive testing.