Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Vortrag (14)
- Zeitschriftenartikel (6)
- Posterpräsentation (6)
- Beitrag zu einem Tagungsband (1)
Schlagworte
- MIC (17)
- Corrosion (11)
- Methanogens (11)
- Microbiologically influenced corrosion (6)
- Environmental Simulation (5)
- Archaea (4)
- Biocorrosion (4)
- Hi-Tension (3)
- Korrosion (3)
- Biofilm (2)
- Flow system (2)
- HI-Tension (2)
- Methanogen (2)
- Mikrobiell beeinflusste Korrosion (2)
- Mikroorganismen (2)
- Sulfate reducing bacteria (2)
- Academia (1)
- Bacterial attachment (1)
- Biocides (1)
- Biodeterioration (1)
- Biotische/abiotische Faktoren (1)
- COST (1)
- COST Action (1)
- Carbon steel (1)
- Contamination (1)
- Corrosion product (1)
- Corrosion products (1)
- Disinfection Fuel (1)
- Environmental condition (1)
- Environmental simulation (1)
- Fenton-like reaction (1)
- Flow Model (1)
- Flow-System (1)
- Flow-system (1)
- Fuel sorption (1)
- Gas storage (1)
- Gesteinskorrosion (1)
- H2-Abbau (1)
- High density polyethylene (1)
- Hydrogen (1)
- Implants (1)
- Interdisciplinarity (1)
- Interdisciplinary (1)
- Iron (1)
- Kontamination von H2 (1)
- Kraftstoffabbau (1)
- Kraftstoffbehälter (1)
- Metallkorrosion (1)
- Metalls (1)
- Methane (1)
- Methanogene (1)
- Methanogenesis (1)
- Mikrobielle Gemeinschaft (1)
- Model (1)
- Modeling (1)
- Modelling (1)
- Modelling studies (1)
- Multiple lines of evidence (1)
- Multiport (1)
- Netzwerk (1)
- Projekte (1)
- Reactive oxygen species (1)
- Reactor conditions (1)
- Ruthenium (1)
- SEM (1)
- SIMS (1)
- SRB (1)
- Silver (1)
- Simulation (1)
- Stakeholder (1)
- UV-irradiation (1)
- Umweltsimulation (1)
- Unterirdische Speicher (1)
- Wasserstofflagerung (1)
Organisationseinheit der BAM
- 4.1 Biologische Materialschädigung und Referenzorganismen (27) (entfernen)
Eingeladener Vortrag
- nein (14)
Bei dem Vortrag werden die potentiellen mikrobiologischen Einflüsse im Falle der Lagerung von Wasserstofflagerung in unterirdischen geologischen Formationen vorgestellt, die Zusammenarbeit mit internen und auch externen Partnern. Der Fokus liegt dabei auf UGF; anaerobe Umgebungen, Sulfate reduzierenden Bakterien, methanogenen Archaea, weiterleitenden Systeme und die Kombination der Untersuchung abiotisch/biotische
As more industrial interests focusing on using salt caverns and repurposed gas or petroleum reservoirs for alternative fuel storage, i.e. CO2/H2, the question raises whether microorganisms may impact the infrastructure, gas purity and storage condition over time.
Environments with high salinity (> 1.5 Meq of NaCl) are resided by halophiles (salt-loving microorganisms). To compensate for the intensive osmotic stress, they have resorted to two main adaptation strategies: 1) production of compatible solutes and 2) accumulation of intracellular KCl. Microbial community analysis of several high salinity environments revealed a number of recurring genera, including Halomonas and Halanaerobium. However, the impact of halophiles on the overall integrity and stability of the storage facilities remain largely unknown.
To evaluate the suitability and stability of saline storage facilities, several model halophilic microorganisms, such as members of Halomonas, will be selected as testing subjects. First, the impact of halophiles on the infrastructure will be determined using an integrative approach by combining a number of techniques, including electrochemistry, TOF-SIMS, SEM/FIB/EDS and FIB-TEM. Second, the abilities of halophiles to alter the fuel composition (i.e. increase/decrease the fractions of H2) will be monitored using gas chromatography by growing them under high pressure.
As a result of climate change and the accompanying mandatory shift to renewable energy resources, microorganisms will continue to play an important role in the energy sector, both to their benefit and detriment. Thus, it is important to achieve a certain level of understanding regarding the activities and mechanisms of halophiles prior to large-scaled excursions.
Microbiologically influenced corrosion (MIC) is a phenomenon of increasing concern which affects various materials and sectors of society. MIC describes the effects, often negative, that a material can experience due to the presence of microorganisms. Unfortunately, although several research groups and industrial actors worldwide have already addressed MIC, discussions are fragmented, while information sharing and willingness to reach out to other disciplines is limited. A truly interdisciplinary approach, that would be logical for this material/biology/chemistry-related challenge, is rarely taken. In this review we highlight critical non-biological aspects of MIC that can sometimes be overlooked by microbiologists working on MIC but are highly relevant for an overall understanding of this phenomenon. Here, we identify gaps, methods and approaches to help solve MIC related challenges, with an emphasis on the MIC of metals. We also discuss the application of existing tools and approaches for managing MIC and propose ideas to promote an improved understanding of MIC. Furthermore, we highlight areas where the insights and expertise of microbiologists are needed to help progress this field.
In the present study, a simple approach was used to investigate the effect of UV-exposure on two high density Polyethylene materials (PE-HD), commonly used for storage tanks, on fuel sorption behavior and colonization by microorganisms. The aim was to investigate whether the sorption behavior of the fuels (diesel/biodiesel) and the colonization by microorganisms, frequently occurring in the fuel, is affected and may lead to undesirable or safety-relevant material changes. We showed that the UV-irradiation leads to significant changes of the sorption behavior due to chemi-crystallization and crosslinking. The fuel Sorption is affected by the UV-induced formation of polar carbonyl and hydroxyl groups predominantly occurring at the surface. With respect to microbial colonization behavior for Bacillus subtilis and Pseudomonas aeruginosa, isolated from a contaminated diesel sample, differences of the initial adhesion could be shown depending on the initial type of polyethylene as well as on the degree of UV-induced degradation.
Microbiologically influenced corrosion (MIC) is an expensive but unpredictable problem for the industries. The most well-known culprit for MIC is the sulfate-reducing microorganisms (SRM), such as members from the genus Desulfovibrio. It has been widely accepted that SRM can contribute significantly to MIC through the production of hydrogen sulfide (HS-) or in some cases a direct electron uptake from the metal surface. However, in a real environmental system, SRM is not exclusive and often involved with other microorganisms that may also contribute to MIC, such as methanogens.
Methanogenic archaea can produce methane (CH4) using H2+CO2, formate, methylated amines or acetate. Methanogens are highly abundant in the environment and many are found in very extreme conditions, such as high temperature and high salinity. Previous researches have demonstrated that methanogens are capable of MIC, though the specific mechanisms are still under investigation. In the oil and gas industry, methanogens are not considered as the main contributor for MIC since the corrosion rates are often too low. However, the tests for methanogen-induced MIC are usually performed at static conditions, which cannot represent the system accurately. Here, we developed a novel anaerobic system to evaluate the corrosion potential of methanogens under flow conditions. We will use the Methanococcus maripaludis KA1 strain, which was isolated from a crude oil tank, as the organism of interest. A separate system for Desulfovibrio alaskensis will be established for corrosion rate comparisons. Furthermore, we will study the synergistic effects of M. maripaludis and D. alaskensis on MIC under flow.
Currently, sulfate-reducing bacteria (SRB) is regarded as the main culprit of microbiologically influenced corrosion (MIC), mainly due to the low reported corrosion rates of other microorganisms. For example, the highest reported corrosion rate for methanogens is 0.065 mm/yr. However, by investigating methanogen-induced microbiologically influenced corrosion (Mi-MIC) using an in-house developed versatile multiport flow test column, extremely high corrosion rates were observed. We analyzed a large set of carbon steel beads, which were sectionally embedded into the test columns as substrates for iron-utilizing methanogen Methanobacterium IM1. After 14 days of operation using glass beads as fillers for section separation, the highest average corrosion rate of Methanobacterium IM1 was 0.2 mm/yr, which doubled that of Desulfovibrio ferrophilus IS5 and Desulfovibrio alaskensis 16109 investigated at the same conditions. At the most corroded region, nearly 80% of the beads lost 1% of their initial weight (fast-corrosion), resulting in an average corrosion rate of 0.2 mm/yr for Methanobacterium IM1-treated columns. When sand was used as filler material to mimic sediment conditions, average corrosion rates for Methanobacterium IM1 increased to 0.3 mm/yr (maximum 0.52 mm/yr) with over 83% of the beads having corrosion rates above 0.3 mm/yr. Scanning electron images of metal coupons extracted from the column showed methanogenic cells were clustered close to the metal surface. Methanobacterium IM1 is a hydrogenotrophic methanogen with higher affinity to metal than H2. Unlike SRB, Methanobacterium IM1 is not restricted to the availability of sulfate concentration in the environment. Thus, the use of the multiport flow column provided a new insight on the corrosion potential of methanogens, particularly in dynamic conditions, that offers new opportunities for monitoring and development of mitigation strategies. Overall, this study shows under certain conditions methanogenic archaea can cause higher corrosion than SRB, specific quantifications, i.e., maximum, average, and minimum corrosion rates can be determined, and that spatial statistical evaluations of MIC can be carried out.
Currently, corrosion rates (CR) and/or corrosion products (CP) obtained for methanogen-induced microbiologically influenced corrosion (Mi-MIC) on carbon steel are mainly analyzed from static-incubations. By using a multiport-flow-column, much higher CRs (0.72 mm/yr) were observed, indicating static-incubations are not suitable for determining the corrosive potential of Mi-MIC. With the combination of various analytical methods (ToF-SIMS/SEM-EDS/SEM-FIB) and contrary to previously published data, we observed that CPs contained phosphorus, oxygen, magnesium, calcium and iron but lacked carbon-related species (e.g. siderite). Overall, siderite nucleation is disrupted by methanogens, as they convert aqueous bicarbonate into carbon dioxide for methanogenesis resulting in increased localized corrosion.