Analytische Chemie
Filtern
Dokumenttyp
Schlagworte
- Cement (13)
- Rheology (6)
- Concrete (4)
- Dye (4)
- Early hydration (4)
- Hydration (4)
- C3A (3)
- Optical Spectroscopy (3)
- Polycarboxylate ether (PCE) (3)
- Additive manufacturing of concrete (2)
- Bingham fluid (2)
- Bio-based concrete (2)
- Cement hydration (2)
- Chemical admixtures (2)
- Delayed addition (2)
- Education (2)
- Non-destructive testing (2)
- Polysaccharides (2)
- Portland cement (2)
- Process monitoring (2)
- Sr isotopes (2)
- Sustainability (2)
- Yield stress (2)
- 1H NMR relaxometry (1)
- 3DCP (1)
- Acoustic emission (1)
- Additive Manufacturing (1)
- Admixtures (1)
- Africa (1)
- Aggregates (1)
- Alite (1)
- Alkali-activated slag (1)
- Aqueous phase of cement paste (1)
- Berliner Tuffsteinfassaden (1)
- Beton (1)
- Betondickglasfenster des Glockenturms am Eiermannbau (1)
- Bingham Fluid (1)
- C3S (1)
- Carbon emission (1)
- Carbon footprint (1)
- Cement Hydration (1)
- Cement, hydration (1)
- Characterization (1)
- Civil Engineering (1)
- Climate (1)
- Clinker reduction (1)
- Control Chart (1)
- Crack Detection (1)
- Cusum (1)
- DFG SPP 2005 (1)
- Dissolution (1)
- Dyes (1)
- Environment (1)
- Expansion (1)
- Fire spalling (1)
- Fließgrenze (1)
- Fluorescence (1)
- Fluorescence Spectroscopy (1)
- Frost salt attack (1)
- Geopolymer (1)
- Gesteinskörnung (1)
- Gold mit Synchrotronstrahlung (1)
- Gypsum (1)
- Heat flow calorimetry (1)
- Heat of hydration (1)
- Hüttensandmehl (1)
- Inorganic polymers (1)
- Iron speciation (1)
- Kaiser-Wilhelm-Gedächtniskirche (1)
- Kandelaber des Ensembles am Charlottenburger Tor (1)
- Korrosion (1)
- Large Aperture Ultrasound System (LAUS) (1)
- Materials (1)
- Method development (1)
- Moisture transport (1)
- Monitoring (1)
- Nonferrous slag (1)
- Optical spectroscopie (1)
- Pergamonmuseums (1)
- Photoluminescence (1)
- Plastic viscosity (1)
- Polycarboxylate ether (1)
- Polycarboxylate ether (PCE), (1)
- Portland clinker (1)
- Proficiency Testing (1)
- Provenance (1)
- Provenancing (1)
- Quality Infrastructure (1)
- Radiografische Untersuchung (1)
- Reflection spectroscopy (1)
- Rheologie (1)
- Robustness (1)
- Schlacke (1)
- Schriftrollen vom Toten Meer (1)
- Sciences (1)
- SealWasteSafe (1)
- Sensitivity (1)
- Shrinkage (1)
- Solid volume fraction (1)
- Sulfid (1)
- Superplasticizer (1)
- Supplementary cementitous materials (1)
- Syngenite (1)
- Ultrasonic Borehole Array (1)
- Upconversion (1)
- Viscosity (1)
- Viskosität (1)
- X-ray absorption near-edge structure (1)
- X-ray absorption spectroscopy (1)
- X-ray diffraction (1)
- Zement (1)
Organisationseinheit der BAM
- 7.4 Baustofftechnologie (33) (entfernen)
Eingeladener Vortrag
- nein (6)
In this paper, we demonstrate the value of 1H NMR relaxometry for studying the hydration of clinker-reduced, more climate-friendly cementitious binders. The results were obtained on typical CEM I cements and sister samples containing two different reactive agricultural ashes as well as non-reactive biochars as supplementary cementitious materials. The findings prove that time-resolved NMR measurements provide valuable additional information when combined with classical heat flow calorimetry.
Alkalisch aktivierte Bindemittel (AAB) und Betone können herkömmliche Zemente beziehungsweise Betone potentiell in vielen Anwendungen ersetzen und dadurch den CO2-Fußabdruck der Bauindustrie wesentlich verkleinern. Zur Untersuchung der Stahlkorrosion in bewehrten („armierten“) Betonbauteilen werden elektrochemische Methoden wie Messungen des Freien Korrosionspotentials, des Polarisationswiderstands oder von Stromdichte-Potential-Kurven eingesetzt. Diese Methoden und die etablierten Grenzwerte zur Detektion von Korrosion sind für die Anwendung bei herkömmlichen Zementen beziehungsweise Betonen entwickelt und erprobt worden. Neue Forschungsergebnisse demonstrieren, dass Unterschiede zwischen den Porenlösungszusammensetzungen von herkömmlichen Zementen und bestimmten AAB sowie anderen schlackehaltigen Zementen erhebliche Unterschiede bei den Ergebnissen der elektrochemischen Messungen bewirken und damit zur fehlerhaften Detektion von Stahlkorrosion führen können. Ursache hierfür sind vor allem reduzierte Schwefelspezies in den Porenlösungen von AAB und anderen schlackehaltigen Zementen.
Safety is a key parameter for the design and construction of buildings. The most widely used construction material to date is concrete that consists of about 15-20 wt.-% cement, which is responsible for the main concrete properties, i.e., strength and durability. Despite many standards regulating the quality of cement, at present, there exists no viable method to track the cement life cycle “from cradle to grave”. This led to an increasing interest in simple and robust methods for studying the processes and changes occurring during the life cycle of cement. In this context, we explored the applicability of fluorescence measurements which can be performed with relatively inexpensive and miniaturized instrumentation yet require robust optical probes which survive the harsh cement environment. Therefore, we developed a platform of lanthanide-based upconversion nanoparticles (UCNPs), consisting of a NaYF4 matrix doped with Yb3+ and Er3+ with sizes between 20 nm and 55 nm, which show characteristic multi-color emission patterns, composed of narrow bands of varying intensity in the ultraviolet, visible, near-infrared, and short-wave spectral region and examined their potential for cement probing and the non-invasive monitoring of the hydration processes occurring during cement formation.
UCNPs of different size and chemical composition were synthesized via a thermal decomposition approach under inert conditions. The tailor-made design of different emission patterns was achieved by tuning particle size and morphology, material composition, and particle surface chemistry in upscaleable syntheses. For cement probing, different types of UCNPs were added to cement and the evolution of the UCNP emission pattern was used to probe in-situ changes of physico-chemical parameters in the cementitious environment during hydration, utilizing a simple and portable custom-designed optical setup. The observed changes in the UCNP emission patterns are characteristic for a given particle size, surface chemistry, and cement composition. In addition to fluorescence measurements, conventional isothermal heat flow calorimetry was used to study the influence of UCNP addition on cement hydration kinetics. Subsequently, both sets of measurements were correlated. Our results underline the potential of our optical approach ad UCNPs for the non-invasive probing of cementitious systems and cement hydration. This can be also exploited for cutting-edge applications of construction materials such as 3D concrete printing.
Additive manufacturing of concrete structures is a novel and emerging technology. Free contouring in civil engineering, which allows for entirely new designs, is a significant advantage. In the future, lower construction costs are expected with increased construction speeds and decreasing required materials and workers. However, architects and civil engineers rely on a certain quality of execution to fulfil construction standards. Although several techniques and approaches demonstrate the advantages, quality control during printing is highly challenging and rarely applied. Due to the continuous mixing process commonly used in 3D concrete printing, it is impossible to exclude variations in the dry mixture or water content, and a test sample cannot be taken as a representative sample for the whole structure. Although mortar properties vary only locally, a defect in one layer during printing could affect the entire integrity of the whole structure . Therefore, real-time process monitoring is required to record and document the printing process. At the Bundesanstalt für Materialforschung und -prüfung (BAM) a new test rig for the additive manufacturing of concrete is built. The primary purpose is measuring and monitoring the properties of a mortar during the printing process. The following study investigates an approach for calculating yield stress and plastic viscosity based on experimentally recorded pressure data. The calculations assume that fresh mortar behaves as a Bingham fluid and that the Buckingham-Reiner-equation is applicable. A test setup consisting of rigid pipes with integrated pressure sensors at different positions is utilized. Monitoring the printing process with different sensors is crucial for the quality control of an ongoing process.
Volumetric changes follow Portland cement hydration reactions: aluminates' hydration is generally expansive, whereas silicates' reaction leads to shrinkage. Determining the volumetric variation at very early ages (i.e., first minutes/hours) presents operational challenges; most standards prescribe the measurement on specimens that are already hardened, while measurements from the fresh state are not standardized. This article reports the first attempt to use in-situ X-ray diffraction (XRD) to measure the early-age volumetric variation of a cementitious paste. For this purpose, a C3A + gypsum paste was assessed for 36 h, measuring its vertical displacement over time through XRD. The results showed that the expansion increased in the first ∼13 h, in line with the ettringite formed up to ∼11 h. In addition, the volumetric expansion agreed well with the heat release in calorimetry. It is concluded that the volumetric variation measurement of cementitious pastes through in-situ XRD is a promising technique, but further studies are needed to make this technique consolidated.
NMR is becoming increasingly popular for the investigation of building materials as it is a non-invasive technology that does not require any sample preparation nor causes damage to the material. Depending on the specific application it can offer insights into properties like porosity and spatial saturation degree as well as pore structure. Moreover it enables the determination of moisture transport properties and the (re-)distribution of internal moisture into different reservoirs or chemical phases upon damage and curing. However, as yet most investigations were carried out using devices originally either designed for geophysical applications or the analysis of rather homogeneous small scale (< 10 mL) samples. This paper describes the capabilities of an NMR tomograph, which has been specifically optimized for the investigation of larger, heterogeneous building material samples (diameters of up to 72 mm, length of up to 700 mm) with a high flexibility due to interchangeable coils allowing for a high SNR and short echo times (50 - 80 m s).
Introduction of a monitoring system for Bingham fluids in additive manufacturing with concrete
(2022)
Freeform additive manufacturing of concrete structures is a rising technology in civil engineering with several fascinating advantages. Nonetheless, to ensure reliability and structural integrity, standards and quality control are required in the future to bring this technology into the market. As the concrete is manufactured continuously, continuous quality control of the printing process is also required, i.e. comprehensive process monitoring. At BAM, a test rig will be installed, enabling the printing of concrete structures with a maximum size of 2 m x 1 m x 1 m (l x w x h). Here, process monitoring is the focus of the test rig. In this study, we show the results of the first pump tests, including the measurement of several parameters such as temperature and pressure along the supply system, i.e. from the concrete pump to the printer head.
Introduction of a monitoring system for Bingham fluids in additive manufacturing with concrete
(2022)
Freeform additive manufacturing of concrete structures is a rising technology in civil engineering with several fascinating advantages. Nonetheless, to ensure reliability and structural integrity, standards and quality control are required in the future to bring this technology into the market. As the concrete is manufactured continuously, continuous quality control of the printing process is also required, i.e. comprehensive process monitoring. At BAM, a test rig will be installed, enabling the printing of concrete structures with a maximum size of 2 m x 1 m x 1 m (l x w x h). Here, process monitoring is the focus of the test rig. In this study, we show the results of the first pump tests, including the measurement of several parameters such as temperature and pressure along the supply system, i.e. from the concrete pump to the printer head.
Sehr geehrte Damen und Herren,
liebe Leserinnen und Leser,
bereits im ersten Band der N.i.Ke. Schriftenreihe des Netzwerks zur interdisziplinären Kulturerhaltung hatte ich angeführt, dass bei der Untersuchung von kulturellen Artefakten naturwissenschaftliche Untersuchungsmethoden zunehmend an Bedeutung gewinnen, sie eigentlich unverzichtbar geworden sind.
Ein besonders einprägsames Beispiel dieser fächerübergreifenden Zusammenarbeit zwischen Geisteswissenschaften, Naturwissenschaften und Restaurierungswissenschaften war die Ausstellung Johannes Vermeer. Vom Innehalten, die in diesem Jahr in der Gemäldegalerie Alter Meister in den staatlichen Kunstsammlungen Dresden gezeigt wurde. Eigens für diese Ausstellung wurde das Gemälde Brieflesendes Mädchen am offenen Fenster einer grundlegenden Restaurierung unterzogen. Diese Restaurierung diente jedoch nicht nur der Reparatur des Bildes. Um sich dem ursprünglichen Zustand des Gemäldes zwischen 1657 und 1659 anzunähern, wurden später hinzugefügte Malschichten großflächig abgenommen. Möglich wurde dies durch unterschiedliche, bildgebende materialwissenschaftliche Untersuchungen im Vorfeld, welche die wissenschaftlichen Grundlagen für die Diskussion über den weiteren Umgang mit der Lesenden schufen.
Materialanalytische Verfahren wurden und werden ständig weiterentwickelt und optimiert. Sei es, um aus einer Vielzahl von Einzelmessungen ein Gesamtbild zu erstellen, oder die Größe einer Probenentnahme so zu reduzieren, dass von einer „minimal-invasiven“ oder „quasi nicht-invasiven“ Untersuchung ausgegangen werden kann. Nun feiert die Bundesanstalt für Materialforschung und -prüfung, zusammen mit ihren Vorgängerinstitutionen, den königlichen Versuchsanstalten, in diesem Jahr ihren einhundertfünfzigsten Geburtstag. Sie blickt damit auf eine lange Tradition materialwissenschaftlicher Analysen zurück, an deren Beginn beispielsweise die metallographischen Untersuchungen von Adolf Martens stehen. Derartige Untersuchungen bilden auch heute noch einen wesentlichen Bestandteil archäometallurgischer Forschung. Die Historie bzw. die Weiterentwicklung der Methodik lässt sich hier besonders gut nachzeichnen. Jedoch blicken auch Verfahren zur Charakterisierung weiterer Werkstoffe, wie Glas, Keramik, oder organischer Materialien auf eine lange Geschichte zurück.
Die in diesem Band der N.i.Ke.-Schriftenreihe präsentierten Beiträge dokumentieren einerseits aktuelle Forschungsarbeiten, die erst in diesem Jahr in entsprechenden Fachjournalen publiziert wurden, andererseits liegen einige der Arbeiten bereits 50 Jahre zurück. Sie bekunden damit nicht nur die materialtechnologische und historische Bandbreite der Projekte, sondern offenbaren die Vielfältigkeit kulturhistorischer oder restauratorischer Fragestellungen, zu deren Beantwortung natur- und materialwissenschaftliche Forschung wesentliche Beiträge liefern können.
Ich bedanke mich bei allen Kolleginnen und Kollegen, die zur Erstellung dieser dritten Ausgabe der N.i.Ke. Schriftenreihe des Netzwerks zur interdisziplinären Kulturerhaltung beigetragen haben. Ihre Aufsätze ermöglichen den Blick in die Vielfältigkeit materialwissenschaftlicher Untersuchungen im Bereich Kunst- und Kulturgut. Ich wünsche Ihnen viel Spaß auf dieser kleinen Zeitreise.
The 87Sr/86Sr isotope ratio can, in principle, be used for provenancing of cement. However, while commercial cements consist of multiple components, no detailed investigation into their individual 87Sr/86Sr isotope ratios or their influence on the integral 87Sr/86Sr isotope ratio of the resulting cement was conducted previously. Therefore, the present study aimed at determining and comparing the conventional 87Sr/86Sr isotope ratios of a diverse set of Portland cements and their corresponding Portland clinkers, the major component of these cements. Two approaches to remove the additives from the cements, i.e. to measure the conventional 87Sr/86Sr isotopic fingerprint of the clinker only, were tested, namely, treatment with a potassium hydroxide/sucrose solution and sieving on a 11-µm sieve. Dissolution in concentrated hydrochloric acid/nitric acid and in diluted nitric acid was employed to determine the 87Sr/86Sr isotope ratios of the cements and the individual clinkers. The aim was to find the most appropriate sample preparation procedure for cement provenancing, and the selection was realised by comparing the 87Sr/86Sr isotope ratios of differently treated cements with those of the corresponding clinkers. None of the methods to separate the clinkers from the cements proved to be satisfactory. However, it was found that the 87Sr/86Sr isotope ratios of clinker and cement generally corresponded, meaning that the latter can be used as a proxy for the clinker 87Sr/86Sr isotope ratio. Finally, the concentrated hydrochloric acid/nitric acid dissolution method was found to be the most suitable sample preparation method for the cements; it is thus recommended for 87Sr/86Sr isotope analyses for cement provenancing.
With the aim of identifying the origin and the manufacturer of a cement, a reliable procedure that provides unambiguous results is needed. Such procedure could resolve practical issues in damage research, liability issues and forensic investigations. A substantial number of attempts for fingerprinting of building materials, including cement, has already been carried out during the last decades. Most of them were based on concentration analysis of the main elements/components. This review provides an overview of provenance studies of cement and the main approaches commonly used. Provenance studies of cement via isotope techniques are also presented and discussed as representatives of the state-of-the-art in the field. Due to the characteristic properties and the occurrence of carefully selected isotope ratios, unique fingerprints of different kinds of materials can be provided by these methods. This property has largely been explored in various scientific fields such as geo- and cosmochemistry, food forensics, archaeology, geochronology, biomedical studies, and climate change processes. However, the potential of isotope techniques in cement and concrete research for provenance studies has barely been investigated.
Therefore, the review outlines a suitable approach using isotope ratios, which could lead to reliable provenancing of cementitious materials in the future.
Tricalcium aluminate (C3A) is found with less than 10% wt. of the total composition; however, during hydration, C3A plays an important role in the early hydration of cement in the presence of gypsum as a set retarder.
The aim of this investigation is to assess the suitability of optical spectroscopy and a dye-based optical probe to monitor early hydration of C3A in the presence of gypsum and hemihydrate. Optical evaluation was performed using steady-state fluorescence and diffuses reflectance spectroscopy (UV-VisDR). Phase characterization during hydration was done with in-situ X-ray diffraction. UV-VisDR with a cyanine dye probe was used to monitor the formation of metastable phases and was employed together with fluorescence spectroscopy, to follow the Aggregation and disaggregation of the dye during hydration. In conclusion, for the first time, a cyanine dye was identified as a feasible and stable probe to monitor C3A hydration changes in the presence of calcium sulfate.
A thorough characterization of starting materials is the precondition for further research, especially for cement, which contains various phases and presents quite a complex material for fundamental scientific investigation. In the paper at hand, the characterization data of the reference cement CEM I 42.5 R used within the priority program 2005 of the German Research Foundation (DFG SPP 2005) are presented from the aspects of chemical and mineralogical compositions as well as physical and chemical properties. The data were collected based on tests conducted by nine research groups involved in this cooperative program. For all data received, the mean values and the corresponding errors were calculated. The results shall be used for the ongoing research within the priority program.
Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products.
The Effect of Low Charge Polycarboxylate on C3A Passivation Monitored by Optical Spectroscopy
(2019)
Tricalcium aluminate (C3A) is less than 10 wt.% of the total cement composition; however, during hydration, the soluble C3A plays an important role in cement setting when mixed with the appropriate amount of sulfate.1 A good understanding about the balance of these components is therefore crucial to follow with the rapid growth of substitution materials and the rising levels of aluminate clinker. The aim of this investigation is the use of optical spectroscopy and in-situ X-ray diffraction utilizing a water-soluble organic dye (dye-S) to monitor early hydration of calcium aluminate (C3A) in the presence of 26 wt.% CaS04.2H2O (G) and PCE polymers with different charge densities (PCE-LC and PCE-HC). Phase characterization and optical evaluation were performed using in-situ X-ray diffraction and steady-state fluorescence and diffuse reflectance spectroscopy. Fluorescence spectroscopy of the reference C3A + dye-S revealed a fast decay in fluorescence intensity. However, in the presence of 26 wt.% G (C3A + dye-S + 26 wt.% G), a gradual increase in fluorescence intensity was observed in the first hours of reaction followed by a plateau that subsequently dropped in intensity after eight hours. The addition of PCE-LC and PCE HC to the mixture exhibited changes in the intensity threshold and overall a higher fluorescence intensity. Dye changes during hydration and structural changes will be further discussed.
The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has enormous influence on the early hydration of cement. C3A as the most reactive phase of Portland cement plays a significant role in early hydration reactions and affects the rheological performance. Therefore, this paper presents experimental results about the influence of delayed addition of PCEs on the Hydration of cement and C3A-gypsum pastes investigated by isothermal heat flow calorimetry. Complementary in-situ XRD was carried out on C3A pastes to analyze hydration and phase changes related to the addition of PCE.
Cement pastes with a delayed addition of PCE showed less Retardation compared to simultaneous addition. The alteration caused by PCE is much more pronounced for C3A-gypsum mixes. With a delayed addition of SP, the hydration of C3A is less retarded or even accelerated. It is obvious that there is less retardation the later the addition of SP. Furthermore, the PCE alter the hydration of C3A when added delayed and exhibit changes in kinetics and hydration rates. XRD results showed that more C3A is dissolved in the presence of PCE. Also, the gypsum depletion occurs earlier in the presence of PCE and even faster with delayed addition. Without PCE AFm starts to form just after the gypsum depletion. However, in the presence of PCE AFm already starts to form at the beginning of the hydration. Due to the faster gypsum depletion in the presence of PCE, also the transformation from ettringite into AFm begins earlier, but takes longer as without SP.
The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has enormous influence on the early hydration of cement. C3A as the most reactive phase of Portland cement plays a significant role in early hydration reactions and affects the rheological performance. Therefore, this talk presents experimental results about the influence of delayed addition of PCEs on the Hydration of alite and C3A-gypsum pastes investigated by isothermal heat flow calorimetry. Complementary in-situ XRD was carried out on C3S and C3A-gypsum pastes to analyze hydration and phase changes related to the addition of PCE. Cement pastes with a delayed addition of PCE showed less retardation compared to simultaneous addition. The alteration caused by PCE is much more pronounced for C3A-gypsum mixes. With a delayed addition of SP, the hydration of C3A is less retarded or even accelerated. It is obvious that there is less retardation the later the addition of SP. Furthermore, the PCE alter the hydration of C3A when added delayed and exhibit changes in kinetics and Hydration rates. XRD results showed that more C3A is dissolved in the presence of PCE. Also, the gypsum depletion occurs earlier in the presence of PCE and even faster with delayed addition. Without PCE AFm starts to form just after the gypsum depletion. However, in the presence of PCE AFm already starts to form at the beginning of the hydration. Due to the faster gypsum depletion in the presence of PCE, also the transformation from ettringite into AFm begins earlier, but takes longer as without SP.
In the 21st century, adequate habitat and functioning infrastructure are critical for global societal and economic stability. In addition, growing urbanisation and environmental pollution cause challenges to societies.
With increasing velocity, humanity faces that the current way of living is not sustainable. Thus, habitat,infrastructure, urbanisation, environment and sustainability are definitively among the most striking challenges of the 21st century.
By consulting, planning, building, maintaining, exploiting and processing of global resources, civil engineers contribute significantly to the existence of these challenges. This is a high responsibility, but due to the heavy involvement, together with adjacent disciplines such as architecture, geosciences, chemistry,
physics, environmental sciences and economics, civil engineers also hold the key to mitigate these challenges and provide a brighter global future.
Solutions towards greener, more sustainable and economically viable materials do exist, and there is ongoing research on how greener technologies can contribute to better livelihood and economic growth, but their level of implementation is limited, a major reason for which is that these approaches require more fundamental understanding rather than standard application.
While today, engineers can choose from a wide range of rheology modifying admixtures, in some parts of the world, these are difficult to access, due to their complex processing. However, alternatives can be bio-based polymers such as polysaccharides from various sources. These are easily accessible all over the world, do not demand for complicated processing, and typically they are more sustainable than many established materials, which are crude oil-based.
The paper presents the effects of acacia gum, cassava starch and the gum of triumfetta pendrata A. Rich on the rheological performance of cementitious systems. It is shown that acacia gum can be as efficient as polycarboxylate based superplasticisers, cassava starch can reduce the yield stress slightly with little effect on the plastic viscosity, and the gum of triumfetta pendrata A. Rich increases the thixotropy of cement pastes with plasticizing polymers significantly.
While today, engineers can choose from a wide range of rheology modifying admixtures, in some parts of the world, these are difficult to access, due to their complex processing. However, alternatives can be bio‐based polymers such as polysaccharides from various sources. These are easily accessible all over the world, do not demand for complicated processing, and typically they are more sustainable than many established materials, which are crude oil‐based.
The paper presents the effects of acacia gum, cassava starch and the gum of triumfetta pendrata A. Rich on the rheological performance of cementitious systems. It is shown that acacia gum can be as efficient as polycarboxylate based superplasticisers, cassava starch can reduce the yield stress slightly with little effect on the plastic viscosity, and the gum of triumfet ta pendrata A. Rich increases the thixotropy of cement pastes with plasticizing polymers significantly.
Structural design and application have always been linked to the compressive strength of concrete as the main relevant criterion. This was justifiable in the past, where concrete consisted of water, ordinary Portland cement and aggregates, but this concept is no longer relevant for modern and more sustainable cement and concrete.
Despite these new developments, existing standards, guidelines and academic curricula have not been much updated and are still used worldwide. There is a need to change this situation by proper education of the users.
This overview describes the challenges that arise at a user Level from the higher complexity of modern concrete, and defines needs and requirements for enhanced applicability of sustainable concrete concepts.
Furthermore, recommendations are given on how better concrete practice can be communicated to all the involved parties, from civil and design engineers to constructors and site-appliers on the construction site.
The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has an enormous influence on the early hydration of cement. The hydration is retarded and the timing of formation and the morphology of hydrates is affected. This short paper presents experimental results about the influence of delayed addition time of PCE SPs on hydration of cement and alite pastes, investigated by isothermal heat flow calorimetry. For cement as well as for alite pastes the hydration is retarded with SP, whereby the high charge PCE has a stronger retarding effect than the low charge PCE. The retardation caused by PCE is much more pronounced for alite than for cement mixes. If PCE is added later to the mix, the induction period is shortened and the hydration is accelerated compared to simultaneous addition. This applies for cement and alite pastes. With delayed PCE addition the alite shows a clearly less retarded setting and main hydration than after simultaneous addition. It is obvious that for alite pastes there is less retardation the later the addition of SP.
The paper presents rheometric results and hydration curves for cementitious systems based on cement mixed with different aqueous phases at solid volume fraction of = 0.45. The varied aqueous phases were deionized water, limewater, the filter residue of a cement paste mixed at w/c = 2.0, and the filtrate of cement paste at solid volume fraction of 0.45. Each cementitious system provided different amounts and sizes of particles formed in the aqueous phase. The pastes were observed with and without polycarboxylate ether based superplasticizer. It was observed that the presence of particles causes higher PCE saturation dosages to achieve a minimum value, but the minimum value is only affected in the case of large particles. In all cases with and without PCE, the presence of small particles causes increased plastic viscosity. In addition, with decreased number and size of hydrates in the aqueous phase the hydration was retarded, which was specifically pronounced in the presence of PCE
Die meisten Einflüsse auf die Rheologie von Beton wirken auf sehr kleinen Skalenebenen. Einflussgrößen im Millimeter oder Zentimeterbereich sind im Wesentlichen auf den Sand und die Gesteinskörnung beschränkt. Letztere machen aber in den meisten Betonen 50 %-70 % des Gesamtvolumens aus, was bei Untersuchungen zur Steuerung der Verarbeitungseigenschaften von Beton häufig vernachlässigt wird. Während Betonzusatzmittel und Zusatzstoffe bei geeigneter Wahl die Rheologie sehr gezielt beeinflussen können, eignen sich Sand und Gesteinskörnung weniger gut zur Steuerung der Rheologie, aber sie tragen zur Rheologie des Gesamtsystems bei. Hierbei können Effekte aus Sand und Gesteinskörnung die Effekte von Zusatzmitteln und Zusatzstoffen überlagern und im ungünstigsten Falle sogar nahezu unwirksam machen. Deshalb sollten Ergebnisse zur Verarbeitbarkeit von Bindemittelsystemen nur mit großer Sorgfalt auf Beton übertragen werden. Es ist wichtig, den Einfluss des Sandes und der Gesteinskörnung besser zu verstehen, um diese so abzustimmen, dass sie Effekte aus Fließmitteln positiv ergänzen anstatt diesen entgegenzuwirken.
Durch eine gezielte Abstimmung lassen sich Kosten wirksam sparen.
Most factors acting on concrete rheology work at an extremely small-scale level. Influencing factors in the millimetre or centimetre area are essentially restricted to sand and aggregates. The latter, however, make up 50 to 70% of the total volume of most concretes – a fact often ignored in research on controlling concrete processing properties.
Whereas suitably chosen concrete admixtures and additives can influence rheology in a very targeted manner, sand and aggregates are less suitable for controlling rheology but nonetheless contribute to the rheology of the Overall system. The actions of sand and aggregate can impose themselves upon the actions of admixtures and additives
and, in unfavourable circumstances, even render them redundant. For this reason, any results concerning the processability of binding agent systems can only be transferred to concrete with great care. It is important to better understand the action of sand and aggregates in order to be able to harmonise them in such a way that they complement the action of superplasticisers positively, instead of
working against them. Savings on costs can also be made by this targeted fine-tuning.
This poster provides an overview of ultrasonic investigations of an engineered test barrier at ERAM Morsleben, which were completed as part of contractual work with the Bundesgesellschaft für Endlagerung mbH (BGE). This includes both experiments with the Large Aperture Ultrasound System (LAUS) and the ultrasonic borehole array. Also included in the poster is a description of the planned BAM thematic project “SealWasteSafe”. In particular, the proposed geopolymer materials are described and future research requirements are detailed.
The state of fresh concrete is predominantly determined by the rheological properties of the cement paste. In order to control performance spectra and requirements of novel concretes and to better understand macroscopic phenomena, comprehensive knowledge of the material behavior of fresh cement suspensions as well as of the complex relationships of mechanisms at the nano and micro scale are necessary. This work focuses on micro and nano rheology of suspensions of cementitious model systems and the influence of polycarboxylate-based admixtures on the rheology. The phenomena are driven by multiple parameters such as adsorption and particle interactions. Hence, the first part examines the interaction between polycarboxylate ether (PCE) and synthesized clinker phases and hydration products as model systems with regard to early hydration products.
Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products.
Acoustic emission testing
(2018)
The African cement, concrete and construction business is growing at rapid pace. The cement sales are expected to grow rapidly until 2050. The number of newly built cement plants increases dramatically and in addition more cements are being imported from outside the continent, e.g. from Turkey, Pakistan, Indonesia, and China, driven by overcapacities in the countries of origin. This causes a high number of potentials and challenges at the same time. Newly built cement plants can operate directly at best technological state of the art and thus incorporate more sustainable technologies as well as produce new and more sustainable products such as cements blended with sustainable supplementary cementitious materials such as calcined clays, and industrial or agricultural by products. At the same time the new variety of binding agent as well as the international imports, which are driven by price considerations, make the cement market prone to quality scatter. This puts pressure on the quality control regulations and institutions to ensure safety of construction, healthy application, and environmental safety for the population. The paper presents possible solutions to build up the rapidly increasing African cement production more sustainably than in the rest of the world as well as the related challenges and obstacles that need to be overcome. Based on experiences with a series of pan-African cement testing laboratory proficiency schemes conclusions are made on technical, regulative and political level.
With ongoing innovation in process technology, the challenges of concrete technology are more and more focused on the rheological optimisation for these processes, since improper mixture stability or poor compaction ability negatively affect the concrete homogeneity and quality. However, along with the increasing complexity of today’s concrete mixture compositions, concrete becomes more prone to failure regarding the casting process. Variable properties of the raw materials typically cause changing workability. The reasons can be found among others in scattering water contents, physical or chemical properties of the cement or varying environmental temperatures. Robustness in the delicately adjusted rheology, however, is of utmost importance for modern and future process technology, from sprayed concrete over pumpable concrete towards 3D-printing, with regard to the long-term strength, the function and the durability. Typically, material induced changes cannot be identified easily due to the complex interactions of concrete constituents. Therefore, a precise and prompt counteraction is impossible. However, it is known that the yield stress can be controlled by addition of supplementary superplasticizer or stabilising agent. In combination with computerized process observation tools that can rapidly interpret and react on changes in the rheology, it is therefore thinkable, that only these two admixture types can adjust the rheology steadily and permanently, regardless of the actual root cause for observed macroscopic rheology change. The presentation will firstly give a comprehensive overview of effects at the interface between pore solution, particles and hydrates, which affect the rheology of fresh concrete. Secondly, ways are recommended how the rheology can be actively manipulated before eventually computerized methods are demonstrated that help to actively and rapidly assess and counteract performance scatter during steady casting processes.
Slags from the nonferrous metals industry have great potential to be used as feedstocks for the production of alkali-activated materials. Until now, however, only very limited information has been available about the structural characteristics of these materials. In the work presented herein, synthetic slags in the CaO–FeOx–SiO2 system, representing typical compositions of Fe-rich slags, and inorganic polymers (IPs) produced from the synthetic slags by activation with alkali Silicate solutions have been studied by means of X-ray absorption near-edge structure (XANES) spectroscopy at the Fe K-edge. The iron in the slags was largely Fe2+, with an average coordination number of approximately 5 for the iron in the amorphous fraction. The increase in average oxidation number after alkali-activation was conceptualized as the consequence of slag dissolution and IP precipitation, and employed to calculate the degrees of reaction of the slags. The degree of reaction of the slags increased with increasing amorphous fraction. The iron in the IPs had an average coordination number of approximately 5; thus, IPs produced from the Fe-rich slags studied here are not Fe-analogs of aluminosilicate geopolymers, but differ significantly in terms of structure from the latter.