- ja (1)
Eingeladener Vortrag
- nein (19)
Processing ultrasonic data by coda wave interferometry to monitor load tests of concrete beams
(2018)
Ultrasonic transmission measurements have been used for decades to monitor concrete elements, mostly on a laboratory scale. Recently, coda wave interferometry (CWI), a technique adapted from seismology, was introduced to civil engineering experiments. It can be used to reveal subtle changes in concrete laboratory samples and even large structural elements without having a transducer directly at the place where the change is taking place. Here, several load tests until failure on large posttensioned concrete beams have been monitored using networks of embedded transducers. To detect subtle effects at the beginning of the experiments and cope with severe changes due to cracking close to failure, the coda wave interferometry procedures had to be modified to an adapted step-wise approach. Using this methodology, we were able to monitor stress distribution and localize large cracks by a relatively simple technique. Implementation of this approach on selected real structures might help to make decisions in infrastructure asset management.
"INFRASTAR aims to develop knowledge, expertise and skills for optimal and reliable management of structures. The generic methodology is applied to bridges and wind turbines in relation to fatigue offering the opportunity to deal with complementary notions (such as old and new asset management, unique and similar structures, wind and traffic actions) while addressing 3 major challenges: 1/ advanced modelling of concrete fatigue behaviour, 2/new non destructive testing methods for early aged damage detection and 3/probabilistic approach of structure reliability under fatigue. Benefit of cross-experience and inter-disciplinary synergies creates new knowledge. INFRASTAR proposes innovative solutions for civil infrastructure asset management so that young scientists acquire a high employment profile in close dialogue between industry and academic partners. Modern engineering methods, including probabilistic approaches, risk and reliability assessment tools, will take into account the effective structural behaviour of existing bridges and wind turbines by exploiting monitored data. Existing methods and current state-of -the art is based on excessive conservatism which produces high costs and hinders sustainability. INFRASTAR improves knowledge for optimising the design of new structures, for more realistic verification of structural safety and more accurate prediction of future lifetime of the existing structures. That is a challenge for a sustainable development because it reduces building material and energy consumption as well as CO2 production. Within the global framework of optimal infrastructure asset management, INFRASTAR will result in a multi-disciplinary body of knowledge covering generic problems from the design stage process of the new civil infrastructures up to recycling after dismantlement. This approach and the proposed methods and tools are new and allow a step forward for innovative and effective process."
Advanced ultrasonic imaging for concrete: Alternative imaging conditions for reverse time migration
(2018)
Ultrasound echo is a widely used NDT technique for determining the internal geometry of structures. Reverse-time migration (RTM) has been recently introduced to NDT applications, as an imaging method for ultrasound data, to overcome some of the limitations (e.g. imaging steeply dipping reflector) experienced by the Synthetic Aperture Focusing Technique (SAFT), the most commonly used imaging algorithm for these measurements.
The standard implementation of RTM also experiences some drawbacks caused by its imaging condition, which is based on the zero-lag of the cross-correlation between source and receiver wavefields and generates high-amplitude low-frequency artifacts. Three alternative imaging conditions, developed for seismic data applications, were tested for their ability to provide better images than the standard cross-correlation: illumination compensation, deconvolution and wavefield decomposition. A polyamide specimen was chosen for the simulation of a synthetic experiment and for real data acquisition. The migrations of both synthetic and real data were performed with the software Madagascar. The illumination imaging condition was able to reduce the low-frequency noise and had a good performance in terms of computing time. The deconvolution improved the resolution in the synthetic tests, but did not showed such benefit for the real experiments. Finally, as for the wavefield decomposition, although it presented some advantages in terms of attenuating the low-frequency noise and some unwanted reflections, it was not able to image the internal structure of the polyamide as well as the cross-correlation did. Suggestions on how to improve the cost-effectiveness of the implementation of the deconvolution and wavefield decomposition were presented, as well as possible investigations that could be carried out in the future, in order to obtain better results with those two imaging conditions.
Ultrasound echo is a widely used NDT technique for determining the internal geometry of structures. Reverse-time migration (RTM) has been recently introduced to NDT applications, as an imaging method for ultrasound data, to overcome some of the limitations (e.g. imaging steeply dipping reflector) experienced by the Synthetic Aperture Focusing Technique (SAFT), the most commonly used imaging algorithm for these measurements.
The standard implementation of RTM also experiences some drawbacks caused by its imaging condition, which is based on the zero-lag of the cross-correlation between source and receiver wavefields and generates high-amplitude low-frequency artifacts. Three alternative imaging conditions, developed for seismic data applications, were tested for their ability to provide better images than the standard cross-correlation: illumination compensation, deconvolution and wavefield decomposition. A polyamide specimen was chosen for the simulation of a synthetic experiment and for real data acquisition. The migrations of both synthetic and real data were performed with the software Madagascar. The illumination imaging condition was able to reduce the low-frequency noise and had a good performance in terms of computing time. The deconvolution improved the resolution in the synthetic tests, but did not showed such benefit for the real experiments. Finally, as for the wavefield decomposition, although it presented some advantages in terms of attenuating the low-frequency noise and some unwanted reflections, it was not able to image the internal structure of the polyamide as well as the cross-correlation did. Suggestions on how to improve the cost-effectiveness of the implementation of the deconvolution and wavefield decomposition were presented, as well as possible investigations that could be carried out in the future, in order to obtain better results with those two imaging conditions.
Seismic interferometry (SI) deals either with the sensible detection of changes in the subsurface or with the reconstruction of virtual signals between two receivers by crosscorrelation of signals from diffuse sources. These concepts can be applied in NDT in civil engineering for various purposes, e. g. to detect changes in bridges. Here it is demonstrated using data from a reference structure on our test site. Practical applications can be expected in the very near future.
Seismic interferometry (SI) deals either with the sensible detection of changes in the subsurface or with the reconstruction of virtual signals between two receivers by crosscorrelation of signals from diffuse sources. These concepts can be applied in NDT in civil engineering for various purposes, e. g. to detect changes in bridges. Here it is demonstrated using data from a reference structure on our test site. Practical applications can be expected in the very near future.
Previous work has shown that ultrasonic monitoring using externally applied or embedded transducers and imaging methods based on coda wave interferometry are able to detect subtle changes in concrete elements. In this study, a limited number of embedded transducers has been used to monitor changes in several 12 m long two-span concrete beams subjected to point or linear loads until failure.
The ultrasonic results showed the high sensitivity to stress changes and the nonlinear character of the associated effects. However, the ultrasonic features showed a very good correlation to several conventional monitoring parameters. For higher loads (significant amount of cracking), the technique had to be modified to cope with large wave velocity variations and high decorrelation compared to the reference signal.
Using a very simple imaging procedure, the 2D stress field inside the beam has been visualized including inhomogeneities and artifact at places where cracking occurred at higher loads. The technique has the potential to be included in real time monitoring systems.
Ultrasonic transmission measurements are used to monitor concrete elements mostly on a laboratory scale since decades.
Recently, coda wave interferometry, a technique adapted from seismology, has been introduced to civil Engineering experiments. It can be used to reveal subtle changes in concrete samples and even large construction elements without having a transducer directly at the location where the change is taking place. The methodology works best with embedded transducers to avoid coupling issues or excessive environmental influence. These transducers can be used for newly built and existing structures. Recently, large concrete beams have been equipped with a network of transducers and loaded until failure. Using code wave interferometry, it was possible to visualize stress fields and damaged areas.
The LAUS: First applications of a new system for ultrasonic imaging of very concrete structures
(2018)
The LAUS (Large Aperture Ultrasonic System) has been developed to image very thick concrete structures, which are not accessible for commercial systems. The device and the corresponding software is the result of joint research of BAM, an ultrasonic instrument manufacturer and University of Kassel, Germany. It consists of 12 separate arrays of 32 point-contact shear wave transducers each, which can be deployed in flexible configurations. Each array is combined with battery and transmitter, receiver and wireless communication electronics.
Three case histories are presented. First the system was deployed on a 5-m thick heavily reinforced foundation slab. The reflection of the slab’s bottom was imaged clearly. In addition, a multiple reflection was registered, thus giving hope that even thicker elements might be imaged by the instrument. Second, the LAUS was used to investigate a massive bridge girder where a heavy rainstorm during concreting had led to imperfections that were visible after removing the formwork was removed. The LAUS could image tendon ducts in 1.8m depth and the backwall closely behind them. Some limited areas showed blurred reflections and were checked by drill holes; these areas were affected by diffuse damage which could be repaired by injections. Third, a large retaining wall was checked for thickness.
Meanwhile, the LAUS has been used in underground waste deposits (nuclear and other) for quality assurance of sealing plugs. A confirmed penetration depth of about 7 m has been reached.
The ageing and decommissioning of nuclear concrete infrastructure (e. g. safety containments) as well as the building and closure of waste repositories gives new challenges to non-destructive testing. For example, the quality assurance of very thick concrete structures is beyond the limitations of commercial ultrasonic instrumentation.
The presentation introduces typical testing tasks and the application of state of the art NDT techniques. In addition, it describes some new developments in ultrasonic testing and monitoring. Specifically, the application of the unique deep penetration system LAUS is shown. Ultrasonic monitoring using embedded transducers to check for subtle and sudden changes in the material is introduced as well.
The propagation of ultrasonic waves in concrete is affected by its micro- and macro-structure, geometry and properties as well as external influences as stress, temperature or moisture. In addition, age and degradation have a strong influence. Therefore, Ultrasound has been used to monitor concrete samples and structures since decades. However, early applications using conventional techniques as time-of flight or changes in amplitudes have been limited to detect changes in a late stage close to serviceability or ultimate load states.
Around 2000, several new, more sensitive techniques adopted from geophysics or other field of material sciences have been introduced to research in ultrasonic monitoring of concrete. The most discussed methodologies are coda wave interferometry, a technique which allows to detect very subtle changes from repeated ultrasonic measurements. Nonlinear acoustic techniques help to identify e. g. cracks even in an inhomogeneous background. Both techniques can be combined.
This paper reviews methods and results achieved so far on the laboratory scale and with full scale models the directions for future research and application is given as well.
The LAUS: First Applications of a New System for Ultrasonic Imaging of Very Concrete Structures
(2019)
The LAUS (Large Aperture Ultrasonic System) has been developed to image very thick concrete structures, which are not accessible for commercial systems. The device and the corresponding software is the result of joint Research of BAM, an ultrasonic instrument manufacturer and University of Kassel, Germany. It consists of 12 separate Arrays of 32 point-contact shear wave transducers each, which can be deployed in flexible configurations. Each array is combined with battery and transmitter, receiver and wireless communication electronics.
Three case histories are presented. First the system was deployed on a 5-m thick heavily reinforced foundation slab.
The reflection of the slab’s bottom was imaged clearly. In addition, a multiple reflection was registered, thus giving hope that even thicker elements might be imaged by the instrument. Second, the LAUS was used to investigate a massive bridge girder where a heavy rainstorm during concreting had led to imperfections that were visible after removing the formwork was removed. The LAUS could image tendon ducts in 1.8m depth and the backwall closely behind them. Some limited areas showed blurred reflections and were checked by drill holes; these areas were affected by diffuse damage which could be repaired by injections. Third, a large retaining wall was checked for thickness.
Meanwhile, the LAUS has been used in underground waste deposits (nuclear and other) for quality assurance of sealing plugs. A confirmed penetration depth of about 7 m has been reached.
Ultrasonic transmission measurements are used to monitor concrete elements mostly on a laboratory scale since decades. Recently, coda wave interferometry, a technique adapted from seismology, has been introduced to civil engineering experiments. It can be used to reveal subtle changes in concrete samples and even large construction elements without having a transducer directly at the location where the change is taking place. The methodology works best with embedded transducers to avoid coupling issues or excessive environmental influence. These transducers can be used for newly built and existing structures. Recently, large concrete beams have been equipped with a network of transducers and loaded until failure. Using code wave interferometry, it was possible to visualize stress fields and damaged areas. This paper gives an overview of the state of the art, recent results achieved at BAM and a task list for further results and development.
Seismic methods are increasingly used to improve ultrasonic imaging and monitoring of concrete. At BAM, we are research mainly the use of Reverse Time Migration to get better images from ultrasonic echo data of thick, complex concrete structures. Coda wave interferometry is used to detect subtle changes in concrete constructions, e. g. using embedded ultasonic transducers.
Ultrasonic non-destructive testing methods have found various applications in quality assurance and condition assessment of nuclear concrete structures. This includes but is not limited to the localization of construction features (thickness measurements, reinforcement, tendon ducts, and others) and damage detection (e. g. corrosion or cracks). However, there are still limitations, e. g. limited penetration depth and resolution, issues when testing hybrid steel/concrete structures as well as absence of standards and regulations.
This presentation will show progress in some of these issues and will focus on advanced instrumentation and validation of ultrasonic NDT for concrete structures.
Ultrasonic echo testing has been limited to a penetration depth of less than one meter in reinforced concrete. The development of the LAUS (Large Aperture Ultrasonic System), using a large array of ultrasonic transducers and wider offsets between transmitter and receiver, allows to reach up to 5 m in reinforced concrete and 9 m in unreinforced concrete. This capability has been demonstrated by collecting data from an engineered salt concrete barrier in an underground nuclear waste storage facility. Due to an increasingly competitive environment, commercial manufacturers will continue to develop equipment with enhanced penetration and/or increased resolution.
To quantify the capabilities and reliability of ultrasonic tests, validation mockups with engineered flaws are required. EPRI and BAM have built a large-scale mockup at a test site close to Berlin (BAM-TTS, Horstwalde) using a design which is repeated at other places. This presentation will also cover the methods deployed on engineered flaws and the repeatability of the test results.
The propagation of ultrasonic waves in concrete is affected by its micro- and macro-structure, geometry and properties as well as external influences as stress, temperature or moisture. In addition, age and degradation have a strong influence. Therefore, Ultrasound has been used to monitor concrete samples and structures since decades. However, early applications using conventional techniques as time-of flight or changes in amplitudes have been limited to detect changes in a late stage close to serviceability or ultimate load states.
Around 2000, several new, more sensitive techniques adopted from geophysics or other field of material sciences have been introduced to research in ultrasonic monitoring of concrete. The most discussed methodologies are coda wave interferometry, a technique which allows to detect very subtle changes from repeated ultrasonic measurements. Nonlinear acoustic techniques help to identify e. g. cracks even in an inhomogeneous background. Both techniques can be combined.
This paper reviews methods and results achieved so far on the laboratory scale and with full scale models the directions for future research and application is given as well.
Fatigue is one of the most prevalent issues, which directly influences the service life expectancy of concrete structures. Fatigue has been investigated for years for steel structures. However, recent findings suggest that concrete structures may also be significantly subjected to fatigue phenomena that could lead to premature failure of certain structural elements. To date, fatigue of reinforced concrete has been given little focus. Knowledge on the influence factors and durability/capacity effects on this material should be improved. Current technological means to measure fatigue in civil structures like bridges and wind turbines (both onshore and offshore) are outdated, imprecise and inappropriate.
Meanwhile, this topic has got much more attention as time-variant loading on concrete structures plays an increasing role, e.g. in bridges with increasing traffic and heavier trucks, and for wind turbines for renewable energy production, e.g. for offshore wind turbine support structures affected by wind and waves.
The European Innovative Training Networks (ITN) Marie Skłodowska-Curie Actions project INFRASTAR (Innovation and Networking for Fatigue and Reliability Analysis of Structures - Training for Assessment of Risk) provides research training for 12 PhD students. The project aims to improve knowledge for optimizing the design of new structures as well as for more realistic verification of structural safety and more accurate prediction of the remaining fatigue lifetime of existing concrete structures.
First, the INFRASTAR research framework is detailed. Then it will be exemplified through the presentation of the major results of the four PhD students involved in the work package dealing with auscultation and monitoring. This includes the development and improvement of Fiber Optics (FO) and Coda Wave Interferometry (CWI) for crack sizing and imagery, new sensor technologies and integration, information management, monitoring strategy for fatigue damage investigation and lifetime prediction.