The thermal stability of the microstructure of a heat-resistant cobalt alloy, which consists of a γ solid solution strengthened with γ'-phase precipitates, has been studied. The temperature behavior of the dissolution of the hardening γ' phase and the kinetics of its coarsening at 700 and 800°C have been determined. It is found that, during prolonged annealing at 800°C, the γ' → β phase transformation occurs.
Scanning Electron Microscopy (SEM) or Transmission Electron Microscopy (TEM) ? This is a question, nowadays discussed in EM labs of research and industry involved in the characterization and metrology of nanoparticles. The Scanning principle is adapted to TEM, the Transmission mode is adapted to Ultra High Resolution SEM. Can modern SEM replace TEM, reach atomic resolution even without Cs corrector or nm lateral resolution for X-ray Spectroscopy (EDX)?
Due to the development of a New Cold Field Emission (NCFE) electron source Hitachi SEMs SU9000 and SU8200 can deliver routinely sub-nm image resolution and EDX mappings at very high count rates and a lateral EDX resolution of a few nm. A TiO2 sample provided by BAM was analysed at 30 kV using low kV STEM – simultaneously with the Through-the-lens (TTL) SE detector, the Bright Field transmission and Dark Field transmission signals. By this method a pixel-precise information of the particle’s surface using SE, its chemical nature using DF-STEM and its crystalline structure using Bright Field signal is given in one 40sec scan. The advantage of this observation mode compared to Ultra Low Voltage imaging is outlined.
The TiO2 material selected for the present inter-laboratory comparison (ILC) was the bipyramidal anatase UT001 batch synthesized hydrothermally by University of Turin in the frame of the EU/FP7 Project SETNanoMetro and carefully prepared on TEM grids by BAM to be distributed to the ILC participants. A clear measurement protocol including data analysis and reporting (including an xls reporting template) has been also prepared by BAM. 14 of 18 participants have measured and reported results which have been already checked by BAM as being conform to the agreed protocol. After receiving the last results (of 4 participants) the ILC data evaluation will be carried out by BAM in line with agreed ISO/TC229 procedures as for the other case sudies.
A proposal of an inter-laboratory study (ILC) on determination of size and shape distribution of TiO2 nanoparticles (NPs) by transmission electron microscopy is presented. The anatase NPs synthesized in a controllable fashion within the EU/FP7 project SETNanoMetro can be considered as shape-defined (bipyramidal) and are offered to complete the list of case studies already in progress within ISO/TC229/JWG2. The main points of the measurement procedure are presented as well as a proposed procedure to evaluate the size and shape according to the standard operation procedure already developed within SETNanoMetro is discussed. Potential ILC participants and a plan with next step to be carried out are proposed.
Scanning Electron Microscopy (SEM) or Transmission Electron Microscopy (TEM) ? This is a question, nowadays discussed in EM labs of research and industry involved in the characterization and metrology of nanoparticles. The Scanning principle is adapted to TEM, the Transmission mode is adapted to Ultra High Resolution SEM. Can modern SEM replace TEM, reach atomic resolution even without Cs corrector or nm lateral resolution for energydispersive X-ray spectroscopy (EDX)?
Due to the development of a New Cold Field Emission (NCFE) electron source Hitachi SEMs SU9000 and SU8200 can deliver routinely sub-nm image resolution and EDX mappings at very high count rates and a lateral EDX resolution of a few nm. A TiO2 sample provided by BAM was analysed at 30kV using low kV STEM – simultaneously with the Through-the-lens (TTL) SE detector, the Bright Field transmitted and Dark Field transmitted signals. By this method a pixel precise information of the particles surface using SE, its chemical nature using DF-STEM and its crystalline structure using Bright Field signal is given in one 40sec scan. The advantage of this observation mode compared to Ultra Low Voltage imaging is outlined.
The primary crystallite size of titania powder relates to its properties in a number of applications. Transmission electron microscopy was used in this interlaboratory comparison (ILC) to measure primary crystallite size and shape distributions for a commercial aggregated titania powder. Data of four size descriptors and two shape descriptors were evaluated across nine laboratories. Data repeatability and reproducibility was evaluated by analysis of variance. One-third of the laboratory pairs had similar size descriptor data, but 83% of the pairs had similar aspect ratio data. Scale descriptor distributions were generally unimodal and were well-described by lognormal reference models. Shape descriptor distributions were multi-modal but data visualization plots demonstrated that the Weibull distribution was preferred to the normal distribution. For the equivalent circular diameter size descriptor, measurement uncertainties of the lognormal distribution scale and width parameters were 9.5% and 22%, respectively. For the aspect ratio shape descriptor, the measurement uncertainties of the Weibull distribution scale and width parameters were 7.0% and 26%, respectively. Both measurement uncertainty estimates and data visualizations should be used to analyze size and shape distributions of particles on the nanoscale.
First results of an inter-laboratory comparsion launched in the frame of ISO/TC 229 'Nanotechnologies' / JWG 2 'Measurement and Characterization' are presented and the further data treatment discussed.
Feret min, Feret and Aspect Ratio of bipyramidal TiO2 nanoparticles as determined according to the measurememnt protocol distributed by BAM are compared for all 17 participants for the first time. The inclusion of the case study into the ongoing ISO/TC 229/JWG 2 project on Measurement of size and shape distribution of nanoparticles by TEM is discussed.
Efficient water electrolysis requires electrode coatings with high catalytic activity. Platinum efficiently catalyzes the hydrogen evolution reaction in acidic environments, but is a rare and expensive metal. The activity achieved per metal atom can be increased if small Pt particles are dispersed onto electrically conductive, highly accessible and stable support materials.
However, the addition of Nafion, a typical binder material used in the manufacture of electrode coatings, can decrease catalytic activity by the blocking of pores and active surface sites. A new approach is reported for the direct synthesis of highly active Nafion-free Pt/C catalyst films consisting of small Pt nanoparticles supported in size-controlled mesopores of a conductive carbon film. The synthesis relies on the co-deposition of suitable Pt and C precursors in the presence of polymer micelles, which act as pore templates. Subsequent carbonization in an inert atmosphere produces porous catalyst films with controlled film thickness, pore size and particle size. The catalysts clearly outperform all Nafion-based Pt/C catalysts reported in the literature, particularly at high current densities.
Of many experimental techniques for measuring particle sizes and size distributions, electron microscopy (EM) is still considered as the gold standard, especially in the nano range (1–100 nm). Furthermore, high-resolution X-ray spectroscopy (EDX) in conjunction with EM can be applied to individul NPs.
Preparation of an EM sample for generic particulate materials is a difficult task. Usually, the particles in a suspension are deposited on a support. However, this procedure includes the drying of larger solvent amounts on the substrate itself, and this can affect the spatial distribution of the deposited particles. One possibility to overcome this is the use of an electrospray system, where the suspension of particles is sprayed onto the substrate in charged droplets that are so small that they either dry off on the substrate immediately without affecting the position of particles, or even already during their flight time to the substrate. Additionally, the charging of particles minimizes agglomeration and aggregation, maximizing the collection of the EM grids.
The prototype of an electrospray deposition System was tested. Electrospray is theoretically described since a long time, but no dedicated commercial instruments are available for the preparation of TEM grids yet, apart from electrostatic deposition of aerosols.
Several materials have been sprayed onto TEM grids and the resulting particle distributions were evaluated. Operation parameters such as the sample flow-rate, capillary – substrate distance, electric field strength and sampling period length have been optimized. It was found that the particles deposited by electrospray generally show a much more homogeneous spatial distribution on the substrate and a substantial increase of the number of single particles (suited to automatic analysis).