Background: Gas sensors are very important in several fields like gas monitoring, safety and environmental applications. In this approach, a new gas sensing concept is investigated which combines the powerful adsorption probability of metal oxide conductive sensors (MOS) with an optical ellipsometric readout. This concept Shows promising results to solve the problems of cross sensitivity of the MOS concept.
Results: Undoped tin oxide (SnOx) and iron doped tin oxide (Fe:SnOx) thin add-on films were prepared by magnetron sputtering on the top of the actual surface plasmon resonance (SPR) sensing gold layer. The films were tested for their sensitivity to several gas species in the surface plasmon resonance enhanced (SPREE) gas measurement. It was found that the undoped tin oxide (SnOx) shows higher sensitivities to propane (C3H8) then to carbon monoxide (CO). By using Fe:SnOx, this relation is inverted. This behavior was explained by a change of the amount of binding sites for CO in the layer due to this iron doping. For hydrogen (H2) no such relation was found but the sensing ability was identical for both layer materials. This observation was related to a different sensing mechanism for H2 which is driven by the Diffusion into the layer instead of adsorption on the surface.
Conclusion: The gas sensing selectivity can be enhanced by tuning the properties of the thin film overcoating. A relation of the binding sites in the doped and undoped SnOx films and the gas sensing abilities for CO and C3H8 was found. This could open the path for optimized gas sensing devices with different coated SPREE sensors.
Over the past decades, the growing industry working for lightweight constructions has demanded materials exhibiting improved properties such as higher mechanical modulus and strength, better chemical resistance and lower costs of production.
It is known that especially nanofibers tend to enhance the mechanical, thermal and electrical properties of polymers. Therefore, some types of nanofibers are already being used embedded in polymeric matrix of sports equipment, aircraft parts and automobile components. However, nanofibers are a relatively new material category, the consequences of which for mankind are not yet fully known. Nanofibers detached from polymeric materials can be released into the environment during, e.g., processing and aging. The risks in dealing with such nanofibers are generally unknown, even if further studies of health aspects are being carried out. Problems always arise when the fibers can penetrate the cells, thus the mechanical rigidity of nanofibers is a key factor in assessing the risks. Common methods describe the geometry of nanofibers. These methods are necessary, but not sufficient to describe the mechanical properties, as for during manufacture and aging these properties may change; the modulus and strength values may differ from those of the original fibers.
Different experimental techniques for nanomechanical testing have been studied using the atomic force microscope, the scanning electron microscope and transmission electron microscope, showing promising results.
This project aims to evaluate the bending stiffness of CNTs with an experimental setup within the Dynamic Scanning Electron Microscope. Based on the Euller-Bernoulli beam theory, the Young’s modulus of CNTs can be obtained using the resonance frequency of mechanically excited nanofibers, its dimensions and density. The resonance frequency is acquired by extracting the signals of the secondary electrons when the nanofibers show significant vibration movement, also possible to be seen on the microscope images. The electronic signals of the secondary electrons are filtered and treated by a lock-in amplifier, so the corresponding amplitude and phase values can be evaluated. This method could be applied to any nanofiber that has the shape similar to a symmetric beam.