8.0 Abteilungsleitung und andere
Filtern
Dokumenttyp
- Zeitschriftenartikel (119) (entfernen)
Schlagworte
- Thermography (23)
- NDT (11)
- Non-destructive testing (9)
- Additive manufacturing (8)
- Laser thermography (8)
- Additive Manufacturing (7)
- Infrared thermography (6)
- GFRP (5)
- Machine learning (5)
- Super resolution (5)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (119)
- 8.0 Abteilungsleitung und andere (119)
- 9 Komponentensicherheit (14)
- 8.5 Röntgenbildgebung (13)
- 5 Werkstofftechnik (8)
- 9.3 Schweißtechnische Fertigungsverfahren (8)
- 1 Analytische Chemie; Referenzmaterialien (6)
- 7 Bauwerkssicherheit (6)
- 9.6 Additive Fertigung metallischer Komponenten (6)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (5)
Paper des Monats
- ja (5)
Low-velocity impact damages were monitored in-situ using an infrared camera before, during and after Impact load. Thermal images were recorded as a function of time at the front side (impact) as well as at the rear side of the plates using a high frame rate. In CFRP and GFRP specimens with different thicknesses and made of various types of fibers and matrix materials, different kind of damages were observed. The sizes of the heated areas being related to the damages and the amount of energy dissipated into heat was determined quantitatively as a function of impact energy and are a measure of the resistance of the different materials against impact load.
In this work, we present a novel approach to photothermal super resolution based thermographic resolution of internal defects using two-dimensional pixel pattern-based active photothermal laser heating in conjunction with subsequent numerical reconstruction to achieve a high-resolution reconstruction of internal defect structures. With the proposed adoption of pixelated patterns generated using laser coupled high-power DLP projector technology the complexity for achieving true two-dimensional super resolution can be dramatically reduced taking a crucial step forward towards widespread practical viability. Furthermore, based on the latest developments in high-power DLP projectors, we present their first application for structured pulsed thermographic inspection of macroscopic metal samples. In addition, a forward solution to the underlying inverse problem is proposed along with an appropriate heuristic to find the regularization parameters necessary for the numerical inversion in a laboratory setting. This allows the generation of synthetic measurement data, opening the door for the application of machine learning based methods for future improvements towards full automation of the method. Finally, the proposed method is experimentally validated and shown to outperform several established conventional thermographic testing techniques while conservatively improving the required measurement times by a factor of 8 compared to currently available photothermal super resolution techniques.
In this work, the limits of using spatially structured heating combined with subsequent photothermal super resolution reconstruction for the thermographic detection and resolution of internal defects are investigated. The approach is based on the application of modern high-power laser projector technology, which is used to repeatedly project varying spatially structured 2D pixel patterns to photothermally heat the object under test. After processing the generated thermographic data using nonlinear convex optimisation in conjunction with exploiting the joint-sparse nature of the defect signals within the individual measurements, a high-resolution 2D-sparse defect/inhomogeneity map is obtained. The main focus of the investigation is set on the influence of the number of individual measurements on the achievable reconstruction quality. Using numerical simulations based on an analytical representation of the forward solution to the underlying inverse problem, the convergence rate over performed measurements of the achievable reconstruction quality is determined. Finally, all findings are experimentally validated by reconstructing a set of internal defects in an additively manufactured sample. In this work, it is shown that for a variety of different defect separation distances, the projection of 50 different pixel patterns allows for a good trade-off between experimental complexity and reconstruction quality.
Thermographic photothermal super resolution reconstruction enables the resolution of internal defects/inhomogeneities below the classical limit, which is governed by the diffusion properties of thermal wave propagation. Based on a combination of the application of special sampling strategies and a subsequent numerical optimization step in post-processing, thermographic super resolution has already proven to be superior to standard thermographic methods in the detection of one-dimensional defect/inhomogeneity structures. In our work, we report an extension of the capabilities of the method for efficient detection and resolution of defect cross sections with fully two-dimensional structured laser-based heating. The reconstruction is carried out using one of two different algorithms that are proposed within this work. Both algorithms utilize the combination of several coherent measurements using convex optimization and exploit the sparse nature of defects/inhomogeneities as is typical for most nondestructive testing scenarios. Finally, the performance of each algorithm is rated on reconstruction quality and algorithmic complexity. The presented experimental approach is based on repeated spatially structured heating by a high power laser. As a result, a two-dimensional sparse defect/inhomogeneity map can be obtained. In addition, the obtained results are compared with those of conventional thermographic inspection methods that make use of homogeneous illumination. Due to the sparse nature of the reconstructed defect/inhomogeneity map, this comparison is performed qualitatively.
This paper studies the dispersion of GPR wave’s phase velocity at different wideband frequencies in plywood and concrete with varying moisture content. This study makes use of two GPR antennas with 2 GHz centre frequency operating in wide angle reflection and refraction (WARR) mode and with computation of spectral analysis of the surface wave (SASW). Computation of phase velocities is based on the Acquisition of the cross-power spectrum and phase unwrap of two distorted ground waves at positions Closer to and farther away from the transmitting antenna. The velocities of the ground waves are found to experience greater dispersion in low frequency regimes within the effective frequency bandwidths determined and thresholded by time–frequency analysis (TFA) and coherence plotting of the ground waves.
This study validates not only the methodology, but also identifies the optimal distance between the first (Rx1) and second (Rx2) receivers as k/2, which is based on a fixed transmitter (Tx) minus the first Receiver (Rx1) distance. It serves as an indication of changeable separation distance when other lower frequency GPR is used because the distances of Tx-Rx1 and Rx1-Rx2 are wavelength dependent and thus also frequency dependent. Effects of moisture contents and chloride contamination in concrete were also characterized according to the dispersion plots . that wave traelling in lower frequencies in GPR wave is much decelerated than that in higher frequencies. This research also contributes to the building of the ‘‘GPRWARR machine” suggested in Annan and Jackson (2017) [1], within which the effects of wave Dispersion on phase velocity can be inversely modelled to characterize variations in the material properties of infrastructure as a means of detecting surface damage.
Classification of Spot-Welded Joints in Laser Thermography Data Using Convolutional Neural Networks
(2021)
Spot welding is a crucial process step in various industries. However, classification of spot welding quality is still a tedious process due to the complexity and sensitivity of the test material, which drain conventional approaches to its limits. In this article, we propose an approach for quality inspection of spot weldings using images from laser thermography data. We propose data preparation approaches based on the underlying physics of spot-welded joints, heated with pulsed laser thermography by analyzing the intensity over time and derive dedicated data filters to generate training datasets. Subsequently, we utilize convolutional neural networks to classify weld quality and compare the performance of different models against each other. We achieve competitive results in terms of classifying the different welding quality classes compared to traditional approaches, reaching an accuracy of more than 95 percent. Finally, we explore the effect of different augmentation methods.
We present an in situ triple coupling of synchrotron X-ray diffraction with Raman spectroscopy, and thermography to study milling reactions in real time. This combination of methods allows a correlation of the structural evolution with temperature information. The temperature information is crucial for understanding both the thermodynamics and reaction kinetics. The reaction mechanisms of three prototypical mechanochemical syntheses, a cocrystal formation, a C@C bond formation (Knoevenagel condensation), and the formation
of a manganese-phosphonate, were elucidated. Trends in the temperature development during milling are identified. The heat of reaction and latent heat of crystallization of the product contribute to the overall temperature increase. A decrease in temperature occurs via release of, for example, water as a byproduct.
Solid and liquid intermediates are detected. The influence of the mechanical impact could be separated from temperature effects caused by the reaction.
Dehydration is a common process occurring in natural environments, rocks, and building materials. Suitable methods for monitoring the changing moisture content should be identified.
We have investigated the impact of dehydration of sandstones on complex conductivity spectra. Spectral induced polarization measurements were performed on five sandstone samples during evaporative drying. The complex conductivity spectra indicate considerable changes with decreasing saturation. The relationship between conductivity and saturation can be described by a power law known as the second empirical Archie equation. Separate saturation exponents have been determined for the real and imaginary parts of conductivity. The imaginary part of conductivity indicates higher saturation exponents for the investigated sandstones compared to the real part. Obviously, the saturation exponents depend on the method used for changing water saturation. Evaporative drying, which is used in our experiments, causes an increase of pore-water salinity and results in lower saturation exponents for the real part of conductivity but higher exponents for the imaginary part in comparison with the classical imbibition/Drainage technique. We evaluate a theoretical approach that considers the influence of pore water salinity on the saturation exponents of the real and imaginary parts of conductivity. The complex conductivity spectra are processed by a Debye decomposition procedure.
The resulting integrating parameters such as direct current resistivity, total chargeability, normalized chargeability, and mean relaxation time indicate a power law dependence on saturation. Our experiments indicate that the imaginary part of conductivity and normalized chargeability have a high sensitivity related to the drying process of rocks and might be suitable indicators to Monitor the changes of moisture content in sandstones.
Integration of fiber reinforcement in high-performance cementitious materials has become widely applied in many fields of construction. One of the most investigated advantages of steel Fiber reinforced concrete (SFRC) is the deceleration of crack growth and hence its improved sustainability.
Additional benefits are associated with its structural properties, as fibers can significantly increase the ductility and the tensile strength of concrete. In some applications it is even possible to entirely replace the conventional reinforcement, leading to significant logistical and environmental benefits.
Fiber reinforcement can, however, have critical disadvantages and even hinder the Performance of concrete, since it can induce an anisotropic material behavior of the mixture if the fibers are not appropriately oriented. For a safe use of SFRC in the future, reliable non-destructive testing (NDT) methods need to be identified to assess the fibers’ orientation in hardened concrete. In this study,
ultrasonic material testing, electrical impedance testing, and X-ray computed tomography have been investigated for this purpose using specially produced samples with biased or random Fiber orientations. We demonstrate the capabilities of each of these NDT techniques for fiber orientation measurements and draw conclusions based on these results about the most promising areas for future research and development.
NMR is becoming increasingly popular for the investigation of building materials as it is a non-invasive technology that does not require any sample preparation nor causes damage to the material. Depending on the specific application it can offer insights into properties like porosity and spatial saturation degree as well as pore structure. Moreover it enables the determination of moisture transport properties and the (re-)distribution of internal moisture into different reservoirs or chemical phases upon damage and curing. However, as yet most investigations were carried out using devices originally either designed for geophysical applications or the analysis of rather homogeneous small scale (< 10 mL) samples. This paper describes the capabilities of an NMR tomograph, which has been specifically optimized for the investigation of larger, heterogeneous building material samples (diameters of up to 72 mm, length of up to 700 mm) with a high flexibility due to interchangeable coils allowing for a high SNR and short echo times (50 - 80 m s).
Relaxation phenomena observed in the electrical low-frequency range (approximately 1 mHz-10 kHz) of natural porous media like sandstones is often assumed to be directly related to the dominant (modal) pore throat sizes measured, for instance, with mercury intrusion porosimetry. Attempts to establish a universally valid relationship between pore size and peak Spectral Induced Polarization (SIP) relaxation time have failed, considering sandstones from very different origins and featuring great variations in textural and chemical compositions as well as in geometrical pore space properties. In addition working with characteristic relaxation times determined in Cole-Cole or Debye decomposition fits to build the relationship have not been successful. In particular, samples with narrow pore throats are often characterized by long SIP relaxation times corresponding to long “characteristic length scales” in these media, assuming that the diffusion coefficients along the electrical double layer were constant. Based on these observations, three different types of SIP relaxation can be distinguished. We present a new way of assessing complex pore spaces of very different sandstones in a multi-methodical approach to combine the benefits of mercury intrusion porosimetry, micro-computed tomography, and nuclear magnetic resonance. In this way, we achieve much deeper insight into the pore space due to the different resolutions and sensitivities of the applied methods to both pore constrictions (throats) and wide pores (pore bodies). We experimentally quantify pore aspect ratios and volume distributions within the two pore regions. We clearly observe systematic differences between three SIP relaxation types identified previously and can attribute the SIP peak relaxation times to measured characteristic length scales within our materials. We highlight selected results for a total of nine sandstones. It seems that SIP relaxation behavior depends on the size difference of the narrow pore throats to the wide pore bodies, which increases from SIP Type 1 to Type 3.
A concept for the application of a magnetocaloric device in energy-efficient air conditioners is introduced. In order to evaluate this concept, a test stand has been developed equipped with a magnetic field source providing about a 1.5-T flux density change into which different Regenerator geometries can be implemented and evaluated. A processing route for the production of profiled magnetocaloric LaFeSiMn-based composite plates by tape casting is presented. The processed plates show a maximum isothermal entropy change of about 3.8 J kg−1 K−1 at a magnetic field change of 1.5 T at 285 K. The hydraulic and thermal performance of regenerator geometries that can be realized by profiled plates is assessed by calculations.
Magnetocaloric composite wires have been studied by pulsed-field measurements up to μ0ΔH = 10 T with a typical rise time of 13 ms in order to evaluate the evolution of the adiabatic temperature change of the core, ΔTad, and to determine the effective temperature change at the surrounding steel jacket, ΔTeff, during the field pulse. An inverse thermal hysteresis is observed for ΔTad due to the delayed thermal transfer. By numerical simulations of application-relevant sinusoidal magnetic field profiles, it can be stated that for field-frequencies of up to two field cycles per second heat can be efficiently transferred from the core to the outside of the jacket. In addition, intense numerical simulations of the temperature change of the core and jacket were performed by varying different parameters, such as frequency, heat capacity, thermal conductivity and interface resistance in order to shed light on their impact on ΔTeff at the outside of the jacket in comparison to ΔTad provided by the core.
The knowledge of the thermal parameters of a particular concrete is essential for thermal design of a building, but also could help to identify and assess the state of a concrete structure. Active thermography has the potential to be applied onsite and to provide a fast investigation of thermal properties. In this work, three different concrete samples were investigated by active thermography in reflection and in transmission setup. It was found that this method yields the same results without direct contact as the Transient Plane Source (TPS) method as an established inspection tool.
Bei der Realisierung von Oberflächen-Schutz-System (OSS) auf Betonflächen ist die tatsächlich erreichte Dicke der Beschichtung ein wesentlicher Parameter, der über die Funktionalität und Langzeitstabilität der aufgetragenen Schicht entscheidet. Die Firma IBOS und die BAM haben in den letzten Jahren gemeinsam einen funktionstüchtigen Prototyp eines Messgeräts zur zerstörungsfreien Schichtdickenmessung für Bodenbeschichtungen entwickelt. Hierin wird die Abkühlkurve eines vorher erwärmten Bereichs berührungslos mit einer IR-Kamera erfasst und mit einem Modell verglichen, was die Bestimmung der Schichtdicke ermöglicht. Im Rahmen dieses Beitrags wird die Umsetzung der Methode unter Laborbedingungen und in der Praxis auf der Baustelle erläutert und diskutiert.
The knowledge about energy release and transient behaviour of flash lamps, used as short-term energy source in flash thermography investigations, is essential for a quantitative analysis of the results as well as for simulations regarding such experiments. Usually, only a rectangular pulse shape of a typical duration of a few milliseconds is regarded when flash lamps pulses are described. This note considers the afterglow period of a flash lamp explicitly and shows that negligence of this afterglow effect leads to a systematic underestimation of the pulse length and the related total energy release. In the reported case, the intensity transient recorded by a Silicon photo diode was transformed into a temperature transient, allowing the study of the real energy release. It turns out that approximately only 50% of the entire pulse energy were released during the usually regarded period of 2.8 ms, while the other half was released within a period of 20 ms with an exponential decay.
Recently, the photothermal determination of the thermophysical properties of concrete under lab conditions was reported. Their values are mainly needed to look at the energy consumption of buildings. Additionally, changes in their values in relation to the initial state might also be a good indicator for material quality or for moisture. The present contribution explains the photothermal method in a more general way to indicate the potential for on-site application. Secondly, a special application case is regarded: the detection of moisture in concrete. Two concrete samples were soaked with water, followed by a drying period, to obtain different levels of water penetration. The water contents were determined by weighing, and the photothermal response was measured. The results show a large influence on the measured temperature transients, which is larger than expected from the original simple model. They clearly provide two points: the photothermal method is suited to detect moisture in concrete, but the magnitude of the actual measurement effect is not yet understood.
High quality tubular products are essential to the oil and gas industry. Quality control during their production focuses on the non-destructive detection of surface defects. The structured light technique is a candidate for the challenge to detect, monitor and evaluate such defects in real-time.
In the present study the automatic processing of structured light measurements is performed and validated. The algorithm for the automatic Analysis of inspection data has an advantage over current data evaluation methods based on individual assessments of operators.
LIBS‐ConSort: Development of a sensor‐based sorting method for construction and demolition waste
(2023)
AbstractA joint project of partners from industry and research institutions approaches the challenge of construction and demolition waste (CDW) sorting by investigating and testing the combination of laser‐induced breakdown spectroscopy (LIBS) with near‐infrared (NIR) spectroscopy and visual imaging. Joint processing of information (data fusion) is expected to significantly improve the sorting quality of various materials like concrete, main masonry building materials, organic components, etc., and may enable the detection and separation of impurities such as SO3‐cotaining building materials (gypsum, aerated concrete, etc.)Focusing on Berlin as an example, the entire value chain will be analyzed to minimize economic / technological barriers and obstacles at the cluster level and to sustainably increase recovery and recycling rates.The objective of this paper is to present current progress and results of the test stand development combining LIBS with NIR spectroscopy and visual imaging. In the future, this laboratory prototype will serve as a fully automated measurement setup to allow real‐time classification of CDW on a conveyor belt.
To date, the destructive extraction and analysis of drilling cores is the main possibility to obtain depth information about damaging water ingress in building floors. The time- and costintensive procedure constitutes an additional burden for building insurances that already list piped water damage as their largest item. With its high sensitivity for water, a ground-penetrating radar (GPR) could provide important support to approach this problem in a non-destructive way. In this research, we study the influence of moisture damage on GPR signals at different floor constructions. For this purpose, a modular specimen with interchangeable layers is developed to vary the screed and insulation material, as well as the respective layer thickness. The obtained data set is then used to investigate suitable signal features to classify three scenarios: dry, damaged insulation, and damaged screed. It was found that analyzing statistical distributions of A-scan features inside one B-scan allows for accurate classification on unknown floor constructions. Combining the features with multivariate data analysis and machine learning was the key to achieve satisfying results. The developed method provides a basis for upcoming validations on real damage cases.
When applying Ground Penetrating Radar (GPR) to assess the moisture content of building materials, different medium properties, dimensions, interfaces and other unknown influences may require specific strategies to achieve useful results. Hence, we present an overview of the various approaches to carry out moisture measurements with GPR in civil engineering (CE). We especially focus on the applied Signal features such as time, amplitude and frequency features and discuss their limitations. Since the majority of publications rely on one single feature when applying moisture measurements, we also hope to encourage the consideration of approaches that combine different signal features for further developments.
Industry 4.0 is all about interconnectivity, sensor-enhanced process control, and data-driven systems. Process analytical technology (PAT) such as online nuclear magnetic resonance (NMR) spectroscopy is gaining in importance, as it increasingly contributes to automation and digitalization in production. In many cases up to now, however, a classical evaluation of process data and their transformation into knowledge is not possible or not economical due to the insufficiently large datasets available. When developing an automated method applicable in process control, sometimes only the basic data of a limited number of batch tests from typical product and process development campaigns are available. However, these datasets are not large enough for training machine-supported procedures. In this work, to overcome this limitation, a new procedure was developed, which allows physically motivated multiplication of the available reference data in order to obtain a sufficiently large dataset for training machine learning algorithms. The underlying example chemical synthesis was measured and analyzed with both application-relevant low-field NMR and high-field NMR spectroscopy as reference method. Artificial neural networks (ANNs) have the potential to infer valuable process information already from relatively limited input data. However, in order to predict the concentration at complex conditions (many reactants and wide concentration ranges), larger ANNs and, therefore, a larger Training dataset are required. We demonstrate that a moderately complex problem with four reactants can be addressed using ANNs in combination with the presented PAT method (low-field NMR) and with the proposed approach to generate meaningful training data.
The quality of additively manufactured (AM) parts is determined by the applied process parameters used and the properties of the feedstock powder. The influence of inner gas pores in feedstock particles on the final AM product is a phenomenon which is difficult to investigate since very few non-destructive measurement techniques are accurate enough to resolve the micropores.
3D X-ray computed tomography (XCT) is increasingly applied during the process chain of AM parts as a non-destructive monitoring and quality control tool and it is able to detect most of the pores.
However, XCT is time-consuming and limited to small amounts of feedstock powder, typically a few milligrams. The aim of the presented approach is to investigate digital radiography of AM feedstock particles as a simple and fast quality check with high throughput. 2D digital radiographs were simulated in order to predict the visibility of pores inside metallic particles for different pore and particle diameters. An experimental validation was performed. It was demonstrated numerically and experimentally that typical gas pores above a certain size (here: 3 to 4.4 µm for the selected X-ray setup), which could be found in metallic microparticles, were reliably detected by digital radiography.
Large-language models (LLMs) such as GPT-4 caught the interest of many scientists. Recent studies suggested that these models could be useful in chemistry and materials science. To explore these possibilities, we organized a hackathon. This article chronicles the projects built as part of this hackathon. Participants employed LLMs for various applications, including predicting properties of molecules and materials, designing novel interfaces for tools, extracting knowledge from unstructured data, and developing new educational applications. The diverse topics and the fact that working prototypes could be generated in less than two days highlight that LLMs will profoundly impact the future of our fields. The rich collection of ideas and projects also indicates that the applications of LLMs are not limited to materials science and chemistry but offer potential benefits to a wide range of scientific disciplines.
The photoacoustic measurement technique is a powerful yet underrepresented method to characterize the thermal transport properties of thin films. For the case of isotropic low thermal diffusivity samples, such as glasses or polymers, we demonstrate a general approach to extract the thermal conductivity with a high degree of significance. We discuss in particular the influence of thermal effusivity, thermal diffusivity, and sample layer thickness on the significance and accuracy of this measurement technique. These fundamental thermal properties guide sample and substrate selection to allow for a feasible thermal transport characterization. Furthermore, our data evaluation allows us to directly extract the thermal conductivity from this transient technique, without separate determination of the volumetric heat capacity, when appropriate boundary conditions are fulfilled.
Using silica, poly(methyl methacrylate) (PMMA) thin films, and various substrates (quartz, steel, and silicon), we verify the quantitative correctness of our analytical approach.
Learned block iterative shrinkage thresholding algorithm for photothermal super resolution imaging
(2022)
Block-sparse regularization is already well known in active thermal imaging and is used for multiple-measurement-based inverse problems. The main bottleneck of this method is the choice of regularization parameters which differs for each experiment. We show the benefits of using a learned block iterative shrinkage thresholding algorithm (LBISTA) that is able to learn the choice of regularization parameters, without the need to manually select them. In addition, LBISTA enables the determination of a suitable weight matrix to solve the underlying inverse problem. Therefore, in this paper we present LBISTA and compare it with state-of-the-art block iterative shrinkage thresholding using synthetically generated and experimental test data from active thermography for defect reconstruction. Our results show that the use of the learned block-sparse optimization approach provides smaller normalized mean square errors for a small fixed number of iterations. Thus, this allows us to improve the convergence speed and only needs a few iterations to generate accurate defect reconstruction in photothermal super-resolution imaging.
Machine learning based multi-sensor fusion for the nondestructive testing of corrosion in concrete
(2020)
Half-cell potential mapping (HP) is the most popular non-destructive testing method (NDT) for locating corrosion damage in concrete. It is generally accepted that HP is susceptible to environmental factors caused by salt-related deterioration, such as different moisture and chloride gradients. Additional NDT methods are able to identify distinctive areas but are not yet used to estimate more accurate test results. We present a Supervised Machine Learning (SML) based approach to data fusion of seven different signal features to obtain higher quality information. SMLs are methods that explore (or learn) relationships between different (sensor) data from predefined data labels. To obtain a representative, labelled data set we conducted a comprehensive experiment simulating the deterioration cycle of a chloride exposed device in the laboratory. Our data set consists of 18 measurement campaigns, each containing HP, Ground Penetrating- Radar, Microwave Moisture and Wenner resistivity data. We compare the performance of different ML approaches. Many outperform the best single method, HP. We describe the intrinsic challenges posed by a data-driven approach in NDT and show how future work can help overcome them.
In this work the global and local mechanical properties of the magnetocaloric intermetallic LaFe11.2Si1.8 alloy are investigated by a combination of different testing and characterization techniques in order to shed light on the partly contradictory data in recent literature. Macroscale compression tests were performed to illuminate the global fracture behavior and evaluate it statistically. LaFe11.2Si1.8 demonstrates a brittle behavior with fracture strains below 0.6% and widely distributed fracture stresses of 180–620 MPa leading to a Weibull modulus of m = 2 to 6. The local mechanical properties, such as hardness and Young's modulus, of the main and secondary phases are examined by nanoindentation and Vickers microhardness tests. An intrinsic strength of the main magnetocaloric phase of at least 2 GPa is estimated. The significantly lower values obtained by compression tests are attributed to the detrimental effect of pores, microcracks, and secondary phases. Microscopic examination of indentation-induced cracks reveals that ductile α-Fe precipitates act as crack arrestors whereas pre-existing cracks at La-rich precipitates provide numerous ‘weak links’ for the initiation of catastrophic fracture. The presented systematic study extends the understanding of the mechanical reliability of La(Fe, Si)13 alloys by revealing the correlations between the mechanical behavior of macroscopic multi-phase samples and the local mechanical properties of the single phases
Direct Laser Writing (DLW) and X-ray computed tomography (XCT) both offer unique possibilities in their respective fields. DLW produces full three-dimensional (3D) polymer structures on the microscale with resolutions below 100 nm. The fabricated structures can be analysed by XCT or X-ray microscopy (XRM), which incorporates additional X-ray lenses, in three dimensions down to a minimal basic spatial resolution of about 500 nm or 50 nm, respectively. In this work, two different DLW structures are analysed via XCT. Internal defects are detected and analysed for the purpose of quality control. Defects and structures with sizes down to 1.5 µm are successfully analysed. A 3D reconstruction and internal, hidden features of the fabricated structures are shown and discussed. In a first-of-its-kind study, we demonstrate the detectability of a single-voxel line inside a fabricated structure that would not be detectable with SEM or light microscopy. Furthermore, the direct fabrication on a PET substrate is shown to overcome the high X-ray absorbance of commonly used glass substrates. Attenuation spectra of SZ2080 and glass substrates are compared to a fabrication route direct on a 170 µm PET foil. The practical aspects of XCT measurements for DLW structures on different substrates will be discussed.
Mass Spectrometry (MS) and Nuclear Magnetic Resonance Spectroscopy (NMR) are valuable analytical and quality control methods for most industrial chemical processes as they provide information on the concentrations of individual compounds and by-products. These processes are traditionally carried out manually and by a specialist, which takes a substantial amount of time and prevents their utilization for real-time closed-loop process control. This paper presents recent advances from two projects that use Artificial Neural Networks (ANNs) to address the challenges of automation and performance-efficient realizations of MS and NMR. In the first part, a complete toolchain has been realized to develop simulated spectra and train ANNs to identify compounds in MS. In the second part, a limited number of experimental NMR spectra have been augmented by simulated spectra, to train an ANN with better prediction performance and speed than state-of-the-art analysis. These results suggest that, in the context of the digital transformation of the process industry, we are now on the threshold of a strongly simplified use of MS and MRS and the accompanying data evaluation by machine-supported procedures, and can utilize both methods much wider for reaction and process monitoring or quality control.
Composites made up of microparticles embedded in a polymeric matrix have attracted increasing attention due to the possibility of tailoring their physical properties by adding the adequate quantity of fillers. As the concentration of these fillers increases, their connectivity changes drastically at a given threshold and therefore the electrical, thermal and optical properties of these composites are expected to exhibit a percolation effect. In this work, the thermal and electrical conductivities along with the emissivity of Composites composed of carbonyl-iron microparticles randomly distributed in a polyester resin matrix are measured, for volume fractions ranging from 0 to 0.55. It is shown that both the thermal and electrical conductivities increase with the particles’ concentration, such that their percolation threshold appears at volume fractions of 0.46 and 0.38, respectively.
The emissivity, on the other hand, decreases as the fillers’ concentration increases, such that it exhibits a substantial decay at a volume fraction of 0.41. The percolation threshold of the emissivity is thus higher than that of the thermal conductivity, but lower than the electrical conductivity one. This dispersion on the percolation concentration is justified by the different physical mechanisms required to activate the electrical, thermal, and optical
responses of the considered composites. The obtained results thus show that the percolation phenomenon can efficiently be used to enhance or reduce the physical properties of particulate composites.
Digital radiographic images were analysed to predict the visibility of image quality indicators (IQI), based on normalized noise power spectra (NNPP) and modulation transfer function (MTF) measurements. The fixed pattern noise of some digital detectors result in different noise spectra, which influence the visibility of different IQIs, depending on the hole diameter. Studies, based on measurement of basic spatial resolution and contrast to noise ratio were performed together with presampled MTF measurements and the NNPS in dependence on the spatial frequency. Plate hole IQIs, step hole IQIs, and equivalent penetrameter sensitivity (EPS) IQIs based on ASTM E 746 were measured to verify the influence of the different parameters. Modelling of digital images was used to verify the applied numeric tools. A study has been performed for imaging plates and digital detector arrays to analyse differences. Formulas for the prediction of the visibility functions for hole type IQIs are derived. In consequence the standards for characterization and classification of computed radiography (ASTM E 2446) and radiography with DDAs (ASTM E 2597) need to be revised.
Extracting statistical characteristics from radiographic films is vital for film system classification and contrast sensitivity evaluation and serves as a basis for film noise simulation. A new method for digitising radiographic films in order to extract these characteristics is presented. The method consists of a camera-based setup and image processing procedure to digitise films. Correct optical density values and granularity can be extracted from the digitised images, which are equal to results obtained by standardised measurement procedures. Specific statistical characteristics of film noise are theoretically derived and subsequently verified by the obtained data, including characteristics such as Gaussianity and spatial spectral characteristics of the optical density fluctuations. It is shown that the presented method correctly measures the granularity of film noise and can therefore replace time-consuming microdensitometer measurements traditionally required for film system classifications. Additionally, the inherent unsharpness of film systems was investigated and compared with literature data. This comparison serves as another validation approach of the presented method.
Generating 2D noise with local, space-varying spectral characteristics is vital where random noise fields with spatially heterogeneous statistical properties are observed and need to be simulated. A realistic, non-stationary noise generator relying on experimental data is presented. That generator is desired in areas such as photography and radiography. For example, before performing actual X-ray imaging in practice, output images are simulated to assess and improve setups. For that purpose, realistic film noise modelling is crucial because noise downgrades the detectability of visual signals. The presented film noise synthesiser improves the realism and value of radiographic simulations significantly, allowing more realistic assessments of radiographic test setups. The method respects space-varying spectral characteristics and probability distributions, locally simulating noise with realistic granularity and contrast. The benefits of this approach are to respect the correlation between noise and image as well as internal correlation, the fast generation of any number of unique noise samples, the exploitation of real experimental data, and its statistical non-stationarity. The combination of these benefits is not available in existing work. Validation of the new technique was undertaken in the field of industrial radiography. While applied to that field here, the technique is general and can also be utilised in any other field where the generation of 2D noise with local, space-varying statistical properties is necessary.
Industrial processes release substantial quantities of waste heat, which can be harvested to generate electricity. At present, the conversion of low grade waste heat to electricity relies solely on thermoelectric materials, but such materials are expensive and have low thermodynamic efficiencies. Although thermomagnetic materials may offer a promising alternative, their performance remains to be evaluated, thereby hindering their real-world application. Here, the efficiency and cost effectiveness of thermomagnetic materials are evaluated for the usage in motors, oscillators, and generators for converting waste heat to electricity. The analysis reveals that up to temperature differences of several 10 K, the best thermomagnetic materials have the potential to compete with thermoelectric materials. Importantly, it is found that the price per watt of some thermomagnetic materials is much lower compared to that of present-day thermoelectrics, which can become competitive with conventional power plants. This materials library enables the selection of the best available thermomagnetic materials for harvesting waste heat and gives guidelines for their future development.
Оперативная характеристика обнаружения как метод оценки достоверности неразрушающего контроля
(2021)
Оперативные характеристики обнаружения в течение многих лет успешно применяют-ся при оценке достоверности неразрушающего контроля. Основными проблемами для их использования, как и при применении любого из методов оценки достоверности, яв-ляются отсутствие информации о действительной дефектной ситуации и ограниченное количество дефектов в образцах объектов контроля. Дополнительной проблемой постро-ения оперативной характеристики обнаружения является отсутствие информации о раз-мерах дефектов и отсутствие универсального размера для различных типов дефектов.
В статье обобщён опыт построения оперативных характеристик по результатам ультра-звукового контроля.
Adopting X-ray computed tomography (XCT) for ex-situ characterization of battery materials has gained interest in the past decade. The main goal of this paper is to demonstrate the effectiveness of several X-ray computer tomography techniques to study commercial batteries. General guidelines are provided to select the most suitable imaging equipment and parameters for investigations of lithium-ion batteries, spanning the length scales from cell to electrode, down to particle level. Relevantly, such parameters would also be suitable for operando experiments.
Safety mechanisms and manufacturing inconsistencies at cell level as well as defects and inhomogeneity in cathode and anode is illustrated and quantified. Furthermore, relation of beam energy and sample-detector-distance on contrast retrieved from attenuation and phase shift is inspected using Synchrotron XCT.
Metallic glasses are known to have a remarkably robust yield strength, admitting Weibull moduli as high as for crystalline engineering alloys. However, their postyielding behavior is strongly varying, with large scatter in both flow stress levels and strains at failure. Using x-ray tomography, we reveal how a strain-dependent internal evolution of shear-band cavities underlies this unpredictable postyielding response.We demonstrate how macroscopic strain softening coincides with the first detection of internal shear-band cavitation. Cavity growth during plastic flow is found to follow a power law, which yields a fractal dimension and a roughness exponent in excellent agreement with self-similar surface properties obtained after fracture. These findings demonstrate how internal microcracking coexists with shear-band plasticity along the plastic part of a stress-strain curve, rationalizing the large variability of plastic flow behavior seen for metallic glasses.
Additive manufacturing (AM) technologies, generally called 3D printing, are widely used because their use provides a high added value in manufacturing complex-shaped components and objects. Defects may occur within the components at different time of manufacturing, and in this regard, non-destructive techniques (NDT) represent a key tool for the quality control of AM components in many industrial fields, such as aerospace, oil and gas, and power industries. In this work, the capability of active thermography and eddy current techniques to detect real imposed defects that are representative of the laser powder bed fusion process has been investigated. A 3D complex shape of defects was revealed by a μCT investigation used as reference results for the other NDT methods. The study was focused on two different types of defects: porosities generated in keyhole mode as well as in lack of fusion mode. Different thermographic and eddy current measurements were carried out on AM samples, providing the capability to detect volumetric irregularly shaped defects using non-destructive methods.
Because of its mobility and ability to investigate exposed surfaces, single-sided (SiS) nuclear magnetic resonance (NMR) technology enables new application fields in geosciences. To test and assess its corresponding potential, we compare longitudinal (T1) and transverse (T2) data measured by SiS NMR with those of conventional geoscientific laboratory NMR. We use reference sandstone samples covering a broad range of pore sizes. Our study demonstrates that the lower signal-to-noise ratio of SiS NMR data generally tends to slightly overestimated widths of relaxation time distributions and consequently pore size distributions. While SiS and conventional NMR produce very similar T1 relaxation data, unbiased SiS NMR results for T2 measurements can only be expected for fine material, i.e. clayey or silty sediments and soils with main relaxation times below 0.05s. This limit is given by the diffusion relaxation rate due to the gradient in the primary magnetic field associated with the SiS NMR. Above that limit, i.e. for coarse material, the relaxation data is strongly attenuated. If considering the diffusion relaxation time of 0.2 s in the numerical data inversion process, the information content >0.2s is blurred over a range larger than that of conventional NMR. However, our results show that principle range and magnitudes of the relaxation time distributions are reconstructed to some extent. Regarding these findings, SiS NMR can be helpful to solve geoscientific issues, e.g. to assess the hydro-mechanical properties of the walls of underground facilities or to provide local soil moisture data sets for calibrating indirect remote techniques on the regional scale. The greatest opportunity provided by the SiS NMR technology is the acquisition of profile relaxation data for rocks with significant bedding structures at the µm scale. With this unique feature, SiS NMR can support the understanding and modeling of hydraulic and diffusional anisotropy behavior of sedimentary rocks.
Photothermal radiometry with an infrared camera allows the contactless temperature measurement of multiple surface pixels simultaneously. A short light pulse heats the sample. The heat propagates through the sample by diffusion and the corresponding temperature evolution is measured at the sample’s surface by an infrared camera. The main drawback in radiometric imaging is the loss of the spatial resolution with increasing depth due to heat diffusion, which results in blurred images for deeper lying structures. We circumvent this information loss due to the diffusion process by using blind structured illumination, combined with a non-linear joint sparsity reconstruction algorithm. The structured illumination is realized by parallel laser lines from a vertical-cavity surface-emitting laser (VCSEL) array controlled by a random binary pattern generator. By using 150 different patterns of structured illumination and our iterative joint sparsity algorithm, it was possible to resolve 1 mm thick lines at a distance down to 0.5 mm, which results in a resolution enhancement of approximately a factor of four compared to the resolution of 5.9 mm for homogenous illuminated thermographic reconstruction.
Im vorliegenden Artikel werden die Ergebnisse des Fragebogens der DGZfP zur Thematik „ZfP 4.0“ vorgestellt und diskutiert. Die Befragung zielte darauf ab, das allgemeine Verständnis der ZfP-Community zur Begrifflichkeit „ZfP 4.0“ herauszuarbeiten und daraus Bedarfe und Handlungsempfehlungen für die identifizierten Herausforderungen abzuleiten. Außerdem zeigt sich aus Sicht der Autor*innen, dass relevante Terminologien zu dem Themenkomplex Digitalisierung einer weiteren Klärung bedürfen, was im Bericht aufgegriffen wird. Im Ausblick zu den angelaufenen Arbeiten im nationalen Fachausschuss ZfP 4.0 und in den sich etablierenden internationalen Fachkreisen werden daraus abgeleitete Perspektiven für die Zukunftsgestaltung vorgestellt.
Reliability of NDT is affected by human factors, which have thus far received the least amount of attention in the reliability assessments. With increased use of automation, in terms of mechanised testing (automation-assisted inspection and the corresponding evaluation of data), higher reliability standards are believed to have been achieved. However, human inspectors, and thus human factors, still play an important role throughout this process and the risks involved in this application are unknown. The aim of this study was to explore for the first time the risks associated with mechanised NDT and find ways of mitigating their effects on the inspection performance. Hence, the objectives were to identify and Analyse potential risks in mechanised NDT and devise measures against them. To address those objectives, a risk assessment in form of a Failure Modes and Effects Analysis (FMEA) was conducted. This analysis revealed potential for failure during both the acquisition and evaluation of NDT data that could be assigned to human, technology, and organisation. Since the existing preventive measures were judged to be insufficient to defend the system from identified failures, new preventive measures were suggested.
Material defects in fiber reinforced polymers such as delaminations can rapidly degrade the material properties or can lead to the failure of a component. Pulse thermography (PT) has proven to be a valuable tool to identify and quantify such defects in opaque materials. However, quantification of delaminations within semitransparent materials is extremely challenging. We present an approach to quantify delaminations within materials being semitransparent within the wavelength ranges of the optical excitation sources as well as of the infrared (IR) camera. PT experimental data of a glass fiber reinforced polymer with a real delamination within the material were reconstructed by one dimensional (1D) mathematical models. These models describe the heat diffusion within the material and consider semitransparency to the excitation source as well to the IR camera, thermal losses at the samples surfaces and a thermal contact resistance between the two layers describing the delamination. By fitting the models to the PT data, we were able to determine the depth of the delamination very accurately. Additionally, we analyzed synthetic PT data from a 2D simulation with our 1D-models to show how the thermal contact resistance is influenced by lateral heat flow within the material.
Pulse thermography (PT) has proven to be a valuable non-destructive testing method to identify and quantify defects in fiber-reinforced polymers. To perform a quantitative defect characterization, the heat diffusion within the material as well as the material parameters must be known. The heterogeneous material structure of glass fiber-reinforced polymers (GFRP) as well as the semitransparency of the material for optical excitation sources of PT is still challenging. For homogeneous semitransparent materials, 1D analytical models describing the temperature distribution are available.
Here, we present an analytical approach to model PT for laterally inhomogeneous semitransparent materials.We show the validity of the model by considering different configurations of the optical heating source, the IR camera, and the differently coated GFRP sample. The model considers the lateral inhomogeneity of the semitransparency by an additional absorption coefficient. It includes additional effects such as thermal losses at the samples surfaces, multilayer systems with thermal contact resistance, and a finite duration of the heating pulse. By using a sufficient complexity of the analytical model, similar values of the material parameters were found for all six investigated configurations by numerical fitting.
Iterative numerical 2D-modelling for quantification of material defects by pulsed thermography
(2019)
This paper presents a method to quantify the geometry of defects such as flat bottom holes (FBH) and notches in opaque materials by a pulse thermography (PT) experiment and a numerical model. The aim was to precisely describe PT experiments in reflection configuration with a simple and fast numerical model in order to use this model and a fit algorithm to quantify defects within the material. The algorithm minimizes the difference between the time sequence of a line shaped region of interest (ROI) on the surface (above the defect) from the PT experiment and the numerical data. Therefore, the experimental data can be reconstructed with the numerical model. In this way, the defect depth of a notch or FBH and its width or diameter was determined simultaneously. A laser was used for heating which was widened to a top hat spatial profile to ensure homogeneous illumination (rectangular impulse profile in time). The numerical simulation considers heating conditions and takes thermal losses due to convection and radiation into account. We quantified the geometry of FBH and notches in steel and polyvinyl chloride plasticized (PVC-U) materials with an accuracy of < 5 %.
Laser powder bed fusion of metallic components (PBF-LB/M) is gaining acceptance in industry. However, the high costs and lengthy qualification processes required for printed components create the need for more effective in-situ monitoring and testing methods. This article proposes multispectral Optical Tomography (OT) as a new approach for monitoring the PBF-LB/M process. Compared to other methods, OT is a low-cost process monitoring method that uses long-time exposure imaging to observe the build process. However, it lacks time resolution compared to expensive thermographic sensor systems. Monochromatic OT (1C-OT) is already commercially available and observes the building process layer-wise using a single wavelength window in the NIR range. Multispectral OT (nC-OT) utilizes a similar setup but can measure multiple wavelength ranges per location simultaneously. By comparing the classical 1C-OT and nC-OT approaches, this article examines the advantages of nC-OT (two channel OT and RGB-OT) in reducing the false positive rate for process deviations and approximating maximum temperatures for a better comparison between different build processes and materials. This could ultimately reduce costs and time for part qualification. The main goal of this contribution is to assess the advantages of nC-OT compared to 1C-OT for in-situ process monitoring of PBF-LB/M.
In-situ monitoring of the Laser Powder Bed Fusion build process via bi- chromatic optical tomography
(2022)
As metal additive manufacturing (AM) is entering industrial serial production of safety relevant components, the need for reliable process qualification is growing continuously. Especially in strictly regulated industries, such as aviation, the use of AM is strongly dependent on ensuring consistent quality of components. Because of its numerous influencing factors, up to now, the metal AM process is not fully controllable. Today, expensive part qualification processes for each single component are common in industry.
This contribution focusses on bi-chromatic optical tomography as a new approach for AM in-situ quality control. In contrast to classical optical tomography, the emitted process radiation is monitored simultaneously with two temperature calibrated cameras at two separate wavelength bands. This approach allows one to estimate the local maximum temperatures during the manufacturing process, thus increases the comparability of monitoring data of different processes. A new process information level at low investment cost is reachable, compared to, e.g., infrared thermography.
The amount of data generated worldwide is constantly increasing. These data come from a wide variety of sources and systems, are processed differently, have a multitude of formats, and are stored in an untraceable and unstructured manner, predominantly in natural language in data silos. This problem can be equally applied to the heterogeneous research data from materials science and engineering. In this domain, ways and solutions are increasingly being generated to smartly link material data together with their contextual information in a uniform and well-structured manner on platforms, thus making them discoverable, retrievable, and reusable for research and industry. Ontologies play a key role in this context. They enable the sustainable representation of expert knowledge and the semantically structured filling of databases with computer-processable data triples.
In this perspective article, we present the project initiative Materials-open-Laboratory (Mat-o-Lab) that aims to provide a collaborative environment for domain experts to digitize their research results and processes and make them fit for data-driven materials research and development. The overarching challenge is to generate connection points to further link data from other domains to harness the promised potential of big materials data and harvest new knowledge.
Additive manufacturing offers a range of novel applications. However, the manufacturing process is complex and the production of almost defect-free parts with high reliability and durability is still a challenge. Thermography is a valuable tool for process surveillance, especially in metal additive manufacturing processes. The high process temperatures allow one to use cameras usually operating in the visible spectral range. Here, we compare the results of measurements during the manufacturing process of a commercial laser metal deposition setup using a mid wavelength infrared camera with those from a short wavelength infrared camera and those from a visual spectrum high-speed camera with band pass filter in the near infrared range.
Im Bauwesen werden Polymerbeschichtungen auf Beton häufig eingesetzt um zum einen, ein bestimmtes Aussehen zu schaffen und zum anderen, das Bauteil vor Alterung, Verschleiß und Schädigung zu schützen. Für praktisch alle Ziele ist die Wirkung von der eigens dafür definierten Schichtdicke der Polymerbeschichtung abhängig. Daher wird die Dicke der Beschichtung nach erfolgtem Schichtauftrag überprüft. Für den in diesem Zusammenhang anspruchsvollen mineralischen Untergrund Beton stehen bislang allerdings nur zerstörende Prüfverfahren zur Verfügung. Aus diesem Grund wurden im Rahmen des Projektes IRKUTSK ein auf aktiver Thermografie basierendes Verfahren sowie ein Gerät für den vor-Ort-Einsatz entwickelt, mit dessen Hilfe eine zerstörungsfreie Schichtdickenbestimmung möglich ist. Hier wird ein kurzer Einblick in das zur Schichtdickenbestimmung entwickelte Thermografieverfahren gegeben. Die Besonderheiten bei der quantitativen Auswertung, die durch die Teiltransparenz der Polymerbeschichtungen auftreten, werden erläutert. Die Funktion des Verfahrens für einlagige Systeme wird anhand von Labormessungen mit verschiedenen optischen Quellen zur thermischen Anregung illustriert.
Pulse and flash thermography are experimental techniques which are widely used in the field of non-destructive testing for materials characterization and defect detection. We recently showed that it is possible to determine quantitatively the thickness of semitransparent polymeric solids by fitting of results of an analytical model to experimental flash thermography data, for both transmission and reflection configuration. However, depending on the chosen experimental configuration, different effective optical absorption coefficients had to be used in the model to properly fit the respective experimental data, although the material was always the same. Here, we show that this effect can be explained by the wavelength dependency of the absorption coefficient of the sample material if a polychromatic light source, such as a flash lamp, is used. We present an extension of the analytical model to describe the decay of the heating irradiance by two instead of only one effective absorption coefficient, greatly extending its applicability. We show that using this extended model, the experimental results from both measurement configurations and for different sample thicknesses can be fitted by a single set of parameters. Additionally, the deviations between experimental and modeled surface temperatures are reduced compared to a single optimized effective absorption coefficient.
We combine three different approaches to greatly enhance the defect reconstruction ability of active thermographic testing. As experimental approach, laser-based structured illumination is performed in a step-wise manner. As an intermediate signal processing step, the virtual wave concept is used in order to effectively convert the notoriously difficult to solve diffusion-based inverse problem into a somewhat milder wavebased inverse problem. As a final step, a compressed-sensing based optimization procedure is applied which efficiently solves the inverse problem by making advantage of the joint sparsity of multiple blind measurements. To evaluate our proposed processing technique, we investigate an additively manufactured stainless steel sample with eight internal defects. The concerted super resolution approach is compared to conventional thermographic reconstruction techniques and shows an at least four times better spatial resolution.
Laser excited super resolution thermal imaging for nondestructive inspection of internal defects
(2020)
A photothermal super resolution technique is proposed for an improved inspection of internal defects. To evaluate the potential of the laser-based thermographic technique, an additively manufactured stainless steel specimen with closely spaced internal cavities is used. Four different experimental configurations in transmission, reflection, stepwise and continuous scanning are investigated. The applied image post-processing method is based on compressed sensing and makes use of the block sparsity from multiple measurement events. This concerted approach of experimental measurement strategy and numerical optimization enables the resolution of internal defects and outperforms conventional thermographic inspection techniques.
This article presents deep unfolding neural networks to handle inverse problems in photothermal radiometry enabling super-resolution (SR) imaging. The photothermal SR approach is a well-known technique to overcome the spatial resolution limitation in photothermal imaging by extracting high-frequency spatial components based on the deconvolution with the thermal point spread function (PSF). However, stable deconvolution can only be achieved by using the sparse structure of defect patterns, which often requires tedious, handcrafted tuning of hyperparameters and results in computationally intensive algorithms. On this account, this article proposes Photothermal-SR-Net, which performs deconvolution by deep unfolding considering the underlying physics. Since defects appear sparsely in materials, our approach includes trained block-sparsity thresholding in each convolutional layer. This enables to super-resolve 2-D thermal images for nondestructive testing (NDT) with a substantially improved convergence rate compared to classic approaches. The performance of the proposed approach is evaluated on various deep unfolding and thresholding approaches. Furthermore, we explored how to increase the reconstruction quality and the computational performance. Thereby, it was found that the computing time for creating high-resolution images could be significantly reduced without decreasing the reconstruction quality by using pixel binning as a preprocessing step.
This paper presents different super resolution reconstruction techniques to overcome the spatial resolution limits in thermography. Pseudo-random blind structured illumination from a onedimensional laser array is used as heat source for super resolution thermography. Pulsed thermography measurements using an infrared camera with a high frame rate sampling lead to a huge amount of data. To handle this large data set, thermographic reconstruction techniques are an essential step of the overall reconstruction process. Four different thermographic reconstruction techniques are analyzed based on the Fourier transform amplitude, principal component analysis, virtual wave reconstruction and the maximum thermogram. The application of those methods results in a sparse basis representation of the measured data and serves as input for a compressed sensing based algorithm called iterative joint sparsity (IJOSP). Since the thermographic reconstruction techniques have a high influence on the result of the IJOSP algorithm, this paper Highlights their Advantages and disadvantages.
In this paper we propose super resolution measurement and post-processing strategies that can be applied in thermography using laser line scanning. The implementation of these techniques facilitates the separation of two closely spaced defects and avoids the expected deterioration of spatial resolution due to heat diffusion. The experimental studies were performed using a high-power laser as heat source in combination with pulsed thermography measurements (step scanning) or with continuous heating measurements (continuous scanning). Our work shows that laser line step scanning as well as continuous scanning both can be used within our developed super resolution (SR) techniques. Our SR techniques make use of a compressed sensing based algorithm in post- processing, the so-called iterative joint sparsity (IJOSP) approach. The IJOSP method benefits from both - the sparse nature of defects in space as well as from the similarity of each measurement. In addition, we show further methods to improve the reconstruction quality e.g. by simple manipulations in thermal image processing such as by considering the effect of the scanning motion or by using different optimization algorithms within the IJOSP approach. These super resolution image processing methods are discussed so that the advantages and disadvantages of each method can be extracted. Our contribution thus provides new approaches for the implementation of super resolution techniques in laser line scanning thermography and informs about which experimental and post-processing parameters should be chosen to better separate two closely spaced defects.