BAM Präsentationen
Filtern
Erscheinungsjahr
- 2021 (2) (entfernen)
Dokumenttyp
- Vortrag (2) (entfernen)
Sprache
- Englisch (2)
Referierte Publikation
- nein (2)
Schlagworte
- Acceptance (1)
- Acoustic emission (1)
- Al-Si alloys (1)
- AlSi12CuMgNi (1)
- Human Factors (1)
- Human-Centered Approach (1)
- Human-Machine Interaction (1)
- Industry 4.0 (1)
- Inspection Personnel (1)
- NDE 4.0 (1)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (2) (entfernen)
Eingeladener Vortrag
- nein (2)
The successful shift to NDE 4.0 will not only require developing and embracing new technologies associated with the fourth industrial revolution or becoming an integral part of the overall Industry 4.0, but also developing and adopting new ways of working. It is undoubtful that people will remain in charge of the inspections. However, it is arguable if the current “procedure-following” “level I-III” paradigm can withstand the changes that come along NDE 4.0. With the increased autonomy and interconnectedness expected with NDT 4.0, the majority of traditional NDE tasks will no longer be needed. Instead, different skills, such as that of programming and adapting systems, as well as problem solving, will become vital for the inspections. Therefore, we suggest that a new paradigm is needed—one in which inspector roles and, thus, also the requirements will have to be reinvented. We expect the inspectors to be relieved from the tedious and error prone aspects of the current system and to take responsibility for increasingly complex automated systems and work in closer collaboration with other experts. Thus, we propose that the traditional inspector roles will be transformed into that of the system developer, caretaker and problem solver, each requiring a specific set of skills and assuming different responsibilities. In this talk, we will present the new roles and discuss the challenges that may arise with them.
Typically, the near-eutectic Al-Si alloys consist of highly interconnected three-dimensional network of the eutectic Silicon (Si) and intermetallics embedded into Aluminium (Al) matrix. For further improvement of the mechanical properties of such alloys, often, one single ceramic reinforcement phase, e.g. silicon carbide (SiC) or aluminium oxide (Al2O3) in the form of fibres or particles is added. However, hybrid reinforcements (fibres and particles) can further improve wear resistance and fracture toughness, and additionally, reduce anisotropy of the material. The engineering of metal matrix composites (MMC) for specific application requirements benefits from a comprehensive knowledge of the failure behaviour. Therefore, damage evolution under compression was investigated on:
- pure near-eutectic AlSi12CuMgNi matrix alloy
- type I: matrix reinforced with random-planar oriented Al2O3 short fibres (15 vol.%)
- type II: matrix reinforced with random-planar oriented Al2O3 short fibres (7 vol.%) and additional SiC particles (15 vol.%)
The analysis of damage mechanism was carried out in two rather independent but complementary studies. First, selected sister samples of every material were exposed to quasi-static compression (traverse control). The compression tests were interrupted at different strain levels. Miniature cylinders with a diameter of 1mm were extracted from the pre-strained samples and investigated by synchrotron computed tomography (SX-µCT) with a spatial resolution of about 0.7 µm. For the pure matrix alloy, microcracks are confined to the intermetallic particles and to the eutectic Si, hence no damage was observed in the Aluminium. The composite type II revealed a more effective strain accumulation (less damage) than type I at low plastic strain (up to 5 %), but a more catastrophic damage development due to cracking of the SiC clusters at higher strain levels.
The second approach to study the damage initiation and accumulation in the materials subjected to compressive load was Acoustic Emission (AE) analysis. In this case the in-situ monitoring of the acoustic emission signal was performed during compression tests on specimens with dimension of several mm. For all three material types, AE activity set at 2% strain. Differences in AE behaviour of the three materials was proven based on AE hitrate, signal peak amplitudes as well as weighted peak frequencies (WPF). Future work focuses on combination of AE and SX-µCT aiming for more detailed knowledge on damage mechanism of metal matrix composites.