Wissenschaftliche Artikel der BAM
Filtern
Dokumenttyp
Sprache
- Englisch (44)
- Portugiesisch (1)
Schlagworte
- Concrete (45) (entfernen)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (26)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (21)
- 7 Bauwerkssicherheit (16)
- 7.4 Baustofftechnologie (9)
- 7.1 Baustoffe (7)
- 7.3 Brandingenieurwesen (3)
- 8.0 Abteilungsleitung und andere (3)
- 8.5 Röntgenbildgebung (3)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.2 Biophotonik (1)
Paper des Monats
- ja (4)
With ongoing innovation in process technology, the challenges of concrete technology are more and more focused on the rheological optimisation for these processes, since improper mixture stability or poor compaction ability negatively affect the concrete homogeneity and quality. However, along with the increasing complexity of today’s concrete mixture compositions, concrete becomes more prone to failure regarding the casting process. Variable properties of the raw materials typically cause changing workability. The reasons can be found among others in scattering water contents, physical or chemical properties of the cement or varying environmental temperatures. Robustness in the delicately adjusted rheology, however, is of utmost importance for modern and future process technology, from sprayed concrete over pumpable concrete towards 3D-printing, with regard to the long-term strength, the function and the durability. Typically, material induced changes cannot be identified easily due to the complex interactions of concrete constituents. Therefore, a precise and prompt counteraction is impossible. However, it is known that the yield stress can be controlled by addition of supplementary superplasticizer or stabilising agent. In combination with computerized process observation tools that can rapidly interpret and react on changes in the rheology, it is therefore thinkable, that only these two admixture types can adjust the rheology steadily and permanently, regardless of the actual root cause for observed macroscopic rheology change. The presentation will firstly give a comprehensive overview of effects at the interface between pore solution, particles and hydrates, which affect the rheology of fresh concrete. Secondly, ways are recommended how the rheology can be actively manipulated before eventually computerized methods are demonstrated that help to actively and rapidly assess and counteract performance scatter during steady casting processes.
Moisture and salt loads of concrete can significantly change its microstructure and consequently lead to chemical and mechanical degradation. However, the non-destructive investigation of moisture and salt present in concrete is still difficult. In order to address and compare the sensitivity of different methods concrete samples with different pore systems realized by varying the w/z ratios have been fabricated. The focus of this study was put on the analysis of ultrasonic long and trans waves measured on the surface and in transmission mode. The results show clear dependencies of all applied methods. With the radar and microwave methods predominantly changes in the concrete moisture could be detected, whereas the different pore systems were not observed to alter the signals. In contrast for the ultrasound method also the ongoing hydration as well as the nature of the pore system strongly influenced the signals. As a consequence in a subsequent drying experiment it was also tried to delineate the effects of moisture and hydration. All specimens have been re-saturated under pressure and the drying experiment was repeated using the same multi-sensor approach.
Recently developed new transducers for ultrasonic transmission, which can be embedded right into concrete, are now used for non-destructive permanent monitoring of concrete. They can be installed during construction or thereafter. Large volumes of concrete can be monitored for changes of material properties by a limited number of transducers. The transducer design, the main properties as well as installation procedures are presented. It is shown that compressional waves with a central frequency of 62 kHz are mainly generated around the transducer's axis. The transducer can be used as a transmitter or receiver. Application examples demonstrate that the transducers can be used to monitor concrete conditions parameters (stress, temperature,
) as well as damages in an early state or the detection of acoustic events (e.g., crack opening). Besides application in civil engineering our setups can also be used for model studies in geosciences.
Ultrasonic echo testing is widely used in non-destructive testing in civil engineering to investigate concrete structures, to measure thickness, and to locate and characterise built-in components or inhomogeneities. Currently, synthetic aperture focusing techniques are mostly used for imaging. These algorithms are highly developed but have some limitations. For example, it is not possible to image the lower boundary of built-in components like tendon ducts or vertical reflectors. We adopted reverse time migration for non-destructive testing in civil engineering in order to improve the imaging of complicated structures in concrete. By using the entire wavefield, including waves reflected more than once, there are fewer limitations compared to synthetic aperture focusing technique algorithms. As a drawback, the required computation is significantly higher than that for the techniques currently used. Simulations for polyamide and concrete structures showed the potential for non-destructive testing. The simulations were followed by experiments at a polyamide specimen. Here, having acquired almost noise-free measurement data to test the algorithm, we were able to determine the shape and size of boreholes with sufficient accuracy. After these successful tests, we performed experiments at a reinforced concrete foundation slab. We obtained information from the data by reverse time migration, which was not accessible by traditional imaging. The imaging of the location and structure of the lower boundary of the concrete foundation slab was improved. Furthermore, vertical reflectors inside the slab were imaged clearly, and more flaws were found. It has been shown that reverse time migration is a step forward in ultrasonic testing in civil engineering.
The changes in the sonic surface wave velocity of concrete under stress were investigated in this paper. Surface wave velocities at
sonic frequency range were measured on a prismatic concrete specimen undergoing several cycles of uniaxial compression. The
loading was applied (or removed) gradually in predefined small steps (stress-controlled). The surface wave velocity was measured
at every load step during both loading and unloading phases. Acoustic Emission (AE) test was conducted simultaneously to
monitor the microcracking activities at different levels of loading. It was found that the sonic surface wave velocity is highly stress
dependent and the velocity-stress relationship follows a particular trend. The observed trend could be explained by a combination
of acoustoelasticity and microcracking theories, each valid over a certain range of applied stresses. Having measured the velocities
while unloading, when the material suffers no further damage, the effect of stress and damage could be differentiated. The slope
of the velocity-stress curves over the elastic region was calculated for different load cycles. This quantity was normalized to yield a
dimensionless nonlinear parameter. This parameter generally increases with the level of induced damage in concrete.