Additive manufacturing (AM) offers a range of novel applications. However, the manufacturing process is complex and the production of defect-free parts with high reliability and durability is still a challenge. Thermography is a valuable tool for process surveillance, especially in metal AM processes. The high process temperatures allow one to use cameras usually operating in the visible spectral range. Here, we compare the results of measurements during the manufacturing process of a commercial laser metal deposition setup using a mid-wavelength-IR camera with those from a visual spectrum high-speed camera with band pass filter in the near-IR range.
Quantification of impact damages in CFRP and GFRP structures with thermography and ultrasonics
(2018)
The extent of damage caused by impacts in fibre reinforced composites depends on the energy of the impacts, on the velocity and the shape of the impacting body, on the material and structure of the composite and on the geometry of the structure. Here, mainly the thickness of the component is essential. The non-destructive evaluation of these damages can be carried out using both ultrasound and active thermography methods. A comparison of the detection sensitivity of these methods for the different damages is carried out in this paper depending on the fibre composite material used (CFRP and GFRP), the thickness of the material and the impact energy. The NDT methods used after the damage are supplemented by thermographic measurements with high temporal resolution, which were already recorded during the impact.
Additively manufactured test specimens made of polyamide 12 (PA 12) by Laser Sintering (LS) as well as of acrylnitril-butadien-styrol (ABS) by Fused Layer Modeling (FLM), were tested with active thermography. For this, two different excitation methods (flash and impulse excitation) were used and compared, regarding the suitability for the detection of constructed and imprinted defects. To increase the quality of the thermograms, data processing methods like thermal signal reconstruction (TSR) and Fourier-Transformation were applied. Furthermore, the long-term stability of the probes towards environmental stress, like UV-radiation, heat, water contact and frost is being investigated in the presented project with artificial weathering tests.
Systematic errors in the evaluation of uncorrected data from thermographic lock-in measurements
(2018)
Lock-in thermography (LT) is based on the correct evaluation of phase differences between the temperature oscillations at different surface regions of the object under test during periodic heating. Since the usual heating procedures contain a DC component, the actual heating pattern achieved is not harmonic. This causes systematic deviations when phase differences are determined by means of harmonic analysis, e.g. with FFT analysis. The resulting errors depend clearly on the ratio between DC and AC amplitude, which is demonstrated at simulated and experimentally recorded temperature transients. Further experimental LT data obtained by different oscillating energy inputs showed a variety of possible shapes of transients with different DC components.
In order to test their suitability different non-destructive methods were performed to inspect a GFRP plate with artificial defects. These defects were manufactured by means of thin PTFE sheets inserted between two plies in three different depth. The inspection methods were microwave reflection, flash thermography and phased array ultrasonics, all applied to the same specimen. Selected results are shown for all methods demonstrating opportunities and limits of the particular inspection methods. The achieved detection limits and further application aspects are compared directly to provide a useful information for the planning of inspection tasks.
Mit additiven Fertigungsverfahren hergestellte Bauteile und Produkte aus Kunststoffen werden zunehmend nicht mehr nur als Prototypen, sondern als voll funktionsfähige Bauteile und Produkte gefertigt. Bedingt durch die Fertigungsprozesse und den schichtweisen Aufbau resultieren physikalische Materialeigenschaften, die stark von den Fertigungsparametern abhängen und zudem anisotrop sind. Von den Fertigungsparametern werden auch die Oberflächeneigenschaften beeinflusst, sodass zu erwarten ist, dass sich die Beständigkeit gegenüber äußeren Umwelteinflüssen bei additiv gefertigten Bauteilen von der konventionell gefertigter unterscheiden kann. Nachfolgend wird daher die Entwicklung eines Qualitätssicherungskonzeptes basierend auf spektroskopischen und zerstörungsfreien Prüfverfahren vorgestellt, in dem der Alterungsprozess von mittels Fused Deposition Modelling (FDM) und mittels Lasersintering (LS) hergestellten Probekörpern untersucht wird.
Der Umfang der durch Impacts in Faserverbundmaterialien erzeugten Schäden ist abhängig von der Energie des Impacts, von der Zusammensetzung und dem Aufbau der Faserverbundwerkstoffe und von der Geometrie der Bauteile und hier im Wesentlichen von der Dicke des Bauteils. Der zerstörungsfreie Nachweis dieser Schädigungen kann sowohl mit Ultraschallverfahren als auch mit Verfahren der aktiven Thermografie erfolgen. Ein Vergleich der Nachweisempfindlichkeiten dieser Verfahren für die unterschiedlichen Schädigungen wird in diesem Beitrag in Abhängigkeit vom verwendeten Faserverbundwerkstoff (CFK und GFK), der Dicke des Materials und von der Impactenergie durchgeführt. Ergänzt werden die im Anschluss an die Schädigung eingesetzten ZfP-Verfahren mit zeitlich hochaufgelösten Thermografiemessungen, die bereits während des Impacts aufgenommen wurden.