Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV.
The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-ANODE) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkollite.
The critical chloride content C(crit) is an indicator for the corrosion resistance of reinforcing steels in concrete. In this article, several experimental methods for determining the critical chloride content C(crit) of mild and an alloyed (12% Cr) steel in cementitious materials are compared. The methods used include accelerated polarization tests and tests using more natural (unpolarized) conditions in which chloride ingress occurs by diffusion and capillary uptake. The advantages and disadvantages of the methods are discussed, in particular, with the objective of reaching a compromise between applicability to practice and feasibility in laboratory testing.
Recently, non-destructive testing in civil engineering (NDT-CE), in particular of concrete components, has successfully mastered the leap from research to practice. Several methods have been established for field inspections to determine the concrete cover of reinforcement or to estimate the compressive strength as well as other parameters related to the concrete material. In addition, the application of nondestructive testing is indispensable, if information about the inner structure - such as the location of rebars and tendon ducts or the damage-related condition assessment to detect grouting defects, honeycombs, delamination, or corrosion - is required. Besides the selection of a suitable NDT method and an appropriate inspection system, the reliability of the results depends largely on the person who applies the non-destructive inspection technique and evaluates the inspection results. To ensure a high quality of non-destructive concrete evaluation as well as to keep the uncertainty caused by the inspection personnel to a minimum, structured, consistent and regulated theoretical as well as practical training of inspection personnel is essential. To close this gap, the subcommittee of education (UA-A) within the committee for NDT-CE of the German Society for Nondestructive Testing (DGZfP) has been reactivated in 2018 to establish uniform training standards for nondestructive concrete inspections in the long term. The subcommittee consists of scientists, practitioners, authorities, and clients. So far, the national standard DIN 4871 “Non-destructive testing - Qualification and Certification of NDT personnel in Civil Engineering (NDT-CE)” was developed and is currently under review. This standard considers the civil-industry-specifics, for example, that standards for NDT of concrete, as well as related product standards with a few exceptions, still do not exist at the moment. Within this presentation, the concept, the connection to ISO 9712 and other standards as well as an overview of the developed German standard DIN 4871 will be presented.