In this work we present results for three typical sealing materials (EPDM, HNBR, FKM) after up to 100 days ageing at high temperature under hydrogen. To allow for a better evaluation of the occurring changes the results are compared with effects of ageing in air on the material properties. Despite the common assumption that ageing under hydrogen atmosphere is expected to be less severe for the material in com-parison to air ageing, this is not seen for every material.
BAM-GGR 023 was published in June 2022
BAM-GGR 023 gives guidance to applicants regarding ageing management for competent authority approved package designs
Ageing management with evaluation of ageing mechanisms according to para 613A of IAEA SSR-6 (Rev. 1) and their effects are part of the general management system.
Essential items are: AMS (systemic-related), AMP (package design-related) and AMD (package-related)
There are different requirements for organization and extent of ageing management depending on type of use
There are also different requirements for ageing evaluation depending on type of use for packaging/package, classification of components and their accessibility and replaceability
Acceptable limits for activity release from transport casks for high-level radioactive material specified in the IAEA regulations must be kept by the integrity of cask body and the cask sealing system. BAM as the German competent authority for mechanical, thermal and containment assessment of packages liable for approval verifies the activity release compliance with the regulatory limits. One of the fundamental aspects in assessment is the specification of conservative package design leakage rates.
To ensure the required package tightness for both, storage, and transport of the cask before and after storage usually metal seals of the Helicoflex® Type are used. Due to the long-term use the seal behavior is influenced by temperature and time. The mechanical and thermal loadings associated with the routine, normal and accident conditions of transport specified in the regulations can have a significant effect on the leak tightness of the sealing system. Whereas the safety for application of new, non- aged Helicoflex® seals is verified sufficiently, there are still technical data gaps concerning the efficiency of aged Helicoflex® seals.
BAM performed experiments to learn more about the sealing efficiency of aged Helicoflex® seals with Aluminum and Silver outer jackets. The seals were compressed in test-flanges and for artificial ageing the complete flange systems were stored in an oven for several month at a high temperature. During the compression and decompression tests after the aging, load-deformation characteristics of the seals, and leakage rates were measured. With these tests a load situation was simulated, which can occur in the regulatory drop test of the cask: Under high impact loads the bolted lid can lift a little for a short moment, allowing a little movement of the seal, so that the contact area can change before compressing again.
The poster presentation will show details about test conditions and first results.
Overview of ongoing research and future prospects on polyethylene neutron shielding materials at BAM
(2023)
The extension of the interim storage period of radioactive waste before disposal will cause additional challenges for the nuclear waste management in Germany, so that an extensive knowledge of the long-term performance of casks, including their components and inventories, will be required for future extended storage licenses.
Ultra-high and high molecular weight polyethylenes ((U)HMW-PE) are used for neutron shielding purposes in casks for storage and transport of spent fuel and high-level waste due to their extremely high hydrogen content. During their service life of several decades as cask components, the PE materials are exposed to neutron and gamma radiation from the radioactive inventory of the casks, mechanical assembling stresses and temperature. All these combined effects affect the material properties of such components which in turn may be crucial for some possible accident scenarios.
At the Bundesanstalt für Materialforschung und -prüfung (BAM), the effects of high temperature exposure in combination with subsequent or previous irradiation were investigated with a comprehensive aging program including thermal aging at 125 °C for different aging periods up to 5 years and irradiation with doses ranging from 50 to 600 kGy.
This contribution provides an overview of the ongoing research related to the structural changes of (U)HMW-PE induced by gamma irradiation and high temperature exposure and focuses on current research perspectives at BAM with regard to the prediction of the dynamic behavior of the material during extended interim storage in case of an accident scenario. First results of the coupled effect of temperature, radiation and mechanical loading will be presented. The effect of microstructural changes induced by gamma irradiation and high temperature on the mechanical behavior of (U)HMW-PE will be assessed.
Elastomeric seals are essential components in the infrastructure which prevent leakage of gas and proper function of technical devices and are therefore highly safety relevant. For proper function a remaining resilience and tolerance to pressure changes is required.
The ageing of elastomers is an undesirable but inevitable process leading to a limited lifetime of rubber products such as seals. Independent of the application, as e.g. automotive, piping or container applications, a long lifetime or at least a timely exchange of a seal before occurrence of critical failure is desired.
Hydrogen is a key element for the energy turnaround and therefore the compatibility of seals with hydrogen is essential. In addition to the effect of hydrogen uptake and release, which might also cause destructive effects such as rapid gas decompression, ageing at high temperature under hydrogen atmosphere is of interest too. Most of the existing work is addressing the performance of new materials and comprises only very limited investigations concerning long-term use and the behaviour of aged materials in contact with hydrogen. As ageing can lead to substantial changes of material properties, it must be evaluated whether these changes are beneficial or deteriorating for the component function.
In this work we present and compare results of the characterisation of three sealing materials (EPDM, HNBR, FKM) after ageing at high temperature under hydrogen and air. Despite the common assumption that ageing under hydrogen atmosphere should be less severe for the material in comparison to air ageing, this is not the case for every material.
Deconvoluting the impact of early-life abuse conditions on the degradation of lithium-ion cells
(2023)
The successful repurposing of degraded lithium-ion (Li-ion) batteries in second-life applications is a vital step towards achieving a circular economy. While reusing aged Li-cells is a promising way of mitigating their overall environmental footprint, it is crucial to anticipate their future safety and performance characteristics . Unfortunately, predicting these properties is a cumbersome task, essentially caused by limited knowledge of the interference of different degradation modes in the cells’ first life.
To still enable estimating of these parameters from a current state, the present study systematically investigates the impacts of abusive conditions in an early phase of the cells’ life on their subsequent degradation behavior. For this purpose, individual Li-cells are initially stressed by different measures such as overcharging, deep-discharging, plating, and deliberate combinations of the aforementioned methods. Electrochemical performance indicators are monitored during subsequent cycling of the cells which provides insights into the interdependencies of different degradation modes induced by specific stress conditions. In this manner, it is clarified whether or not the total degradation can be determined by a convolution or a superposition of individual deterioration effects and, thus, be described as a multidimensional state function.
This knowledge will finally contribute to a better understanding of the performance and safety behavior of degraded Li-ion batteries which can help to successfully implement them into second-life applications.
The storage of spent fuel and high level radioactive waste in Germany is performed in interim storage containers with double lid systems. The lids are bolted and equipped with metal seals (e.g. Helicoflex®) to ensure the safe enclosure of the inventory. The used metal seals have a layered structure consisting of three components as can be seen schematically in the cross-sectional view in Fig. 1.
In the center a helical spring is positioned that is surrounded by two C-shaped jackets and is mainly responsible for generation of the required restoring force. The inner jacket is made of stainless steel and homogenizes the restoring force of the helical spring. The outer jacket is made of silver or aluminium which both are soft metals in comparison to the contact partners (lid and container body). During bolting of the lid to the container body the seal is compressed. The generated restoring force of the helical spring causes a plastic deformation of the outer jacket and adapts to the surfaces of the lid and the container body. Hence, leakage paths are closed and the sealing function is generated.
Typical durations for existing interim storage licenses in Germany are 40 years, but it can be expected that they have to be extended to longer periods as a final repository will not be available before the end of the running licence periods. This extension of license periods requires a solid understanding of the long-term behaviour of the seals under storage conditions. To meet this challenge long-term investigations have been started at Bundesanstalt für Materialforschung und –prüfung (BAM) in 2009. These tests focus on seals assembled in test flanges which are stored at temperatures ranging from room temperature to 150 °C for accelerated ageing. The aged seals are tested repeatedly after certain ageing steps and the leakage rate as indicator for sealing performance, the remaining seal force, and the useable resilience upon decompression are determined.
In the poster an update on the performed investigations in respect to earlier publications (Grelle et al. 2019, Goral et al. 2023) will be given and the implications of the results for resilient long term safety will be presented. Additionally, a focus will be laid on the currently planned further investigations and the question “What is additionally needed for evaluation of an interim storage period extension in regard to the used metal seals?” will be addressed.
With our experiments we want to simulate a load situation which can result from a cask vertical drop test. The lid can lift a little for a very short moment and that can perhaps result in a little movement of the seal, a little rotation or a little lateral movement, so that the contact section can change. The aim of the project is to learn more about the sealing efficiency after the seal is compressed again. What we know from former component tests with non-aged seals is, that the leakage rate measured after one or more decompression /compression cycles with seal movement becomes significant higher. And this result is considered for specification of design leakage rates for release calculation in safety cases.
In the recent years we all have learned more about the significant influence of temperature and time on seal behavior and so the plan was to do similar experiments with aged seals, just to get an idea about seal behavior and achievable leakage rates.
What we did in detail is:
We compressed Helicoflex-seals of both design types, with Aluminum and Silver outer jackets, in testflanges and aged them in an oven at a temperature of 125°C for 3 months to produce seal properties comparable with properties after several years use at more typical operating temperatures between 90 and 100°C.
After this ageing procedure we opened the flanges completely, moved the seal a little to vary the contact area and compressed the flanges again. What we measured during all compression and decompression cycles was the load, the deformation and -as long as possible- the leakage rates.
At BAM, which is a federal institute for materials research and testing in Germany, it is one of our tasks to evaluate the safety of casks designed for transport and/or storage of radioactive material. This includes assessment of elastomeric seals applied in the casks. Besides examining the low-temperature behaviour and irradiation effects of elastomeric seals, it is our goal to estimate the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. Therefore, we started an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) which are aged at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) up to five years. In order to assess sealability, O-rings were aged in compression by 25 % (corresponding to the compression during service) between plates as well as in flanges that allow leakage rate measurements. For comparison, uncompressed O-rings were aged as well. Further methods characterising seal performance are compression stress relaxation (CSR) reflecting the loss of sealing force of a compressed seal over time, and compression set (CS) which represents the recovery behaviour of a seal after release from compression. Additionally, material properties such as hardness, elastic modulus, glass transition temperature and viscoelastic loss factor as well as relaxation and recovery behaviour are examined in order to understand the underlying ageing mechanisms in each material. For obtaining results closely related to practical conditions, O-rings with a full-scale cord diameter of 10 mm were aged. However, this set-up can lead to heterogeneous aging caused by diffusion-limited oxidation (DLO) effects, resulting in distorted bulk properties such as compression stress relaxation and compression set. However, if DLO-affected data is excluded, extrapolations of CS data are possible using time-temperature shifts and Arrhenius graphs.
For selecting an appropriate end-of-lifetime criterion, leakage rate measurements were performed, since leakage rate is the only characteristic directly correlated to the performance of the sealing system. A significant increase in leakage rate was considered as the end of the lifetime. However, the O-rings remained leak tight under static conditions and even exhibited an improved, i.e. decreased leakage rate while other properties already indicated strong deterioration. These tests were extended by seal tests with fast partial decompression.
Overall an update will be given on the current investigations and results and the planned activities.
Based on the preliminary presentations in this task force it is repeated how a basic population scatters and its degradation influences properties statistically. There is a remainder on the issue of accepting borderline populations due to the minimum burst ratio requirement.
Then it is explained in detail how the analysis of minimum requirements by a Monte-Carlo-simulation works. The result with respect to the further reduced minimum burst ratio of 2.0 is summarised and means a two-step approach of two scatter levels requiring two different minimum burst ratios.
The methods for evaluating batch tests are analysed. A proposal for integration a statistical analysis is described in detail.
Finally, the positive effect of proof testing is shown and its dependence from the real ageing is shown.
This ends in the recommendation to have a stronger and quantitative look on real ageing and to follow the 2 proposed sets of criteria for a safe usage of hydrogen storage systems.