While alkali-activated binders offer certain advantages over traditional Portland cement binders, particu¬larly in terms of resistance against chemical attacks and potentially environmental footprint, their degra¬dation mechanisms remain incompletely understood at present, specifically carbonation. Thus, this study investigates the impact of natural and accelerated carbonation (1% and 4% CO2) on three different compositions of alkali-activated concretes: 100% calcined clay (C100) binder, 100% ground blast furnace slag (S100) binder, and a 40% calcined clay and 60% blast furnace slag blend (C40S60). C100 concretes exhibit faster carbonation kinetics, with five times greater natural carbonation depths than S100. This difference diminishes under accelerated carbonation, showing a 1.5 times difference for 1% CO2 and complete carbonation for 4% CO2 at 90 days. The results thus confirm that accelerated carbonation testing of low-Ca alkali-activated concretes yields results that are not representative of natural carbonation. The C40S60 sample demonstrates a carbonation profile similar to a CEM I concrete, i.e., a high carbonation resistance. Microstructure analysis indicates the formation of three polymorphs of calcium carbonate for S100 (calcite, vaterite, and aragonite), with a higher CO2 concentration favouring aragonite over vaterite. C100 exhibits no calcium carbonates; instead, sodium carbonates form, including trona for 4% CO2 and natrite for both accelerated tests. C40S60 shows calcium and sodium carbonates, although to a lesser extent, containing predominantly calcite and minor signals of natrite. Suitable compositions, like C40S60, prove as effective during natural or accelerated carbonation tests as conventional Portland cement concrete.
Dredging sediment refers to materials removed from the bottom of a water body during dredging operations. Mainly the dreading mud contains clay, silt, sand, water, and alkalis. This work incorporated dredging mud into the calcium sulfoaluminate cement at replacement levels of 0%, 10%, 30%, and 50% by weight. Pastes were evaluated after 1d, 28d, and 90d- hydration through mechanical strengths and the reaction rate by isothermal conduction calorimetry. XRD and MIP characterized the reaction products. The findings showed that small replacements (10% and 30%) increased early strength with higher ettringite formation in the system at 1d of curing. However, the evolution of mechanical strength was lower than the reference (0% replacement) over time. The results showed that in low replacement dosages, the dredging mud act as a nucleation site for the hydration of calcium sulfoaluminate phases.