The applicability of 1D-quadrupole-model on the depth estimation of overload-induced delaminations is tested in this contribution. While classical 1D-methods like Pulsed Phase Transformation and Thermographic Signal Reconstruction determine the depth of a defect by one parameter, a two-layer quadrupole model provides two parameters: depth and thermal resistance. In addition, the convectional losses at the surfaces may be considered. The defect investigated is a large-scale delamination in glass fibre reinforced polymer generated by tension overload.
In diesem Beitrag werden zerstörungsfreie Untersuchungen mittels aktiver Thermografie an Probekörpern aus CFK und GFK mit unterschiedlichen künstlichen Fehlstellen vorgestellt. Dabei wird die zeitliche und örtliche Temperaturverteilung nach Erwärmung mit Blitzlampen oder mit einem Infrarot-Strahler mit einer Infrarot-Kamera erfasst. Zur Rekonstruktion der Messdaten wurde ein numerisches Modell entwickelt. Dazu war die Bestimmung der thermischen und optischen Materialeigenschaften erforderlich.
Die Befragung zur Bestimmung relevanter Defekte in Faserverbundwerkstoffen im Rahmen des VITCEA-Projektes wird vorgestellt. Die so erhaltene "Hitparade" der Defekte kann als Ausgangspunkt für einen Fehlerkatalog dienen. Außerdem wird über die Herstellung von Überlastdefekten berichtet, welche sich an bestehende Normen (teilweise aus anderen Bereichen) anlehnt
Die tiefgreifende Reparatur von Faserverbundwerkstoffen stellt durch deren inneren Aufbau eine besondere Herausforderung dar, die unter anderem bei der Instandhaltung von Rotorblättern von Windkraftanlagen zum Tragen kommt. Um die Reparaturen von Rotorblattschalen zu untersuchen und zu optimieren, wurden an der BAM Sandwich-Schalenprüfkörper aus Glasfaserkunststoff (GFK) entwickelt. Nachdem in diese Schalenprüfkörper Modell-Reparaturen eingebracht wurden, werden zyklische mechanische Ermüdungsversuche bis zum Bruch durchgeführt. Vorrangiges Ziel ist es, den Einfluss verschiedener Reparaturvariablen auf die Ermüdungslebensdauer der Struktur zu verstehen, sowie die stabilste Reparaturmethode zu bestimmen.
Während der zyklischen Lastversuche wurden regelmäßig in-situ Messungen mit einer Thermografie Kamera und einem optischen Felddehnungsmesssystem durchgeführt. Durch beide Messmethoden lassen sich Eigenschaften der Probekörper zeitlich und räumlich aufgelöst darstellen.
Während die Felddehnungsmessungen Aufschluss über die Verformung an der Oberfläche geben, erfasst die thermische Inspektion Temperaturänderungen an der Oberfläche. Besonders die thermografischen Messwerte bilden hier das oberflächennahe Volumen ab, in dem sich Temperaturänderungen an der Oberfläche abzeichnen.
Die Messergebnisse beider Systeme stellen also verschiede aber korrelierte Parameter dar. Denn die zyklische Belastung (Bewegung) ruft eine periodische Temperaturänderung im Bauteil hervor. Dieser so genannte Thermoeleastische Effekt kann durch eine Lockin-Analyse der Temperaturtransienten (Temperaturverläufe) nachgewiesen werden. Die räumliche Darstellung der thermischen Effekte lässt Rückschlüsse auf die tatsächliche Lastverteilung im Probekörpervolumen zu.
Darüber hinaus führen nichtelastische Verformungen zu einer zusätzlichen Wärmefreisetzung, die durch geeignete Auswerteverfahren ebenfalls nachgewiesen werden können. Entsprechende Hot-Spots in der räumlichen Verteilung erlauben eine frühzeitige Erkennung besonders belasteter Bereiche lange vor dem eigentlichen Bauteil-Versagen. Das gestattet die Lokalisierung des Initial-Schadens, was mit der numerischen Spannungsanalyse korreliert werden kann und die Entwicklung und Bewertung verschiedener Reparaturstrategien.
Influence of the real energy input on the sensitivity of thermographic testing in case of GFRP
(2018)
Thermographic testing (TT) is an upcoming nondestructive method, which requires no contact at all to the specimen and can be applied on larger areas simultaneously. The measurement concept is based on the production of a thermal imbalance at the surface of the object under test. When the surface of this object is heated by an external source for a certain time, the surface temperature drops subsequently, influenced by inner defects of the sample. This leads to thermal contrasts at the surface. It is crucial that those contrasts are large enough to be detectable above the noise level. In a first approximation, the observed temperature contrast at a defect is proportional to the energy which was really introduced into the specimen during the heating period. However, the real energy input in a TT experiment is almost always unknown due to distinct parameters of the experimental setup or the material investigated. Typically, only the power consumption of the heating sources is reported, sometimes combined with the distance to the specimen surface.
This contribution describes the thermographic inspection of a rear side thickness variation from 1 to 2 cm at GFRP. This could represent a rear side adhesive bond i.e. in a wind turbine rotor blade. The front side heating was realized by usual halogen lamps with variable radiation power. The detected temperature contrast at the front side will be related to the different energy inputs determined by means of a simple analytical model applied to the experimental data. Additionally, the experimental data are compared with results of FEM simulations performed by COMSOL Multiphysics.
The results clearly demonstrate the key role of the real energy input in a real TT setup, if detection limits have to be evaluated.
Motivation:
- Reduktion der CO 2 Emissionen von Verbrennungsmotoren durch den Einsatz von LNG als alternativer Kraftstoff
- Aktuell werden doppelwandige Edelstahltanks mit Vakuumisolation für den Transport eingesetzt
- Reduktion des Tankgewichts und Vereinfachung der Konstruktion soll durch die Substitution mit GFK inklusive einer Isolationsschicht erreicht werden
- Leichtere Überprüfung von einwandigen Tankkonstruktionen
- Günstiges Versagensverhalten von GFK im Brandfall
Zusammenfassung:
- Thermische Performance kann mit Isolation aus PU Schaum erreicht werden
- Messung der Abdampfrate bildet einfache Möglichkeit zur Bestimmung der thermischen Performance
- Mikrorisse in der Matrix führen zur Leckage -> Liner notwendig
- Biegemodul bis 30 MPa vergleichbar, danach Abfall um ca. 50 % bei tiefen Temperaturen
Ausblick:
- Prüfung von GFK Proben mit Fasern in 0°-Orientierung
- Prüfung der thermischen Performance mit Demonstratoreinheiten verschiedene Größen
- Entwicklung einer Skalierungsfunktion, um Ergebnisse von druckloser Prüfung auf Druckanstieg zu übertragen
Im EMRP-Projekt VITCEA werden komplementäre ZFP-Verfahren zur Prüfung von Faserverbundwerkstoffen weiterentwickelt und validiert. In diesem Beitrag werden Ergebnisse verschiedener Techniken der aktiven Thermografie und des Ultraschalls vorgestellt. Die Nachweisempfindlichkeiten bezüglich künstlicher und natürlicher Fehler mit unterschiedlichen lateralen Ausdehnungen und in verschiedenen Tiefen werden miteinander verglichen.