Datei im Netzwerk der BAM verfügbar ("Closed Access")
Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (17)
- Beitrag zu einem Tagungsband (14)
- Vortrag (6)
- Beitrag zu einem Sammelband (2)
- Sonstiges (1)
- Posterpräsentation (1)
Schlagworte
- Temperature (10)
- Wear (10)
- Friction (6)
- Ceramics (3)
- Hardness (3)
- Hot steam (3)
- Lubricated sliding (3)
- Niobium carbide (3)
- Tribofilm (3)
- Abrasion (2)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (6)
Pristine, reduced, and alkylated graphene oxides are applied as lubricating additives in paraffin grease. It has revealed that their crystalline structure governs the tribological properties of grease for steel tribo-pair. The microstructural analyses of grease samples showed that a loose fiber network of soap in the presence of graphene-based additive allows their facile release for efficient lubrication. The surface analyses based on the microscopic and elemental mapping show the development of a graphene-derived protective film on the worn scars, which protected the tribo-surfaces and subsided the wear. The reduced graphene oxide (rGO) with the interlamellar distance of 0.35 nm in the (002) plane provided minimum resistance to shear and exhibited maximum reduction in coefficient of friction (COF) for the paraffin grease. The presence of oxygen functionalities in the basal of pristine and alkylated graphene oxide (GO) compromised the interlamellar shearing under tribo-stress; consequently, higher COF than that of rGO.
Tribological properties of ultrahigh-molecular weight polyethylene (UHMWPE) and cross-linked polyethylene (XLPE) were studied in two different wear modes. Firstly, reciprocating sliding wear studies under non-conformal contact investigated the effects of counterface surface roughness (polished, lapped and ground) of Ti6Al4V on the friction and wear of the polyethylenes. Secondly, two-body abrasive wear studies in conformal contact against different abrasive grit size papers were also carried out to ascertain the wear sensitivity of the polyethylenes under these adverse conditions. Wear mechanisms were studied using optical and scanning electron micrographs. The results of the reciprocating sliding wear studies showed that surface roughness of the counterface influenced friction and wear characteristics although no correlation was found between the coefficient of friction and specific wear rate. XLPE demonstrated wear sensitivity, particularly under severe abrasive wear condition. The results indicated that the performance of the polyethylenes greatly depends upon the tribological system under which it is operating.
Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates.
The wear rates of self-mated alumina couples show that friction as well as wear is largely determined by the above-mentioned hydro-thermal conditions. The presence of water and its amount available in the surrounding system either in liquid or in gaseous form plays a key role for friction and wear behavior and can be beneficial for the tribological profile of steam degradation resistant materials. Hot steam enhances the tribo-chemical formations of oxides and hydroxides on MgO-ZrO2 alumina and antimony impregnated carbon.
The accurate EDS microanalysis of light elements such as boron and carbon by spectrum imaging will be demonstrated using a sintered hard ceramic material composed of the three major phases titanium boride (TiB2), titanium carbide (TiC), silicon carbide (SiC) and minor phases, sub-μm in size.
The combination of these three materials leads to improved mechanical and tribological properties. Silicon carbide is a material used for mechanical seals. It has the disadvantage of reduced failsafe running functions, causing increased wear when running dry. The added titanium components (TiC and TiB2) improve the failsafe running functions. This technology has already been transferred to industrial applications.
Niobium carbide is a ceramic material which can be used with excellent results to replace tungsten carbide with cobalt binder. Furthermore, it might be manufactured by classic ceramic technologies and even colloidal processing. To achieve high toughness and strength, it is necessary to have a perfect mix of hard phase and binder, which is mainly achieved by ball milling. Mechanical and physical properties as well as results on different tribological and application-oriented machining tests are presented. The results have been compared with results obtained with NbC grades with Co and Fe3Al binders as well as with pure binderless hot-pressed NbC and SPS sintered Nb2O5.
The manufacturing of NbC with Ni binder with addition of titanium carbide by using a colloidal process for blending the different powders without a milling step were investigated. The the sintering process and formation of the resulting microstructures, the phase relations and the hardness of the produced cermet materials are characterized.
Niobium-titanium carbide cermets with nickel binder have been prepared by colloidal processing in water without a milling step by using Poly-diallyl-dimethyl-ammonium chloride (Poly-DADMAC) as a dispersant. Homogeneous microstructures with relative densities larger than 99% of the theoretical density have been achieved by gas pressure sintering in argon atmosphere. However, mechanical properties like hardness and strength were slightly decreased due to precipitation of free carbon.
The friction and wear properties of polyetherimide composites under dry oscillating sliding condition at room temperature (RT) as well as at elevated temperature (120 °C) was investigated. The polymer specimens were made to oscillate against steel cylinder as a counterpart. The friction and wear properties of PEI and composites were strongly influenced by the temperature. In case of carbon fiber composite abrasive action of carbon fibers has severely damaged the counterpart and resulted in accelerated wear of the composite at RT. Solid lubricants filled (PTFE, MoS2, graphite) along with glass fiber is beneficial in improving the friction and wear performance of the PEI composite at RT, whereas at elevated temperature wear performance was deteriorated.
The influence of temperature and counterbody material on the tribological properties of a-C:H
coatings deposited on Cronidur 30 steel has been investigated in a lubricated ball on disk
contact situation with alpha-alumina and silicon nitride as counterbodies. The results show, that the wear volumes of the systems increase exponentially with increasing temperature, for alpha-alumina more than for silicon nitride. Two different wear mechanisms seem to have a
major influence: First, the abrasive action due to materials hardness and second, the tribo-oxidation when silicon nitride is counter material.
Performance and efficiency of piezo-electric stick-slip actuators are dependent on the waveform of the electrical actuation of the piezo-stack. This paper compares between a conventional saw-tooth actuation with two waveforms that feature softer acceleration in order to minimize the duration of the slip-phase. It is shown that the proposed waveforms increase both maximum mechanical output power (by 43%) and overall efficiency (by 25%) of the examined actuator.
Tribological properties of neat polyetherimide (PEI), glass, carbon fiber, and solid lubricants filled PEI composites are presented in this article. The aim of this study was to investigate the friction and wear properties of these composites under dry oscillating sliding condition at room temperature (RT) as well as at elevated temperature (120 °C). The polymer specimens were made to oscillate against steel cylinder as a counterpart. The friction and wear properties of PEI and composites were strongly influenced by the temperature. Incorporation of carbon fiber in the PEI matrix has increased the wear rate at RT, while at elevated temperature this trend was opposite. Abrasive action of carbon fibers has severely damaged the counterpart and resulted in accelerated wear of the composite at RT. Solid lubricants filled (PTFE, MoS2, graphite) along with glass fiber is beneficial in improving the friction and wear performance of the PEI composite at RT, whereas at elevated temperature wear performance was deteriorated. Tribological performance of neat PEI and glass fiber composite was similar with each other at RT. Scanning electron micrographs and optical micrographs of the worn polymer specimens and the steel cylinders was used to study the possible wear mechanisms. The present test results were also compared with data available on the reciprocating wear of PEI and composites in the literature and trends have been reported.
Untersucht wurden Verschleißpartikel als elektronentransparente Proben auf dünnen Trägerfolien mit einem hochauflösendem Rasterelektronenmikroskop und energiedispersiver Röntgenspektrometrie im Transmissionsmodus.
Die hohe laterale Auflösung dieser modernen Methoden ermöglicht eine morphologische Charakterisierung der Verschleißpartikel bis in den nm-Bereich. Die hochauflösende Elementanalyse erlaubt eine Interpretation der Zusammensetzung und damit Rückschlüsse auf die Verschleißpartikelbildung. Die tribologischen Untersuchungen sind an einem Modell-Verschleißtribometer nach DIN 51834-2 geschmiert, aber ohne Ölkreislauf, durchgeführt worden. Die Präparation der Verschleißpartikel über eine Entnahme und Übertragung einer geringen Schmierstoffmenge mit einer Mikropipette auf eine TEM-Trägerfolie ist mit einem geringen Aufwand möglich. Der präparative Aufwand ist relativ gering. Das benötigte Schmierstoffvolumen beträgt wenige Mikroliter (0,001 ml).
Die Untersuchung zeigt die geringe geometrische Größe der Verschleißpartikel und bestätigt indirekt die These der Reaktionsschichtbildung mit einer geringen Schichtdicke, die ständig verschleißt und sich stetig neu bildet. Die beschriebenen Verschleißprozesse sind in der Modell-Verschleiß-Prüfung mit sehr hohen Pressungen am Versuchsbeginn nachweisbar.
The influence of temperature and counterbody material on the tribological properties of a-C:H coatings deposited on Cronidur 30 steel has been investigated in a lubricated ball on disk contact situation. The results show, that the wear volumes of the system increase exponentially with increasing temperature. Two different wear mechanisms seem to have a major influence: First, the abrasive action due to materials hardness and second, the tribooxidation when silicon nitride is counter material.
A new method for sampling wear particles directly from the lubricant reservoir has been developed and applied successfully for analyzing wear particles by high-resolution scanning electron microscopy in transmission mode having coupled energy-dispersive X-ray spectroscopy. The lubricated tribological testing was carried out with fully formulated as well as with non-formulated synthetic base oil. It was possible to analyze individual particles with dimensions as small as about 5–30 nm which are likely the 'primary' wear particles. A majority of the particles, however, are agglomerated and, thus, lead to the formation of larger agglomerates of up to a few micrometers. Chemical analysis led to the conclusion that most of the observed particles generated in formulated oil, especially the larger ones, are composed of the additives of the lubricant oil. In non-formulated base oil, the primary particles are of similar dimensions but contain only iron, chromium and oxygen, but most likely stem from the mating materials. This finding points to the fact that the main wear mechanism under lubricated conditions with fully formulated oil is more like a continuous shearing process rather than a catastrophic failure with the generation of larger primary particles. When the oil is non-formulated, however, several wear mechanisms act simultaneously and the wear rate is increased significantly. Generated larger primary particles are milled down to the nanoscale. When the oil is fully formulated, wear mainly takes places at the additive layer or tribofilm; thus, the steel surface is protected.
Tribological studies on neat polyetherketone (PEK) and glass fiber reinforced PEK composite were carried out at room and elevated temperature (120 °C). The objective of this study was to characterize for friction and wear properties under dry reciprocating sliding condition at different experimental conditions. The polymer specimens were made to oscillate against steel cylinder as a counterpart. This kind of contact condition are frequently found in bushes, sliding bearing, electronic parts, seals, etc. The friction and wear behavior of neat PEK and composite was quite different at room temperature and elevated temperature. It was observed that glass fiber reinforcement is beneficial in controlling the wear of PEK matrix at room temperature than at elevated temperature. The test results are discussed by considering the surface properties i.e. material removal and film transfer formation. Scanning electron micrographs and optical micrographs of the worn polymer and steel cylinder was used to study the wear mechanisms.
The topography of wear scars on the surface of a steel disc coated with a diamond-like carbon (DLC) layer has been investigated with an Atomic Force Microscope (AFM). AFM topography images have been combined together taking advantage of the stitching technique for the study of wear scars in their initial stage. Moreover, the topography of the sample has been acquired before and after the sliding tests. In this way even very small changes of the sample surface (<10 nm) can be detected. Three main phenomena taking place at the very initial stage of wear could be identified: the abrasion of small asperities bulging out of the sample surface, the carving of swallow grooves with depth under 20 nm, and the partial or total closure of cavities present on the surface. This last phenomenon shows that, before the carving of a wear scar, the plastic deformation of particular regions of the sample, i.e. the volume around the cavities, takes place already after few cycles (in this case between 400 and 800) in the initial phase of the sliding test.
Stribeck curve
(2014)
The importance of lubricants in virtually all fields of the engineering industry is reflected by an increasing scientific research of the basic principles. Energy efficiency and material saving are just two core objectives of the employment of high-tech lubricants. The encyclopedia presents a comprehensive overview of the current state of knowledge in the realm of lubrication. All the aspects of fundamental data, underlying concepts and use cases, as well as theoretical research and last but not least terminology are covered in hundreds of essays and definitions, authored by experts in their respective fields, from industry and academic institutes.
The tribological behavior of different low infrared (IR) emission ceramic materials from the titanate group has been investigated at room temperature under gross slip fretting conditions against 100Cr6 ball bearing steel and α-alumina as the counterface materials. For all material pairs, friction and wear depended largely on the relative humidity of the environment. When paired with steel the low IR-emission ceramic disks showed higher wear resistance. Under dry conditions, almost no wear was found on the low IR-emission ceramic specimen. The high wear on the steel counter body is caused not only by tribo-oxidation, which is the main wear mechanism, but also by abrasion. In dry conditions a COF of 0.6 and in humid conditions a COF of 0.2 have been measured. When paired with α-alumina the results on wear are just opposite to those with steel counterbody and the low IR-emission ceramic materials show much lower wear resistance under all conditions. This is explained by the predominance of abrasion and the relatively large difference in hardness between the low IR-emission ceramic and α-alumina. In high humidity environments the results point to the formation of stable reaction layers causing lower friction and wear.
Fretting
(2014)
The importance of lubricants in virtually all fields of the engineering industry is reflected by an increasing scientific research of the basic principles. Energy efficiency and material saving are just two core objectives of the employment of high-tech lubricants. The encyclopedia presents a comprehensive overview of the current state of knowledge in the realm of lubrication. All the aspects of fundamental data, underlying concepts and use cases, as well as theoretical research and last but not least terminology are covered in hundreds of essays and definitions, authored by experts in their respective fields, from industry and academic institutes.
Untersucht wurden Verschleißpartikel als elektronen-transparente Proben auf dünnen Trägerfolien mit einem hochauflösendem Rasterelektronenmikroskop und energiedispersiver Röntgenspektrometrie im Transmissionsmodus. Die hohe laterale Auflösung dieser modernen Methoden ermöglicht eine morphologische Charakterisierung der Verschleißpartikel bis in den nm-Bereich. Die hochauflösende Elementanalyse erlaubt eine Interpretation der Zusammensetzung und damit Rückschlüsse auf die Verschleißpartikelbildung.
Die tribologischen Untersuchungen sind an einem Modell-Verschleißtribometer nach DIN 51834-2 geschmiert, aber ohne Ölkreislauf, durchgeführt worden. Die Präparation der Verschleißpartikel über eine Entnahme und Übertragung einer geringen Schmierstoffmenge mit einer Mikropipette auf eine TEM-Trägerfolie ist mit einem geringen Aufwand möglich. Der präparative Aufwand ist relativ gering. Das benötigte Schmierstoffvolumen beträgt wenige Mikroliter (0,001ml).
Die Untersuchung zeigt die geringe geometrische Größe der Verschleißpartikel und bestätigt indirekt die These der Reaktionsschichtbildung mit einer geringen Schichtdicke, die ständig verschleißt und sich stetig neu bildet. Die beschriebenen Verschleißprozesse sind in der Modell-Verschleiß-Prüfung mit sehr hohen Pressungen am Versuchsbeginn nachweisbar.
This paper presents a dry sliding tribo-couple (DLC/monolithic oxide ceramics), where the tribological quantities are more or less in a wide ränge independent of the sliding speed. The DLC film is composed of a specific mixture of sp3 /sp2 hybridized carbon. Self-mated ceramic/ceramic couples of MgO-Zr02, alpha-AI203 or SSiC are with their coefficients of friction above 0.45 not so lubricious, whereas the coefficients of friction of the tribocouples MgO-Zr02/DLC and alpha-AbOVDLC ranged between 0.075 and 0.15 under dry sliding. The coefficients of friction for these tribo-couples tend to decrease with increase sliding speed from 0.03 m/s to 6 m/s. The dry wear rates of the thin film is low (<10‘7 mm3/Nm) and perfectly independent from sliding velocity.
In this article we demonstrate the use of atomic force microscopy (AFM) measurements for the study of macroscopic wear scars. By stitching AFM images acquired over the wear scar, the detailed structure of the scar can be characterized even when the scar is much wider than the typical maximum scan range of the AFM (50–100 µm). The results obtained by AFM are compared with those yielded by white light interferometry (WLI). The comparison validates the WLI measurements; at the same time, it shows decisive differences in the resolutions of these two methods. As a consequence, AFM measurements are necessary whenever a precise characterization of the structure of the scar is required. However, since stitching of AFM images is rather time-consuming, white light interferometry is recommended as a faster method whenever experiments are aimed at just a gross characterization of the scar and the measurement of mean quantities (e.g. the wear volume).
Stick-slip and wear behavior of ceramic and polymer materials under reciprocating sliding conditions
(2013)
In many technical applications not only the actual friction coefficient is of importance, but rather the constancy relevant for the functionality. Due to inconstant ffiction values, positioning processes can be substantially influenced as well as vibrations can be induced. The appearance of this tribological effect, named stick-slip, depends on different factors such as sliding speed, relative humidity and ambient temperature occurring primarily after long operating periods. Beside ambient conditions the choice of materials in contact is the main influencing factor of an inconstant coefficient of friction during operating. Certain polymers are well known for their stick-slip tendencies in technical applications. These are on the one hand different modifications of PTFE (polytetrafluoroethylene) reinforced with glass fibers, bronze or graphite and on the other hand thermoplastics such as PE (polyester) or Pf (polyimide). The difference between static and dynamic values of the ffiction force is decisive for stick-slip phenomena. Furthermore, the stick-slip tendency of polymers strongly depends on the elastic material properties. Main softening material areas, which can be found in the contact, represent particularly vulnerable areas. The high friction value in the contact area decreases in most cases by increasing sliding speeds. However, beside polymers ceramic materials can also offer tendencies to stick-slip motion. Klaffke et al. already investigated the influence of ceramic materials on the stick-slip behavior in.
Zero wear (Null Verschleiß)
(2012)
Recent developments in contact mechanics and microfribology have shown that it is very important to study surface modification effects for quantification of „Zero wear“ (plastic deformation of upper parts of asperities) during sliding friction. The present work considers experimental and Simulation data on the Formation of elastic and plastic contact areas during sliding friction on rough surfaces. The Simulation of discrete contact was carried out using as a source the AFMimages of real surface topography at micro/nanoscale.
The approach for quantification of „zero wear“, proposed here, is not using common Statistical Parameters of roughness, but it considers contact areas on asperities.
In these areas some regions are undergoing plastic deformation which influences surface Transformation during sliding friction. Also, the workhardening effect was taken into account in the Simulation
of sliding friction. This enabled a rnore successful fit of experimental data. The results obtained of the Computer simulations will provide a way of studying friction force at the initial stage of the running-in process.
Main focus was on the correlation of the coefficient of friction (COF) with the geometrical parameters of the surface during early stage of the running-in period. TiN, TiAlN and AlTiN coatings were prepared by using rotating cathode arc evaporation unit. The roughness of the WC-Co substrate Ra ranged from 0.05 to 0.2 µm and the coating thickness was 2.3 ± 0.2 µm. Part of the samples were subjected to the surface modification by the drag grinding finishing. Geometrical parameters of the surface were evaluated by means of atomic force microscopy (AFM) and fretting tests were conducted with 10 mm diameter alumina ball under 2 N load, 100 µm slip distance and the frequency of 10 Hz. It was found that the distribution of macroparticles strongly influences the geometrical parameters of the surface and the number of macroparticles increases with increasing Al content in the coating. In the case of the positive skewness Ssq of the coating surface, the kurtosis Sku provides a statistically significant effect on the COF, namely the COF depends inversely on the kurtosis Sku. The kurtosis value for TiN was the highest among as-deposited coatings, subsequently, the slowest increase rate in the COF was observed for the TiN coating.
Im Vortrag wird neben der apparativen Prüftechnik das allgemeine methodische Vorgehen für Modell-Verschleißuntersuchungen im Bereich des partial slip vorgestellt. Im Detail wird für Dental-Implantat-Werkstoffe eine Rangfolge aufgestellt, die vergleichend die Verschleißresistenz unterschiedlicher Ti-basierter Werkstoffe zeigt. Wird durch die Kaubewegung eine mehrachsige Beanspruchung in die Kontaktflächen der Schraubverbindung eingeleitet, kann durch partial slip im Randbereich dieser Kontaktfläche ein Verschleißprozess initiiert werden, der die Lockerung des Implantats begünstigt. Eine gute Verschleißresistenz verhindert oder schiebt die vorzeitige Lockerung hinaus.
Um das Werkstoffverhalten in Bezug auf eine vorzeitige Lockerung der Implantatkrone bei geschraubten zweiteiligen Implantaten zu charakterisieren, wurden zylindrische Probekörper unter partial slip Fretting-Bedingungen mit Zyklenzahlen bis n = 200 000 beansprucht. Die Frequenz der aufgebrachten Tangentialkraft betrug 2 Hz, um die Kaubewegung zu simulieren.
Die tribologischen Untersuchungen wurden auf einem Eigenbau-Tribometer mit der Kontaktgeometrie „gekreuzte Zylinder“ durchgeführt. Die zylindrischen Proben wurden aus den Werkstoffen Titan Grade 4 und der Ti-Legierung Ti6AI4V gefertigt. Ein Teil dieser Ti-basierten Proben wurde oberflächengehärtet. Die bisher erzielten Ergebnisse zeigen, dass die oberflächenbehandelten Proben dazu neigen, unter der Belastung die Kontaktfläche zu vergrößern. Dies deutet auf einen Effekt bekannt als „junction growth“ und damit auf eine erhöhte Versetzungsbeweglichkeit der randschichtgehärteten Proben hin. Einen Einfluss der Zwischenstoffe konnte nicht nachgewiesen werden.
The wear behaviour of thin steel wires has been analyzed under oscillating sliding conditions in crossed cylinders contact geometry. The focus of this analysis was the influence of the crossing angle between the wires on the wear. The wires used had 0.45 mm in diameter and the material was cold-drawn eutectoid carbon steel (0.8% C) with a tensile strength higher than 2800 MPa. Two different types of tests were carried out, the first one representing the influence of the crossing angle for a constant load and the second one representing the influence of the crossing angle with constant contact pressure. In the first type of tests it was seen that as the contact angle decreases the contact pressure decreases too and hence less energy specific wear resistance is observed. As a consequence less wear is produced, thus increasing the life of the wires. In the second type of tests it was seen that with constant contact pressure but different crossing angles, nearly the same energy specific wear resistance was observed. This points at an identical wear behaviour in both type of tests but with a running-in and a steady state period as two different wear periods. The tests showed that the running in period may play an important role in the overall wear particle generation and hence the wear occurring in the steady state period is rather mild.
Different fretting tests of thin steel wires under different conditions (loads, strokes, number of cycles and mean pressures) were performed. The wires used had 0.45 mm in diameter and the material was a cold-drawn eutectoid carbon steel (0.8% C) with a tensile strength over 2800 MPa. The tests were carried out with 90° "crossed cylinders" configuration varying the stroke, normal load and testing time (number of cycles). Afterwards the volumetric wear was obtained using surface profilometry with diamond stylus.
With a classical study of the coefficient of wear with respect to the sliding distance, the results show that the wear coefficient increases with normal load and stroke, consequently, for the same sliding distance, the wear produced was higher when the load and/or stroke is increased. In this work, the coefficient of wear is decreasing continuously as the test is running. In order to analyze better the wear behaviour, another method, in which the volumetric wear is compared with respect to the Archard's loading factor, is proposed. As result of this method, two distinctive behaviours were detected; one corresponds to the running-in period with a more aggressive wear behaviour and the second one to the stable steady state period. In all the tests the running-in period was similar with regard to the wear rates but in the stable period the wear rates were increasing with higher loads or strokes.