A new concept for the ecotoxicological assessment of plastics under consideration of aging processes
(2023)
Microplastics are widely distributed in aquatic and terrestrial environments, but up to now less is known about (eco)toxicological impacts under realistic conditions. Research so far has focused mainly on impacts on organisms by fresh, single‐origin plastic fragments or beads. However, plastics found in the environment are complex in composition, this means different polymer types and sources, with and without additives and in all stages of age, and therefore, in a more or less advanced stage of degradation. For oxidized degradation products that might be released from plastic materials during aging, there is a lack of information on potentially adverse effects on aquatic biota. The latter is of particular interest as oxidized degradation products might become more water soluble due to higher polarity and are more bioavailable, therefore. The present study focused on plastic leachates of polystyrene (PS) and polylactic acid (PLA), which were derived from alternating stress by hydrolysis and ultraviolet (UV) radiation—representing a realistic scenario in the environment. Test specimens of PS, PLA, or a PLA/PS layer (each 50%) were alternately exposed to UV radiation for 5 days followed by hydrolysis for 2 days, for several weeks alternating. Ecotoxicological effects of the storage water (artificial freshwater) of the test specimens and additionally, in a second experimental setup, the effects of five potential polymer degradation products were detected by 72 h algae growth inhibition tests with Desmodesmus subspicatus. Results clearly indicate inhibitory effects on algae growth by contaminants in the storage water of stressed plastics with increasing growth inhibition of proceeding hydrolysis and UV stress times. Different polymers caused variable inhibitions of algae growth with stronger inhibitions by PS and less effects by PLA and the mixed layer of both. Moreover, not microplastic particles but the resulting dissolved degradation products after aging caused the ecotoxicological effects—with strong effects by the oxidized degradation products. The existing data highlight the relevance of plastic aging as a framework for microplastic ecotoxicity evaluation and allow a proof of concept.
Degradation of polyurethanes in various environments – Effects on molecular mass and crosslinking
(2019)
The increasing application of polyurethanes (PU) in safety relevant sectors (fire protection, insulation, medicine technique) requires detailed knowledge of the stability and reliability of these materials. Different climate factors are supposed to induce diverse and overlapping degradation reactions. The knowledge of these degradation mechanisms is necessary for an estimation of the period of application depending on usage of the material. An essential property of a polymeric system is represented by the molecular weight. Since a change of the molecular weight is a measure for the chemical stability of a polymer, size-exclusion chromatography (SEC) was used to monitor changes of the molecular weight of thermoplastic polyether- and polyester urethane (TPU) exposed to thermal, hydrolytic and photo-oxidative (UV) degradation conditions for several days. Thermal treatments were performed at elevated temperatures (100 - 200 °C) under oxidative (air) as well as non-oxidative (nitrogen) conditions to evaluate the specific influence of oxygen on the degradation. At higher temperatures (≥ 175 °C) a fast decrease of the molecular masses of both PU accompanied by a high degree of crosslinking was found. At lower temperatures (≤ 150 °C) the polymers remained widely unaffected by thermal degradation within the investigated degradation interval of up to two weeks, which was already known from FTIR spectroscopy[1]. In contrast to that, UV treatment at 25 °C at less than 10 % rel. humidity (RH) resulted in a fast crosslinking, whereas the molecular masses of both PU decreased slower than during the thermal treatments. The depth of penetration of the UV radiation was determined using 3D printed PU samples with different thicknesses. Hydrolysis based degradation effects were less significant. Only slight molecular mass changes were detected at temperatures ≤ 80 °C within a time span of 14 days, while no crosslinking could be measured. Considering the degradation results at the investigated exposure parameters, it could be shown that ester-based PU in general exhibits a significant higher stability compared to ether-based materials.
Size-exclusion chromatography (SEC) was used to monitor changes of the molecular masses of thermoplastic polyether – and polyester urethane (TPU) exposed to thermal, hydrolytic, and photo-oxidative (UV) Degradation conditions for several days. The thermal treatment was performed at elevated temperatures (100–200 °C) under oxidative (air) as well as non-oxidative (nitrogen) conditions to evaluate the specific influence of oxygen on the degradation. At higher temperatures (≥175 °C) a fast decrease of the molecular masses of both PU accompanied by a high degree of crosslinking was found. At lower temperatures (≤150 °C) the polymers remained widely unaffected by thermal degradation within the investigated degradation interval of up to two weeks. Surprisingly, the influence of oxygen (air) was found to be less distinct. In contrast to that, UV treatment at 25 °C at less than 10% rel. humidity (RH) resulted in a fast crosslinking, whereas the molecular masses of both PU decreased slower than for thermal treatments. The depth of penetration of the UV radiation was estimated using 3D printed PU samples with different thicknesses. Hydrolysis based degradation effects were less significant. Only slight molecular mass changes were detected at temperatures ≤80 °C within a time span of 14 days, while no crosslinking could be measured. Considering the degradation results at the investigated exposure parameters, it could be shown that esterbased PU in general exhibits a significant higher stability compared to ether-based materials.