The sensitivity of low-loss perfluorinated polymer optical fiber (PF-POF) to gamma radiation is investigated for on-line radiation monitoring purposes. The radiation-induced attenuation (RIA) of a commercial PF-POF based on Cytop material is measured in the visible spectral region. The fiber RIA shows strong wavelength dependence with rapid increase towards the blue side of the spectrum. The wide range of radiation sensitivities is available via careful selection of appropriate monitoring wavelength. The accessible sensitivities span from 1.6 ± 0.2 dBm-1/kGy measured at 750 nm to 18.3 ± 0.7 dBm-1/kGy measured at 420 nm. The fairly high radiation sensitivity as well as its wide tunability makes the fiber a promising candidate for a broad range of applications.
The paper presents the first complex study of Gamma radiation effects on a low-loss perfluorinated polymer optical fiber (PF-POF) based on Cytop® polymer. Influence of gamma radiation on fiber’s optical, mechanical and climatic performance is investigated. The radiation-induced attenuation (RIA) in the visible and near-infrared region (0.4 μm-1.7 mm) is measured and its origins are discussed. Besides attenuation increase, radiation is also shown to decrease the thermal degradation stability of the fiber and to increase its susceptibility to water. With regard to complex fiber transmission performance upon irradiation, the optimal operation wavelength region of PF-POF-based systems intended for use in Radiation environments is determined to be around 1.1 μm. On the other hand, the investigated fiber holds potential for low-cost RIA-based optical fiber dosimetry applications with sensitivity as high as 260 dBm⁻¹/kGy in the visible region.
Gamma radiation induced effects in perfluorinated polymer optical fibers for sensing applications
(2015)
Radiation induced attenuation in perfluorinated polymer optical fiber was investigated as a potential mean for online. in situ gamma radiation monitoring. Spectral dependence of radiation induced attenuation was measured in the visible and near infrared range. Attenuation spectrum exhibits sharp increase both towards the ultraviolet and infrared side of the spectrum with 3 distinct peaks around 1400 nm. The fiber sensitivity to gamma radiation was further evaluated at two commonly used IR wavelengths (1310nm and l550nm} by pre- and post-irradiation optical time-domain reflectometry measurements. The examined fiber is sensitive up to lOO kGy of total absorbed dose with only minor saturation towards the large dose values. The influence of gamma radiation on the fiber mechanical properties was studied as well. Up to the maximal dose of 100 kGy, no significant deterioration of fiber strength and elasticity was observed.