Most additive manufacturing (AM) techniques have in common that material is spread out as thin layers of a dried powder/granulate by a roller or a shaker system. These layers are mostly characterized by a low packing rate. On the other hand, appreciable densities can be reached by the use of ceramic slurries. In this context, the layer-wise slurry deposition (LSD) has been developed. Specific features of the LSD process are reflected on the basis of already existing additive manufacturing technologies. The microstructure of laser-sintered bodies will be discussed, and strategies for an improved microstructure during sintering will be introduced.
Laser-fused K0.5Na0.5NbO3 (KNN) powder of 75% transparent fraction has been sintered by pressureless sintering, spark plasma sintering (SPS), and hot isostatic pressing (HIP). The laser-fused KNN has a fictive temperature of 503 °C and an onset crystallization temperature of around 529 °C. The results have shown that sintering of the laser-fused KNN powder utilizing the viscous flow of the transparent microspheres (amorphous content)–at the kinetic window (26 °C)–is possible. The highest yield relative density is around 83% at a sintering temperature of 525 °C and at a sintering pressure of 280 MPa. Limited density has been reached because of formation of crystalline surface layers around the amorphous areas. The samples hipped at 525 °C have low piezoelectric coefficient d33 of 5 pC/N because of the residual porosity that led to early dielectric breakdown during the polarization. The sintering behavior, the resulting microstructure as well as the measured properties will be discussed.
Porous Al2O3 with high porosity (~45%), remarkable flexural strength (~70 MPa), and low dimensional change (~1–2%), was produced by indirect 3D printing and reaction bonding. Coarse Al with good flowability was carried out printing green body. The green body was heat treated to get fully oxidized, volume expansion during oxidation simultaneously formed strong neck bonding, not only brought good strength, but also restricted shrinkage. Porous Al2O3 with architecture of macro pores designed by 3D printing and micro pores in the strut formed by packing of particles was obtained. The near zero shrinkage can facilitate precise design of product with complex shape.
Selective laser sintering of ceramic powders is a promising technique for the additive manufacturing of complex- and delicate-shaped ceramic parts. Most techniques have in common that the powder to be sintered is spread to a thin layer as a dry powder by means of a roller or shaker system. These layers have a relatively low density. On the other hand, appreciable densities can be reached with the use of ceramic slurries as the starting material. Therefore, the layer-wise slurry deposition (LSD) process has been developed. Layer stacks, i.e. powder beds, built up by employing the LSD technology exhibit a density comparable to ceramic powder compacts processed by means of conventional forming technologies. Writing the layer information with a focused laser beam in these dense ceramic powder compacts enables the manufacture of ceramic bodies with a high density and precision in contour.