- nein (9)
A laser induced breakdown spectroscopy (LIBS) system was combined with the Gas Tungsten Arc (GTA) Welding process for the in situ measurement of chemical compositions in austenitic stainless steels during welding. The purpose of this project is to develop a prototype of an online chemical composition control system for welding applications. One of the use cases of this new LIBS-based measurement system can be the controlling of potentially dangerous emissions during the welding process in order to improve the working safety conditions. Further, the control of the weld pool composition allows governing the weld pool solidification behavior and thus allows reducing the resultant susceptibility for solidification cracking. The composition of the weld seam is from the metallurgical point of view the most critical parameter for the occurrence of weld defects1. Conventional inspection methods for weld seams as e.g. ultrasonic inspection are ex situ and cannot prevent the defects. For that reason automated in situ analysis systems for weld defect detection are much more efficient2. Beyond that, the proposed LIBS-based analysis system allows to study the correlation between the occurrence of weld defects and the chemical composition of the weld pool or the region where solid and liquid phase coexist.
A laser induced breakdown spectroscopy (LIBS) system was combined with the Gas Tungsten Arc (TIG) Welding process for the in situ monitoring of chemical compositions in austenitic stainless steels during welding. The purpose of this project is to develop a prototype of an online chemical composition control system for welding applications. One of the use cases of this new LIBS-based measurement system can be the controlling of potentially dangerous emissions during the welding process in order to improve the working safety conditions.
Time- and space-resolved in situ LIBS measurements of chemical compositions during TIG-welding
(2017)
An in situ monitoring of chemical compositions in the weld pool and the heat affected zone (HAZ) can enable the control of the welding process through the regulation of the welding parameters, and thus can prevent possible weld defects.
The most critical parameter for hot cracking -from a metallurgical point of view- is the chemical composition of the weld pool.
Chemical composition can be measured and quantified during the welding process with the LIBS technique having the appropriate calibration measurements.
The Tungsten Inert Gas (TIG) welding process was combined with a Laser-Induced Breakdown Spectroscopy (LIBS) system for the in situ measurement of chemical compositions in austenitic stainless steels. The main aim of this project was the development of a prototype for a real-time chemical composition analysis system for welding applications. In principle, the measurement of the weld pool composition allows governing the weld pool solidification behaviour by controlling the welding parameters. This control loop allows avoiding weld defects.
Chemical compositions of the weld seam is from a metallurgical point of view the most critical parameter for the occurrence of weld defects. Additionally, this new LIBS-based measurement system can be used for the monitoring and controlling of potentially dangerous emissions during the welding process in order to improve the working safety conditions. Preliminary investigations show that the chemical composition measurement of welds with LIBS is possible during and after welding.
In situ laser-induced breakdown spectroscopy measurements in stainless steels during TIG welding
(2018)
Chemical composition of the welding seam and HAZ has significant effect on weld quality. Current inspection methods for weld seams measure and investigate post factum and cannot prevent weld defects. Element burn-off may significantly affect solidification leading to embrittlement or cracking Control of weld chemical compositions insures a controlled solidification and resistance to related weld defects. A prototype of a LIBS controlled welding process is presented.
Chemical composition of the welding seam and HAZ has significant effect on weld quality. Current inspection methods for weld seams measure and investigate post factum and cannot prevent weld defects. Element burn-off may significantly affect solidification leading to embrittlement or cracking Control of weld chemical compositions insures a controlled solidification and resistance to related weld defects.
A laser-induced breakdown spectroscopy (LIBS) system was combined with a bead-on-plate Tungsten Inert Gas (TIG) welding process for the in situ measurement of chemical compositions in austenitic stainless steels during welding.Monitoring the weld pool's chemical composition allows governing the weld pool solidification behavior, and thus enables the reduction of susceptibility to weld defects. Conventional inspection methods for weld seams (e.g. ultrasonic inspection) cannot be performed during the welding process. The analysis system also allows in situ study of the correlation between the occurrence ofweld defects and changes in the chemical composition in theweld pool or in the two-phase regionwhere solid and liquid phase coexist. First experiments showed that both the shielding Ar gas and the welding arc plasma have a significant effect on the selected Cr II, Ni II and MnII characteristicemissions, namely an artificial increase of intensity values via unspecific emission in the spectra.
In situ investigations showed that this artificial intensity increase reached a maximum in presence of weld plume. Moreover, an explicit decay has been observedwith the termination of thewelding plumedue to infrared radiation during sample cooling. Furthermore, LIBS can be used after welding to map element distribution. For austenitic stainless steels,Mnaccumulations on both sides of theweld could be detected between the heat affected zone (HAZ) and the base material.
Die chemische Zusammensetzung der Schweißnaht und WEZ haben einen wesentlichen Einfluss auf die Schweißnahtqualität. Aktuelle Prüfmethoden für Schweißnähte können post factum messen und die Schweißfehler nicht verhindern.
Das Abbrandverhalten kann über die Erstarrung wesentlichen Einfluss haben und zu Versprödung oder Rissbildung führen. Die in situ Überwachung der chemischen Zusammensetzung der Schweißnähte gewährleistet eine kontrollierte Verfestigung und Beständigkeit gegen Schweißfehler. Ein in situ Schweißnahtprüfverfahren mittels LIBS wurde entwickelt.
TIG welding process was monitored using LIBS for the in situ measurement of chemical compositions in austenitic stainless steels. This research aims to prototype a real-time chemical composition analysis system for welding applications and prove the feasibility of such a quality control loop.
The chemical compositions of the weld pool, considering the welding metallurgy, is the most critical parameter for any occurring weld defects, e.g. hot cracking. Hence, controlling the weld pool chemical composition allows governing of the weld pool solidification behavior by monitoring and adjusting the respective welding parameters, e.g. welding current.
LIBS measurements were conducted during a TIG-welding process. The effect of the welding plasma on the LIBS signal was thoroughly investigated by varying various LIBS settings, e.g. delay and exposure time. Quantification of the main alloying elements Cr and Ni in the weld pool during welding was achieved by univariate calibration procedure.