Datei im Netzwerk der BAM verfügbar ("Closed Access")
Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (11)
- Zeitschriftenartikel (8)
- Posterpräsentation (5)
- Beitrag zu einem Tagungsband (4)
Schlagworte
- Dislocation (9)
- Creep (6)
- Microstructure (6)
- Scanning transmission electron microscopy (STEM) (4)
- Superalloy (4)
- TEM (4)
- Diffraction contrast (3)
- EBSD (3)
- Microscopy (3)
- Transmission electron microscopy (3)
Organisationseinheit der BAM
This work investigates the effect of the tribotesting parameters (temperature, atmosphere, and third body chemical composition) on the coefficient of friction (CoF) during pin-on-disc dry (PoD) sliding tribotests using artificial third bodies. The third body comprised nanometric Fe3O4-based binary to quaternary chemical compositions containing copper, graphite, and zirconia. These mixtures were manually or ball-milled prepared, and pin-on-disc tribotests were conducted at 23 °C and 400 °C under air or nitrogen atmospheres. Combining PoD and artificial third body to create synthetic tribofilms might be useful for testing new formulations of Cu-free friction materials. Microstructural characterisation of the tribofilms was used to study the stability of the Fe3O4, copper, and graphite nanoparticles under different testing conditions to understand their effects on the CoF. For the Fe3O4-C-ZrO2-X systems, the ball milling mixing promoted the formation of turbostratic graphite in the tribofilm, impairing the lubricating effect of the graphite under air atmosphere at 23 °C. The formation of monoclinic CuO in the tribofilms during tribotests at 400 °C under air and N2 atmospheres promoted a lubricating effect.
The present work describes the shear creep behavior of the superalloy LEK 94 at temperatures between 980 and 1050 °C and shear stresses between 50 and 140 MPa for loading on the macroscopic crystallographic shear system (MCSS) (011)[01-1]. The strain rate versus strain curves show short primary and extended secondary creep regimes. We find an apparent activation energy for creep of Qapp = 466 kJ/mol and a Norton-law stress exponent of n = 6. With scanning transmission electron microscopy, we characterize three material states that differ in temperature, applied stress, and accumulated strain/time. Rafting develops perpendicular to the maximum principal stress direction, gamma channels fill with dislocations, superdislocations cut gamma' particles, and dislocation networks form at gamma/gamma' interfaces. Our findings are in agreement with previous results for high-temperature and low-stress [001] and [110] tensile creep testing, and for shear creep testing of the superalloys CMSX-4 and CMSX-6 on the MCSSs (111)[01-1] and (001)[100]. The parameters that characterize the evolving gamma/gamma' microstructure and the evolving dislocation substructures depend on creep temperature, stress, strain, and time.
A great amount of material properties is strongly influenced by dislocations, the carriers of plastic deformation. It is therefore paramount to have appropriate tools to quantify dislocation substructures with regard to their features, e.g., dislocation density, Burgers vectors or line direction. While the transmission electron microscope (TEM) has been the most widely-used equipment implemented to investigate dislocations, it usually is limited to the two-dimensional (2D) observation of three-dimensional (3D) structures. We reconstruct, visualize and quantify 3D dislocation substructure models from only two TEM images (stereo pairs) and assess the results. The reconstruction is based on the manual interactive tracing of filiform objects on both images of the stereo pair. The reconstruction and quantification method are demonstrated on dark field (DF) scanning (S)TEM micrographs of dislocation substructures imaged under diffraction contrast conditions. For this purpose, thick regions (> 300 nm) of TEM foils are analyzed, which are extracted from a Ni-base superalloy single crystal after high temperature creep deformation. It is shown how the method allows 3D quantification from stereo pairs in a wide range of tilt conditions, achieving line length and orientation uncertainties of 3% and 7°, respectively. Parameters that affect the quality of such reconstructions are discussed.
Thermodynamic study of a refractory complex concentrated alloy (rCCA) using the CALPHAD method
(2019)
Multi-principal-element alloys (MPEAs), have recently come to the attention of the scientific community due to their potential for improving properties such as, e.g. mechanical strength and oxidation resistance in high temperature structural applications. The AlMo0.5NbTa0.5TiZr refractory (r)CCA is one such candidate, showing a two-phase microstructure after a two-stage heat treatment under argon atmosphere at a controlled cooling rate. Since the application conditions intended for this alloy require a long-term high temperature (> 700 °C) mechanical and oxidation resistance, it becomes necessary to assess the possible phase development in this regime. The diagrams reveal that two BCC-based phases could form during alloy solidification, where one phase would be enriched with Mo, Nb and Ta while the other phase, with Al, Ti and Zr. Activity oxides diagrams show that a stable form of aluminum oxide (α-Al2O3, Pearson symbol: hR10, corundum) can be formed.
Unlike conventional alloys, which typically consist of one main element, high-entropy alloys (HEAs) contain five or more principal elements, which broaden chemical complexity and with it a realm of synergistic mechanisms. The AlMo0.5NbTa0.5TiZr HEA initiated a subclass of Al-containing refractory (r)HEAs that has recently drawn attention [2]. The alloy has a superalloy-resembling B2/bcc nanostructure, which inspired its name refractory high entropy superalloy (RSA). With high-temperature (HT) compressive strengths beyond conventional Ni-based superalloys, this nanostructure could be used for improved HT structural applications. However, in the application-relevant HT regime the Al-Zr-rich B2 phase decomposes to form a hexagonal Al-Zr-based intermetallic (Al4-xZr5; x: 0..1) [3,4]. This work explores the fascinating yet fatal micromechanisms associated to this phase transformation, in the context of creep, annealing and oxidation experiments performed between 800 and 1200 °C.
The material was produced by arc-melting and heat treatment in argon, which lead to grain boundaries decorated with up to 7%. Interrupted constant-load creep tests were performed under vacuum (at 10-4 Pa), at 900–1100 °C with external tensile stresses of 30–120 MPa. Oxidation experiments were separately conducted for 24 hours at 800 and 1000 °C in both dry (21% O2 + 79% N2) and humid (8% O2 + 74% N2 + 18% H2O) air. After the experiments, the samples were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy to reveal degradation mechanisms. Crystallographic texture, orientation relationships and stabilization of an oxygen-containing iso structure (Al4-xZr5(Ox-y); y: 0..x) of the Al-Zr-rich intermetallic are found and discussed.
Subsurface characterization of high-strength high-interstitial austenitic steels after impact wear
(2018)
The microstructure of the subsurface after impact wear of three high-strength high interstitial austenitic steels has been analysed using transmission electron microscopy (TEM) in alloys with C and N as interstitial elements. In all cases, a nanocrystalline region followed by a transition zone and a cold-worked area are present. Additionally, microhardness and nano-scratching tests were conducted to study the wear-related properties of the impact subsurface and the base material. The results of the microstructural analysis reveal that the following mechanisms are involved during impact wear: abrasion (ploughing), microcrack formation associated with contact fatigue, entrapment and adhesion of SiO2 particles. The analysis of the wear-related properties indicates that the subsurface acts as a self-protective layer that prevents the deterioration of the substrate.
Additive manufacturing (AM) of metallic alloys has gained momentum in the past decade for industrial applications. The microstructures of AM metallic alloys are complex and hierarchical from the macroscopic to the nanometer scale. When using laser-based powder bed fusion (L-PBF) process, two main microstructural features emerge at the nanoscale: the melt pool boundaries (MPB) and the solidification cellular substructure.
Here, details of the MPB are revealed to clearly show the three-dimensional nature of MPBs with changes of cell growth of direction and their relation to their surrounding cellular substructure, as investigated by transmission electron microscopy (TEM) for L-PBF 316L austenitic stainless steel (cf. Figure 1). A hitherto unknown modulated substructure with a period of 21 nm is further discovered within cells as the result of a partial Ga+-focused ion beam-induced ferritic transformation of the austenite. Cell cores and cell boundaries differ notably regarding the modulated substructure.
The realistic description of plastic deformation caused by dislocations demands the representative measurement of their features, e.g., Burgers vector, slip plane, line direction and density. In the case of bulk deformation of technical alloys, reliable data must be ensured for large regions. Nonetheless, the (thin) filiform nature of dislocations and also the heterogeneity in some microstructures additionally require flexible analysis techniques that resolve the details of their interactions. Strong and clear channeling contrasts, faint extinction contours and the absence of chromatic aberration make scanning transmission electron microscopy (STEM) an ideal imaging mode in wide and thick regions of TEM foils, as opposed to conventional (C)TEM. It is the purpose of this contribution to show how STEM can be applied for quantitative measurement of dislocation features. Furthermore, a new tool will be presented, which enables the three-dimensional (3D) reconstruction, visualization and quantification of dislocation densities and directions from stereo-pairs. The application of these techniques will be shown on a monocrystalline Ni-base superalloy, an important class of structural materials that has been implemented in the first row blades of gas turbines. The examples are extracted from specimens subjected to creep deformation at high temperature and low stress under various macroscopic deformation geometries. The spacial and angular accuracy are discussed as well as possible sources of error.
Automated electron backscatter diffraction (EBSD) is generally unable to distinguish between multiple cubic phases in a specimen without additional information, such as that obtained by simultaneous energy dispersive X-ray spectroscopy (EDS). Small particles of phases with relatively similar compositions push the limits of phase identification using simultaneous EBSD and EDS, and a mismatch exists between the spatial resolutions of these two techniques due to them having different electron interaction volumes. In a recent paper, the present authors explored using backscatter detectors mounted on top of the EBSD detector to obtain atomic number (Z) contrast images that could be used for phase segmentation in cases where the results from the EBSD and EDS signals remain ambiguous. In the present work, we show that similar information can be obtained from the raw EBSD patterns themselves at higher spatial resolution than was obtained from the backscatter detectors, with the additional advantage of having no spatial mismatch between the data collection grids.
The creep anisotropy of the single crystal superalloy LEK 94 deformed in tension along [0 0 1] and [1 1 0] directions at 1293 K and 160 MPa was investigated. Elementary microstructural processes which are responsible for a higher increase in creep rates with strain during [1 1 0] as compared to [0 0 1] tensile loading were identified. [1 1 0] tensile creep is associated with a higher number of γ' phase cutting events, where two dislocations with equal Burgers vectors of type <1 1 0> jointly shear the γ' phase. The resulting <2 2 0>-type superdislocation can move by glide. In contrast, during [0 0 1] tensile loading, two dislocations with different <1 1 0>-type Burgers vectors must combine for γ' phase cutting. The resulting <2 0 0>-type superdislocations can only move by a combination of glide and climb. The evolution of dislocation networks during creep determines the nature of the γ' phase cutting events. The higher [1 1 0] creep rates at strains exceeding 2% result from a combination of a higher number of cutting events (density of mobile dislocations in γ') and a higher superdislocation mobility (<2 2 0> glide) in the γ' phase.