The knowledge about energy release and transient behaviour of flash lamps, used as short-term energy source in flash thermography investigations, is essential for a quantitative analysis of the results as well as for simulations regarding such experiments. Usually, only a rectangular pulse shape of a typical duration of a few milliseconds is regarded when flash lamps pulses are described. This note considers the afterglow period of a flash lamp explicitly and shows that negligence of this afterglow effect leads to a systematic underestimation of the pulse length and the related total energy release. In the reported case, the intensity transient recorded by a Silicon photo diode was transformed into a temperature transient, allowing the study of the real energy release. It turns out that approximately only 50% of the entire pulse energy were released during the usually regarded period of 2.8 ms, while the other half was released within a period of 20 ms with an exponential decay.
Pulse and flash thermography are experimental techniques which are widely used in the field of non-destructive testing for materials characterization and defect detection. We recently showed that it is possible to determine quantitatively the thickness of semitransparent polymeric solids by fitting of results of an analytical model to experimental flash thermography data, for both transmission and reflection configuration. However, depending on the chosen experimental configuration, different effective optical absorption coefficients had to be used in the model to properly fit the respective experimental data, although the material was always the same. Here, we show that this effect can be explained by the wavelength dependency of the absorption coefficient of the sample material if a polychromatic light source, such as a flash lamp, is used. We present an extension of the analytical model to describe the decay of the heating irradiance by two instead of only one effective absorption coefficient, greatly extending its applicability. We show that using this extended model, the experimental results from both measurement configurations and for different sample thicknesses can be fitted by a single set of parameters. Additionally, the deviations between experimental and modeled surface temperatures are reduced compared to a single optimized effective absorption coefficient.
Impact damages and delaminations in fibre-reinforced composites (FRC) might not be visible at the surface, but could have an influence on the resistance and on the long-term behaviour of the component. Therefore, and especially for safety relevant structures, non-destructive methods are required for the assessment of such damages.
Active thermography methods are suitable to characterize damages after loading using different kind of excitation techniques and various configurations of infrared (IR) camera and heating sources. Here, flash lamps, impulse excitation with infrared radiator and lock-in technique with halogen lamps or widened laser beams are suited. In addition, non-optical sources like sonotrodes (requiring direct contact to the structure) or induction generators (only suited for carbon fibre reinforced polymer (CFRP) structures) could be applied as well. For the investigation of the evolution of the damage during the impact, passive thermography can be applied in-situ. Elastic and plastic deformations alter the temperature of the structure and thus the temperature on the surface.
In this contribution, at first the general principles of quantitative defect characterisation in FRC using active thermography with flash, impulse and lock-in excitation are described. Optical and thermal properties of the FRC material and its anisotropy are considered. Results of phase differences obtained at flat bottom holes with flash and lock-in thermography are compared for qualifying both methods for quantitative defect characterization. Secondly, the damage evolution of CFRP and GFRP structures under impact load and static tensile loading is described. The spatial and temporal evolution of the surface temperature enables us to distinguish matrix cracks or fibre-matrix separation from delaminations between the layers. Afterwards, all results for loading defects, obtained by passive and active thermography, are compared with each other. Fig. 1 and 2 show the difference of passive and flash thermography obtained at impact and tensile loaded CFRP plates, respectively. As one purpose of these investigations is the development of standards within national (DIN) and European (CEN) standardisation bodies, new draft and final standards are presented and further needs are discussed at the end of the presentation.
In flash thermography, the temperature transient is strongly influenced by the temporal shape of the heating pulse for samples with high thermal diffusivity or very thin samples. Here, we present a closed phenomenological approximation of the temporal shape of pulses of Xe-flash lamps. It is a non-stitched solution, has a simple Laplace transform and is suitable for different lamps and energy settings. It is demonstrated that simulated temperature transients, based on this approximation, are well consistent with experimental data.