The rapid mass calorimeter (RMC) was used as a screening tool based on accelerated fire testing to assess flame-retarded thermoplastic polyurethane (TPU). The reliability of RMC results was proven with the cone calorimeter as reference fire test. The influence of melamine cyanurate (MC) concentration on the fire performance of TPU was investigated, along with some flame-retardant combinations such as MC with aluminium diethylphosphinate (AlPi), aluminium trihydrate (ATH), and melamine polyphosphate (MPP). The two-stage burning behaviour of TPU was investigated in detail; the first stage corresponds mainly to the hard segments' decomposition and has a much lower effective heat of combustion (EHC) than the second stage, in which mainly the soft segments decompose and an intensive liquid pool fire is observed in the cone calorimeter set-up. In addition to fire testing with the cone calorimeter, RMC, and UL 94 flammability tests, the decomposition of the materials was investigated using thermogravimetric analysis coupled with infrared spectrometry (TGeFTIR). TPU/MC/AlPi shows the most promising results, achieving V-0 classification in UL 94 and reducing the extreme peak heat release rate (PHRR) of the liquid pool fire from 3154 kW/m2 to 635 kW/m2. Using MC/AlPi/MPP enhances the latter PHRR reduction further. The decomposition products identified in the gas phase via TGeFTIR reveal specific MCeAlPi eMPP interactions, as they differ from products seen in systems with MC/AlPi or MC/MPP. Correlations between RMC and cone calorimeter results were examined and presented in the final part of the paper. Several characteristics correlate strongly, pointing out that RMC is a reliable high-throughput fire testing method to screen multicomponent flame-retardant solutions in TPU.
The residual post-fire mechanical properties of fiber-reinforced epoxy composites are influenced by their fire residues after burning. This study uses intumescent/low-melting glass flame retardants to tailor fire residues in epoxy resin. Processibility of prepregs and their quality are analysed for transfer of the flame-retardant epoxy resins to layered glass-fiber reinforced composites. Minimal effects were found on the pre-fire flexural strengths of the composites due to low loading of the flame retardants. However, when transferred to glass-fiber reinforced composites, the fire residues diminish significantly. Further studies are required to improve theoretical and experimental estimations of the post-fire mechanics of the composites.
The transfer of flame-retardant epoxy resin formulations to composites for structural and lightweight applications in the energy and transport sector can be complex and requires systematic investigation. Here, uncoated and silane-coated ammonium polyphosphate (APP, Si-APP) intumescent compounds are transferred to prepregs using a Bisphenol A diglycidyl ether (DGEBA) resin matrix to 0/90o bidirectional glass fibers with an aerial weight of 600 g/m2. Inorganic silicates (InSi) are added to improve the fire residues of the composites after combustion and the total amount of flame retardants in the resin formulations was 10% by weight. The prepregs' fiber volume content (FVC) is corroborated using in-process measurements and thermogravimetric analysis. This was found to be approximately 60% for the composites containing APP, which is ideal for load-bearing applications with high mechanical strength. However, the Si-APP containing prepregs showed an inconsistent FVC potentially due to interactions with the commercial sizing of the glass fibers. The composites subsequently prepared are analysed for potential filtration effects of the additives via SEM after immobilization in a cured resin and platinum sputtering. The inter-laminar shear strength and the mechanical strength of the composites are compared via three-point bending tests. Additionally, the fire performance of the composites is analysed using cone calorimetry. It was found there was minimal impact of the loading of the flame retardants on the delamination of the composites and the flexural strength. However, the high density of the glass fibers possibly results in a suppression of the mode of action of the flame retardants in the composites. Therefore, the fire residues of the composites are further compared using SEM, and the flame-retardant modes of action upon transfer are investigated.
The residual post-fire mechanical properties of fiber-reinforced epoxy composites are influenced by their fire residues after burning. This study uses intumescent/low-melting glass flame retardants to tailor fire residues in epoxy resin. Processibility of prepregs and their quality are analysed for transfer of the flame-retardant epoxy resins to layered glass-fiber reinforced composites. Minimal effects were found on the pre-fire flexural strengths of the composites due to low loading of the flame retardants. However, when transferred to glass-fiber reinforced composites, the fire residues diminish significantly. Further studies are required to improve theoretical and experimental estimations of the post-fire mechanics of the composites.
The incorporation of nanoparticles like multilayer graphene (MLG) into elastomeric composites boosts their technical performance, such as their mechanical behavior and electrical conductivity. Common filler types (carbon black (CB) and aluminum trihydroxide (ATH)) generally fulfill single, specific purposes and are often used in high loadings. CB typically reinforces rubber mechanically, while ATH increases flame retardancy. Small amounts of MLG reduce these high filler contents and maintain the multifunctional characteristics of rubber composites. In chlorosulfonated polyethylene (CSM) + ATH, an intrinsically flame-retardant rubber was designed to achieve the highest standards such as maximum average of heat emission (MARHE) <90 kW m−2, 3 phrMLG was substituted for 15 phr CB and/or 3 phr ATH via an industrially applicable processing approach. Replacing either CB or ATH resulted in a property profile that was multifunctionally improved in terms of features such as mechanical performance, reduced sorption, and flame retardance. MLG nanocomposites are reported to show promise as an industrially utilizable route to obtain multifunctional high-performance rubbers.
Whereas the degradation of flame retardant polymers has been discussed since decades, only more recently, the lifetime of the flame retardancy itself becomes an important factor, e.g. for cables used as building products. In this work, several kinds of accelerated artificial ageing tests are performed simulating different environmental exposures and thus highlighting different degradation mechanisms: artificial accelerated weathering, climatic chamber, water immersion, salt spray chamber, and autoclave test. The durability is expected to be different for different flame-retardant materials. Thus, various sets of halogen-free fire-retarded polymers were investigated: ethylene vinyl acetate (EVA) with aluminum hydroxide (ATH), boehmite and synergists, ester-based and ether-based thermoplastic polyurethane (TPU) with melamine cyanurate (MC), aluminum diethylphosphinate (AlPi), and boehmite, and glass fiber reinforced polyamide 66 (PA66) with AlPi-based mixtures.
Intensive degradation of the surface was observed, e.g. yielding discoloration and yellowing, EVA showed cracking when weathered. Changes in chemical structure was investigated by ATR-FTIR. The flammability was investigated with the cone calorimeter, UL-94 classification, and oxygen index (LOI). The flame retardancy of most of the materials studied degraded only slightly for the investigated exposure times. EVA/ATH achieved an improved LOI due to flame retardants agglomeration at the surface. Sets of materials, based on EVA and TPU, were also investigated as cable jackets. While flame retarded EVA exhibited no dripping during burning, TPU flame-retarded with MC cables showed pronounced melt-dripping. Cone calorimeter tests were carried out using cable rafts as well as our self-made cable module test, simulating a vertical bundle of cables at the bench scale. The comparison of different fire tests, different exposure conditions, and different materials carved out the specific degradation phenomena with respect to each of these parameters.
Most of this work was supported by the IGF Project (18926 N) of the Fördergemeinschaft für das Süddeutsche Kunststoff-Zentrum e.V., supported by the AiF within the framework of the program “Förderung der Industriellen Gemeinschaftsforschung (IGF)” of the German Federal Ministry for Economic Affairs and Energy based on a decision of the Deutschen Bundestag.
Only the nano-scaled structure of the nanocomposite and the dispersion of nanoparticles within the polymer matrix harbor multifunctional potential including superior fire retardancy. Thus, this chapter focuses on the dispersion of nanoplates, based mainly on studies of layered silicates and graphene/graphene-related nanoplates. The nanostructure and properties of the nanocomposites are dependent mainly on thermodynamic and kinetic factors during preparation. Improving nano-dispersion often directly improves flame retardancy. Therefore, the modification of the nanoplates as well as the preparation of nanocomposites becomes very important to control this dispersion. The dispersion of nanoplates functions as a prerequisite for the formation of an efficient protective layer, changing the melt flow and dripping behavior, or the improvement of the char properties.
After introducing into the activities and competence of BAM in the field of fire science, several aspects of successful and tailored flame retardancy of polyolefins are discussed. The talk gives an overview of the works relevant for developing flame retardant polyolefins performed in the working group flame retardancy of polymers. The hypothesis of conservation of effective heat of combustion is proposed. The role of charring, inert fillers, protection layer, and intumescence is assessed for flame retarded polyolefins. Distinct routes of optimization sketched. Examples of controlling the dripping and melt flow to obtain the desired fire behaviour are discussed. Finally the cable modul for the cone calorimeter is presented.
The main flame retardant modes of action are known, nevertheless in practise the detailed scientific understanding usually falls short, when it comes to modern multicomponent systems, the important tiny optimizations, or quantifying in terms of specific fire properties. The description of the flame retardant modes of action remains usually vague and fragmentary. This talk tries to deliver thought-provoking impulses how the understanding of the fire behaviour and flame retardancy can be utilized to direct the development of future flame retardant polymer products. Some overseen details are picked up as well as rethinking of concepts memorised long ago is encouraged to discover something new. Furthermore, the talk tries to fill the gap between flame retardant modes of action and fire performance constituting a product. This talk promotes the evidence-based development of flame retardant polymers.
Combining buffing leather fibers from industrial waste streams with ammonium polyphosphate and bentonite clay is proposed as a flame-retardant additive for polypropylene. The paper addresses how they can be processed into attractive composites with the desired mechanical properties. Buffing leather fibers function as a multifunctional bio-filler and as a synergist for the flame retardant, resulting in fire retardancy successful enough to increase the oxygen index (LOI) by up to 7 vol.-% and to achieve a V0 UL 94 classification. Impressively reduced heat release rates are obtained in the cone calorimeter at 50 kW/m2 irradiation; for instance, the maximum average rate heat evolved (MARHE) drops from 765 to below 200 kW m 2. The synergistic effects are quantified and shown to be very strong for LOI and MARHE. This work opens the door to use waste buffing leather fibers as a promising multifunctional and synergistic bio-filler.
Leather is a widely used material for thousands of years and in modern days it is produced on industrial scale. This production produces high amounts of organic waste during the tannery process. These fibers can become a resource and act as a multi-functional bio-filler in flame retardant composites.
This project investigates two leather fibers towards their ability to enhance the flame-retardancy in different composites. These composites use ammonium polyphosphate (APP) or aluminum trihydroxide (ATH) as flame retardants. Different silicon based synergists support polymers with ATH to reduce the load of flame retardant. The different modes of action (charring, gas phase activity, barrier effect) can be quantified of each composite.
The new composites form a stable char layer resulting in an increase in residue, lower peak heat release rates (pHRR) and higher limiting oxygen index (LOI). In addition, the ratings in the UL94-classification increased up to V-0.
Leather is a widely used material for thousands of years and in modern days it is produced on industrial scale. This production produces high amounts of organic waste during the tannery process. These fibers can become a resource and act as a multi-functional bio-filler in flame retardant composites.
This project investigates two leather fibers towards their ability to enhance the flame-retardancy in different composites. These composites use ammonium polyphosphate (APP) or aluminum trihydroxide (ATH) as flame retardants. Different synergists support polymers with ATH.
The new composites form a stable char layer resulting in an increase in residue, lower peak heat release rates (pHRR) and higher limiting oxygen index (LOI). In addition, the ratings in the UL94-classification increased up to V-0.
In this work, a series of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) derivative salts containing phosphorus and nitrogen were synthesized, and their effects on mechanical properties, thermal stability and flame retardancy of flexible polyurethane foam (FPUF) were investigated. Studies have shown that the addition of DOPO derivatives will increase the tensile strength, compression set, and compression hardness of FPUF, but it will lead to a decrease in elongation at break. Thermogravimetric analysis showed that the initial decomposition temperature of FPUF containing DOPO derivatives was reduecd, but the char reside was significantly improved. A series of combustion tests indicated that the addition of DOPO derivative salts can improve the flame retardancy of FPUF, of which 10-hydroxy-9,10-dihydro-9-oxa-10 phosphaphenanthrene-10-oxide dicyandiamide salt (D-DICY) exhibited the best flame retardancy. When the load of D-DICY was 20 phr, the limiting oxygen index (LOI) of foam reached 24.5%, and the peak heat release rate and total heat release were decreased by 55.7% and 52.9%, respectively. Furthermore, based on the analysis of the gas phase combustion products and the char residue of the condensed phase, the possible flame retardant mechanism was proposed.
Pressure-sensitive adhesive tapes are used in several industrial applications such as con-struction, railway vehicles and the automotive sector,where the burning behavior is ofcrucial importance. Flame retarded adhesivetapes are developed and provided, however,often without considering the interaction of adhesive tapes and the bonded materialsduring burning nor the contribution of the tapes to fire protection goal of the bondedcomponents in distinct fire tests. This publication delivers an empirical comprehensiveknowledge how adhesive tapes and their flame retardancy effect the burning behaviorof bonded materials. With a special focus on the interaction between the single compo-nents, one flame retarded tape and one tapewithout flame retardant are examined inscenarios of emerging and developing fires, along with their bonds with the commonmaterials wood, zinc-plated steel, mineral wool, polycarbonate, and polymethylmethacry-late. The flame retardant significantly improved the flame retardancy of the tape as afree-standing object and yielded a V-2 rating in UL 94 vertical test and raised the OxygenIndex by 5 vol.%. In bonds, or rather laminates, the investigations prove that the choiceof carrier and substrates are the factors with the greatest impact on the fire propertiesand can change the peak of heat release rate and the maximum average rate of heatemission up to 25%. This research yielded a good empirical overall understanding of thefire behavior of adhesive tapes and bonded materials. Thus, it serves as a guide for tapemanufacturers and applicants to develop tapes and bonds more substrate specific.
To ensure fire safety, polymers are filled with flame retardants and smoke suppressants. To meet the highest requirements, it is essential to understand the decomposition of those polymeric materials. This study reveals interactions between polymer, smoke suppressants, and flame retardants, and discusses their impact on the materials’ flame retardancy, smoke emission, smoke toxicity, and particle emission in conventional loadings to provide deeper general understanding. Low melting oxide glass, melem, spherical silica, sepiolite, melamine polyphosphate, and boehmite in an aluminum diethylphosphinate flame-retarded polyamide 6.6 were investigated. All smoke suppressants improve the protective layer and act as an adjuvant. Silica and melem performed best under forced flaming conditions. Spherical silica reduces the peak of heat release rate by 39% and the total heat evolved by 14%, whereas 10 wt% melem lowers the total smoke production by 41%. Melem alters the mode of action of aluminum diethylphosphinate from gas to more condensed phase activity. This change reduces flame inhibition and hence smoke toxicity, but further improves the protective layer due to charring reactions in the decomposition mechanism. In addition, the sizes of the smoke particles decrease because of the prolonged time in the pyrolytic zone. This study highlights that interactions between polymer, flame retardants, and smoke suppressants can significantly determine the smoking and burning behavior.
Replacing antimony trioxide (ATO) in flame retardant formulations is an urgent task due to its toxicity. There are indications that calcium hypophosphite (CaP) may be a promising replacement. This study investigates the decomposition, fire behavior, and smoke release of brominated flame-retarded acrylonitrile butadiene styrene (ABS) under various fire scenarios like ignition, developing fire and smoldering, while replacing ATO with CaP and CaP/talc. Adding 4 wt.-% of talc to CaP formulations showed beneficial effects on flammability due to changes in the viscosity and barrier properties. Synergism between 8 wt.-% talc and CaP improved the protective layer in the developing fire scenario, resulting in a ∼60 % decrease in the peak of heat release rate and reduction of ∼21 % in total smoke production (ref. ABS+Br+ATO). With a conventional index of toxicity (CIT) of below 0.75, ABS+Br+CaP passes the highest requirements according to EN 45545-2. Overall, the CaP/talc materials improve flame retardancy, show less smoke emission under forced flaming conditions, and prevent chronic intoxication and environmental pollution through smoke particles contaminated with antimony.
As most of polymeric materials are inherently flammable, flame retardants (FR) are commonly used to reduce their fire risks. Nevertheless, these flame retardant materials are often detrimental to smoke parameters like specific optical density or smoke toxicity. The influence of several smoke suppressants (SP)-zinc stannate, zinc phosphate, titanium oxide and hydrotalcite-were investigated with respect to flame retardancy, smoke emission, particle emission and smoke toxicity in a diethyl aluminum phosphinate (AlPi) flame retardant polyamide 6.6 (PA6.6). It was shown that the interaction between SP, FR and polymer is crucial for smoke and fire properties and can change the mode of action of the FR as well the decomposition mechanism of the polymer. Small amounts of SP show less effect on forced flaming behavior and the optical density, but they can influence flammability and the particle size distribution of the soot particles. The flame retardancy was significantly enhanced by 5 wt.-% zinc stannate in PA6.6 under forced flaming conditions. The charring mechanism was improved, and the mode of action of AlPi switched from the gas to the condensed phase. This resulted of in a reduced PHRR and TSP and an increase in residue yield. The smoke toxicity and optical density were reduced in the smoke density chamber as well. The smoke particles shifted to smaller sizes as the time in the pyrolytic zone increased. The formation of a dense char is assumed to be the key factor to enhance smoke suppression and flame retardancy properties.
Material solutions that meet both circular bioeconomy policies and high technical requirements have become a matter of particular interest. In this work, a prospectively abundant proteinrich waste resource for the manufacturing of flame-retardant epoxy biocomposites, as well as for the synthesis of biobased flame retardants or adjuvants, is introduced. Different biomass fillers sourced from the cultivation of the mealworm beetle Tenebrio molitor are embedded in a bioepoxy resin cured with tannic acid and investigated regarding the fire performance of the thermosets. By means of spectroscopic and thermal analysis (attenuated total reflectance FTIR spectroscopy, thermogravimetric analysis-coupled FTIR spectroscopy, and differential scanning calorimetry), the influence of the biomass microparticles on the curing and thermal degradation behavior is evaluated. The final performance of the biocomposites is assessed based on fire testing methodology (limited oxygen index, UL-94, and cone calorimetry). Providing a high charring efficiency in the specific tannic acid-based epoxy matrix, the protein-rich adult beetle is further investigated in combination with commercial environmentally benign flame retardants in view of its potential as an adjuvant. The results highlight a char forming effect of nonvegan fillers in the presence of tannic acid, particularly during thermal decomposition, and point toward the potential of protein-based flame retardants from industrial insect rearing for future formulations.
Products and by-products of the invertebrate and vertebrate farming, respectively, are shown to be promising bio-based flame retardant adjuvants in epoxy thermosets. While the addition of bone meal results in the formation of an inorganic shield, protein-based powders from insects provide an intumescent behavior under forced flaming conditions. Combining the latter with a common flame retardant such as ethylene diamine phosphate, the charring efficiency and self-extinguishing properties can be further enhanced.
Revolutionizing our polymer industry for adaption to a sustainable carbon circular economy has become one of today’s most demanding challenges. Exploiting renewable resources to replace fossil-fuel—based plastics with biopolymers such as poly(lactic acid) (PLA) is inevitable while using waste streams as a raw material resource at least is promising. When it comes to using PLA as technical polymer, its high flammability must be addressed by flame retardants compatible with the thermoplastic processing of PLA and its compostability. This study proposes microalgae enriched with phosphorus from wastewater (P-Algae) as an elegant way towards a kind of sustainable organophosphorus flame retardant. The concept is demonstrated by investigating the processing, pyrolysis, flammability, and fire behavior of PLA/P-Algae, while varying the P-Algae content and comparing P-Algae with four alternative bio-fillers (phosphorylated lignin, biochar, thermally treated sewage sludge, and metal phytate) with different P-contents as meaningful benchmarks.
A phosphorous soybean-oil–based polyol was derived via epoxidation and ring opening reaction as an alternative to petrochemical-based polyol for the synthesis of flexible polyurethane foams (FPUFs). 5-wt.% and 10-wt.% of expandable graphite (EG) were added to further improve flame retardancy. The mechanical properties (tensile strength and compression stress) of the foams were investigated. Thermogravimetric analysis (TGA) coupled with Fourier-transform infrared (FTIR) were conducted to evaluate the pyrolysis; limiting oxygen index (LOI), UL 94 and cone calorimeter were performed to analyze the fire performance of the foams; smoke density chamber was used to investigate the smoke released during burning. When 10-wt.% of EG was used, the flame retardancy of the foams was much enhanced due to the synergistic effect between phosphorus and EG. The char yield was three times higher (54wt.%). The fire load MARHE approached 100 kWm−2, half of the value expected for a superposition. The combination of phosphorous polyols and EG is proposed as strategy for future flame retarded FPUFs.
A series of flexible polyurethane foams (FPUFs) were prepared with single and different combinations of flame retardants and additives. Expandable graphite (EG), phosphorous polyol (OP), copper (II) oxide (CuO), and/or castor oil (CAS) were added to FPUF during the foam preparation in a one-step process. The purpose of the study is to evaluate the synergistic effects of the flame retardants, additives, and the presence of bio-based content on the mechanical properties, flame retardancy, and smoke behavior of FPUFs. The combination of 10 wt % EG and 5 wt % OP in FPUF significantly improves the char yield. In the cone calorimeter experiment, the char yield is nearly three times higher than that with 10 wt % EG alone. The smoke behavior is additionally evaluated in a smoke density chamber (SDC). Comparing the samples with a single flame retardant, 10 wt % EG in FPUF considerably reduces the amount of smoke released and the emission of toxic gases. Replacing the amount of 10 wt % polyether polyol in FPUF with CAS maintains the physical and mechanical properties and fire behavior and enhances the bio-based content. The presence of 0.1 wt % CuO in FPUF effectively reduces the emission of hydrogen cyanide. As a result, this study proposes a multicomponent flame retardant strategy for FPUF to enhance the biomass content and address the weaknesses in flame retardancy, smoke, and toxic gas emissions. A starting point is disclosed for future product development.
Leather is among the most ancient, widely used materials worldwide. Industrial-scale leather production produces large quantities of organic waste attained during shaving and buffing steps during processing. In this study, leather wastes (LW) are used as fillers in flame retarded polymer composites. LW is investigated as a multifunctional bio-filler that enhances the fire performance of flame retarded poly(ethylene–vinyl acetate) (EVA) containing phosphorus flame retardants (P-FRs) ammonium polyphosphate (APP) or a melamine-encapsulated APP (eAPP). Using LW from tanneries as adjuvants to enhance P-FRs in EVA reduces industrial wastes that otherwise require costly waste management solutions. Materials are characterized multi-methodically via mechanical tests, electron microscopy, rheology, thermogravimetric analysis, evolved gas analysis, and condensed phase FTIR, also reaction-to-small-flames and cone calorimeter tests. EVA containing 10 wt-% LW and 20 wt-% P-FRs achieve 20% reductions in fire loads versus EVA, and up to 10% reduction in effective heats of combustion versus EVA with equal (30 wt-%) P-FR loadings. Enhanced char stabilization of EVA composites with LW and P-FRs lowered peaks of heat release rates up to 53% compared to EVA, and up to 40% compared to equal P-FRs loadings. Synergisms between LW and P-FRs in EVA are quantified. A chemical decomposition mechanism is proposed.
Valorizing “non-vegan” bio-fillers: Synergists for phosphorus flame retardants in epoxy resins
(2022)
Sustainable, biogenic flame retardant adjuvants for epoxy resins are receiving increased focus. Zoological products like insects, bone meal, and eggshells are available in large quantities, but remain uninvestigated as functional fillers to epoxy resins, although they are potential synergists to flame retardants. The efficacy and flame retardancy of “non-vegan” additives in combination with flame retardants is investigated and the fire behavior and thermal decomposition of bio-sourced epoxy resin composites is characterized. By comparing the fire performance of composites containing flame retardants or fillers at varying loadings (5, 10, and 20%), their role as synergists that enhance the function of organophosphorus flame retardants in bio-epoxy composites is identified and quantified. Peak heat release rates were 44% lower in composites containing both filler and flame retardant versus those containing only flame retardants, and fire loads were reduced by 44% versus the pure resin, highlighting the ability of “non-vegan” fillers to function as synergists.
The demands for modern flame retardants are higher than ever: a flame retardant must function effectively in a certain polymer matrix and avoid critical alterations to the material’s properties. Ideally, a flame retardant additive should be easily miscible and show no sign of leaching or blooming from the matrix. Additionally, the flame retardant should be non-toxic, non-accumulating and biocompatible. Hyperbranched polymers are a promising group of multifunctional flame retardants which fulfill these demands: their complex shape enables high miscibility and avoids leaching or blooming, while their high molecular weight potentially increases biocompatibility and lowers accumulation and toxicity. Moreover, they exhibit a low impact on polymer properties and a good flame retardant performance.
This work examines the efficacy and mode of action of phosphorus-based hyperbranched polymeric flame retardants in bisphenol A-based epoxy matrices. To investigate the effect of the complex shape, the hyperbranched polymers are compared to their corresponding monomeric variants. Furthermore, the materials are synthesized to contain systematically varying oxygen-to-nitrogen ratios, allowing for new insight into what role the chemical surrounding of phosphorous plays in flame retardant efficacy.
Using a multi-methodical approach, including thermogravimetric analysis coupled with Fourier transform infrared spectroscopy (FTIR), hot stage FTIR, micro combustion calorimetry, differential scanning calorimetry, oxygen index (LOI), UL-94 tests and cone calorimetry experiments, the decomposition mechanisms and the flame retardant modes of action of these flame retardants in epoxy resins are investigated, shedding new light on the chemistry of flame retardancy.