7.2 Ingenieurbau
Filtern
Erscheinungsjahr
- 2018 (4) (entfernen)
Dokumenttyp
Schlagworte
- Offshore (2)
- Acoustic emission testing (1)
- Compressive cyclic loading (1)
- Crack (1)
- Cracks (1)
- Detection (1)
- Energy (1)
- Ermüdung (1)
- Fatigue (1)
- Fatigue damage (1)
- Grouted Connection (1)
- High-strength concrete (1)
- Imperfektion (1)
- Luminescence (1)
- Non-destructive testing (1)
- Rehabilitation (1)
- Repair (1)
- Schrauben (1)
- Size effect (1)
- Slenderness effect (1)
- Ultrasonic testing (1)
- Vorspannung (1)
- Windenergieanlage (1)
Organisationseinheit der BAM
- 7.2 Ingenieurbau (4) (entfernen)
The worldwide spread of windfarms brings new challenges, especially for concrete structures as a part of towers, connecting joints and foundations of wind turbines. High-cyclic loadings in such structures lead to a high relevance of the subject of fatigue. A proper assessment of the fatigue strength of concrete demands therefore a basis of reliable experimental data and the development of standardized testing methods. This article presents first results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung) which is a part of a joint project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject investigates the effects of size and slenderness of the specimens on the fatigue behaviour of high strength concrete at different stress levels. Not only the fatigue strength, but also the fatigue process itself is monitored by means of several measurement methods. Strain measurements are used to calculate the load dependent elastic modulus in the fatigue hysteresis as indicators for fatigue development. Furthermore, the application of non-destructive methods like acoustic emission analysis and ultrasonic measurement in laboratory tests gives a deeper insight into damage processes under cyclic loading. The results shall be used to improve design rules for concrete members under fatigue load and to develop or improve non-destructive techniques for in-service structural health monitoring.
Remediation of Cracks Formed in Grouted Connections of Offshore Energy Structures under Static Loads
(2018)
The future energy demand necessitates the exploration of all potential energy sources both onshore and offshore. Global trend has shifted towards offshore energy, which can be obtained from either carbon intensive or renewable options, hence requiring structures such as rigs, platforms, and monopiles. Most of these structures adopt easily installable construction techniques, where lower foundation need to be connected with the super structure by mean of grouted composite joints. Generally, these composite connections have exterior sleeve, interior pile and infill grout. Being located in remote offshore conditions, connections can experience considerable adverse loading during their lifetimes. Degradations were reported inside similar connections, which were installed in last three decades. Besides, grouting in the offshore sites may often be proven difficult, which eventually leads to reduced capacity of connections in the long run. Thus, repair and rehabilitation of such connections should be planned ahead to minimize operational delays and costs in the future. This study aims at characterizing the nature of crack generation in grouted connections and thereby identifying the potential of repair using suitable repair material. Scaled grouted joints were manufactured using a novel mold, and connections were loaded under static load to visualize the main failure pattern. The failure mechanism and loading capacity are found compatible to previous results from earlier literature. Grouted connection was then repaired using cementitious injectable grout. The effectiveness of the repair system is also discussed.
In structural parts under vibrational loading fatigue cracks can initiate and grow, which can lead to structural failure. Conventional non-destructive testing methods for crack detection provide just a snapshot of fatigue crack evolution, whereas crack luminescence coating realizes clear visibility of the entire crack formation. Fatigue causing cyclic tensile tests and examinations on special test bodies allowing control of the crack opening width demonstrate a high sensitivity of the coating.
Bei Monopfahlgründungen von Offshore-Windenergieanlagen wird die Verbindung zwischen Monopfahl und Übergangsstück als geschraubter Ringflansch ausgeführt. Die zunehmende Leistungsfähigkeit der Windenergieanlagen führt zu immer größeren Schnittgrößen in diesem Anschluss. In der Folge erhöhen sich nicht nur die Querschnittsabmessungen, sondern es kommen auch zunehmend größere Schrauben zum Einsatz. Da die einschlägigen Regelwerke zur Bemessung dieser Verbindungen nicht für Schrauben der Größen M64 oder M72 konzipiert wurden, stellt sich die Frage der Übertragbarkeit auf solche Anwendungsfälle.
Im Rahmen des Aufsatzes werden Einflüsse diskutiert, die eine Herabsetzung der Schraubentragfähigkeit verursachen könnten. Diese Einflüsse, vornehmlich geometrische Imperfektionen, werden systematisch untersucht und ergänzend in praxisrelevanten Beispielen bewertet. Die somit gewonnenen Erkenntnisse werden für die abschließende Beurteilung der großen Schrauben in Ringflanschverbindungen herangezogen.