5 Werkstofftechnik
Filtern
Erscheinungsjahr
- 2020 (50) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (50) (entfernen)
Sprache
- Englisch (49)
- Mehrsprachig (1)
Schlagworte
- EBSD (5)
- Additive manufacturing (4)
- Additive Manufacturing (3)
- Electron backscatter diffraction (2)
- Grain boundary (2)
- High entropy alloys (2)
- LPBF (2)
- LTCC (2)
- Orientation precision (2)
- Quasicrystal (2)
- Texture (2)
- Thermodynamics (2)
- X-ray diffraction (2)
- 2PP (1)
- 3D printing (1)
- 3D-printing (1)
- AISI 304L (1)
- AISI 316L (1)
- ATZ (1)
- Aggressive environments (1)
- Alkali aluminosilicate glasses (1)
- Alpha-tricalcium phosphate (1)
- Alumina (1)
- Alumina toughened zirconia (1)
- Angle measurement (1)
- Approximant (1)
- Atom probe tomography (1)
- Automated analysis (1)
- Bacterial attachment (1)
- Binder Jetting (1)
- Bio Ceramics (1)
- Bioactive glass scaffold (1)
- Bone marrow-derived mesenchymal stem cell (1)
- CCUS (1)
- CO2 pipeline transport (1)
- Carbon Fiber Reinforced Plastics (1)
- Carbon Fibre (1)
- Carbon steel (1)
- Cement-based materials (1)
- Ceramic nano particles (1)
- Ceramics (1)
- Chrystal orientation (1)
- Clay ISRU (1)
- Compositionally complex alloys (1)
- Computed Tomography (1)
- Confined catalyst (1)
- Cooling rate (1)
- Corrosion (1)
- Corrosion resistance (1)
- CrCoNi (1)
- CrMnFeCoNi (1)
- Crack evolution (1)
- Cracks (1)
- Cryogenic (1)
- Cryogenic cycling (1)
- Crystal growth velocity (1)
- Crystal orientation (1)
- DCB geometry (1)
- Data processing (1)
- Defect detection (1)
- Degradation (1)
- Degradation signatures (1)
- Densty-based Thermodynamics (1)
- Deuterium (1)
- Differential scanning calorimetry (1)
- Diffraction Enhanced Imaging (1)
- Diffusivity (1)
- Disorientation (1)
- Double notched creep specimen (1)
- EXAFS (1)
- Endothelial progenitor cell (1)
- Epoxy Resin (1)
- Fatigue (1)
- Fatigue striations (1)
- Fibre reinforced plastic (1)
- Fuel sorption (1)
- Gas flow assisted powder deposition (1)
- Glass (1)
- Glass ceramic (1)
- Glass transition (1)
- Gnomonic projections (1)
- Grain Boundary Segregation (1)
- Grain Boundary Spinodal (1)
- Granules (1)
- High - temperature (1)
- High density polyethylene (1)
- High entropy alloy (1)
- High temperature corrosion (1)
- High temperature oxidation (1)
- High-Entropy Alloys (1)
- Hot pressing (1)
- Hot stage microscopy (1)
- Hybrid Manufacturing (1)
- Hydrogen (1)
- Hydrous glass (1)
- Impurities (1)
- In situ tensile test (1)
- In-situ ED-XRD (1)
- Inconel 686 (1)
- Inconel 718 (1)
- Indentation fracture toughness (1)
- Infrared spectroscopy (1)
- Interfacial strength (1)
- Internal friction (1)
- Ionic porosity (1)
- Iron (1)
- Kernel average misorientation (1)
- Kikuchi diffraction (1)
- Kikuchi patterns (1)
- LIBS (1)
- Laser Powder Bed Fusion (1)
- Laser cladding (1)
- Lattice rotation (1)
- Lattices (1)
- Layered manganese oxide (1)
- Layerwise Slurry Deposition (1)
- Low expansion (1)
- Low-loading (1)
- Lunar regolith (1)
- MGS-1 regolith simulant (1)
- Mars (1)
- Matrix residual stress (1)
- Mechanical properties (1)
- Medium entropy alloys (1)
- Melting (1)
- Metal and alloys (1)
- Metallic glass (1)
- Microstrucrue Design (1)
- Microstructure (1)
- Mixed conductors (1)
- Mn-oxides (1)
- Multilayer ceramic technology (1)
- NMR spectroscopy (1)
- Nano-ceramic-additive-manufacturing photoresin (1)
- NanoCAM (1)
- Nanoparticles (1)
- Nb3Sn (1)
- Neutron Diffraction (1)
- Non-serrated inhomogeneous flow (1)
- Online Process Monitoring (1)
- Oxyfuel (1)
- Oxygen evolution reaction (1)
- Packaging (1)
- Particle size (1)
- Pattern matching (1)
- Permeability (1)
- Permittivity reduction (1)
- Phase Diagram (1)
- Phase transformation (1)
- Phase transformations (1)
- Plasma imaging (1)
- Polyethylene (1)
- Polymer analysis/characterization (1)
- Polyolefins (1)
- Porosification (1)
- Powder diffraction (1)
- Projection center (1)
- Quality assurance (1)
- Reaction Sintering (1)
- Rejuvenation (1)
- Relaxation (1)
- Residual Stress (1)
- Residual stress (1)
- SEM (1)
- Scaffold (1)
- Scanning electron microscopy (1)
- SchwarzP cells (1)
- Schwingstreifen (1)
- Shadowgraphy (1)
- Single crystal Ni-Base superalloys (1)
- Sintering (1)
- Slow crack growth (1)
- Slurry (1)
- Smectite (1)
- Soda-lime silicate glass (1)
- Solubility (1)
- Split-vacancy defect complexes (1)
- Spray drying (1)
- Stable crack growth (1)
- Stress distribution (1)
- Stress intensity factor (1)
- Structural dynamics (1)
- Synchrotron micro-tomography (1)
- TEM (1)
- Thermal cycling (1)
- Thermal desorption mass spectrometry (1)
- Thermoelectric properties (1)
- Thermography (1)
- Thermoplastic prepreg (1)
- Thermoset composition (1)
- Three-dimensional Bone tissue engineering (1)
- ToF-SIMS (1)
- Transformer (1)
- Transmission electron microscopy (1)
- Transmission electron microscopy (TEM) (1)
- Two-photon polymerization (1)
- UV-irradiation (1)
- Ultrasound (1)
- Unidirectional composites (1)
- Vickers indentation (1)
- Volatiles from thermosets (1)
- Volume changes (1)
- Water content (1)
- Water speciation (1)
- Wet chemical etching (1)
- X-ray Diffraction (1)
- X-ray absorption spectroscopy (1)
- X-ray refraction (1)
- Zirconia (1)
- Zirconia-toughened alumina (1)
- hydrogen storage (1)
Organisationseinheit der BAM
- 5 Werkstofftechnik (50)
- 5.1 Mikrostruktur Design und Degradation (18)
- 5.4 Multimateriale Fertigungsprozesse (13)
- 6 Materialchemie (7)
- 5.3 Polymere Verbundwerkstoffe (6)
- 5.6 Glas (6)
- 5.0 Abteilungsleitung und andere (5)
- 7 Bauwerkssicherheit (4)
- 8 Zerstörungsfreie Prüfung (4)
- 5.2 Metallische Hochtemperaturwerkstoffe (3)
Paper des Monats
- ja (1)
On the influence of crystallography on creep of circular notched single crystal superalloy specimens
(2020)
The present work contributes to a better understanding of the effect of stress multiaxiality on the creep behavior of single crystal Ni-base superalloys. For this purpose we studied the creep deformation and rupture behavior of double notched miniature creep tensile specimens loaded in three crystallographic directions [100], [110] and [111] (creep conditions: 950 °C and 400 MPa net section stress). Crystal plasticity finite element method (CPFEM) was used to analyze the creep stress and strain distributions during creep. Double notched specimens have the advantage that when one notch fails, the other is still intact and allows to study a material state which is close to rupture. No notch root cracking was observed, while microstructural damage (pores and micro cracks) were frequently observed in the center of the notch root region. This is in agreement with the FEM results (high axial stress and high hydrostatic stress in the center of the notched specimen). Twinning was observed in the notch regions of [110] and [111] specimens, and <112> {111} twins were detected and analyzed using orientation imaging scanning electron microscopy. The present work shows that high lattice rotations can be detected in SXs after creep fracture, but they are associated with the high strains accumulated in the final rupture event.
Hydrocarbons fuel our economy. Furthermore, intermediate goods and consumer products are often hydrocarbon-based. Beside all the progress they made possible, hydrogen-containing substances can have severe detrimental effects on materials exposed to them. Hydrogen-assisted failure of iron alloys has been recognised more than a century ago. The present study aims to providing further insight into the degradation of the austenitic stainless steel AISI 304L (EN 1.4307) exposed to hydrogen. To this end, samples were electrochemically charged with the hydrogen isotope deuterium (2H, D) and analysed by scanning electron microscopy (SEM), electron back-scatter diffraction (EBSD) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). It was found that deuterium caused a phase transformation from the original γ austenite into ε- and α’-martensite. Despite their low solubility for hydrogen, viz. deuterium, the newly formed phases showed high deuterium concentration which was attributed to the increased density of traps. Information about the behaviour of deuterium in the material subjected to external mechanical load was gathered. A four-point-bending device was developed for this purpose. This allowed to analyse in-situ pre-charged samples in the ToF-SIMS during the application of external mechanical load. The results indicate a movement of deuterium towards the regions of highest stress.
Accelerator magnets that can reach magnetic fields well beyond the Nb-Ti performance limits are presently being built and developed, using Nb3Sn superconductors. This technology requires reaction heat treatment (RHT) of the magnet coils, during which Nb3Sn is formed from its ductile precursor materials (a “wind and react” approach). The Nb3Sn microstructure and microchemistry are strongly influenced by the conductor fabrication route, and by the Phase changes during RHT. By combining in situ differential scanning calorimetry, high Energy synchrotron x-ray diffraction, and micro-tomography experiments, we have acquired a unique data set that describes in great detail the phase and microstructure changes that take place during the processing of restacked rod process (RRP), powder-in-tube (PIT), and internal tin (IT) Nb3Sn wires. At temperatures below 450 ° the phase evolutions in the three wire types are similar, with respectively solid state interdiffusion of Cu and Sn, Cu6Sn5 formation, and Cu6Sn5 peritectic transformation. Distinct differences in phase evolutions in the wires are found when temperatures exceed 450 °C. The volume changes of the conductor during RHT are a difficulty in the production of Nb3Sn accelerator magnets. We compare the wire diameter changes measured in situ by dilatometry with the phase and void volume evolution of the three types of Nb3Sn wire. Unlike the Nb3Sn wire length changes, the wire diameter evolution is characteristic for each Nb3Sn wire type. The strongest volume increase, of about 5%, is observed in the RRP wire, where the main diameter increase occurs above 600 °C upon Nb3Sn formation.
The impact fracture behavior of two common high-density polyethylene grades for container applications were intensively studied by the instrumented Charpy impact test after well-defined exposure to UV-irradiation. Individual stages of the impact event, such as crack initiation and crack propagation energy as well as maximum impact load, were investigated from the recorded load–deflection curves. UV-induced material property changes were further investigated by infrared spectroscopy, differential scanning calorimetry, and dynamic-mechanical analysis as well as density measurements. Based on the results of the Charpy impact test, three indicators were identified to describe the extend of photooxidation on high-density polyethylene: (a) a reduced Charpy impact strength—at least to half of its initial value for a distinctly brittle impact fracture, (b) a marked decrease in the crack propagation contribution to the impact strength, and (c) an increase of the brittle features of the fracture surface.
Calcium cobaltite Ca3Co4O9, abbreviated Co349, is a promising thermoelectric material for high‐temperature applications in air. Its anisotropic properties can be assigned to polycrystalline parts by texturing. Tape casting and pressure‐assisted sintering (PAS) are a possible future way for a cost‐effective mass‐production of thermoelectric generators. This study examines the influence of pressure and dwell time during PAS at 900°C of tape‐cast Co349 on texture and thermoelectric properties. Tape casting aligns lentoid Co349. PAS results in a textured Co349 microstructure with the thermoelectrically favorable ab‐direction perpendicular to the pressing direction. By pressure variation during sintering, the microstructure of Co349 can be tailored either toward a maximum figure of merit as required for energy harvesting or toward a maximum power factor as required for energy harvesting. Moderate pressure of 2.5 MPa results in 25% porosity and a textured microstructure with a figure of merit of 0.13 at 700°C, two times higher than the dry‐pressed, pressureless‐sintered reference. A pressure of 7.5 MPa leads to 94% density and a high power factor of 326 µW/mK2 at 800°C, which is 11 times higher than the dry‐pressed reference (30 MPa) from the same powder.
One of the most ubiquitous and important defects in solids is oxygen. Knowledge about the solubility and diffusivity of oxygen in materials is crucial to understand a number of important technological processes, such as oxidation, corrosion, and heterogeneous catalysis. Density-functional theory calculations of the thermodynamics and kinetics of oxygen in cobalt show that oxygen diffusing into the two close-packed phases, namely α (hcp) and β (fcc), strongly interacts with vacancies.We observe the formation of oxygen split-vacancy centers (V-Oi-V) in both phases, and we show that this defect complex exhibits a similar migration energy barrier to the vacancy and oxygen interstitials. In contrast to the vacancy and oxygen interstitials, the oxygen split-vacancy centers exhibit an anisotropic strain field that couples to applied stress, making it possible to observe them through an internal friction experiment on quenched cobalt.
An extensive set of information about the diffracting volume is carried by EBSD patterns: the crystal lattice, the reciprocal lattice, the crystal structure, the crystal symmetry, the mean periodic number of the diffracting phase, the source point from where it has been projected (projection centre), the crystal orientation, the sample topography (local tilt), the (preparation) quality of defect density of the crystal, and possible pattern overlaps. Some of this information is used regularly in conventional EBSD analyses software while others are still waiting for a more widespread application. Despite the wealth of information available, the accuracy and precision of the data that are presently extracted from conventional EBSD patterns are often well below the actual physical limits. Using a selection of example applications, we will demonstrate the gain in angular resolution possible using relatively low-resolution patterns of approximately 20k pixels in combination with pattern matching (PM) approaches. In this way, fine details in a microstructure can be revealed which would otherwise be hidden in the orientation noise.
Fatigue failure of a component can occur at service loads considerably lower than the yield strength of the material. Under fatigue loading condition, the material in the vicinity of the tip of a propagating crack repeatedly deforms plastically, leaving microscopic marks on the crack surface, commonly known as fatigue striations. Counting and measuring fatigue striations is a method in estimating the number of loading cycles a component went through until fracture. Some studies suggest a one-to-one relation between the number of fatigue striations and the number of load cycles, but this relation is still debatable, given that there are many factors influencing the formation of those striations. The main purpose of this work is to analyze the influence of microstructure and mechanical strength on the formation of fatigue striations in structural steels, in order to understand how these material properties are related to the fatigue crack behavior. For such, standard Charpy-V samples were subjected to hardness, fatigue and impact testing. Metallography was performed to characterize the microstructure, and a fractographic analysis by using optical and scanning electron microscopy was carried out to investigate the fracture surface. This study shows that steels with higher ductility have a closer one-to-one relation than those with a higher tensile strength. Above a certain level of tensile strength, fatigue striations do form rarely or completely disappear.
Calcium alkali metal (potassium and sodium) double and triple phosphates have been synthesized in different ways. Was for the first time used reaction sintering to produce ceramics based on calcium alkali metal mixed phosphates and investigated the densification behavior of mixed phosphate-based multiphase materials during sintering by this method. Was presented the microstructure of polished surfaces of sintered samples differing in phase composition and determined the density of ceramics prepared using reaction mixtures differing in composition. The effect of reaction sintering on the porosity of the ceramics has been assessed. Using stereolithographic printing and reaction sintering, was produced macroporous mixed Calcium phosphate-based ceramic implants. Their compressive strength has been determined to be 0.78 ± 0.21 MPa for two-phase samples and 1.02 ± 0.13 MPa for three-phase samples.
Segregation to grain boundaries affects their cohesion, corrosion, and embrittlement and plays a critical role in heterogeneous nucleation. In order to quantitatively study segregation and low-dimensional phase separation at grain boundaries, here, we apply a density-based phase-field model. The current model describes the grain-boundary thermodynamic properties based on available bulk thermodynamic data, while the grain-boundary-density profile is obtained using atomistic simulations. To benchmark the performance of the model, Mn grain-boundary segregation in the Fe–Mn system is studied. 3D simulation results are compared against atom probe tomography measurements conducted for three alloy compositions. We show that a continuous increase in the alloy composition results in a discontinuous jump in the segregation isotherm. The jump corresponds to a spinodal Phase separation at grain boundary. For alloy compositions above the jump, we reveal an interfacial transient spinodal phase separation.
The transient spinodal phenomenon opens opportunities for knowledge-based microstructure design through the chemical manipulation of grain boundaries. The proposed density-based model provides a powerful tool to study thermodynamics and kinetics of segregation and phase changes at grain boundaries.