5 Werkstofftechnik
Filtern
Dokumenttyp
- Zeitschriftenartikel (1)
- Vortrag (1)
Sprache
- Englisch (2)
Schlagworte
- Bacterial attachment (1)
- Contamination (1)
- Fuel sorption (1)
- Gas storage (1)
- High density polyethylene (1)
- Hydrogen (1)
- Microbiologically influenced corrosion (1)
- UV-irradiation (1)
Organisationseinheit der BAM
- 4 Material und Umwelt (2)
- 4.1 Biologische Materialschädigung und Referenzorganismen (2)
- 5 Werkstofftechnik (2)
- 2 Prozess- und Anlagensicherheit (1)
- 2.1 Sicherheit von Energieträgern (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 5.3 Polymere Verbundwerkstoffe (1)
- 6 Materialchemie (1)
- 6.2 Material- und Oberflächentechnologien (1)
- 7 Bauwerkssicherheit (1)
Eingeladener Vortrag
- nein (1)
As more industrial interests focusing on using salt caverns and repurposed gas or petroleum reservoirs for alternative fuel storage, i.e. CO2/H2, the question raises whether microorganisms may impact the infrastructure, gas purity and storage condition over time.
Environments with high salinity (> 1.5 Meq of NaCl) are resided by halophiles (salt-loving microorganisms). To compensate for the intensive osmotic stress, they have resorted to two main adaptation strategies: 1) production of compatible solutes and 2) accumulation of intracellular KCl. Microbial community analysis of several high salinity environments revealed a number of recurring genera, including Halomonas and Halanaerobium. However, the impact of halophiles on the overall integrity and stability of the storage facilities remain largely unknown.
To evaluate the suitability and stability of saline storage facilities, several model halophilic microorganisms, such as members of Halomonas, will be selected as testing subjects. First, the impact of halophiles on the infrastructure will be determined using an integrative approach by combining a number of techniques, including electrochemistry, TOF-SIMS, SEM/FIB/EDS and FIB-TEM. Second, the abilities of halophiles to alter the fuel composition (i.e. increase/decrease the fractions of H2) will be monitored using gas chromatography by growing them under high pressure.
As a result of climate change and the accompanying mandatory shift to renewable energy resources, microorganisms will continue to play an important role in the energy sector, both to their benefit and detriment. Thus, it is important to achieve a certain level of understanding regarding the activities and mechanisms of halophiles prior to large-scaled excursions.
In the present study, a simple approach was used to investigate the effect of UV-exposure on two high density Polyethylene materials (PE-HD), commonly used for storage tanks, on fuel sorption behavior and colonization by microorganisms. The aim was to investigate whether the sorption behavior of the fuels (diesel/biodiesel) and the colonization by microorganisms, frequently occurring in the fuel, is affected and may lead to undesirable or safety-relevant material changes. We showed that the UV-irradiation leads to significant changes of the sorption behavior due to chemi-crystallization and crosslinking. The fuel Sorption is affected by the UV-induced formation of polar carbonyl and hydroxyl groups predominantly occurring at the surface. With respect to microbial colonization behavior for Bacillus subtilis and Pseudomonas aeruginosa, isolated from a contaminated diesel sample, differences of the initial adhesion could be shown depending on the initial type of polyethylene as well as on the degree of UV-induced degradation.