4.2 Material-Mikrobiom Wechselwirkungen
Filtern
Dokumenttyp
- Posterpräsentation (24) (entfernen)
Referierte Publikation
- nein (24)
Schlagworte
- Nano (4)
- OECD (3)
- Analytical method (2)
- Capsules (2)
- Cascade impactor (2)
- Chamber test (2)
- EN 16516 (2)
- ESEM (2)
- ISO 16000-6 (2)
- Material emissions (2)
Organisationseinheit der BAM
- 4 Material und Umwelt (24)
- 4.2 Material-Mikrobiom Wechselwirkungen (24)
- 1 Analytische Chemie; Referenzmaterialien (4)
- 4.5 Kunst- und Kulturgutanalyse (3)
- 5 Werkstofftechnik (3)
- 1.9 Chemische und optische Sensorik (2)
- 5.4 Multimateriale Fertigungsprozesse (2)
- 6 Materialchemie (2)
- 6.3 Strukturanalytik (2)
- 8 Zerstörungsfreie Prüfung (2)
In addition to previously reported results on the simulated aging of polystyrene samples (PS) containing 1 wt. % hexabromocyclododecane (HBCD), we present the first results of our investigations of polypropylene (PP)-samples containing 0.1 wt. % BDE-209. All studied polymer samples were exposed to a defined weathering schedule in a climate chamber in accordance to regulation EN ISO 4892-3:2006.For the determination of BDE-209 in the collected rain water samples derived from the used climate chamber, the samples were prepared in accordance with a validated protocol. Before the analyses, each sample was spiked with 2 µL of isotopically labeled BDE-209 (13C10-BDE-209) to serve as internal standard (ISTD) in the performed stable isotope dilution analysis. Subsequently the samples were extracted with isooctane, the obtained aliquots of the extracts were concentrated to 200 µL and 2 µL of the resulting solution were injected to the GC/MS for quantification.
Additionally, the total bromine contents are monitored for the aged and untreated samples using laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS) as well as X-ray fluorescence analysis (XRF) as non-destructive and rapid method. Furthermore, results from surface analysis using environmental scanning electron microscopy (ESEM) for morphological characterization of the aged and untreated samples were presented and discussed. In general, the resulting data from the accelerated aging will be compared to those from the natural weathering experiments (“atmospheric exposure”, in soil).
The atmospheric exposure was performed by placing the samples on a weathering rack, which is aligned in SW direction (in a 45° angle to the horizon). The weathering data were regularly recorded by Deutscher Wetterdienst at this site. The surfaces of the test specimens (aged and stored references) were analyzed by ESEM as well as by LA-ICP-MS and by XRF. The surface of PS and PP specimens aged outdoors present the aging under real conditions and allow the comparison to the accelerated aged specimens by means of the weathering chamber. This way, we explore the efficiency of the accelerated aging procedure, which provides the advantage of well-defined and reproducible conditions compared to natural weathering, as a tool for testing different plastic materials.
Additionally “in soil” experiments were conducted in-door in a well characterized testing soil. The soil (boulder-clay, sand with 12 % loam, particle size in total 0.2-4 mm) is filled in a free-draining concrete basin inside of an air-conditioned room. In this manner, TOC, water capacity and humidity are recorded parameters. To assure a washing out process from the samples by the raining water, the target water content is calculated to 8%. The actual humidity is measured by a tensiometer, assuring the duration of the raining period. The water content is additionally monitored by weight of the basin, capturing water from raining periods. The correct humidity is a fundamental parameter for biological activity. Samples of PS resp. PP were of dimension 10x1cm and 5 specimens were placed up to the half in the soil per basin. Microbial activity of the soil, monitored by the reference polyurethane, sets HBCD resp. BDE-209 of the samples free and will be leached from the samples by raining water. Thereafter these will be captured by passive samplers placed in a distinct distance to the samples in the soil. The “in soil” experiments are complementary to the weathering experiments due to the biological activity in the soil. These experiments simulate the fate of the brominated flame retardants in the biosphere.
This poster summarizes the points that need to be addressed towards the standardization of an efficient procedure for the analysis of VVOC emissions: Standard mixture generation and investigations on mutual reactivity, selection of an appropriate sorbent combination, water management and choice of a suited GC column.
The particle size distribution is considered the most relevant information for nanoscale property identification and material characterization. The current OECD test guideline on particle size and size distribution (TG 110) is not applicable to ‘nano-sized’ objects. In this project we thus develop a new OECD test guideline for the measurement of the size and size distribution of particles and fibers with at least one dimension in the nanoscale. A fiber is defined as an object having an aspect ratio of length/diameter l/d >3. The width and length of each fiber should be measured concurrently.
In order to measure the particle size distributions, many techniques are available. 9 methods for particles and 2 methods for fibres have been tested in a prevalidation study and appropriate methods will be compared in an interlaboratory round robin test starting in February 2019.
The particle size distribution is considered the most relevant information for nanoscale property identification and material characterization. The current OECD test guideline on particle size and size distribution (TG 110) is not applicable to ‘nano-sized’ objects. In this project we thus develop a new OECD test guideline for the measurement of the size and size distribution of particles and fibers with at least one dimension in the range of 1 - 1000 nm. A fiber is defined as an object having an aspect ratio of length/diameter l/d >3. The width and length of each fiber should be measured concurrently.
In order to measure the particle size distributions, many techniques are available. 9 methods for particles and 2 methods for fibres have been tested in a prevalidation study and appropriate methods will be compared in an interlaboratory round robin test starting in February 2019.
Sintered bioactive glass scaffolds of defined shape and porosity, e.g. made via additive manufacturing, must provide sufficient bioactivity and sinterability. As higher bioactivity is often linked to high corrosion and crystallization tendency, a certain compromise between sintering ability and bioactivity is therefore required. Groh et al. developed a fluoride-containing bioactive glass (F3), which allows fiber drawing and shows a bioactivity well comparable to that of Bioglass®45S5.
To study whether and to what extent the sinterability of F3 glass powder is controlled by particle size, coarse and fine F3 glass powders (300-310µm and 0-32µm) were prepared by crushing, sieving and milling. Sintering, degassing and phase transformation during heating were studied with heating microscopy, vacuum hot extraction (VHE), DTA, XRD, and SEM.
For the coarse glass powder, sintering proceeds slowly and is limited by surface crystallization of primary Na2CaSi2O6 crystals. Although the crystallization onset of Na2CaSi2O6 is shifted to lower temperature, full densification is attained for the fine powder. This finding indicate that certain porosity might be tuned via particle size variation. Above 900°C, intensive foaming is evident for the fine powder. VHE studies revealed that carbon species are the main foaming source.
A mobile Bruker S2 Picofox TXRF spectrometer has been used in two field campaigns within the EMPIR env07 AEROMET project for the on-site analysis of cascade impactor aerosol samples.The results show that even at moderate air pollution levels – i.e.PM10 fairly below 20 μg/m³ - element mass concentrations in air in the range of 100 pg/m³could be measured in up to 13 size bins after sampling times of less than only 0.5 days.
Quality Improvement of VOC chamber emission tests observed for 10 years with round robin tests
(2018)
In Europe, the Construction Products Regulation (CPR, 2011/305/EU) sets basic requirements (BR) on how construction works must be designed and built. BR 3 “hygiene, health and the environment” states low emissions of toxic gases, Volatile Organic Compounds (VOCVOCs), particles, etc. from building materials. Meanwhile, a worldwide network of professional Commercial and non-commercial laboratories performing emission tests for the evaluation of products for interior use has been established.
Therefore, comparability of test results must be ensured. The participation in Round Robin Tests (RRTRRTs) is a means to prove a laboratory’s proficiency. Since 2006 BAM offers such proficiency test for emission chamber test every two years.
Any commercially available product on the market can be used as reference material, provided it is thoroughly characterised. However, these materials often emit only a few and material specific VOCs and appropriate homogeneity is not given. Therefore, alternative materials should be found. BAM used different materials over the years. Currently, the best suited reference material is a cured lacquer surface which contained several VOCs added to the liquid lacquer system. The round robin tests 2014, 2016 and 2018 were conducted with such a system.
Compounds like Styrene or n-Alkanes like Decane or Tridecane were tested in many of the proficiency test operated by BAM. Up to now the relative standard deviation of these compounds decrease continuously. Starting with values about 30 % in 2008 we reached values for the mentioned compounds 15 to 20 % now. But even for more polar compounds improved results were received.
Over the years the results of a large group of laboratories detected many compounds with much higher accuracy than at the beginning. So, the comparability between results of different laboratories becomes much better.
Micro-(nano-)encapsulation technology involves building of a barrier between the core and the environment and offers a number of benefits to preserve the functional and physicochemical properties of core material. Tremendous progress has been made in synthesizing well-defined capsules to achieve desired properties such as particle size, chemical composition, and controlled release of the payload.
Encapsulation of volatile organic compounds (VOCs) that could evaporate with a defined rate is of immense interest for application in emission reference materials (ERM). These are urgently needed for quality assurance and quality control purposes (QA/QC) required by test standards for the determination of chemical emissions of construction and other materials for interior use. As such ERMs are hardly available on the market, the EU-funded EMPIR project MetrIAQ [1] was started to fill this gap by developing a material with temporally constant emission of VOCs typically found in indoor air.
Different capsules in a size range between 5 and 50 μm were synthesized through an interfacial polyaddition/polycondensation reaction in direct (water-in-oil) system. As VOC several types of hydrophobic liquid materials were used. After synthesis, the morphology and physicochemical properties of capsules were characterized by electron microscopy, FTIR and DSC/TGA. An encapsulation efficiency up to 90% could be reached. The emission kinetic of volatile agents was studied in emission test chambers at 23 °C and 50% RH for 14 days. First results indicate that variation of the cross-linking grade of the shell material is one important parameter to adjust the desired emission rate. The overall aim is to achieve a consistent emission profile that decreases by less than 10 % over a target period of at least 14 days.
Micro-(nano-)encapsulation technology involves building a barrier between the core and the environment and offers several benefits to preserve the functional and physicochemical properties of core material. Tremendous progress has been made in synthesizing well-defined capsules to achieve desired properties such as particle size, chemical composition, and controlled release of loaded compounds.
Encapsulation of volatile organic compounds (VOCs) that could evaporate with a defined rate is of immense interest for application in emission reference materials (ERM). These are urgently needed for quality assurance and quality control purposes (QA/QC) required by test standards for the determination of chemical emissions of construction and other materials for interior use. As such ERMs are hardly available on the market, the EU-funded EMPIR project MetrIAQ was started to fill this gap by developing a material with temporally constant emission of VOCs typically found in indoor air.