3.4 Sicherheit von Lagerbehältern
Filtern
Dokumenttyp
- Vortrag (6)
Sprache
- Englisch (6)
Referierte Publikation
- nein (6)
Schlagworte
- Compression set (3)
- Ageing (2)
- Compression stress relaxation (2)
- Modelling (2)
- (U)HMWPE (1)
- Arrhenius (1)
- CSR (1)
- Compression Set (1)
- Continuous compression stress relaxation (1)
- FTIR (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (6) (entfernen)
Overview of ongoing research and future prospects on polyethylene neutron shielding materials at BAM
(2023)
The extension of the interim storage period of radioactive waste before disposal will cause additional challenges for the nuclear waste management in Germany, so that an extensive knowledge of the long-term performance of casks, including their components and inventories, will be required for future extended storage licenses.
Ultra-high and high molecular weight polyethylenes ((U)HMW-PE) are used for neutron shielding purposes in casks for storage and transport of spent fuel and high-level waste due to their extremely high hydrogen content. During their service life of several decades as cask components, the PE materials are exposed to neutron and gamma radiation from the radioactive inventory of the casks, mechanical assembling stresses and temperature. All these combined effects affect the material properties of such components which in turn may be crucial for some possible accident scenarios.
At the Bundesanstalt für Materialforschung und -prüfung (BAM), the effects of high temperature exposure in combination with subsequent or previous irradiation were investigated with a comprehensive aging program including thermal aging at 125 °C for different aging periods up to 5 years and irradiation with doses ranging from 50 to 600 kGy.
This contribution provides an overview of the ongoing research related to the structural changes of (U)HMW-PE induced by gamma irradiation and high temperature exposure and focuses on current research perspectives at BAM with regard to the prediction of the dynamic behavior of the material during extended interim storage in case of an accident scenario. First results of the coupled effect of temperature, radiation and mechanical loading will be presented. The effect of microstructural changes induced by gamma irradiation and high temperature on the mechanical behavior of (U)HMW-PE will be assessed.
Hydrogenated nitrile butadiene rubber (HNBR) elastomer was thermo-oxidatively aged at different temperatures up to 150°C. Fourier transform infrared spectroscopy (FTIR), compression stress relaxation (CSR) and IRHD microhardness were used to characterise the chemo-mechanical changes of HNBR O-rings during thermo-oxidative ageing. FTIR shows the development of carbonyl, methyl and ester groups but the nitrile content was not affected by ageing. The effect of sample geometry during CSR was investigated. CSR data were converted through integrated kinetic laws. The conversion has proven its sensibility to detect heterogeneous ageing. This was confirmed by the IRHD measurements across the section of O-rings. Oxidation profiles were determined by applying the model of Wise et al. to the IRHD experimental results.
During an extensive test programme at the Bundesanstalt für Materialforschung und prüfung, material property changes of EPDM O-rings were investigated at different ageing times and an ageing temperature of 125 °C. To exclude possible diffusion limited oxidation (DLO) effects that can distort the data, IRHD micro hardness measurements were performed over the cross-section of compressed O-rings. Continuous stress relaxation measurements were conducted on samples free of DLO effects. The additional effect of physical processes to irreversible chemical ones during a long-term thermal exposure is quantified by the analysis of compression set measurements under various test conditions. By combining the different experimental methods, characteristic times relative to the degradation processes were determined. On the basis of experimental data, a microphysically motivated model that takes into account reversible and irreversible processes was developed. The parameter identification strategy of the material model is based on our experimental investigations on homogeneously aged elastomer O-rings. The simulated results are in good agreement with the experiments.
The main task of the division "Safety of Storage Containers" at BAM is the safety assessment of storage containers for radioactive waste. A sufficient sealing of bolted lid systems for the safe containment of the waste for transport, storage and disposal is very important. Extensive knowledge of the change of the elastomer’s properties during ageing and the availability of reliable end-of-lifetime criteria is mandatory to guarantee long term safe enclosure.
In a long-term test programme over 5 years we have studied the degradation and the change of sealing properties of several elastomers, including EPDM, at four different ageing temperatures (75 °C, 100 °C, 125 °C and 150 °C). Compression stress relaxation (CSR) and compression set (CS) experiments were carried out. It has been found that when the data does not cover a sufficient time frame necessary for the evolution of the degradation of a chosen property, a curvature in the Arrhenius relationship is observed. For CSR, the curvature was observed for samples aged up to 186 days. As for CS experiments, the curvature was detected for sample aged up to 2 years. To cover the possible lack of experimental long-term data at low temperatures, a numerical model for CSR was developed and longer ageing times for the simulation were adopted. A degradation-rate based model for the evolution of degradative processes is proposed. The main advantage of the model is the possibility to quickly validate the interpolation at lower temperatures within the range of slower chemical processes without forcing an Arrhenius straight-line extrapolation. The model was also applied to CS experiments and validated by the 5 years experimental results where the curvature was gone, and the degradation property has followed an Arrhenius relationship. In the figure the contribution of the two degradative processes are shown over CS and CSR respectively.
Elastomer seals are used in many industrial applications due to their excellent mechanical properties at a wide range of temperatures. Their high versatility and recovery potential under several load conditions make them well suitable for the application in containers designed for transport, storage and/or disposal of radioactive materials. In containers for low and intermediate level radioactive waste, elastomer seals are used as barrier seals, and as auxiliary seals in storage and transportation casks (dual purpose casks) for heat generating radioactive waste, such as spent fuel and high-level waste. While a seal exchange at defined intervals is typical in many conventional applications, it is impossible or at least hard to perform when principles of minimization of radiation exposure have to be considered and prohibit an unnecessary cask handling. An extensive knowledge of the change of the elastomer’s properties during aging and the availability of reliable end-of-lifetime criteria to guarantee the permanent safe enclosure of the radioactive material is mandatory. As BAM is involved in most of the national cask licensing procedures and in the evaluation of cask-related long-term safety issues, great efforts have been already made and are still planned to scientifically support this task.
Compression stress relaxation and compression set were identified as key indicators of elastomer long-term performance and quantitatively investigated in comprehensive test programs. Among other representative types of elastomers, specimens made from ethylene propylene diene rubber (EPDM) were tested before, during and after aging to capture the most important of their complex mechanical properties.
In the presented study, exemplary results were used to simulate the compression stress relaxation and the compression set of elastomer O-rings during aging. Regarding the influence of temperature, the time temperature superposition principle is applied in the relaxation analysis of elastomer O-rings. The proposed model is implemented in the commercial finite element software ABAQUS/Standard® [1] with a sequential temperature displacement coupling. Numerical results match the experimental compression stress relaxation measurements well. The prediction of compression set values after long-term aging shows a relatively good agreement with the experimental results. Nevertheless, all input parameters derived from the specimen tests, additional assumptions concerning boundary conditions and modeling strategy are discussed with regard to the identified slight discrepancies.
The possibility to extend the finite element model to represent the O-ring seal’s ability to recover after a (fast) partial release is taken into account
At the Bundesanstalt für Materialforschung und -prüfung (BAM) in Division 3.4 Safety of Storage Containers, one of our tasks is to evaluate the safety of containers designed for disposal of low and intermediate radioactive waste. As such containers might be transported before and stored until disposal, safe enclosure of the radioactive inventory is important for this time span.
Elastomer O-rings are widely used as barrier seals in these containers. Thus, as for many other applications, an understanding of the practical effects of ageing degradation on elastomer seals during long-term exposure is mandatory for predicting the lifetime of such components. According to a long-term test programme on three kinds of rubbers (EPDM and FKM (relevant for application), HNBR (for comparison)), over several years we have studied the degradation and the change of mechanical properties (e.g. hardness, strain at break) at four different ageing temperatures (75 °C, 100 °C, 125 °C and 150 °C) as well as the change of sealing properties. Continuous and intermittent compression stress relaxation (CSR) measurements were performed in order to investigate the respective contribution of crosslinking and chain scission to the observed degradation effects. Thus, the degradation kinetics and mechanisms could be resolved more clearly. For assessing the seal performance, compression set (CS) and leakage rate measurements were conducted. The experimental results showed that the O-rings remained leak-tight under purely static conditions even when CSR, CS and mechanical properties already indicated far advanced degradation. For this reason, a modified leakage test involving a small and rapid partial decompression of the seal was developed that enabled determining an end-of-lifetime criterion for O-rings with a safety margin for thermal shrinkage and vibrations.