Analysis of the dielectric and electromechanical properties of the cellular polypropylene ferroelectret films (EMFIT) evidences their high potential for the application in the air-coupled ultrasonic transducers. Simple prototype transducers, based on the EMFIT films, were developed and their high sensitivity was proved in the air-coupled ultrasonic experiment. Amplitude and delay time scanned images of the polyethylene step wedge with holes, obtained in both pulse-echo and transmission modes, demonstrate that non-contact ultrasonic imaging with EMFIT transducers is possible.
Electromechanical response of polypropylene ferroelectret transducers under application of high-voltage pulses was measured by laser Doppler vibrometry and compared with results of ultrasonic through-air transmission between two ferroelectret transducers. The electromechanical response was completely explained by piezoelectric and electrostrictive effects. The electrostrictive effect dominates at high voltages and provides significant enlargement of the transducer constant, up to factor of 2.5. The induced strain of 1.7% was achieved at – 2000 V. The nonlinear ultrasonic transmission was shown to be well described by the piezoelectric and electrostrictive response of transmitter, except in the range of high negative exciting voltages where some limitation of the transmitted signal was observed. This limitation seems not to be a fundamental one and does not abolish the advantages of high-voltage excitation of polypropylene ferroelectret transducers.