This report is based on a three-year experience as coordinator of the ACP-EU funded SPIN project. The project involved eight African and three European partners. Practical and unforeseeable problems are addressed that occurred during the project implementation and ways how they were successfully solved are reported. The major problems in many African institutions were administrations that are not used to work in multi-national consortia and a lack of institutional support for the African researchers. In Europe a misjudgement of the African boundary conditions as well as inflexible administrations caused problems. Finally the funding scheme did not always allow to easily overcome the high number of unexpected practical problems. A major deficit identified during the project was a general trend in Africa to underestimate the role of research for the development of the continent. Most universities focus on teaching applied sciences, which is without doubt important to cover the market need for qualified staff in the rapidly growing African industries. However, this makes it unattractive for highly qualified performers to conduct research on the continent. Furthermore this leads to the situation that the curricula can only contain second hand knowledge. In order to attract international high level researchers, it is suggested to install multi-national regional excellence research centres that only promote PhD and post-doc research on a level that can cope with highest international excellence. High level research is often perceived as not capable of focusing on immediate actual problems that many African economies have to cope with.. However, it is considered to be very sustainable in terms of autonomy and mastering future challenges.
The economic use of chemical admixtures depends on supply chains. Therefore, in most regions ins sub-Saharan Africa (SSA), the use of admixtures is not common practice. This amplifies the unfavorable framework for concrete construction such as fragmentary supply chains, high local cement prices, and unfavorable construction site facilities in this region significantly. The use of superplasticizer (SP) and stabilizing agents (STA) can enhance the concrete technology in SSA, since they can disassociate the concrete quality from external boundary influences. After providing a general overview of the peculiarities of the SSA boundary framework, economic concepts are provided, how existing material solutions can be significantly improved by the use of SPs and STAs based on locally available materials such as lignosulphonates and cassava starch. Finally a three step optimization process is described that helps developing flowable concrete based on materials that can be accessed in most locations in SSA.
Over the last decades concrete has evolved from a simple mass construction material towards a sophisticated multi-component system. The design parameters for the mixture composition of concrete have significantly increased from strength based towards overall or specific performance based. As a result the variety of concrete has increased yielding a number of special concrete technologies such as Self-Compacting Concrete (SCC), High-Performance Concrete (HPC), Strain Hardening Cement Based Composites (SHCC), and many others. Due to their complex mixture compositions and a multitude of possible interactions between constituents, these concrete types are preferably composed of special components like well-defined powders and sophisticated chemical admixtures. This makes such concrete technology expensive and limits their application to regions with the required material supply chains. The paper puts focus on materials, which are less well studied in conjunction with high performance concrete, but which are available in many developing countries, and in particular sub-Saharan Africa. The paper shows how sec can be designed without polycarboxylate ether superplasticizer and well defined fillers, but with lignosulphonate, cassava starch and rice husk ash. The positive effect of well processed rice husk ashes is demonstrated. Furthermore results are presented of SHCC where typical components like polyvinyl alcohol fibres and fluy ash are replaced by sisal fibres and limestone filler, respectively. The results point out that high performance concrete applications do not have to be limited to a boundary framework with availability of well-defined raw material supply structures and sophisticated admixtures or fibres. Concepts are presented how innovative concrete technologies can be developed based on indigenous materials.
Rheological optimisation for flowable mixture compositions specified for African boundary conditions
(2013)
To date concrete technology is not yet well established in sub-Saharan Africa but considering the construction technological challenges of the region, without doubt, concrete will play a major role in future. The social, economic, and geographic boundary conditions distinguish greatly from those that can be found in many other regions of the world, where concrete is considerably well established. Düring the last decades, concrete technology underwent a rapid evolution process, but in most countries, where concrete is already well established, innovations are difficult to be brought into practice, Africa, currently has the opportunity and potential, of directly establishing the best available practice in concrete technology.
The conclusion is drawn that self-compacting concrete (SCC) or highly flowable concrete is a reasonable solution for African construction sites. Since on most African construction sites the disadvantageous concreting environment is the most crucial factor for the concrete quality, the outstanding workability properties outweigh any disadvantages of SCC.
Based on this consideration, concepts are developed, how to bring about robust SCC cost-efficiently and reliably into practice as pre-mixed dry compound under consideration of local materials such as rice husk ashes, bagasse ashes, natural pozzolans, cassava starch and lignosulphonate.
There is a wide range of research worldwide on supplementary cementitious materials (SCMs) such as fly ash and slag for substituting pure cement. Such materials are suitable to be considered in a cementitious system with ordinary Portland cement (OPC) due to their high pozzolanic properties. In addition, majority of the SCMs are said to significantly improve concrete properties especially in terms of increased strength and durability. Unfortunately, the production of such SCMs is not entirely eco-friendly and also limited to certain parts of the world, hence one has to look at alternative options.
The issue of availability of resources is a strong concept that is ever-increasing, and the use of more eco-friendly SCMs in a cementitious system is furthermore attractive. Hence this paper addresses the use of eco-friendly SCMs in concrete such as rice husk ash (RHA). Despite the fact that extensive research has been done on this material, its application in a cementitious system to obtain sufficient concrete properties is still rather limited. In a country like Tanzania, high strength concrete construction is applicable in special construction cases but certainly not a high priority. Majority of construction is still undertaken using normal strength concrete. In a ternary cementitious system consisting of OPC, RHA and other readily available resources such as limestone filler (LSF), normal strength concrete can still be produced having good performance and suitable for regular on-site construction. This paper explains a possible application of obtaining sufficient concrete properties from the available resources.
Rice husk as (RHA) is an eco-friendly material, which can be used as a supplementary cementitious material (SCM) in cement and concrete. Due to the high water demand for the material, superplasticizers (SPs) are essential to improve the performance. However, the interaction between the SPs and RHA systems is limited. This paper investigates the interaction of the binders with three SPs, i.e. two polycarboxylate ethers (PCEs) and one lignosulphonate (LS). The investigations are performed on blended systems of mortar containing various percentages of RHA and limestone powder (LSP). LSP is used in this research to improve the workability of the mortar. The results from the zeta potential (ZP) shows that the SPs are extremely dependent on the pH of the suspension. At higher pH values such as in a cementitious system, the ZP becomes less negative indicating that the ions in the suspension interact with the carboxyl groups in the backbone of the polymers thus reducing the surface charges of the SP. The mini-slump flow shows that the workability of the blended mortar systems is significantly improved with the addition of SPs. LS systems with increasing RHA is observed to have similar workability as the control mix over time. The compressive strength test results show increased strength for all mortar specimens with added RHA and LSP at later ages.
Superplasticizers (SPs) have been employed in concrete technology for decades to improve the workability of concrete in its fresh state. The addition of SPs in cement-based systems affects the early properties. Although the interaction of the cement particles with various SPs has been extensively researched, there still exists limited research on the interaction of SPs with supplementary cementitious materials such as rice husk ash (RHA). This paper investigates the rheological properties and early hydration kinetics of RHA-blended systems with three types of SPs, a polycarboxylate ether (PCE) and two lignosulphonates (LS-acc and LS-ret). In rheological properties, the addition of SP causes an initial improvement of workability as the yield stress is significantly reduced. The pastes with PCE and LS-acc show a slight increase of yield stress over time whereas pastes with LS-ret tend to lower the yield stress slightly over time, further improving the workability. Without SP, pastes with RHA show a lower yield stress but an increase in plastic viscosity as cement is further replaced with RHA. The addition of the LS SPs is observed to lower the plastic viscosity but remains constant with further replacement of cement with RHA. This indicates that LS SPs further adsorbs on RHA particles and hydration products produced causing dispersion of the particles
within the system. In early hydration kinetics, pastes with PCE retard hydration and the degree of retardation is further increased with LS SPs. In the presence of RHA, the retardation of LS SP systems is significantly reduced. The pastes with PCE show more ettringite in the SEM micrographs, but is observed to be shorter needles. This indicates an initial good workability for PCE. However, C-S-H and CH were observed to be low in quantity, whereby the pastes with LS show more nucleation sites for C-S-H and CH. The ettringite needles in the LS systems were similar in quantity and more elongated in some cases but not abundant as in the PCE systems.