Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (55) (entfernen)
Schlagworte
- DSC (8)
- Elastomer (7)
- Compression set (5)
- DMA (5)
- Glass transition (5)
- Crosslinking (4)
- Dynamic mechanical analysis (4)
- Low temperature behaviour (4)
- Prepreg (4)
- Sealing material (4)
- Ultrasound (4)
- Vulcanisation (4)
- Cross-linking (3)
- Cure process (3)
- Curemeter (3)
- Dielectric parameters (3)
- EVA (3)
- Microwave methods (3)
- Prozesskontrolle (3)
- Thermoset (3)
- Ultraschall (3)
- Vitrification (3)
- Aushärtegrad (2)
- Aushärtung (2)
- Biodiesel (2)
- Carbon fibre (2)
- DMTA (2)
- Druckverformungsrest (2)
- Dynamic-mechanical analysis (2)
- Elastomere (2)
- Elastomers (2)
- Epoxy (2)
- Fuel sorption (2)
- Gelation (2)
- Impact strength (2)
- Kochversuch (2)
- Monitoring (2)
- Moulding compound (2)
- PE-HD (2)
- Phenolharz (2)
- Sensoren (2)
- Thermosets (2)
- Vulcanization (2)
- Vulkanisation (2)
- Acoustic propagation (1)
- Adhesion (1)
- Aminoharz (1)
- Atomic force microscope (1)
- Aushärtungsverlauf (1)
- Autoclave (1)
- Bakelit (1)
- Bauteilversuche (1)
- CFC (1)
- CRP (1)
- Cellular polypropylene (1)
- Charpy impact test (1)
- Component test (1)
- Composite material (1)
- Composites (1)
- Cross linked polyethylene insulation (1)
- Crystal melting (1)
- Cure (1)
- Curing (1)
- Degree of cure (1)
- Degree of curing (1)
- Desorption (1)
- Devitrification (1)
- Dichtung (1)
- Dichtungen (1)
- Dielektrik (1)
- Differential scanning calorimetry (1)
- Elastic-plastic properties (1)
- Elektroinstallationsteile (1)
- Epoxidharz (1)
- Epoxy system (1)
- Ethylene vinyl acetate (1)
- Ferroelectret (1)
- Fertigungskontrolle (1)
- Filled rubber compounds (1)
- Force-distance curves (1)
- Glass transition temperature (1)
- Glasübergang (1)
- Gütesicherung (1)
- Harnstoffformasse (1)
- Harnstoffharz (1)
- Harnstoffharze (1)
- Indentation (1)
- Injection moulding (1)
- Interdiffusion (1)
- Interphase/interface (1)
- Keramische Grünfolien (1)
- Klebfolie (1)
- Kunstharze (1)
- Low temperature (1)
- Materialparameter (1)
- Materialprüfungsamt (1)
- Mechanical variables measurement (1)
- Mechanische Prüfung (1)
- Melamine (1)
- Mould (1)
- Mould wall coupling (1)
- Nasschemische Analyse (1)
- Natural rubber (1)
- O-Ring (1)
- O-Ringe (1)
- O-ring (1)
- On-line monitoring (1)
- Online control (1)
- Ozonbeständigkeit (1)
- Ozonkonzentrationsbestimmung (1)
- Phenol (1)
- Phenolharze (1)
- Phenolic resin (1)
- Photovoltaik (1)
- Polymer (1)
- Post-curing (1)
- Process controlling (1)
- Qualitätssicherung (1)
- Relaxation (1)
- Resins (1)
- Rheology (1)
- Rtm (1)
- Schallgeschwindgkeit (1)
- Schallgeschwindigkeit (1)
- Schrumpf (1)
- Schubmodul (1)
- Seal (1)
- Sensors (1)
- Silicone rubber (1)
- Sound velocity (1)
- Spectroscopy (1)
- Spritzgießen (1)
- TMDSC (1)
- Technische Vereinigung (1)
- Temerature (1)
- Thermal analysis (1)
- Thermal properties (1)
- Thermische Analyse (1)
- Thermoset manufacturing (1)
- Tiefe Temperatur (1)
- Time-temperature superposition principle (1)
- UV-Spektroskopie (1)
- Ultrasonic (1)
- Ultrasonic monitoring (1)
- Ultrasound sensors (1)
- Verlustmodul (1)
- Vernetzung (1)
- Vernetzungsreaktion (1)
- Verzug (1)
- Viscoelastic (1)
Rubber is widely used as sealing material in various applications. In many fields the sealing function at low temperatures is necessary. Therefore the understanding of failure mechanisms is of high importance. Rubbers are normally used above their glass-rubber transition region but the minimum working temperature limit is not defined precisely. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties. The results of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are combined with the results of the standardized compression set according to ISO 815 respectively a modified test using the DMA equipment.
Über die in der Technik weit verbreitete typisierte Harnstoffformmasse UF 131.5, ein Aminoplast, wird berichtet, dass sie im Zuge der thermisch aktivierten Vernetzungsreaktion wegen "Überhärtung" mangelhafte Eigenschaften annimmt. Zur Verifizierung dieses Effektes werden mithilfe der Ultraschall-Prozesskontrolle gezielt Proben unterschiedlicher Aushärtegrade hergestellt. Sie werden mit verschiedenen Methoden, wie der "Kochprobe" und der Thermoanalyse, charakterisiert und auf ihre Materialeigenschaften untersucht. Dabei zeigt sich ein deutlicher Einfluss der Härtezeit auf die Glasübergangstemperatur der Formmasse. In den mechanischen Eigenschaften ist eine Veränderung allerdings nur in der Schlagzähigkeit festzustellen, die sich mit steigender Härtezeit sogar wesentlich verbessert.
Epoxy carbon-fibre prepreg, Hexcel Type 6376 HTS, was investigated using Dynamic Mechanical Analysis (DMA). The DMA characteristic parameters are storage modulus E', loss modulus E' and loss factor tanδ. These parameters are ideally suited to observe the vitrification, referred to as glass transition, resulting from the cross-linking reaction. Detection of the cure state may also be achieved by determining the momentary glass transition temperature of partially cured samples. The consequent use of a multi-frequency measuring regime was used to derive the apparent activation energy for the glass transition process. Different temperature programs were also applied to monitor the curing process directly, as well as to investigate the different states of incomplete cure reached in preceding curing steps. The intention was to provide better understanding of the consequences of an interrupted autoclave curing process and to use DMA to detect the cure state achieved. With DMA, the continuation of an incomplete curing process also can be monitored. DMA measurements up to 300 °C showed, furthermore, that the final glass transition temperature was reduced by thermal degradation at high temperatures.
Epoxy composites used for high-end structural applications are typically cured under the influence of temperature and pressure causing a number of complex chemical and physical transformations. On heating a mould, temperature gradients will occur through the component which will depend largely on the thermophysical properties of the specific composite. The crosslinking reaction is exothermic leading to additional heat release, thus complicating heat transportation models. If such effects are not accounted for, it can lead to variations in resin flow, poor fibre wetting causing voiding and inhomogeneous cure, leading to shrinkage and unfavourable variations in moulded part geometry. Limited information is available for thermal models used in the manufacture of reinforced thermosets. Autoclave [1, 2] and laser or infra-red curing processes [3, 4] typically use constant values determined on fully cured parts. In this work, the variation in thermal conductivity (K) (W/(m K)), thermal diffusivity (a) (m(2)/s) and specific heat capacity at constant pressure (c(p)) (J/(g K) is determined for a carbon fibre prepreg during cure. It is the intention to improve understanding of how these parameters are related to chemical or physical transformations occurring during cure, and where estimates or shortcuts may be used for heat transfer models
Elastomers are widely used as the main sealing materials for containers for low and intermediate level radioactive waste and as an additional component to metal seals in spent fuel and high active waste containers. The safe encapsulation of the radioactive container inventory has to be guaranteed according to regulation and appropriate guidelines for long term storage periods as well as for temperatures as low as -40°C during transport. Therefore, the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance. It is known that the material properties of elastomers are strongly temperature dependent. At low temperatures, this is caused by the rubber-glass transition (abbreviated: glass transition). During continuous cooling, the material changes from a rubber-like entropy elastic to a stiff energy elastic behaviour, which allows nearly no strain or retraction. Hence, rubbers are normally used above their glass transition, but the minimum working temperature limit is not defined precisely; this can cause problems during the above noted applications. Therefore, the lower operation temperature limit of elastomer seals must be determined in dependence of the material properties. Differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) are combined with standardised measurements to determine the compression set according to ISO 815. To reduce the test time of the standard tests, a faster technique than normally used was developed. Additionally, the breakdown temperature of the sealing function of complete O ring seals was measured in a component test set-up to compare it with the results of the other tests. The experimental set-up is capable of measuring the leakage rate at low temperatures by the pressure rise method. A fluorocarbon rubber (FKM) was selected for this investigation as it is often used for radioactive waste containers. The materials (seals and test sheets) were purchased from a commercial seal producer.