Filtern
Erscheinungsjahr
Dokumenttyp
Schlagworte
- Aushärtung (2)
- Epoxy (2)
- Ultraschall (2)
- Ultrasound (2)
- Compositbauteil (1)
- Composite material (1)
- Composites (1)
- Cross-linking (1)
- Cure process (1)
- DMA (1)
- Degree of cure (1)
- Epxidharz (1)
- Gelation (1)
- Glass transition (1)
- Harzinjektionsverfahren (1)
- High temperature (1)
- Materialparameter (1)
- Modulus (1)
- Mould (1)
- Mould wall coupling (1)
- Prepreg (1)
- Process controlling (1)
- Prozesskontrolle (1)
- RTM (1)
- Rtm (1)
- Sensoren (1)
- Sensors (1)
- Thermoset (1)
- Thermoset manufacturing (1)
- Ultrasonic monitoring (1)
- Ultrasound sensors (1)
- Vernetzungsreaktion (1)
- Vitrification (1)
- tan delta (1)
Zusammenfassung
Der Ausgangspunkt für diese Arbeiten ist eine in [1] beschriebene Ultraschall-(US)-Sensorik zur Aushärtungskontrolle. Sie wurde für rieselfähige Formmassen entwickelt [2,3]. Darauf aufbauend ist es das Ziel der vorliegenden Arbeit, die Voraussetzungen für den Einsatz dieser Sensorik beim Harzinjektionsverfahren zu schaffen und ihre Kalibrierung durch rheologische und DSC-Messungen zu ermöglichen.
Der erste Teil des Beitrages beschäftigt sich mit dem technologischen Ablauf des Harzinjektionsverfahren und den Einsatzmöglichkeiten der US-Sensorik bei dieser Technologie. Ergebnisse von Schallgeschwindigkeits- und Dämpfungsmessungen für EP-Harze werden vorgestellt.
Im zweiten Teil wird auf das Kalibrieren der US-Sensorik für den Verarbeiter eingegangen. Es kann mittels der bisherigen Prozessführung oder durch Vergleich mit den Ergebnissen anderer Mess-Verfahren wie Rheometer- oder Differential-Scanning-Calerometry-(DSC)-Messungen erfolgen.
In recent years eure monitoring with ultrasonic methods became more important. An on-line measurement System for industrial applications is presented in this paper. It operates in through-transmission and the measured parameters are the sound velocity and the attenuation of the sound wave. An objective of this paper is to establish the ränge of possible applications for an ultrasonic eure monitoring System.
Einfluss hoher Temperaturen und Drücke auf die Ultraschalleigenschaften eines Komposit-Prüfkopfes
(2004)
The technique normally used to measure Cp during isothermal cure is Temperature Modulated - Dynamic Scanning Calorimetry TM-DSC. It is however not standardised, experimentally complicated and quite time intensive. As will be shown, Cp may also be estimated during isothermal cure just from using dynamic heating experiments on a fully cured sample. Such values are often sufficient for isothermal heat transfer models that otherwise employ a constant Cp value obtained from the fully cured epoxy. Secondly, the results from dynamic heating experiments provide a quick means, in comparison to isothermal TMDSC measurements, of estimating Cp variation during cure as well as providing a good estimate value for Cp towards the end of isothermal cure. As will be shown, such values obtained from a standardised measurement procedure are very helpful in setting up TMDSC experiments that are more sensitive to experimental error influenced by factors such as sample weight and geometry.
The DSC results illustrate that the measured heat capacity Cp for a fully cured epoxy over a temperature range are very similar to values for samples partially cured at corresponding isothermal temperatures, under the prerequisite that vitrification takes place. In such cases the primary influence on Cp is specific measurement temperature and not degree of cure. For isothermal cure temperatures investigated between 150 and 200 °C, the total change of Cp during cure is nearly constant and correlates well with values published by authors on other epoxy based systems. Taking Cp variation as constant, it is possible from just dynamic heating experiments on the cured epoxy to estimate Cp for the uncured epoxy system at specific cure temperatures. The next step would be to estimate the full Cp profile during isothermal cure, however, in such cases, the time to vitrification would also be needed as additional information.
The curing conditions play an important role in the quality assurance of composite products.
Especially as composite materials are widely used in high tech areas so that they are required to fulfil high quality Standards. Some problems which occur during curing, for instance undercuring, can hardly be detected using Standard NDT investigations, mainly because they are manifested only at high temperatures, particularly close to glass-rubber-transition. On-line eure monitoring has the outstanding advantage that it can monitor the material parameters even at the highest temperatures possible.
In recent years eure monitoring with ultrasonic methods has become more populär. In comparison to dielectric methods mechanical parameters are measured directly. The quantities to be measured are the velocity and the attenuation of the sound wave. On this basis the storage and loss modulus can be calculated. Depending on the form of excitation with longitudinal or transversal waves these moduli are referred to as long wave or shear modulus.
Well developed Computer based technology and sensor materials are available in the non-destructive testing (NDT) market. The measuring equipment employed a commercial NDT System, which worked computer-aided. With a special Software the demands of automatic Operation under industrial conditions was accomplished. This measurement equipment was tested on composites. Its structure, performance and some practical results will be presented in the following paper.
Ultrasound on-line NDT methods have been demonstrated as a useful tool for monitoring the curing reaction of thermosets. In order to achieve this ultrasound sensors are incorporated into compression, injection and RTM (resin transfer) mould. For many commercial products imprints or any surface markings upon the moulded product are undesirable. Due to its physical properties ultrasound has a large advantage over other techniques for similar applications. The sound wave can pass through the wall of the mould and direct contact with the moulded part is not required. In this particular case one fundamental problem is a good coupling of the sensors to the mould wall. Several mediums came into question but because of the high technical (e. g. temperature and long time stability) and practical demands, it was decided that dry (non-fluid) coupling would be the most promising candidate. A handful of coupling foils suitable also at high temperatures and for long time application under industrial conditions were tested and are presented in this paper.
Making Cure Visible
(2005)
Das Fließ-Härtungs-Verhalten von Duroplastformmassen wird gegenwärtig nur
unvollständig durch empirische Größen beschrieben. Diese ungenauen und
unsicheren Angaben können zu Schwierigkeiten bei der optimalen Einstellung
der Fertigungsmaschinen des Verarbeiters führen. Insbesondere Veränderungen
der Formmasseeigenschaften während des Transportes und der Lagerung stören
die Produktion. Das vorgestellte Messverfahren mit Ultraschall-sensoren ermöglicht
die schnelle und vollständige Erfassung des Fließ-Härtungs-Verhaltens, auch
während des technologischen Prozesses. Experimentelle Ergebnisse zu
Alterungs-erscheinungen dieser Formmassen illustrieren den Nutzen des
Verfahrens für Formmasse-produzenten und -verarbeiter.
Epoxy carbon-fibre prepreg, Hexcel Type 6376 HTS, was investigated using Dynamic Mechanical Analysis (DMA). The DMA characteristic parameters are storage modulus E', loss modulus E' and loss factor tanδ. These parameters are ideally suited to observe the vitrification, referred to as glass transition, resulting from the cross-linking reaction. Detection of the cure state may also be achieved by determining the momentary glass transition temperature of partially cured samples. The consequent use of a multi-frequency measuring regime was used to derive the apparent activation energy for the glass transition process. Different temperature programs were also applied to monitor the curing process directly, as well as to investigate the different states of incomplete cure reached in preceding curing steps. The intention was to provide better understanding of the consequences of an interrupted autoclave curing process and to use DMA to detect the cure state achieved. With DMA, the continuation of an incomplete curing process also can be monitored. DMA measurements up to 300 °C showed, furthermore, that the final glass transition temperature was reduced by thermal degradation at high temperatures.