Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (55) (entfernen)
Schlagworte
- DSC (8)
- Elastomer (7)
- Compression set (5)
- DMA (5)
- Glass transition (5)
- Crosslinking (4)
- Dynamic mechanical analysis (4)
- Low temperature behaviour (4)
- Prepreg (4)
- Sealing material (4)
- Ultrasound (4)
- Vulcanisation (4)
- Cross-linking (3)
- Cure process (3)
- Curemeter (3)
- Dielectric parameters (3)
- EVA (3)
- Microwave methods (3)
- Prozesskontrolle (3)
- Thermoset (3)
- Ultraschall (3)
- Vitrification (3)
- Aushärtegrad (2)
- Aushärtung (2)
- Biodiesel (2)
- Carbon fibre (2)
- DMTA (2)
- Druckverformungsrest (2)
- Dynamic-mechanical analysis (2)
- Elastomere (2)
- Elastomers (2)
- Epoxy (2)
- Fuel sorption (2)
- Gelation (2)
- Impact strength (2)
- Kochversuch (2)
- Monitoring (2)
- Moulding compound (2)
- PE-HD (2)
- Phenolharz (2)
- Sensoren (2)
- Thermosets (2)
- Vulcanization (2)
- Vulkanisation (2)
- Acoustic propagation (1)
- Adhesion (1)
- Aminoharz (1)
- Atomic force microscope (1)
- Aushärtungsverlauf (1)
- Autoclave (1)
- Bakelit (1)
- Bauteilversuche (1)
- CFC (1)
- CRP (1)
- Cellular polypropylene (1)
- Charpy impact test (1)
- Component test (1)
- Composite material (1)
- Composites (1)
- Cross linked polyethylene insulation (1)
- Crystal melting (1)
- Cure (1)
- Curing (1)
- Degree of cure (1)
- Degree of curing (1)
- Desorption (1)
- Devitrification (1)
- Dichtung (1)
- Dichtungen (1)
- Dielektrik (1)
- Differential scanning calorimetry (1)
- Elastic-plastic properties (1)
- Elektroinstallationsteile (1)
- Epoxidharz (1)
- Epoxy system (1)
- Ethylene vinyl acetate (1)
- Ferroelectret (1)
- Fertigungskontrolle (1)
- Filled rubber compounds (1)
- Force-distance curves (1)
- Glass transition temperature (1)
- Glasübergang (1)
- Gütesicherung (1)
- Harnstoffformasse (1)
- Harnstoffharz (1)
- Harnstoffharze (1)
- Indentation (1)
- Injection moulding (1)
- Interdiffusion (1)
- Interphase/interface (1)
- Keramische Grünfolien (1)
- Klebfolie (1)
- Kunstharze (1)
- Low temperature (1)
- Materialparameter (1)
- Materialprüfungsamt (1)
- Mechanical variables measurement (1)
- Mechanische Prüfung (1)
- Melamine (1)
- Mould (1)
- Mould wall coupling (1)
- Nasschemische Analyse (1)
- Natural rubber (1)
- O-Ring (1)
- O-Ringe (1)
- O-ring (1)
- On-line monitoring (1)
- Online control (1)
- Ozonbeständigkeit (1)
- Ozonkonzentrationsbestimmung (1)
- Phenol (1)
- Phenolharze (1)
- Phenolic resin (1)
- Photovoltaik (1)
- Polymer (1)
- Post-curing (1)
- Process controlling (1)
- Qualitätssicherung (1)
- Relaxation (1)
- Resins (1)
- Rheology (1)
- Rtm (1)
- Schallgeschwindgkeit (1)
- Schallgeschwindigkeit (1)
- Schrumpf (1)
- Schubmodul (1)
- Seal (1)
- Sensors (1)
- Silicone rubber (1)
- Sound velocity (1)
- Spectroscopy (1)
- Spritzgießen (1)
- TMDSC (1)
- Technische Vereinigung (1)
- Temerature (1)
- Thermal analysis (1)
- Thermal properties (1)
- Thermische Analyse (1)
- Thermoset manufacturing (1)
- Tiefe Temperatur (1)
- Time-temperature superposition principle (1)
- UV-Spektroskopie (1)
- Ultrasonic (1)
- Ultrasonic monitoring (1)
- Ultrasound sensors (1)
- Verlustmodul (1)
- Vernetzung (1)
- Vernetzungsreaktion (1)
- Verzug (1)
- Viscoelastic (1)
Carbon-fibre prepregs have found widespread use in lightweight applications. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. Prepreg materials are generally pre-cured so that they have a higher molecular weight than typical resins in order to reduce resin flow, which facilitates storage and later processing properties.
The measurements were carried out using commercially available materials and follow the published DMA investigations of the same material. TMDSC was used to find the correlation between curing conditions, the degree of cure and glass transition temperature. TMDSC has the advantage over standard DSC that it enables better determination of the glass transition temperature, which is often accompanied by an exothermic curing reaction, and thus overshadowed. The influence of the amplitude of temperature modulation was tested in preliminary experiments. For non-cured material a glass transition temperature of approximately 0 °C was determined; whereas for the totally cured material it was approximately 230 °C. The changes in degree of cure, temperature of actual glass transition and post-reaction are given as a function of curing time at 180 °C. The correlation between actual glass transition temperature and degree of cure is derived.
Carbon fibre prepregs have found widespread application in lightweight constructions. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. DMA measurements under temperature conditions similar to an autoclave programme were carried out using commercially available prepreg material with a high glass transition temperature. The characteristic of the temperature programme was a dynamic heating segment at 1.5 K/min followed by a longer isothermal segment at 180 °C. The courses of the storage modulus E', loss modulus E'' and tanδ were recorded. The measuring frequency was varied between 1 Hz and 33.3 Hz. Gelation and vitrification are assigned. The influence of the measuring frequency on the time to vitrification and the correlation with DSC are discussed. The reaction does not end even after 10 h curing at 180 °C, which is interpreted as the slow cessation of the reaction caused by vitrification.
Harnstoff-Formmassen gehören zu den duroplastischen Formmassen, die im Werkzeug chemisch vernetzen und so ihre herausragende Temperaturbeständigkeit erreichen.
Im Wettbewerb mit Thermoplasten weisen Formmassen den Nachteil auf, dass die Vernetzungsreaktion eine kritische Zeit bedingt, damit die Glasübergangstemperatur soweit verschoben werden kann, dass die heißen Teile stabil und blasenfrei entformt werden können. Die Zykluszeiten sind bei Formmassen daher deutlich höher als bei Thermoplasten.
Eine Möglichkeit, die Zykluszeit zu verringern, wäre die Erhöhung der Werkzeugtemperatur, da bekanntlich eine Erhöhung der Reaktionstemperatur um 10 K zu einer Verdoppelung der Reaktionsgeschwindigkeit führt.
Allerdings wird dabei das Zeitfenster für die Entformung optimal gehärteter Teile deutlich kleiner, der Prozess anfälliger gegen Schwankungen im Prozess und in der Formmasse-Zusammensetzung. Mit einer Online-Kontrolle des Vernetzungszustands sollte es aber gelingen, den Prozess auch bei einer höheren Werkzeugtemperatur noch stabil zu beherrschen. In der vorliegenden Arbeit wird die Methode der dielektrischen Prozesskontrolle in der Fertigung von Spritzgieß-Formteilen erprobt und die Möglichkeiten einer Prozesssteuerung werden herausgearbeitet.