Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (36)
- Beitrag zu einem Tagungsband (17)
- Beitrag zu einem Sammelband (8)
- Vortrag (3)
- Posterpräsentation (2)
- Buchkapitel (1)
Sprache
- Englisch (67) (entfernen)
Schlagworte
- DSC (7)
- Ultrasound (7)
- Compression set (6)
- DMA (6)
- Dynamic mechanical analysis (6)
- Elastomer (6)
- Glass transition (6)
- Prepreg (5)
- Epoxy (4)
- Low temperature behaviour (4)
- Sealing material (4)
- Cross-linking (3)
- Crosslinking (3)
- Cure process (3)
- Curemeter (3)
- Dichtungen (3)
- Moulding compound (3)
- Thermoset (3)
- Vitrification (3)
- Vulcanisation (3)
- Vulcanization (3)
- Autoclave (2)
- Biodiesel (2)
- Carbon fibre (2)
- Curing (2)
- Dielectric parameters (2)
- Differential scanning calorimetry (2)
- Dynamic-mechanical analysis (2)
- EVA (2)
- Elastomere (2)
- Elastomers (2)
- Fuel sorption (2)
- Gelation (2)
- Impact strength (2)
- Low temperature (2)
- Microwave methods (2)
- PE-HD (2)
- Phenolic resin (2)
- Rheology (2)
- Sound velocity (2)
- Tieftemperaturverhalten (2)
- Ultraschall (2)
- Acoustic propagation (1)
- Adhesion (1)
- Atomic force microscope (1)
- Bauteilversuche (1)
- CFC (1)
- CRP (1)
- Cellular polypropylene (1)
- Charpy impact test (1)
- Component test (1)
- Composite material (1)
- Composites (1)
- Cross linked polyethylene insulation (1)
- Crystal melting (1)
- Cure monitoring (1)
- Curing behaviour (1)
- Curing degree (1)
- DMTA (1)
- Degree of cure (1)
- Degree of curing (1)
- Desorption (1)
- Devitrification (1)
- Dielectric relaxation (1)
- Differential Scanning Calorimetry (1)
- Druckverformungsrest (1)
- Dynamic Mechanical Analysis (1)
- Elastic-plastic properties (1)
- Epoxy system (1)
- Ethylene vinyl acetate (1)
- Ferroelectret (1)
- Ferroelectric polymer (1)
- Fertigungskontrolle (1)
- Filled rubber compounds (1)
- Force-distance curves (1)
- Glass transition temperature (1)
- High pressure DSC (1)
- High temperature (1)
- Incoming goods inspection (1)
- Indentation (1)
- Injection moulding (1)
- Interdiffusion (1)
- Interphase/interface (1)
- Kinetic (1)
- Leakage rate (1)
- Mechanical variables measurement (1)
- Melamine (1)
- Modulus (1)
- Monitoring (1)
- Mould (1)
- Mould wall coupling (1)
- Natural rubber (1)
- O-Ringe (1)
- O-ring (1)
- On-line monitoring (1)
- Online control (1)
- P(VDF-HFP) (1)
- Phenol (1)
- Poly(vinylidene(fluoride - hexafluoropropylene) (1)
- Polymer (1)
- Post curing (1)
- Post-curing (1)
- Process controlling (1)
- Process optimization (1)
- Prozesskontrolle (1)
- Qualitätssicherung (1)
- RTM (1)
- Reaction kinetic (1)
- Relaxation (1)
- Resin transfer moulding (1)
- Resins (1)
- Rheologie (1)
- Rtm (1)
- Rubber seals (1)
- Schallgeschwindigkeit (1)
- Seal (1)
- Sensors (1)
- Silicone rubber (1)
- Sound damping (1)
- Spectroscopy (1)
- TMDSC (1)
- Temerature (1)
- Thermal analysis (1)
- Thermal properties (1)
- Thermoset manufacturing (1)
- Thermosets (1)
- Tiefe Temperatur (1)
- Time-temperature superposition principle (1)
- Ultrasonic (1)
- Ultrasonic monitoring (1)
- Ultrasound sensors (1)
- Uniaxial stretching (1)
- Urea rsin (1)
- Vernetzungsreaktion (1)
- Viscoelastic (1)
- Vulkanisation (1)
- tan delta (1)
Eingeladener Vortrag
- nein (3)
A new method for the evaluation of the low temperature properties of rubber materials is presented. The method emulates the standardized compression set measurement, which is frequently used for sealing materials, but can be performed within a considerably shorter time. The results are compared with the standard test and found to be qualitatively the same. Slight differences are discussed on the basis of the differences in the measurement procedures. Further data evaluation is done by fitting functions to describe the material behaviour.
Partial discharges may cause damage to electrical insulation of high voltage equipment. They initiate elastic waves in the insulating material, e.g. in the stress cone of an outdoor termination. Localisation of the origin of such elastic waves can help to predict serious damaging processes in the electrical insulation. In order to measure and evaluate the wave propagation effects in typical multilayered elastomeric structures, knowledge of the material properties is required. The propagating velocity and the attenuation of longitudinal waves are important parameters. Values for these quantities found in the literature were not appropriate. Therefore, for cross-linked polyethylene (XLPE) and cured liquid silicone rubber (LSR), the longitudinal wave velocity and the attenuation were evaluated in the temperature interval from -20°C to 50°C and in the frequency range from 200 kHz to 600 kHz using a two-sample ultrasound technique. The loss factor was determined from these measured quantities. Additionally, low frequency Dynamic Mechanical Thermal Analysis (DMTA) was applied to investigate LSR and XLPE in a temperature interval between -100 and 50°C and to check qualitatively the ultrasound data.
Adhesion of amorphous polymers as a function of temperature probed with AFM force-distance curves
(2005)
Forcedisplacement curves have been obtained with a commercial atomic force microscope at different temperatures and probe rates on a thick film of poly(n-butyl methacrylate) and on two films of polystyrene with different molecular weight. In a previous publication [B. Cappella, S.K. Kaliappan, H. Sturm, Macromolecules 38 (2005)1874] the analysis of forcedisplacement curves has been focused on the stiffness and on the Young's modulus of the samples. In the present publication we consider the temperature dependence of the work of adhesion. We have obtained master curves of the work of adhesion at fixed maximum loads and, by comparing the results of the two analysis, we show that the work of adhesion follows the WilliamsLandelFerry equation with the same coefficients previously found for the Young's modulus. Furthermore, we show that the temperature dependence of the work of adhesion of the polymers is a consequence of the temperature dependence of the tipsample contact area and in the end of the temperature dependence of the stiffness and of the elasticplastic properties of the samples.
The investigation of low temperature properties of elastomeric sealing materials by means of thermo-analytical methods is a sound way to get information about the glass transition process.
The breakdown temperature of the sealing function of O-ring seals was measured in a component test setup depending on material and degree of compression.
An in depth explanation of the observed component tests behaviour is currently in preparation. It requires the results of thermo-analytical methods and measurements as the compression set (not shown here). With that, a model was developed to describe the correlation between physical material parameters and observed component behaviour.
Carbon fibre prepregs have found widespread application in lightweight constructions. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. DMA measurements under temperature conditions similar to an autoclave programme were carried out using commercially available prepreg material with a high glass transition temperature. The characteristic of the temperature programme was a dynamic heating segment at 1.5 K/min followed by a longer isothermal segment at 180 °C. The courses of the storage modulus E', loss modulus E'' and tanδ were recorded. The measuring frequency was varied between 1 Hz and 33.3 Hz. Gelation and vitrification are assigned. The influence of the measuring frequency on the time to vitrification and the correlation with DSC are discussed. The reaction does not end even after 10 h curing at 180 °C, which is interpreted as the slow cessation of the reaction caused by vitrification.
Rubbers are often used for seal applications due to their special material properties and easy use. In many applications the material is exposed to low temperatures during Operation. Therefore it is important to know the material behavior at low temperatures to determine the temperature ränge that allows a Safe Operation of the seal, e.g. in storage and transport Containers for radioactive materials.
The seal function of an elastomer is limited in temperature by the rubber-glass transition during which the material properties change from rubber-like to stiff and glass-like. For a given application this correlation is not trivial and therefore needs an in-depth investigation under consideration of the physical properties and the
application conditions.
In this work different analytical methods are used to characterize the material behavior at low temperature in the ränge of the glass-rubber-transition and are compared with the quality of Operation of a component which is here defined by the detected leakage rate.
The prospects of modern thermoanalytical methods for characterisation
of flow, curing and final mechanical behaviour of
moulding compounds were demonstrated. Using urea resin
moulding compounds from different manufacturers the possibilities
of the various techniques could be shown. With comparatively
low effort, fundamental information can be gained
before production process had been started. On this basis it is
possible to make appropriate material selection at an early
point in the process chain. On the basis of thermoanalytical
data an incoming goods inspection can be established. Also it
is easy to control the compliance with the conditions of delivery.
In some cases it could also be helpful to have stored analysis
data especially when problems appear in manufacturing
process or unexpected part damages occur
With the ultrasound measuring system it is possible to transfer
the findings from the analytical methods directly to the processes
in the mould. The application of ultrasound provides
Dynamic Mechanical Analysis in the mould. Beside quality
assurance ultrasound can also be used for process optimisation,
especially for reduction of cycle time. In an advanced form
ultrasound information can be used as a basis for improved
machine control based on material state. The ultrasound measuring
system developed by ISK Iserlohn and BAM can be
obtained from the ISK.
The method for the determination of compression set values with a Dynamic Mechanical Analysis (DMA) setup at low temperatures, which was presented previously, allows a much faster and readily automated procedure than the standardized compression set test according to ISO 815-2. This method is applied to a series of different elastomeric materials that are commonly used for sealing applications. The results of the compression set test are compared with results from thermal analysis to allow an in depth comparison of the material behaviour at low temperatures.
Furthermore, a comparison between two EPDM materials is presented. These materials show very similar properties determined by thermo analytical methods such as Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) but differ clearly in their compression set behaviour. This comparison shows the importance and value of information of the compression set test in addition to thermal analysis to judge the behaviour of sealing materials and confirms the relevance of the new compression set test method for the investigation of low temperature properties of elastomers.
The curing conditions play an important role in the quality assurance of composite products.
Especially as composite materials are widely used in high tech areas so that they are required to fulfil high quality Standards. Some problems which occur during curing, for instance undercuring, can hardly be detected using Standard NDT investigations, mainly because they are manifested only at high temperatures, particularly close to glass-rubber-transition. On-line eure monitoring has the outstanding advantage that it can monitor the material parameters even at the highest temperatures possible.
In recent years eure monitoring with ultrasonic methods has become more populär. In comparison to dielectric methods mechanical parameters are measured directly. The quantities to be measured are the velocity and the attenuation of the sound wave. On this basis the storage and loss modulus can be calculated. Depending on the form of excitation with longitudinal or transversal waves these moduli are referred to as long wave or shear modulus.
Well developed Computer based technology and sensor materials are available in the non-destructive testing (NDT) market. The measuring equipment employed a commercial NDT System, which worked computer-aided. With a special Software the demands of automatic Operation under industrial conditions was accomplished. This measurement equipment was tested on composites. Its structure, performance and some practical results will be presented in the following paper.
Ultrasound on-line NDT methods have been demonstrated as a useful tool for monitoring the curing reaction of thermosets. In order to achieve this ultrasound sensors are incorporated into compression, injection and RTM (resin transfer) mould. For many commercial products imprints or any surface markings upon the moulded product are undesirable. Due to its physical properties ultrasound has a large advantage over other techniques for similar applications. The sound wave can pass through the wall of the mould and direct contact with the moulded part is not required. In this particular case one fundamental problem is a good coupling of the sensors to the mould wall. Several mediums came into question but because of the high technical (e. g. temperature and long time stability) and practical demands, it was decided that dry (non-fluid) coupling would be the most promising candidate. A handful of coupling foils suitable also at high temperatures and for long time application under industrial conditions were tested and are presented in this paper.
In processing fibre-reinforced composites, the curing reaction can be significantly retarded if the temperature and reaction time are not optimally set. In such situations, complete curing is sometimes impossible under practically relevant conditions. It is difficult for processors to recognize or detect incomplete curing. The equilibrium glass transition temperature plays an important role in complete curing in the production process.
Cure monitoring of epoxy films by heatable in situ FTIR analysis: Correlation to composite parts
(2014)
The curing mechanism of an epoxy film containing dicyandiamide (DICY) and an epoxy formulation based on diglycidyl ether of Bisphenol A (DGEBA) polymer was studied as a function of various temperature programs. The investigation was performed in situ, using a thin film of the epoxy mixture on a silicon wafer substrate in a heatable transmission tool of a FTIR spectrometer. Based on these model-curing experiments, a major curing mechanism was proposed, taking into account the appearance, the decrease, and the development of characteristic bands at various temperatures. The conclusions of the model curing were correlated to FTIR measurements on a real, 50-mm-thick glass fiber reinforced component composite part from a technical process. It could be shown that characteristic bands that develop at curing temperatures above 150°C appear especially in the center of the thick sample. From the chemical or molecular point of view, this demonstrates the established technician's understanding that temperature control inside a large-scale fiber composite of, for example, aircraft, wind-turbine, automotive applications component is of major importance.
Carbon-fibre prepregs have found widespread use in lightweight applications. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. Prepreg materials are generally pre-cured so that they have a higher molecular weight than typical resins in order to reduce resin flow, which facilitates storage and later processing properties.
The measurements were carried out using commercially available materials and follow the published DMA investigations of the same material. TMDSC was used to find the correlation between curing conditions, the degree of cure and glass transition temperature. TMDSC has the advantage over standard DSC that it enables better determination of the glass transition temperature, which is often accompanied by an exothermic curing reaction, and thus overshadowed. The influence of the amplitude of temperature modulation was tested in preliminary experiments. For non-cured material a glass transition temperature of approximately 0 °C was determined; whereas for the totally cured material it was approximately 230 °C. The changes in degree of cure, temperature of actual glass transition and post-reaction are given as a function of curing time at 180 °C. The correlation between actual glass transition temperature and degree of cure is derived.
Epoxy composites used for high-end structural applications are typically cured under the influence of temperature and pressure causing a number of complex chemical and physical transformations. On heating a mould, temperature gradients will occur through the component which will depend largely on the thermophysical properties of the specific composite. The crosslinking reaction is exothermic leading to additional heat release, thus complicating heat transportation models. If such effects are not accounted for, it can lead to variations in resin flow, poor fibre wetting causing voiding and inhomogeneous cure, leading to shrinkage and unfavourable variations in moulded part geometry. Limited information is available for thermal models used in the manufacture of reinforced thermosets. Autoclave [1, 2] and laser or infra-red curing processes [3, 4] typically use constant values determined on fully cured parts. In this work, the variation in thermal conductivity (K) (W/(m K)), thermal diffusivity (a) (m(2)/s) and specific heat capacity at constant pressure (c(p)) (J/(g K) is determined for a carbon fibre prepreg during cure. It is the intention to improve understanding of how these parameters are related to chemical or physical transformations occurring during cure, and where estimates or shortcuts may be used for heat transfer models
The technique normally used to measure Cp during isothermal cure is Temperature Modulated - Dynamic Scanning Calorimetry TM-DSC. It is however not standardised, experimentally complicated and quite time intensive. As will be shown, Cp may also be estimated during isothermal cure just from using dynamic heating experiments on a fully cured sample. Such values are often sufficient for isothermal heat transfer models that otherwise employ a constant Cp value obtained from the fully cured epoxy. Secondly, the results from dynamic heating experiments provide a quick means, in comparison to isothermal TMDSC measurements, of estimating Cp variation during cure as well as providing a good estimate value for Cp towards the end of isothermal cure. As will be shown, such values obtained from a standardised measurement procedure are very helpful in setting up TMDSC experiments that are more sensitive to experimental error influenced by factors such as sample weight and geometry.
The DSC results illustrate that the measured heat capacity Cp for a fully cured epoxy over a temperature range are very similar to values for samples partially cured at corresponding isothermal temperatures, under the prerequisite that vitrification takes place. In such cases the primary influence on Cp is specific measurement temperature and not degree of cure. For isothermal cure temperatures investigated between 150 and 200 °C, the total change of Cp during cure is nearly constant and correlates well with values published by authors on other epoxy based systems. Taking Cp variation as constant, it is possible from just dynamic heating experiments on the cured epoxy to estimate Cp for the uncured epoxy system at specific cure temperatures. The next step would be to estimate the full Cp profile during isothermal cure, however, in such cases, the time to vitrification would also be needed as additional information.
With an extended contact and non-contact mode scanning force microscope samples with different heterogeneous electrical properties can be characterized. The contact mode method allows the determination of local electric conductivities of heterogeneous systems at the sample surfaces. An interpretation of this behaviour can be obtained in combination with other SFM modes such as topography, friction and compliance used simultaneously. The non-contact mode SFM allows to get more information about the local surface charge of heterogeneous samples. In this paper two new SFM approaches will be discussed on examples of carbon-fibre reinforced, organic and ceramic materials