Healable materials could play an important role in reducing the environmental footprint of our
modern technological society through extending the life cycles of consumer products and constructions. However, as most healing processes are carried out by heat alone, the ability to heal damage generally kills the parent material’s thermal and mechanical properties. Here we
present a dynamic covalent polymer network whose thermal healing ability can be switched ‘on’ and ‘off’ on demand by light, thereby providing local control over repair while retaining the advantageous macroscopic properties of static polymer networks. We employ a photoswitchable furan-based crosslinker, which reacts with short and mobile maleimidesubstituted poly(lauryl methacrylate) chains forming strong covalent bonds while simultaneously allowing the reversible, spatiotemporally resolved control over thermally induced de- and re-crosslinking. We reason that our system can be adapted to more complex materials and has the potential to impact applications in responsive coatings, photolithography and microfabrication.
FIB Milling and Canneling
(2007)
We have studied the anisotropic milling of Cu with respect to the milling rate and the milling topography, as well. The background is twofold: i) anisotropic milling has to be taken into account during the preparation of TEM specimens and in the manufacturing of micro parts from crystalline materials, and ii) the orientation depending milling behaviour can be used to generate topographies with specific properties with respect to, for example, adsorption, wear, and corrosion.
During focused ion beam microscopy (FIB) of crystalline materials imaging contrast and milling result are effected by orientation of the crystals with respect to the incident ion beam. This is due to the possibility of ion channeling along preferred crystal directions which effects the depth at which interaction between ions and specimen atoms takes place. As a result of channeling emission of ion induced secondary electrons (iiSE) and secondary ions (SI) as well as the sputter rate decreases.
Theoretical channeling orientations and critical angles can be calculated.
These effects have been studied quantitatively for polycrystalline recrystallized Cu as a typical model case.