The following paper focuses on the evolution of micro damage in short fibre reinforced polyamide. Therefore, tube samples are subjected to uni- and biaxial fatigue loadings. The evolution of micro damage is analysed by the non-destructive method of X-ray refraction analysis with consideration of the fibre orientation distribution. For validation of the applied micro damage models, fractographic analyses are performed.
Concluding some general results, it has been observed that the load ratio influences the quantitative dominance of micro damage, whereas occuring damage phenomena depend on the type of loading (i.e. tension and torsion). Thus, zones in the Haigh-diagram are detected, where the occurence of damage mechanisms qualitatively and quantitatively changes. This is a basis for further research regarding anisotropic damage criteria.
Fatigue life evaluation of spar cap materials by four point bending test on width-tapered specimens
(2015)
The presented research project focuses on an effective method to evaluate the fatigue strength of thick unidirectional laminates to be applied in spar caps. Therefore, a width-tapered bending specimen was developed for a four point loading set up. Static and fatigue loading was performed with the load ratio of R=-1. The complex stress state was investigated numerically with a finite element analysis. Finally, the concept was proven experimentally on specimens made of pultruded fibre rods. The fatigue behaviour of continuous tapered width by water jet cutting was compared to discrete tapering by rod-drop.
Fatigue life evaluation of spar cap materials by four point bending test on width-tapered specimensa
(2015)
The presented research project focuses on an effective method to evaluate the fatigue strength of thick unidirectional laminates to be applied in spar caps. Therefore, a width-tapered bending specimen was developed for a four point loading set up. Static and fatigue loading was performed with the load ratio of R=-1. The complex stress state was investigated numerically with a finite element analysis. Finally, the concept was proven experimentally on specimens made of pultruded fibre rods. The fatigue behaviour of continuous tapered width by water jet cutting was compared to discrete tapering by rod-drop.