Filtern
Dokumenttyp
- Zeitschriftenartikel (19)
- Beitrag zu einem Tagungsband (10)
- Vortrag (3)
Schlagworte
- Laser beam welding (19)
- Electromagnetic weld pool support (11)
- Lorentz force (9)
- Natural convection (8)
- Electromagnetic weld pool control (7)
- Hartmann effect (7)
- Marangoni stresses (5)
- Duplex stainless steel (4)
- Marangoni flow (4)
- Aluminium (2)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (3)
A multi-physics numerical model was developed to investigate the influence of a steady magnetic field aligned perpendicular to the welding direction during partial penetration high power laser beam welding of aluminium in downhand position. Three-dimensional heat transfer, fluid dynamics including phase transition and electromagnetic field partial differential equations were successfully solved with the finite element differential equation solver COMSOL Multiphysics 4.2. The implemented material model used temperature-dependent properties up to evaporation temperature. Marangoni convection in the surface region of the weld pool, natural convection due to the gravitational field and latent heat of solidliquid phase transition were taken into account. Solidification was modelled by the CarmanKozeny equation for porous media morphology. The flow pattern in the melt as well as the weld bead geometry were significantly changed by the induced Lorentz force distribution in the liquid metal. It reveals that the application of a steady magnetic field to laser beam welding with corresponding Hartmann numbers Ha2 ≈ 104 allows for a suppression of the characteristic wineglass-shape of the weld cross section caused by thermocapillary flow. The numerical results are in good agreement with experimental results obtained with welding of AlMg3 with a 16 kW disc laser. The steady magnetic field was delivered by permanent magnets mounted on both lateral sides of the weld specimen. The maximum magnetic flux density was around 500 mT. It shows, that the applied magnetic field has a predominant dissipating effect on the weld pool dynamics independently of its polarity.
Im Rahmen eines AiF-Forschungsvorhabens wurde die Beeinflussung des Schweißprozesses mittels generierter Wechselstrom-Magnetfelder (ACMagnetfelder) beim Laserstrahlschweißen von Aluminiumlegierungen untersucht. Das vorrangige Augenmerk galt hierbei der Entfernung von Poren sowie der Stabilisierung der Schweißnahtoberfläche zur Vermeidung von rauen Schweißnähten. Das Schweißen mit Einsatz des AC-Magneten erzeugte im Vergleich zu den Referenznähten deutlich flachere Schweißnähte mit reduzierter Porenanzahl, die typische Schuppenstruktur wurde unterdrückt. Das Magnetfeld bewirkte bei entsprechenden Parametern der magnetischen Flussdichte und der Frequenz eine Halbierung der Rauigkeit der Schweißnahtoberfläche. Neben der Oberflächenberuhigung wurde auch die Verteilung von Poren in der Schmelze beeinflusst. Es konnte nachgewiesen werden, dass bei einer geeigneten Auswahl der Parameter von AC-Magnetfeldern die Porositätsanteile in der Schweißnaht auf ein Zehntel gegenüber den Referenzschweißnähten reduziert werden können.-----------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
Within the framework of an AiF research project, investigations were conducted into the influences exerted on the welding process using generated alternating current (AC) magnetic fields during the laser beam welding of aluminium alloys. In this respect, attention was principally paid to removing pores and to stabilising the weld surface in order to avoid rough welds. In comparison with the reference welds, welding utilising the AC magnet produced considerably flatter welds with a reduced number of pores and the typical ripple structure was suppressed. With corresponding parameters for the magnetic flux density and the frequency, the roughness of the weld surface was halved using the magnetic field. In addition to the surface stabilisation, influences were also exerted on the distribution of pores in the molten metal. It was possible to prove that, by selecting suitable parameters for AC magnetic fields, the porosity proportions in the weld can be reduced to one tenth of those in the reference welds.
The main characteristic feature of deep penetration laser beam welding is a large temperature difference between the plasma cavity (keyhole) in the centre of the weld pool and the melting/solidification front. Large temperature gradients in the weld pool result in a very intensive thermocapillary (Marangoni) convection. The weld pool surface width becomes very large and unstable. However, an externally applied oscillating magnetic field can stabilize the surface of the melt (the Garnier-Moreau effect, 1983). In the present work this technology was used to stabilize the surface of the weld pool in partial penetration 4.4 kW Nd:YAG laser beam welding of AW-5754 alloyin PA position. The AC magnet was mounted on the laser welding head. The oscillating magnet field was oriented perpendicular to the welding direction. It was found that the AC magnet field can drastically reduce the surface roughness of welds. The analysis of the x-ray images shows a rastic reduction of porosity content in the welds. This effect can be explained as a result of electromagnetic ectification of the melt.
An oscillating (AC) magnet field was used to suppress porosity formation and to stabilize the surface of the weld pool in bead-on-plate partial penetration 4.4 kW Nd:YAG laser beam welding of AW-5754 plates in PA position. The magnet was mounted on the laser welding head. The magnet field (up to 0.4 T and 10 kHz) was oriented perpendicular the welding direction.
The analysis of the weld cross-sections and x-ray images shows a drastic reduction (up to 90%) of porosity contents in the welds. The observed effects can be explained in terms of electromagnetically (EM)
induced 'Archimedes' forces as well as the EM stirring flow in the weld pool. Moreover, usage of AC magnetic fields results in a significant reduction (up to 50%) of the surface roughness of the welds. This effect can be explained in terms of electromagnetic (EM)
contribution to the surface tension (the Garnier-Moreau effect)
The objective of this study was to investigate the influence of externally applied magnetic fields on the weld quality in laser beam welding. The optimization of the process parameters was performed using the results of computer simulations. Welding tests were performed with up to 20 kW laser beam power. It was shown that the AC magnet with 3 kW power supply allows for a prevention of the gravity drop-out for full penetration welding of 20 mm thick stainless steel plates. For partial penetration welding it was shown that an0.5 T DC magnetic field is enough for a suppression of convective flows in the weld pool. Partial penetration welding tests with 4 kW beam power showed that the application of AC magnetic fields can reduce weld porosity by a factor of 10 compared to the reference joints. The weld surface roughness was improved by 50%.
A three-dimensional turbulent steady state numerical model was used to investigate the influence of an alternating current (AC) magnetic field during high power laser beam keyhole welding of 20 mm thick stainless steel AISI 304 being modeled as an ideal non-ferromagnetic material. Three-dimensional heat transfer and fluid dynamics as well as the electromagnetic field equations were solved with the finite element package COMSOL Multiphysics 4.2 taking into account the most important physical effects of the process. Namely, the thermo-capillary (Marangoni) convection at the weld pool boundaries, natural convection due to gravity and density differences in the melt volume as well as latent heat of solidliquid phase transitions at the phase boundaries were included in the model.
It is shown that the gravity drop-out associated with the welding of thick plates due to the hydrostatic pressure can be prevented by the application of AC magnetic field between 80 mT and 135 mT for corresponding oscillation frequencies between 1 kHz and 10 kHz below the weld specimen. Experimentally, a value of the magnetic flux density of around 230 mT was found to be necessary to allow for single-pass laser beam welding without sagging or drop-out of melt for a 20 mm thick combination of austenitic stainless steel AISI 304 and ferritic construction steel S235JRC at an oscillation frequency of around 2.6 kHz.
An electromagnetic weld pool support system for 20 mm thick duplex stainless steel AISI 2205 was investigated numerically and compared to experiments. In our former publications, it was shown how an alternating current (AC) magnetic field below the process zone directed perpendicular to the welding direction can induce vertically directed Lorentz forces. These can counteract the gravitational forces and allow for a suppression of material drop-out for austenitic stainless steels and aluminum alloys. In this investigation, we additionally adopted a steady-state complex magnetic permeability model for the consideration of the magnetic hysteresis behavior due to the ferritic characteristics of the material. The model was calibrated against the Jiles–Atherton model. The material model was also successfully tested against an experimental configuration before welding with a 30 mm diameter cylinder of austenitic stainless steel sur-rounded by duplex stainless steel. Thereby, the effects of the Curie temperature on the magnetic characteristics in the vicinity of the later welding zone were simulated. The welding process was modeled with a three-dimensional turbulent steady-state model including heat transfer and fluid dy-namics as well as the electromagnetic field equations. Main physical effects, the thermo-capillary (Marangoni) convection at the weld pool boundaries, the natural convection due to gravity as well as latent heat of solid–liquid phase transitions at the phase boundaries were accounted for in the model. The feedback of the electromagnetic forces on the weld pool was described in terms of the electromagnetic-induced pressure. The finite element software COMSOL Multiphysics 4.2 was used in this investigation. It is shown that the gravity drop-out associated with the welding of 20 mm thick duplex stainless steel plates due to the hydrostatic pressure can be prevented by the application of AC magnetic fields between around 70 and 90 mT. The corresponding oscillation frequencies were between 1 and 10 kHz and the electromagnetic AC powers were between 1 and 2.3 kW. In the experiments, values of the electromagnetic AC power between 1.6 and 2.4 kW at os-cillation frequencies between 1.2 and 2.5 kHz were found to be optimal to avoid melt sagging or drop-out of melt in single pass full-penetration laser beam welding of 15 and 20 mm thick AISI 2205.
An electromagnetic weld pool support system for 20 mm thick duplex stainless steel AISI 2205 was investigated numerically and compared to experiments. In our former publications, it was shown how an AC magnetic field below the process zone directed perpendicular to the welding direction can induce vertically directed Lorentz forces. These can counteract the gravitational forces and allow for a suppression of material drop-out for austenitic stainless steels and aluminum alloys. In this investigation, we additionally adopted a steady-state complex magnetic permeability model for the consideration of the magnetic hysteresis behavior due to the ferritic characteristics of the material. The model was calibrated against the Jiles-Atherton model. The material model was also successfully tested against an experimental configuration before welding with a 30 mm diameter cylinder of austenitic stainless steel surrounded by duplex stainless steel. Thereby, the effects of the Curie temperature on the magnetic characteristics in the vicinity of the later welding zone were simulated. The welding process was modelled with a 3D turbulent steady-state model including heat transfer and fluid dynamics as well as the electromagnetic field equations. Main physical effects, the thermo-capillary (Marangoni) convection at the weld pool boundaries, the natural convection due to gravity as well as latent heat of solid–liquid phase transitions at the phase boundaries were accounted for in the model. The feedback of the electromagnetic forces on the weld pool was described in terms of the electromagneticinduced pressure. The FE software COMSOL Multiphysics 4.2 was used in this investigation. It is shown that the gravity drop-out associated with the welding of 20 mm thick duplex stainless steel plates due to the hydrostatic pressure can be prevented by the application of AC magnetic fields between around 70 mT and 90 mT. The corresponding oscillation frequencies were between 1 kHz and 10 kHz and the electromagnetic AC powers were between 1 kW and 2.3 kW. In the experiments, values of the electromagnetic AC power between 1.6 kW and 2.4 kW at oscillation frequencies between 1.2 kHz and 2.5 kHz were found to be optimal to avoid melt sagging or drop-out of melt in single pass fullpenetration laser beam welding of 15 mm and 20 mm thick AISI 2205.
A multi-physics numerical model was developed to investigate the influence of a steady magnetic field during partial penetration keyhole laser beam welding of an aluminum plate in flat position. Three-dimensional heat transfer, fluid dynamics including phase transition and electromagnetic field partial differential equations were solved with the finite element differential equation solver COMSOL Multiphysics. The magnetic field was aligned perpendicularly to the welding direction. The main objective of these simulations was to estimate the critical value of the magnetic field needed to suppress convective flows in the weld pool during high-power (up to 20 kW) laser beam welding of aluminum alloys with up to 20 mm deep weld pool. It reveals that steady magnetic fields with corresponding Hartmann numbers Ha^2 ~ 10^4 based on the half-width of the weld pool can effectively suppress convective flows in the weld pool. Moreover, the typically occurring wineglass-shape of the weld cross section caused by thermo-capillary flow is weakened.
Full penetration high power bead-on-plate laser beam welding tests of up to 20 mm thick 2205 duplex steel plates were performed in PA position. A contactless inductive electromagnetic (EM) weld pool support system was used to prevent gravity drop-out of the melt. Welding experiments with 15 mm thick plates were carried out using IPG fiber laser YLR 20000 and Yb:YAG thin disk laser TruDisk 16002. The laser power needed to achieve a full penetration was found to be 10.9 and 8.56 kW for welding velocity of 1.0 and 0.5 m min−1, respectively. Reference welds without weld pool support demonstrate excessive root sag. The optimal value of the alternating current(AC) power needed to completely compensate the sagging on the root side was found to be ≈1.6 kW for both values of the welding velocity. The same EM weld pool support system was used in welding tests with 20 mm thick plates. The laser beam power (TRUMPF Yb:YAG thin disk laser TruDisk 16002) needed to reach a full penetration for 0.5 m min−1 was found to be 13.9 kW. Full penetration welding without EM weld pool support is not possible—the surface tension cannot stop the gravity drop-out of the melt. The AC power needed to completely compensate the gravity was found to be 2 kW.
Full penetration high power bead-on-plate laser beam welding tests of up to 20 mm thick 2205 duplex steel plates were performed in PA position. A contactless inductive electromagnetic (EM) weld pool support system was used to prevent gravity drop-out of the melt. Welding experiments with 15 mm thick plates were carried out using IPG fiber laser YLR 20000 and Yb:YAG thin disk laser TruDisk 16002. The laser power needed to achieve a full penetration was found to be 10.9 and 8.56kW for welding velocity of 1.0 and 0.5 m min(-1), respectively. Reference welds without weld pool support demonstrate excessive root sag. The optimal value of the alternating current (AC) power needed to completely compensate the sagging on the root side was found to be approximate to 1.6 kW for both values of the welding velocity. The same EM weld pool support system was used in welding tests with 20 mm thick plates. The laser beam power (TRUMPF Yb:YAG thin disk laser TruDisk 16002) needed to reach a full penetration for 0.5 m min(-1) was found to be 13.9 kW. Full penetration welding without EM weld pool support is not possible-the surface tension cannot stop the gravity drop-out of the melt. The AC power needed to completely compensate the gravity was found to be 2 kW. (C) 2016 Laser Institute of America
High power laser beam welding of austenitic stainless steel with electromagnetic weld pool support
(2013)
The paper describes an experimental investigation of high power laser beam welding with an electromagnetic weld pool support for up to 20 mm thick plates made of duplex steel (AISI 2205) and mild steel (S235JR). The results of the welding tests show a successful application of this technology at ferromagnetic metals. Irregular sagging was suppressed successfully. An ac-power of less than 2 kW at oscillation frequencies between 800 Hz and 1.7 kHz is necessary for a full compasation of the hydrostatic pressure. Thus, it was demonstrated that the electromagnetic weld pool support is not only limited to non-ferromagnetic metals like austenitic steels. For future studies with duplex steel, the use of filler material has to take into account with regard to the balance of the mixed austenitic and ferritic phases.
High-power laser welding of austenitic stainless steel with electromagnetic control of weld pool
(2014)
Laser deep-penetration welding became a widely applied tool in industrial applications due to available laser power of 20 kW and more for the single-pass welding of steel plates of up to 20 mm thikness. Above a critical limit, liquid metal tends to drop out of the bead due to hydrostatic pressure. Laser welding, in contrast to electron beam welding technique, allows for an electromagnetic manipulation of fluid flow in the weld pool. AC electromagnetic system for compensation of the hydrostatic pressure by induced Lorentz forces in the melt was experimentally and numerically investigated for single-pass full-penetration welding of up to 20 mm thikness austenitic stainless steel plates of grade AISI 304. It was shown that the application of 200-234 mT magnetic fields at oscillation frequency of around 2.6 kHZ lead to a full compensation of hydrostatic forces in the melt for plate 10-20 mm thick, respectively. Coupled fluid flow, thermal and electromagnetic finite element simulations were done with different applied magnetic flux densities and oscillation frequencies calculating for the optimal magnetic field strength to avoid melt sagging in the weld pool. The simulation results point to a lower magnetic field density needed for that purpose. The reason for that can lie in the magnetic properties of the material not being totally non-ferromagnetic. 17 Ref., 1 Table, 5 Figures.
During laser beam welding of aluminum alloys an electromagnetic field may favour pore outgassing through the top oxide layer. High frequencies cause a small penetration depth and thus exert a stabilizing effect on the weld surface. The point at which the laser beam between the two magnetic poles hits the workpiece surface is crucial to the influence of the magnetic field on the weld surface roughness. Using analyzed parameters for different laser points of application cause a change in weld surface roughness could be observed. The weld surface roughness could be reduced by 50%. The outgassing effect in terms of a reduction of pores could be observed for all parameter sets investigated.
Das bislang zur Vermeidung unzulässiger Wurzelüberhöhungen beim Laserstrahlschweißen von Aluminiumlegierungen bzw. austenitischem Stahl eingesetzte Verfahren der elektromagnetischen Schmelzbadstütze konnte innerhalb der vorliegenden Untersuchung erfolgreich zur Kompensation des hydrostatischen Druckes von ferromagnetischen Stählen übertragen werden. Es wurden dabei Laserstrahlschweißversuche in PA-Position an bis zu 20 mm dickem Duplexstahl 1.4462 sowie Baustahl S235JR durchgeführt. Unter konstanten Schweißparametern wurden Durchschweißungen generiert. Dem hydrostatischen Druck wurde unter Verwendung der Technologie zur elektromagnetischen Schmelzbadunterstützung durch Variation der Oszillationsfrequenz und der AC-Leistung des Magnetsystems entgegengewirkt.
Zunächst konzentrierten sich die Versuche auf den Duplexstahl 1.4462, welcher jeweils aus 50 % Ferrit und Austenit besteht. Hierbei konnte festgestellt werden, dass zur idealen Kompensation von 15 mm bei einer Frequenz von 1,7 kHz eine AC-Leistung von 1,6 kW erforderlich ist, die Schweißnähte aber bereits bei einer AC-Leistung von ca. 0,8 kW in die Bewertungsgruppe B der DIN EN ISO 13919-1:1996-09 eingeordent werden können. Zur idealen Kompensation des hydrostatischen Druckes bei 20 mm dickem Duplexstahl war eine um 20 % höhere AC-Leistung notwendig. Im Anschluss an die Versuche mit dem Duplexstahl wurden die Untersuchungen auf bis zu 20 mm dicke Proben aus Baustahl S235JR erweitert. Für 15 mm konnten die Schweißnähte bei einer Frequenz von 1,7 kHz ab einer AC-Leistung von 1,3 kW in die Bewertungsgruppe B eingeordnet werden. Zur idealen Kompensation von 20 mm dickem Baustahl war eine AC-Leistung von 1,6 kW bei einer Frequenz von 636 Hz nötig. Mit steigender AC-Leistung konnte in allen Versuchsreihen eine sukzessive Verringerung
der Wurzelüberhöhung demonstriert werden.