Recently three of the authors of this paper presented analytical solutions for reference loads of plate geometries with semi-elliptical surface cracks subjected to tension, bending, combined tension-bending and biaxial tension. These solutions were shown to provide more accurate crack driving force estimates than the conventional limit load solutions available in the literature, and the method behind them allowed for a wider application range. Within the present paper a methodology for the fracture analysis of thick-wall pressurized pipes using the R6 assessment method and considering both, biaxial and combined tension-bending loading is developed and validated. The analyses are carried out analytically, and the comparison between the predicted critical loads and experimental burst test failure loads shows satisfying agreement, this way demonstrating the potential of the proposed method.
In a number of previous papers, the authors have proposed a model for fracture mechanics based prediction of the S-N characteristics of metallic components with large microstructural defects. Here, an extension to materials that do not show large defects onto the fracture surfaces is provided. In such cases, an approach based on a so-called cyclic R-curve analysis is proposed for the determination of the initial flaw size, which has to be used in the calculation of fatigue crack propagation. The principle is explained and demonstrated by a first application to a welded joint.
Although fatigue crack propagation and fracture cause a large part of failure events in industrial practice, fracture mechanics in failure analysis seems to be still a side issue. Starting from an introduction into important basic questions of failure analysis and fracture mechanics, the authors specify what kind of questions in failure analysis can be effectively solved by fracture mechanics (and which can't). They illustrate their discussion with a number of 13 case studies from the literature. Much more pronounced than in the design stage the benefit of fracture mechanics in failure analysis depends on its accuracy. This is limited by both, intrinsic factors of the method and the availability and quality of the input information. The authors discuss the various aspects and provide the reader with some background information which, as they believe, will be helpful for better understanding the prospects and limitations of fracture mechanics in failure analysis and the conditions of its application.