Heterogeneous, gradual or structured morphology of fire residues plays an important role in fire retardancy of polymers. A scanning electron microscope with an attached energy dispersive X-ray spectrometer (SEM/EDX) is highlighted as a powerful tool for the advanced characterization of such complex fire residues, since it offers high resolution in combination with both good depth of field and analysis of chemical composition. Two examples are presented: First, comprehensive SEM/EDX investigation on a complex structured fire residue of glass fibre reinforced polyamide 6,6 (PA 66-GF) flame retarded by diethylaluminium phosphinate, melamine polyphosphate and some zinc borate. A multilayered surface crust (thickness ~ 24 µm) covers a rather hollow area stabilized by GF glued together. The resulting efficient thermal insulation results in self-extinguishing before pyrolysis is completed, even under forced-flaming combustion. Second, sophisticated, quasi online SEM/EDX imaging of the formation of residual protection layer in layered silicate epoxy resin nanocomposites (LSEC). Burning specimens were quenched in liquid nitrogen for subsequent analyses. Different zones were distinguished in the condensed phase characterized by distinct processes such as melting and ablation of organic material, as well as agglomeration, depletion, exfoliation and reorientation of the LS.
Combinations of different common flame retardants in wood–plastic composites (WPCs) are tested to identify synergistic or antagonistic effects with the goal of improving the fire performance of WPCs. Flame retardants investigated are expandable graphite (EG), ammonium polyphosphate (APP), and red phosphorus (RP) and combinations of two of them are used. The fire behavior is studied by cone calorimetric measurements. Additional thermogravimetry is used for further investigations. The fire tests show that EG has the highest potential for flame retardancy, but due to its expansion it cracks the formed residue layer. Combinations of EG with RP or with high amounts of APP are able to suppress this cracking.
Flame retarded wood-plastic composites (WPCs) should allow safe application in areas of fire risk. Halogen-free flame retardants can contain high amounts of nitrogen, phosphorus or sulphur, which may serve as nutrition source for wood degrading fungi and accelerate wood decay. Therefore, the material resistance of WPCs with each of four flame retardants against both fire or fungal decay was examined in comparison to WPC without flame retardant. Expandable graphite showed the best performance against fire in cone calorimetry and radiant panel testing. Two ammonium polyphosphates and a third nitrogen-containing flame retardant were not as effective. Contrary to the possibility that flame retardants might enhance fungal decay of WPC, the opposite effect occurred in case of the wood-degrading fungi Trametes versicolor and Coniophora puteana according to determination of mass loss and decrease of bending modulus of elasticity. Only the surface mould Alternaria alternata slightly increased the degradation of WPCs with nitrogen-containing flame retardants compared to WPC without flame retardant according to mass loss data and FTIR-ATR analyses. Finally, WPC including expandable graphite as flame retardant was effective against both fire and fungal decay.
In this study, we investigated the basic knowledge necessary to develop flame-retarded woodplastic composite (WPC) materials by focusing on decking boards. Therefore, the respective effects of geometry, material composition, and moisture were studied by performing cone calorimetric measurements. Using hollow-shaped geometries removes combustible material and reduces the fire load but simultaneously increases fire propagation. The best results were achieved by using high-wood contents. The addition of talc can reduce the intensity of burning. Moisture also has a positive effect on burning behavior. Apart from the well-known mechanism of water, a change was observed in the resultant residue.
The reactivity of the flame retardant and its decomposition temperature control the condensed-phase action in bisphenol A polycarbonate/acrylonitrile–butadiene–styrene/polytetrafluoroethylene (PC/ABSPTFE) blends. Thus, to increase charring in the condensed phase of PC/ABSPTFE + aryl phosphate, two halogen-free flame retardants were synthesized: 3,3,5-trimethylcyclohexylbisphenol bis(diphenyl phosphate) (TMC-BDP) and bisphenol A bis(diethyl phosphate) (BEP). Their performance is compared to bisphenol A bis(diphenyl phosphate) (BDP) in PC/ABSPTFE blend. The comprehensive study was carried out using thermogravimetry (TG); TG coupled with Fourier transform infrared spectrometer (TG-FTIR); the Underwriters Laboratory burning chamber (UL 94); limiting oxygen index (LOI); cone calorimeter at different irradiations; tensile, bending and heat distortion temperature tests; as well as rheological studies and differential scanning calorimeter (DSC). With respect to pyrolysis, TMC-BDP works as well as BDP in the PC/ABSPTFE blend by enhancing the cross-linking of PC, whereas BEP shows worse performance because it prefers cross-linking with itself rather than with PC. As to its fire behavior, PC/ABSPTFE + TMC-BDP presents results very similar to PC/ABSPTFE + BDP; the blend PC/ABSPTFE + BEP shows lower flame inhibition and higher total heat evolved (THE). The UL 94 for the materials with TMC-BDP and BDP improved from HB to V0 for specimens of 3.2 mm thickness compared to PC/ABSPTFE and PC/ABSPTFE + BEP; the LOI increased from around 24% up to around 28%, respectively. BEP works as the strongest plasticizer in PC/ABSPTFE, whereas the blends with TMC-BDP and BDP present the same rheological properties. PC/ABSPTFE + TMC-BDP exhibits the best mechanical properties among all flame-retarded blends.
A new flame retardant based on an ammonium phosphonate is studied with respect to its thermal decomposition and its mode of action in wood-plastic composites (WPCs). The measurements are carried out by means of fire tests (cone calorimeter) and pyrolysis investigations (thermogravimetry, infrared spectroscopy). The flame retardant acts mainly in the condensed phase by increasing the amount of residue formed by the wood part in the WPC. Additional flame dilution is achieved by the release of water, ammonia and carbon dioxide during the decomposition of the flame retardant.