Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (85)
- Vortrag (67)
- Beitrag zu einem Sammelband (12)
- Beitrag zu einem Tagungsband (11)
- Posterpräsentation (4)
- Buchkapitel (1)
- Dissertation (1)
- Sonstiges (1)
Schlagworte
- Mikroplastik (32)
- Microplastics (22)
- Analytik (15)
- TED-GC-MS (14)
- Fire retardancy (12)
- Microplastic (12)
- Flame retardancy (9)
- Analysis (8)
- Pyrolysis (8)
- Flame retardance (7)
Organisationseinheit der BAM
- 6 Materialchemie (47)
- 6.6 Physik und chemische Analytik der Polymere (47)
- 1 Analytische Chemie; Referenzmaterialien (8)
- 5 Werkstofftechnik (6)
- 5.3 Polymere Verbundwerkstoffe (6)
- 1.4 Prozessanalytik (4)
- 1.7 Organische Spuren- und Lebensmittelanalytik (4)
- 4 Material und Umwelt (2)
- 4.3 Schadstofftransfer und Umwelttechnologien (2)
- 7 Bauwerkssicherheit (2)
Paper des Monats
- ja (2)
Eingeladener Vortrag
- nein (67)
The pyrolysis and the flame retardancy of poly(butylene terephthalate) (PBT) containing aluminum diethylphosphinate (AlPi) and nanometric Fe2O3 were investigated using thermal analysis, evolved gas analysis (Thermogravimetry-FTIR), flammability tests (LOI, UL 94), cone calorimeter measurements and chemical analysis of residue (FTIR). AlPi mainly acts as a flame inhibitor in the gas phase, through the release of diethylphosphinic acid. A small amount of Fe2O3 in PBT promotes the formation of a carbonaceous char in the condensed phase. The combination of 5 and 8 wt% AlPi, respectively, with 2 wt% metal oxides achieves V-0 classification in the UL 94 test thanks to complementary action mechanisms. Using PBT/metal oxide nanocomposites shows a significant increase in the flame retardancy efficiency of AlPi in PBT and thus opens the route to surprisingly sufficient additive contents as low as 7 wt%.
A comprehensive characterization of the thermal and the fire behaviour is presented for polypropylene (PP) flax compounds containing ammonium polyphosphate (APP) and expandable graphite as fire retardants. Thermogravimetry coupled with an evolved gas analysis (TG-FTIR) was performed to ensure a significant thermal analysis. The fire response under forced flaming conditions was studied using a cone calorimeter. The external heat flux was varied between 30 and 70 kW m-2 so that the results could be evaluated for different fire scenarios and tests. Different flammability tests (UL 94, limiting oxygen index, glow wire test, GMI 60261) were performed and the results compared with the cone calorimeter data. The different char forming mechanisms are described and the resulting fire retardancy is classified. The successful and ecological friendly fire retardancy is a technological breakthrough for PP/flax biocomposites.
The thermal decomposition and the fire behavior of glass fiber reinforced polyamide 66 (PA-66) and high impact polystyrene (HIPS) containing red phosphorus (P4) were investigated. For glass fiber reinforced PA-66, P4 promotes char formation in the condensed phase. Barrier effects and the reduction of combustible volatiles were identified as fire retardancy mechanisms. For HIPS, P4 acts in the gas phase, mainly trapping radicals. The heat release per mass loss polymer is reduced due to an incomplete combustion.
The fire retardancy mechanism of aluminium diethyl phosphinate (AlPi) and AlPi in combination with melamine polyphosphate (MPP) was investigated in glass-fibre reinforced polyamide 6 (PA6/GF) by analysing the pyrolysis, flammability and fire behaviour. AlPi in PA6/GF-AlPi partly vaporises as AlPi and partly decomposes to volatile diethylphosphinic acid (subsequently called phosphinic acid) and aluminium phosphate residue. In fire a predominant gas-phase action was observed, but the material did not reach a V-0 classification for the moderate additive content used. For the combination of both AlPi and MPP in PA6/GF-AlPi-MPP a synergistic effect occurred, because of the reaction of MPP with AlPi. Aluminium phosphate is formed in the residue and melamine and phosphinic acid are released in the gas phase. The aluminium phosphate acts as a barrier for fuel and heat transport, whereas the melamine release results in fuel dilution and the phosphinic acid formation in flame inhibition. The higher amount of aluminium phosphate in PA6/GF-AlPi-MPP stabilised the residue in flammability tests in comparison to PA6/GF-AlPi, so that this material achieved a V-0 classification in the UL 94 test.